CN104804667A - Improved moistureproof binder for paper boxes - Google Patents

Abstract

An improved moistureproof binder for paper boxes is prepared from the following raw materials in parts by weight: 9-14 parts of plant starch, 3-8 parts of 2,6-di-tert-butyl p-cresol, 4-9 parts of cellulose, 5-10 parts of diisocyanate, 4-8 parts of dipropylene glycol, 4-10 parts of ethidene diamine, 7-11 parts of vinyl acetate emulsion, 2-6 parts of potassium perchlorate, 1-4 parts of aluminium trichloride, 4-10 parts of waste polystyrene foam, 3-6 parts of alkylbenzene, 1-4 parts of a stabilizer, 4-8 parts of polylactic acid and 5-11 parts of ethyl alcohol. The improved moistureproof binder for paper boxes provided by the invention has the benefits that no harm to a human body is caused, the cohesiveness is good, and a certain moistureproof effect is achieved.

Description

A kind of moistureproof binding agent for carton of improvement

Technical field

The present invention relates to a kind of carton binding agent of waterproof.

Background technology

Along with the Economic development of China, material flow industry have also been obtained and develops fast.Owing to needing the article of circulation to get more and more, the demand for packaging carton is also increasing.Paper product particularly Corrugated Box are produced, and use sodium silicate in decades more.Because its alkalescence is large, the easy moisture absorption, normal accumulation of salt in the surface soil whiting causes paper product to be out of shape, to peel off, and even corrodes commodity, causing the rotten tremendous economic loss such as to scrap.Along with the progress of modern technologies, binding agent is improved further.But existing binding agent can not meet user demand, Long Term Contact can cause certain injury to human body.

Summary of the invention

For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of carton binding agent, does not injure human body, and cohesiveness is good simultaneously, and has certain moisture-proof role.

For solving prior art problem, technical scheme provided by the invention is, a kind of moistureproof binding agent for carton of improvement, and it is made up of the raw material of following parts by weight:

Plant amylum 9-14 part, 2,6-toluene di-tert-butyl phenol 3-8 part, Mierocrystalline cellulose 4-9 part, vulcabond 5-10 part, dipropylene glycol 4-8 part, quadrol 4-10 part, vinyl acetate between to for plastic base emulsion 7-11 part, potassium perchlorate 2-6 part, aluminum chloride 1-4 part, waste polystyrene foam 4-10 part, alkylbenzene 3-6 part, stablizer 1-4 part, poly(lactic acid) 4-8 part, ethanol 5-11 part.

The invention has the beneficial effects as follows: carton binding agent of the present invention, do not injure human body, cohesiveness is good simultaneously, and has certain moisture-proof role.

Embodiment

embodiment 1

The moistureproof binding agent for carton of improvement, it is made up of the raw material of following parts by weight:

Plant amylum 9 parts, 2,6-toluene di-tert-butyl phenol 3 parts, Mierocrystalline cellulose 4 parts, vulcabond 5 parts, dipropylene glycol 4 parts, quadrol 4 parts, vinyl acetate between to for plastic base emulsion 7 parts, potassium perchlorate 2 parts, aluminum chloride 1 part, waste polystyrene foam 4 parts, alkylbenzene 3 parts, stablizer 1 part, poly(lactic acid) 4 parts, ethanol 5-part.

embodiment 2

The moistureproof binding agent for carton of improvement, it is made up of the raw material of following parts by weight:

Plant amylum 14 parts, 2,6-toluene di-tert-butyl phenol 8 parts, Mierocrystalline cellulose 9 parts, vulcabond 10 parts, dipropylene glycol 8 parts, quadrol 10 parts, vinyl acetate between to for plastic base emulsion 11 parts, potassium perchlorate 6 parts, aluminum chloride 4 parts, waste polystyrene foam 10 parts, alkylbenzene 6 parts, stablizer 4 parts, poly(lactic acid) 8 parts, ethanol 11 parts.

Claims (1)

1. the moistureproof binding agent for carton improved, is characterized in that: it is made up of the raw material of following parts by weight:

Plant amylum 9-14 part, 2,6-toluene di-tert-butyl phenol 3-8 part, Mierocrystalline cellulose 4-9 part, vulcabond 5-10 part, dipropylene glycol 4-8 part, quadrol 4-10 part, vinyl acetate between to for plastic base emulsion 7-11 part, potassium perchlorate 2-6 part, aluminum chloride 1-4 part, waste polystyrene foam 4-10 part, alkylbenzene 3-6 part, stablizer 1-4 part, poly(lactic acid) 4-8 part, ethanol 5-11 part.