CN104817849B - A kind of inorganic modified Colophonium and preparation method thereof - Google Patents
A kind of inorganic modified Colophonium and preparation method thereof Download PDFInfo
- Publication number
- CN104817849B CN104817849B CN201510228986.2A CN201510228986A CN104817849B CN 104817849 B CN104817849 B CN 104817849B CN 201510228986 A CN201510228986 A CN 201510228986A CN 104817849 B CN104817849 B CN 104817849B
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic modified
- mesh
- albite
- colophonium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of inorganic modified Colophonium and preparation method thereof, this inorganic modified Colophonium is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite 5.5～15.5 parts, albite 3.5～10.5 parts, silica white 4～8 parts, microcrystalline Cellulose 1～2 parts, triethanolamine 0.5～1 part, auxiliary agent 2～4 parts；Described auxiliary agent is Iran's rubber oil tapped oil or furfural extract oil.The inorganic modified Colophonium that the present invention relates to not only temperature control effect is notable, and cost is relatively low, technique simple, easy construction.
Description
Technical field
The invention belongs to pavement material technical field, be specifically related to a kind of inorganic modified Colophonium and preparation method thereof.
Background technology
Rut is the important disease that bituminous paving exists, and studies have found that, high temperature is the most direct inducement that rut produces,
High temperature makes the rheological property of Colophonium convert to plasticity from viscoelasticity, and stiffness modulus declines to a great extent, and its non-deformability drastically reduces,
Serious rut just occurs under the effect of vehicular load.At present, when solving the rut problem of bituminous paving, mainly take
Improving the technical measures of stability at high temperature of asphalt mixture, i.e. by asphalt modification being improved the high-temperature behavior of Colophonium, or using
Extruded aggregate aggregate grading etc. improves the rutting resistance of asphalt.Engineering practice proves the application of these technology also
Can not fundamentally solve rut problem.
Summary of the invention
The technical problem to be solved is for above-mentioned the deficiencies in the prior art, it is provided that a kind of inorganic modified Colophonium and
Its preparation method.This inorganic modified Colophonium with boracite and albite as primary raw material, make use of albite carrier function and
The hot-cast socket of boracite and thermal balance effect, under the carrier function of albite, the road surface Nei Ji that the factors such as solar radiation are caused
Heat build-up amount is diffused, and boracite utilizes bigger specific surface area and the heat comprehensive engagement of self, is absorbing Colophonium coagulation
Under conditions of soil heat, by the hot-cast socket performance of self, it is achieved the output of heat, thus reduce the internal total amount of heat of Colophonium,
Realize the cooling effect to bituminous paving, the notable high temperature rut disease alleviating bituminous paving；Meanwhile, in the winter time under low temperature condition,
Albite by the concave/convex-shaped structure of self, can change the specific heat capacity of asphalt material, hinders heat to scatter and disappear, meanwhile, and boracite
Then utilize the thermal balance of self, it is achieved the equivalent of heat is kept, thus reaches comprehensive heat accumulation purpose；Silica white can change
The high-temperature behavior of kind Colophonium；Microcrystalline Cellulose can improve the cryogenic property of Colophonium；Triethanolamine and auxiliary agent can the side's of enhancing boron
The compatibility between stone and albite and Colophonium.Temperature control effect of the present invention is notable, and can improve the pavement performance of Colophonium, with
Shi Chengben is relatively low, technique is simple, easy construction.
The technical solution used in the present invention is:
A kind of inorganic modified Colophonium, this inorganic modified Colophonium is become by the mixed raw material of following weight portion: basic asphalt 100 parts,
Boracite 5.5～15.5 parts, albite 3.5～10.5 parts, silica white 4～8 parts, microcrystalline Cellulose 1～2 parts, three second
Hydramine 0.5～1 part, auxiliary agent 2～4 parts；Described auxiliary agent is Iran's rubber oil tapped oil or furfural extract oil.
Preferably, the parts by weight of described raw material are: basic asphalt 100 parts, boracite 9.5～13.5 parts, albite
5.5～10.5 parts, silica white 6～8 parts, microcrystalline Cellulose 1.5～2 parts, triethanolamine 0.5～1 part, auxiliary agent 3～4 parts.
It is highly preferred that the parts by weight of described raw material are: basic asphalt 100 parts, boracite 10 parts, albite 8 parts,
Silica white 6 parts, microcrystalline Cellulose 1.5 parts, triethanolamine 1 part, auxiliary agent 3 parts.
Described basic asphalt is matrix pitch, SBS modified pitch, SBR modified pitch, rubber modified asphalt one therein.
Preferably, described boracite is chambersite, and fineness is 100 mesh, 300 mesh, 500 mesh or 1000 mesh.
Preferably, described albite is albite in powder, and fineness is 100 mesh, 300 mesh, 500 mesh or 1000 mesh.
Preferably, described silica white is column layer chromatography silicone rubber powder or tlc silica gel powder, and fineness is 100～400 mesh.
Preferably, described microcrystalline Cellulose is the microcrystalline Cellulose of content of cellulose >=80%.
Preferably, the purity of described triethanolamine to reach more than 80%.
Described weight portion can be gram, two, jin, the weight metering unit such as kilogram, ton.
Present invention also offers the preparation method of above-mentioned inorganic modified Colophonium, comprise the following steps: basic asphalt is heated to
120 DEG C～160 DEG C, then first basic asphalt after heating adds triethanolamine and auxiliary agent, the side's of being stirring evenly and then adding into boron
Stone, albite, silica white and microcrystalline Cellulose；High-speed shearing machine is used to be sheared by the mixture obtained under 1000r/min
10 minutes, then high speed shear 30 minutes under 4000r/min～5000r/min, obtain this inorganic modified Colophonium.
The present invention compared with prior art has the advantage that
1, boracite and albite are applied in road engineering at home and abroad still belong to the first time by the present invention, the most not
See relevant report.
2, the inorganic modified Colophonium of the present invention is with boracite and albite as primary raw material, the Appropriate application carrier of albite
Act on the hot-cast socket with boracite and thermal balance effect.Under the carrier function of albite, the road that the factors such as solar radiation are caused
Gather heat in face to be diffused, and boracite utilizes bigger specific surface area and the heat comprehensive engagement of self, absorb drip
Under conditions of blue or green concrete heat, by the hot-cast socket performance of self, it is achieved the output of heat, thus it is internal total to reduce Colophonium
Heat, it is achieved the cooling effect to bituminous paving, the notable high temperature rut disease alleviating bituminous paving；Meanwhile, low temperature in the winter time
In the case of, albite by the concave/convex-shaped structure of self, can change the specific heat capacity of asphalt material, hinders heat to scatter and disappear, with
Time, boracite then utilizes the thermal balance of self, it is achieved keeps the equivalent of heat, thus reaches comprehensive heat accumulation purpose.This
The bright inorganic modified Colophonium related to not only temperature control effect is notable, and cost is relatively low, technique simple, easy construction.
Detailed description of the invention
Below by embodiment, technical scheme is described in further detail, but does not limit the protection model of the present invention
Enclose.
Embodiment 1
A kind of inorganic modified Colophonium, is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite 5.5 parts,
Albite 3.5 parts, silica white 4 parts, microcrystalline Cellulose 1 part, triethanolamine 0.5 part, auxiliary agent 2 parts；Described auxiliary agent is
Iran's rubber oil tapped oil.Described basic asphalt is shell 90# matrix pitch；Described boracite is chambersite, and fineness is
100 mesh；Described albite is albite in powder, and fineness is 100 mesh；Described silica white is column layer chromatography silicone rubber powder, and fineness is
100～400 mesh；Described microcrystalline Cellulose is the microcrystalline Cellulose of content of cellulose >=80%；The purity of described triethanolamine to reach
To more than 80%.
The preparation method of the inorganic modified Colophonium of the present embodiment is: basic asphalt is heated to 120 DEG C, then first after heating
Basic asphalt adds triethanolamine and auxiliary agent, is stirring evenly and then adding into boracite, albite, silica white and microcrystalline Cellulose；
High-speed shearing machine is used to be sheared 10 minutes by the mixture obtained under 1000r/min, then high speed shear under 4000r/min
30 minutes, obtain this inorganic modified Colophonium.
Embodiment 2
The inorganic modified Colophonium of the present embodiment, is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite
10.5 parts, albite 6.5 parts, silica white 6 parts, microcrystalline Cellulose 1.5 parts, triethanolamine 0.5 part, auxiliary agent 3 parts；
Described auxiliary agent is furfural extract oil.Described basic asphalt is shell 90# matrix pitch；Described boracite is chambersite, fineness
It is 300 mesh；Described albite is albite in powder, and fineness is 100 mesh；Described silica white is column layer chromatography silicone rubber powder, fineness
It is 100～400 mesh；
The preparation method of the inorganic modified Colophonium of the present embodiment is: basic asphalt is heated to 140 DEG C, then first after heating
Basic asphalt adds triethanolamine and auxiliary agent, is stirring evenly and then adding into boracite, albite, silica white and microcrystalline Cellulose；
High-speed shearing machine is used to be sheared 10 minutes by the mixture obtained under 1000r/min, then high speed shear under 4000r/min
30 minutes, obtain this inorganic modified Colophonium.
Embodiment 3
The inorganic modified Colophonium of the present embodiment, is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite
15.5 parts, albite 10.5 parts, silica white 8 parts, microcrystalline Cellulose 2 parts, triethanolamine 1 part, auxiliary agent 4 parts；Described
Auxiliary agent is Iran's rubber oil tapped oil.Described basic asphalt is shell 90# matrix pitch；Described boracite is chambersite, carefully
Degree is 500 mesh；Described albite is albite in powder, and fineness is 300 mesh；Described silica white is column layer chromatography silicone rubber powder, carefully
Degree is 100～400 mesh；
The preparation method of the inorganic modified Colophonium of the present embodiment is: basic asphalt is heated to 160 DEG C, then first after heating
Basic asphalt adds triethanolamine and auxiliary agent, is stirring evenly and then adding into boracite, albite, silica white and microcrystalline Cellulose；
High-speed shearing machine is used to be sheared 10 minutes by the mixture obtained under 1000r/min, then high speed shear under 4000r/min
30 minutes, obtain this inorganic modified Colophonium.
Embodiment 4
The inorganic modified Colophonium of the present embodiment, is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite
10 parts, albite 8 parts, silica white 6 parts, microcrystalline Cellulose 1.5 parts, triethanolamine 1 part, auxiliary agent 3 parts；Described help
Agent is furfural extract oil.Described basic asphalt is shell 90# matrix pitch；Described boracite is chambersite, and fineness is 1000
Mesh；Described albite is albite in powder, and fineness is 500 mesh；Described silica white is tlc silica gel powder, fineness be 100～
400 mesh；
The preparation method of the inorganic modified Colophonium of the present embodiment is: basic asphalt is heated to 120 DEG C, then first after heating
Basic asphalt adds triethanolamine and auxiliary agent, is stirring evenly and then adding into boracite, albite, silica white and microcrystalline Cellulose；
High-speed shearing machine is used to be sheared 10 minutes by the mixture obtained under 1000r/min, then high speed shear under 5000r/min
30 minutes, obtain this inorganic modified Colophonium.
Embodiment 5
The inorganic modified Colophonium of the present embodiment, is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite
15.5 parts, albite 10.5 parts, silica white 4 parts, microcrystalline Cellulose 1 part, triethanolamine 0.5 part, auxiliary agent 2 parts；Institute
State auxiliary agent for Iran's rubber oil tapped oil.Described basic asphalt is shell 90# matrix pitch；Described boracite is chambersite,
Fineness is 1000 mesh；Described albite is albite in powder, and fineness is 1000 mesh；Described silica white is tlc silica gel powder,
Fineness is 100～400 mesh；
The preparation method of the inorganic modified Colophonium of the present embodiment is: basic asphalt is heated to 160 DEG C, then first after heating
Basic asphalt adds triethanolamine and auxiliary agent, is stirring evenly and then adding into boracite, albite, silica white and microcrystalline Cellulose；
High-speed shearing machine is used to be sheared 10 minutes by the mixture obtained under 1000r/min, then high speed shear under 5000r/min
30 minutes, obtain this inorganic modified Colophonium.
Embodiment 6
The inorganic modified Colophonium of the present embodiment, is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite
10.5 parts, albite 7 parts, silica white 4 parts, microcrystalline Cellulose 1 part, triethanolamine 0.5 part, auxiliary agent 2 parts；Described
Auxiliary agent is Iran's rubber oil tapped oil.Described basic asphalt is SBS modified pitch, and described boracite is chambersite, fineness
It is 1000 mesh；Described albite is albite in powder, and fineness is 1000 mesh；Described silica white is tlc silica gel powder, carefully
Degree is 100～400 mesh；
The preparation method of the inorganic modified Colophonium of the present embodiment is: basic asphalt is heated to 160 DEG C, then first after heating
Basic asphalt adds triethanolamine and auxiliary agent, is stirring evenly and then adding into boracite, albite, silica white and microcrystalline Cellulose；
High-speed shearing machine is used to be sheared 10 minutes by the mixture obtained under 1000r/min, then high speed shear under 5000r/min
30 minutes, obtain this inorganic modified Colophonium.
Embodiment 7
The inorganic modified Colophonium of the present embodiment, is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite
10.5 parts, albite 7 parts, silica white 4 parts, microcrystalline Cellulose 1 part, triethanolamine 0.5 part, auxiliary agent 2 parts；Described
Auxiliary agent is Iran's rubber oil tapped oil.Described basic asphalt is SBR modified pitch, and described boracite is chambersite, fineness
It is 1000 mesh；Described albite is albite in powder, and fineness is 1000 mesh；Described silica white is tlc silica gel powder, carefully
Degree is 100～400 mesh；
The preparation method of the inorganic modified Colophonium of the present embodiment is: basic asphalt is heated to 160 DEG C, then first after heating
Basic asphalt adds triethanolamine and auxiliary agent, is stirring evenly and then adding into boracite, albite, silica white and microcrystalline Cellulose；
High-speed shearing machine is used to be sheared 10 minutes by the mixture obtained under 1000r/min, then high speed shear under 5000r/min
30 minutes, obtain this inorganic modified Colophonium.
Embodiment 8
The inorganic modified Colophonium of the present embodiment, is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite
10.5 parts, albite 7 parts, silica white 4 parts, microcrystalline Cellulose 1 part, triethanolamine 0.5 part, auxiliary agent 2 parts；Described
Auxiliary agent is Iran's rubber oil tapped oil.Described basic asphalt is rubber modified asphalt, and described boracite is chambersite, fineness
It is 1000 mesh；Described albite is albite in powder, and fineness is 1000 mesh；Described silica white is tlc silica gel powder, carefully
Degree is 100～400 mesh；
The preparation method of the inorganic modified Colophonium of the present embodiment is: basic asphalt is heated to 160 DEG C, then first after heating
Basic asphalt adds triethanolamine and auxiliary agent, is stirring evenly and then adding into boracite, albite, silica white and microcrystalline Cellulose；
High-speed shearing machine is used to be sheared 10 minutes by the mixture obtained under 1000r/min, then high speed shear under 5000r/min
30 minutes, obtain this inorganic modified Colophonium.
Its indices of inorganic modified Colophonium that embodiment 1-8 prepares see table shown in 1.
Table 1 embodiment 1-8 inorganic modified Colophonium properties
Remarks: temperature control performance test uses the inorganic modified Colophonium of embodiment to prepare corresponding rut plate test specimen and tests.
As can be seen from the above table, the inorganic modified penetration of bitumens of the present invention, softening point and ductility is utilized all to reach road stone
The requirement that oil asphalt specifies, and the pavement performance of Colophonium can be improved, the temperature of asphaltic road-mix surface course can also be controlled simultaneously.
The above, be only presently preferred embodiments of the present invention, and the present invention not does any restriction, every according to inventive technique essence
Any simple modification, change and the equivalent structure change being made above example, all still falls within technical solution of the present invention
In protection domain.
Claims (10)
1. an inorganic modified Colophonium, it is characterized in that: this inorganic modified Colophonium is become by the mixed raw material of following weight portion: basic asphalt 100 parts, boracite 5.5～15.5 parts, albite 3.5～10.5 parts, silica white 4～8 parts, microcrystalline Cellulose 1～2 parts, triethanolamine 0.5～1 part, auxiliary agent 2～4 parts；Described auxiliary agent is Iran's rubber oil tapped oil or furfural extract oil.
Inorganic modified Colophonium the most according to claim 1, it is characterised in that: the parts by weight of described raw material are: basic asphalt 100 parts, boracite 9.5～13.5 parts, albite 5.5～10.5 parts, silica white 6～8 parts, microcrystalline Cellulose 1.5～2 parts, triethanolamine 0.5～1 part, auxiliary agent 3～4 parts.
Inorganic modified Colophonium the most according to claim 2, it is characterised in that: the parts by weight of described raw material are: basic asphalt 100 parts, boracite 10 parts, albite 8 parts, silica white 6 parts, microcrystalline Cellulose 1.5 parts, triethanolamine 1 part, auxiliary agent 3 parts.
4. according to the inorganic modified Colophonium described in any one of claim 1-3, it is characterised in that: described basic asphalt is matrix pitch, SBS modified pitch, rubber modified asphalt one therein.
Inorganic modified Colophonium the most according to claim 4, it is characterised in that: described basic asphalt is matrix pitch, SBS modified pitch, SBR modified pitch one therein.
6. according to the inorganic modified Colophonium described in any one of claim 1-3, it is characterised in that: described boracite is chambersite, and fineness is 100 mesh, 300 mesh, 500 mesh or 1000 mesh.
7. according to the inorganic modified Colophonium described in any one of claim 1-3, it is characterised in that: described albite is albite in powder, and fineness is 100 mesh, 300 mesh, 500 mesh or 1000 mesh.
8. according to the inorganic modified Colophonium described in any one of claim 1-3, it is characterised in that: described silica white is column layer chromatography silicone rubber powder or tlc silica gel powder, and fineness is 100～400 mesh.
9. according to the inorganic modified Colophonium described in any one of claim 1-3, it is characterised in that: described microcrystalline Cellulose is the microcrystalline Cellulose of content of cellulose >=80%.
10. the preparation method of inorganic modified Colophonium described in any one of claim 1-9, it is characterized in that: comprise the following steps: basic asphalt is heated to 120 DEG C～160 DEG C, then first basic asphalt after heating adds triethanolamine and auxiliary agent, be stirring evenly and then adding into boracite, albite, silica white and microcrystalline Cellulose；High-speed shearing machine is used to be sheared 10 minutes by the mixture obtained under 1000r/min, then high speed shear 30 minutes under 4000r/min～5000r/min, obtain this inorganic modified Colophonium.