CN104805424A - Surface treatment fluid for water electrolysis polar plate - Google Patents
Surface treatment fluid for water electrolysis polar plate Download PDFInfo
- Publication number
- CN104805424A CN104805424A CN201510139909.XA CN201510139909A CN104805424A CN 104805424 A CN104805424 A CN 104805424A CN 201510139909 A CN201510139909 A CN 201510139909A CN 104805424 A CN104805424 A CN 104805424A
- Authority
- CN
- China
- Prior art keywords
- board surface
- surface treatment
- treatment solution
- water electrolysis
- polar board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a use method of a surface treatment fluid for a water electrolysis polar plate. The surface treatment fluid is characterized by comprising the following components: 5wt%-12wt% of nitrilotriacetic acid, 0.5wt%-3wt% of a complexing agent, 0.2wt%-2wt% of a corrosion inhibitor, 0.1wt%-0.5wt% of a surfactant, 0.02wt%-2wt% of a pH regulator and the balance of water, wherein the pH of the treatment fluid is 3-6. The use method comprises the following steps: the surface of a carbon steel polar plate is cleaned; deoiling, washing and pickling procedures are performed sequentially to remove oil stain, dust and corrosion attached to the surface of the polar plate; the polar plate is soaked in the treatment fluid at the temperature of 40 DEG C for 15 min, taken out, washed with clean water and dried.
Description
The application is divisional application, the invention and created name of original application: water electrolysis polar board surface treatment solution, application number: 201210538474.2, the applying date: 2012.12.13.
Technical field
The present invention relates to a kind of solvent that the surface of carbon steel pole plate is processed, belong to field of metal surface treatment technology.
Background technology
Water electrolysis makes water decomposite hydrogen or oxygen under galvanic effect.In a whole set of water electrolysis equipment, electrolyzer is one of its most crucial device.Industrial conventional water electrolyzer regularly to be laminated to up to a hundred electrolytic chamber by dozens of as required and forms.Each electrolytic chamber is made up of positive plate, oxygen catalysis electrode, choke barrier film, insulated enclosure pad, hydrogen catalysis electrode, negative plate etc.Positive plate and negative plate adopt carbon steel steel plate to make usually.Due to Strong acidic electrolyte composition electrolytic solution to metal, there is strong corrodibility, so the electrolytic solution of electrolyzer generally adopt concentration be 25% to 30% potassium hydroxide or sodium hydroxide solution.Under the effect of electric field, potassium ion or sodium ion move to negative pole, and hydroxide ion moves to positive pole, thus separate out hydrogen and oxygen.In order to reduce overpotential, reduce power consumption, the working temperature of electrolyzer is generally 85 DEG C to 90 DEG C.Such alkali concn and temperature very easily cause alkaline etching to carbon steel steel plate, so antianode plate and negative plate must carry out rotproofing.Because the caustic corrosion resistance performance of pure nickel is very excellent, at present, water electrolysis industry adopts the cathode-anode plate of carbon steel steel plate as water electrolyzer of nickel plating usually.According to result of study display, due to nickel plating carbon steel pole plate in fact and can not plated nickel dam fully coated, nickel layer inevitably has micropore.When pole plate is in the electrolytic solution of harmful ion formation, these harmful ions can enter in the micropore of nickel layer, and enrichment in micropore, with iron ion generation hydrolysis reaction, form the acid that corrodibility is extremely strong, continue to corrode pole plate.In addition, because nickel layer is a kind of coating of cathodic, the standard potential of nickel is-0.25V, and the standard potential of iron is-0.44V, and nickel layer and plain steel can form a pair galvanic couple, electrochemical reaction will occur in the electrolytic solution when they expose simultaneously.Iron in micropore is anode, loses electronics and is dissolved; Nickel is outside negative electrode, obtains electronics, and water electrolysis is released hydrogen.It can thus be appreciated that the possibility that the nickel plating carbon steel pole plate adopting general technology to make is corroded is very big.Once pole plate occurs that serious corrosion can cause hydrogen or oxygen gas to be gone here and there mutually, leak alkali and electrical short, probably set off an explosion, threaten the safety of personnel and equipment.
Summary of the invention
The technical problem to be solved in the present invention is, proposing a kind of for processing the surface of carbon steel pole plate, effectively can improve the water electrolysis polar board surface treatment solution of the erosion resistance after pole plate nickel plating.
The present invention is the technical scheme solving the problems of the technologies described above proposition: a kind of water electrolysis polar board surface treatment solution, comprise following composition: the complexon I of 5wt% to 12wt%, the complexing agent of 0.5wt% to 3wt%, the inhibiter of 0.2wt% to 2wt%, the tensio-active agent of 0.1wt% to 0.5wt, the pH adjusting agent of 0.02wt% to 2wt%, all the other are water; The pH value of described treatment solution is 3 to 6.
Above-mentioned complexing agent is one or more in Trisodium Citrate, Sodium.alpha.-hydroxypropionate, sodium malate.
Above-mentioned inhibiter is one or more in benzotriazole, potassiumiodide, Methylbenzotriazole.
Above-mentioned tensio-active agent is one or more in sodium lauryl sulphate, Sodium dodecylbenzene sulfonate or n-octyl sodium sulfate.
Above-mentioned pH adjusting agent is one or both in trolamine, triethylamine.
Above-mentioned pH adjusting agent is one or both in trolamine, triethylamine.
The present invention has positive effect: water electrolysis polar board surface treatment solution of the present invention is using complexon I as main component; using complexing agent, inhibiter, tensio-active agent as ancillary component; fine and close protective membrane can be formed on the surface of pole plate; effectively isolate iron to contact with nickel layer, effectively promote the erosion resistance of pole plate.Complexon I does two by three carboxyls by respective oxygen and nitrogen can form complex compound with iron ion coordinating to four-coordination, and sequestering power is extremely strong; Add the erosion resistance that complexing agent and inhibiter can improve protective membrane further, add the surface tension that tensio-active agent can significantly improve protective membrane and make pole plate protective membrane finer and close.Do not adopt passivator in treatment solution of the present invention, adopt complexing agent, inhibiter with exceeding, but the complexon I that a large amount of employing is with low cost, under the prerequisite ensureing quality of forming film, greatly can reduce production cost, be with a wide range of applications.
Embodiment
(embodiment 1)
The water electrolysis polar board surface treatment solution of the present embodiment, comprises following composition: the complexon I of 10wt%, the Trisodium Citrate of 3wt%, the benzotriazole of 1wt%, the sodium lauryl sulphate of 0.3wt%, and all the other are water, is 3 by trolamine adjust ph.
The water electrolysis polar board surface treatment solution of the present embodiment, during use, first cleans the polar board surface of carbon steel material, successively through oil removing, washing, pickling process, will be attached to the removing such as greasy dirt, dust, corrosion of polar board surface.Then pole plate being immersed in temperature is 15min in the treatment solution of 40 DEG C, rinses and dry after taking-up with clear water, and bake out temperature is 90 DEG C.Polar board surface forms corrosion-resisting protective film.
(embodiment 2)
The water electrolysis polar board surface treatment solution of the present embodiment, comprises following composition: the complexon I of 8wt%, the Sodium.alpha.-hydroxypropionate of 1wt%, the potassiumiodide of 0.5wt%, the Sodium dodecylbenzene sulfonate of 0.2wt%, and all the other are water, is 4.5 by triethylamine adjust ph.
The water electrolysis polar board surface treatment solution of the present embodiment, during use, first cleans the polar board surface of carbon steel material, successively through oil removing, washing, pickling process, will be attached to the removing such as greasy dirt, dust, corrosion of polar board surface.Then pole plate being immersed in temperature is 20min in the treatment solution of 25 DEG C, rinses and dry after taking-up with clear water, and bake out temperature is 80 DEG C.Polar board surface forms corrosion-resisting protective film.
(embodiment 3)
The water electrolysis polar board surface treatment solution of the present embodiment, comprises following composition: the complexon I of 12wt%, the sodium malate of 2wt%, the Methylbenzotriazole of 0.5wt%, the n-octyl sodium sulfate of 0.2wt%, and all the other are water, is 4 by trolamine adjust ph.
The water electrolysis polar board surface treatment solution of the present embodiment, during use, first cleans the polar board surface of carbon steel material, successively through oil removing, washing, pickling process, will be attached to the removing such as greasy dirt, dust, corrosion of polar board surface.Then pole plate being immersed in temperature is 12min in the treatment solution of 35 DEG C, rinses and dry after taking-up with clear water, and bake out temperature is 120 DEG C.Polar board surface forms corrosion-resisting protective film.
Adopt common process to carry out nickel plating to the pole plate after adopting the water electrolysis polar board surface treatment solution process of embodiment 1 to 3, then carry out SaltSprayTest.Sample is put into salt-spray cabinet, and adopt the NaCl solution of 5%, humidity is 70%, and temperature is 50 DEG C, and continue spraying 8h every day, continuous 8 days, polar board surface was without obvious corrosion phenomenon.
Claims (2)
1. a water electrolysis polar board surface treatment solution, it is characterized in that, comprise following composition: the complexon I of 5wt% to 12wt%, the complexing agent of 0.5wt% to 3wt%, the inhibiter of 0.2wt% to 2wt%, the tensio-active agent of 0.1wt% to 0.5wt, the pH adjusting agent of 0.02wt% to 2wt%, all the other are water; The pH value of described treatment solution is 3 to 6;
Described complexing agent is Trisodium Citrate; Described inhibiter is benzotriazole; Described tensio-active agent is sodium lauryl sulphate.
2. the using method of a water electrolysis polar board surface treatment solution according to claim 1, it is characterized in that comprising: clean the polar board surface of carbon steel material, successively through oil removing, washing, pickling process, with by being attached to the greasy dirt of polar board surface, dust, corrosion remove;
Pole plate being immersed in temperature is 15min in the treatment solution of 40 DEG C, rinses and dry after taking-up with clear water.