CN104805964A - Composite metal waterproof, heat insulation and silencing coil - Google Patents
Composite metal waterproof, heat insulation and silencing coil Download PDFInfo
- Publication number
- CN104805964A CN104805964A CN201510193380.XA CN201510193380A CN104805964A CN 104805964 A CN104805964 A CN 104805964A CN 201510193380 A CN201510193380 A CN 201510193380A CN 104805964 A CN104805964 A CN 104805964A
- Authority
- CN
- China
- Prior art keywords
- coiled material
- heat
- metal
- waterproof
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a composite metal waterproof, heat insulation and silencing coil, in particular to a metal coil with waterproof, heat insulation and silencing effects. The metal coil is manufactured by the following steps of 1, selecting a modified asphalt with softening point of 60-70 DEG C, putting into a melting furnace, and melting into liquid asphalt; 2, coating the melted liquid asphalt onto a single surface layer of the metal coil, and uniformly and flatly scraping the coating layer by a scraping plate, with the asphalt coating thickness of 1-1.5cm; 3, using a smoke suction and heat radiating air pipe to radiate the heat of the coating asphalt to 40 DEG C, coating and adhering a glass fiber net onto the asphalt layer, and attaching and coating an aluminum foil or a tin foil onto the surface of the asphalt layer; 4, densely flattening the whole attaching layer by traction and rolling through a rolling shaft; 5, coiling the rolled finished coil into the coil, so as to form the composite metal waterproof, heat insulation and silencing coil. The metal coil has the advantages that the metal coil is used for manufacturing rain sheds, composite steel tiles and various rainproof tops; the waterproof and heat insulation effects are realized, the sound of water dripping is avoided, and the service life of a metal plate is prolonged.
Description
Technical field
The present invention relates to a kind of metal coiled material, specifically the quiet coiled material of a kind of composition metal waterproof and heat-insulating.
Background technology
A lot of builder's temporary shed and awning now, metal coiled material generally can be adopted to fend off rain as paulin, but due to common metal coiled material easy-to-rust after suffering rainwater, long-time use cannot be guaranteed at all, and when raining, raindrop drops on coiled material also can send the sound, and the drip sound in blocks at night directly affects rest, and single metal coiled material is also undesirable in heat insulation.
Summary of the invention
The object of the present invention is to provide the quiet coiled material of a kind of composition metal waterproof and heat-insulating, there is the effect of waterproof, heat insulation, quiet and durable anti-corrosion.
Present invention resides in metal coiled material surface smear pitch, the technical scheme adopted is: the metal coiled material with waterproof and heat-insulating muting function, makes as follows:
Step 1, the ameliorative pitch selecting softening point to be 60 ~ 70 DEG C, put into melting furnace and be molten into liquid bitumen;
Step 2, the liquid bitumen after fusing is spread upon the single surface course of metal coiled material, while smearing, strike off evenly with scraper plate by smear layer, its thickness smearing pitch is 1 ~ 1.5mm;
Step 3, employing smoking heat radiating air duct make to smear bitumen layer and dispel the heat after 40 DEG C, are posted in bitumen layer by glass fiber mesh, then are covered in the surface of bitumen layer with aluminium platinum or tin platinum;
Step 4, the entirety after pasting rolled by traction and roller bearing to make it paste layer closely smooth;
Step 5, be composition metal waterproof, heat insulation quiet coiled material by wound into a roll for the coiled material finished product after above-mentioned rolling.
In technique scheme: described metal coiled material is galvanized sheet coiled material, color steel coiled material, aluminium sheet coiled material or corrosion resistant plate coiled material, and its coil thickness is 0.15 ~ 0.7mm.
Aluminium platinum involved in step 3 or its thickness of tin platinum are 0.08 ~ 0.15mm.
The present invention has following advantageous effect: by metal coiled material being adopted above-mentioned so a kind of technical scheme, the composition metal coiled material formed is owing to being 4 × 4mm glass fiber aluminium by bitumen layer and grid, the scientific disposal on tin top layer, can allow coiled material in use, effectively can play and prevent corrosion, durable effect, particularly under the prerequisite of waterproof, also add the heat insulation effect with eliminating the sound that drips, solve current simple metal coiled material easy corrosion and not heat insulation and easy generation when using as Peng Ding to drip the problem of the sound, have durable, waterproof, heat insulation and quiet effect.
Detailed description of the invention
Embodiment 1:
Metal coiled material selects zinc-plated coiled material, and thickness is 0.15mm, and step 1, the ameliorative pitch selecting softening point to be 60 DEG C, put into melting furnace and be molten into liquid bitumen; Step 2, the liquid bitumen after fusing is spread upon the single surface course of metal coiled material, while smearing, strike off evenly with scraper plate by smear layer, its thickness smearing pitch is 1mm; Step 3, employing smoking heat radiating air duct make to smear bitumen layer and dispel the heat after 40 DEG C, are posted in bitumen layer by glass fiber mesh, then are covered in the surface of bitumen layer with aluminium platinum or tin platinum; Step 4, the entirety after pasting rolled by traction and roller bearing to make it paste layer closely smooth; Step 5, be composition metal waterproof, heat insulation quiet coiled material by wound into a roll for the coiled material finished product after above-mentioned rolling.
Aluminium platinum thickness involved in step 3 is 0.08mm.
The grid of the glass fiber mesh used in step 3 is 4 × 4mm.
Embodiment 2:
Metal coiled material selects color steel coiled material, and thickness is 0.5mm, and step 1, the ameliorative pitch selecting softening point to be 60 DEG C, put into melting furnace and be molten into liquid bitumen; Step 2, the liquid bitumen after fusing is spread upon the single surface course of metal coiled material, while smearing, strike off evenly with scraper plate by smear layer, its thickness smearing pitch is 1.3mm; Step 3, employing smoking heat radiating air duct make to smear bitumen layer and dispel the heat after 40 DEG C, are posted in bitumen layer by glass fiber mesh, then are covered in the surface of bitumen layer with aluminium platinum or tin platinum; Step 4, the entirety after pasting rolled by traction and roller bearing to make it paste layer closely smooth; Step 5, be composition metal waterproof, heat insulation quiet coiled material by wound into a roll for the coiled material finished product after above-mentioned rolling.
Aluminium platinum thickness involved in step 3 is 0.1mm.
The grid of the glass fiber mesh used in step 3 is 4 × 4mm.
Embodiment 3:
Metal coiled material aluminium coiled sheet plate, thickness is 0.7mm, and step 1, the ameliorative pitch selecting softening point to be 70 DEG C, put into melting furnace and be molten into liquid bitumen; Step 2, the liquid bitumen after fusing is spread upon the single surface course of metal coiled material, while smearing, strike off evenly with scraper plate by smear layer, its thickness smearing pitch is 1mm; Step 3, employing smoking heat radiating air duct make to smear bitumen layer and dispel the heat after 40 DEG C, are posted in bitumen layer by glass fiber mesh, then are covered in the surface of bitumen layer with aluminium platinum or tin platinum; Step 4, the entirety after pasting rolled by traction and roller bearing to make it paste layer closely smooth; Step 5, be composition metal waterproof, heat insulation quiet coiled material by wound into a roll for the coiled material finished product after above-mentioned rolling.
Tin platinum thickness involved in step 3 is 0.15mm.
The grid of the glass fiber mesh used in step 3 is 4 × 4mm.
Embodiment 4:
Metal coiled material selects stainless steel coiled material, and thickness is 0.3mm, and step 1, the ameliorative pitch selecting softening point to be 70 DEG C, put into melting furnace and be molten into liquid bitumen; Step 2, the liquid bitumen after fusing is spread upon the single surface course of metal coiled material, while smearing, strike off evenly with scraper plate by smear layer, its thickness smearing pitch is 1.5mm; Step 3, employing smoking heat radiating air duct make to smear bitumen layer and dispel the heat after 40 DEG C, are covered in the surface of bitumen layer with aluminium platinum or tin platinum; Step 4, the entirety after pasting rolled by traction and roller bearing to make it paste layer closely smooth; Step 5, be composition metal waterproof, heat insulation quiet coiled material by wound into a roll for the coiled material finished product after above-mentioned rolling.
Tin platinum thickness involved in step 3 is 0.15mm.
The grid of the glass fiber mesh used in step 3 is 4 × 4mm.
During concrete enforcement, Overall Steps involved in the present invention all can adopt production run equipment to complete, that is: the optional electric-heating container of molten asphalt, metal coiled material can adopt spool drawing-off, while drawing-off, machine automatization mode is adopted to smear liquid bitumen, and adopt location scraper plate blade coating even simultaneously, make bitumen layer uniform ground, prevent from exposing space, because scraper plate adopts locate mode blade coating, can setting height space, make coating layer thickness consistent and reach the thickness of production engineering specifications, can directly arrange on rear side of scraper plate exhaust column fall apart cigarette heat absorption, under the 40 DEG C of state status reaching setting, after continuous mechanical compaction roll rolls, adopt roller bearing rolling.
Glass fiber mesh involved in the present invention in the specific implementation, can, according to the needs of market and user, also can select grid on market to be the product of 5 × 5mm or 6 × 6mm.
Described ameliorative pitch for can not dissolve under sunlight high-temperature condition, and low temperature can not harden the pitch of drawing crack, and this pitch is commercially a lot.
Claims (4)
1. the quiet coiled material of composition metal waterproof and heat-insulating, is included in metal coiled material surface smear pitch, it is characterized in that: the metal coiled material with waterproof and heat-insulating muting function makes as follows:
Step 1, the ameliorative pitch selecting softening point to be 60 ~ 70 DEG C, put into melting furnace and be molten into liquid bitumen;
Step 2, the liquid bitumen after fusing is spread upon the single surface course of metal coiled material, while smearing, strike off evenly with scraper plate by smear layer, its thickness smearing pitch is 1 ~ 1.5mm;
Step 3, employing smoking heat radiating air duct make to smear bitumen layer and dispel the heat after 40 DEG C, are posted in bitumen layer by glass fiber mesh, then are covered in the surface of bitumen layer with aluminium platinum or tin platinum;
Step 4, the entirety after pasting rolled by traction and roller bearing to make it paste layer closely smooth;
Step 5, be composition metal waterproof, heat insulation quiet coiled material by wound into a roll for the coiled material finished product after above-mentioned rolling.
2. the quiet coiled material of composition metal waterproof and heat-insulating according to claim 1, is characterized in that: described metal coiled material is galvanized sheet coiled material, color steel coiled material, aluminium sheet coiled material or corrosion resistant plate coiled material, and its coil thickness is 0.15 ~ 0.7mm.
3. the quiet coiled material of composition metal waterproof and heat-insulating according to claim 1, is characterized in that: aluminium platinum involved in step 3 or its thickness of tin platinum are 0.08 ~ 0.15mm.
4. the quiet coiled material of composition metal waterproof and heat-insulating according to claim 1, is characterized in that: the grid of the glass fiber mesh used in step 3 is 4 × 4mm.