CN104804323A - PVC tubular product - Google Patents
PVC tubular product Download PDFInfo
- Publication number
- CN104804323A CN104804323A CN201510146839.0A CN201510146839A CN104804323A CN 104804323 A CN104804323 A CN 104804323A CN 201510146839 A CN201510146839 A CN 201510146839A CN 104804323 A CN104804323 A CN 104804323A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- toughner
- polyvinyl chloride
- resins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PVC tubular product which is prepared from the following raw materials in parts by weight: 35-65 parts of polyvinyl chloride resin, 6-10 parts of acrylic rubber, 7-11 parts of acrylonitrile-styrene, 6-11 parts of calcium stearate, 9-18 parts of polyethylene wax, 10-15 parts of acrylate copolymer, 10-15 parts of titanium dioxide, 5-10 parts of an organic tin heat stabilizer, 5-9 parts of a flexibilizer, 7-12 parts of tribasic lead sulfate and 2-5 parts of a lubricant. The invention further discloses a PVC tubular product preparation method. Through the method, the tensile strength and notch strength of the PVC tubular product provided by the invention are increased by more than 2 times than those of common PVC tubular products, the elongation at break is increased to 99% and the plasticizing time is decreased by 165 seconds and the PVC tubular product is applicable to biaxial tension.
Description
Technical field
The present invention relates to material of construction, particularly relate to a kind of PVC.
Background technology
In the production of polychloroethylene pipes, by the self-strengthening of stretch processes, its radial performance can be strengthened while maintenance tubing axial property.General PVC ductility is not enough, fragility is comparatively large, is difficult to the processing adapting to two-way stretch self-enhancement PVC, the serious application space constraining PVC.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of PVC tubing, and its tensile strength and notch strength increase more than 2 times than general PVC, and 99% of elongation at break raising, fusion time decreases 165S, is applicable to the PVC of two-way stretch.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of PVC tubing, be made up of the raw material of following parts by weight: polyvinyl chloride (PVC) RESINS 35-65 part, acrylic elastomer 6-10 part, acrylonitrile-styrene 7-11 part, calcium stearate 6-11 part, polyethylene wax 9-18 part, acrylic acid esters co-polymer 10-15 part, titanium dioxide 10-15 part, organo-tin het stabilizer 5-10 part, toughner 5-9 part, tribasic lead sulfate 7-12 part, lubricant 2 ~ 5 parts.
In the present invention's preferred embodiments, PVC tubing is made up of the raw material of following parts by weight: polyvinyl chloride (PVC) RESINS 45-60 part, acrylic elastomer 8-10 part, acrylonitrile-styrene 8-11 part, calcium stearate 9-11 part, polyethylene wax 12-18 part, acrylic acid esters co-polymer 12-15 part, titanium dioxide 12-15 part, organo-tin het stabilizer 7-9 part, toughner 6-9 part, tribasic lead sulfate 8-10 part, lubricant 3 ~ 5 parts.
In the present invention's preferred embodiments, PVC tubing is made up of the raw material of following parts by weight: polyvinyl chloride (PVC) RESINS 55 parts, acrylic elastomer 9.5 parts, acrylonitrile-styrene 10.5 parts, calcium stearate 10 parts, polyethylene wax 15 parts, acrylic acid esters co-polymer 13 parts, titanium dioxide 14 parts, organo-tin het stabilizer 8 parts, toughner 8 parts, tribasic lead sulfate 8.5 parts, lubricant 4.5 parts.
In the present invention's preferred embodiments, described toughner is ACR core-shell structure copolymer toughner.
A preparation method for PVC tubing, comprises the following steps:
Step one, by ready polyvinyl chloride (PVC) RESINS and other auxiliary agents, according to polyvinyl chloride (PVC) RESINS 55 parts, acrylic elastomer 9.5 parts, calcium stearate 10 parts, titanium dioxide 14 parts, toughner 8 parts, the amount that tribasic lead sulfate is 8.5 parts adds in mixing machine and mixes, and is then heated to 75 ~ 85 DEG C;
Step 2, continue to stir the material in mixing machine, and add acrylonitrile-styrene 10.5 parts successively, acrylic acid esters co-polymer 13 parts, polyethylene wax 15 parts, organo-tin het stabilizer 8 parts carry out stirring and add after lubricant 4.5 parts stirs after being warmed to 105 ~ 110 DEG C again and be cooled to 55 DEG C of dischargings;
Step 3, material mixed in advance to be joined in forcing machine through processes such as melting, plasticizing, mixing from the continuous extruded material of head, be PVC material.
The invention has the beneficial effects as follows: a kind of PVC tubing of the present invention, its tensile strength and notch strength increase more than 2 times than general PVC, and 99% of elongation at break raising, fusion time decreases 165S, is applicable to the PVC of two-way stretch.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
A kind of PVC tubing is made up of the raw material of following parts by weight: polyvinyl chloride (PVC) RESINS 55 parts, acrylic elastomer 9.5 parts, acrylonitrile-styrene 10.5 parts, calcium stearate 10 parts, polyethylene wax 15 parts, acrylic acid esters co-polymer 13 parts, titanium dioxide 14 parts, organo-tin het stabilizer 8 parts, toughner 8 parts, tribasic lead sulfate 8.5 parts, lubricant 4.5 parts.
The preparation method of above-mentioned PVC tubing, comprises the following steps:
Step one, by ready polyvinyl chloride (PVC) RESINS and other auxiliary agents, according to polyvinyl chloride (PVC) RESINS 55 parts, acrylic elastomer 9.5 parts, calcium stearate 10 parts, titanium dioxide 14 parts, toughner 8 parts, the amount that tribasic lead sulfate is 8.5 parts adds in mixing machine and mixes, and is then heated to 85 DEG C;
Step 2, continue to stir the material in mixing machine, and add acrylonitrile-styrene 10.5 parts successively, acrylic acid esters co-polymer 13 parts, polyethylene wax 15 parts, organo-tin het stabilizer 8 parts carry out stirring and add after lubricant 4.5 parts stirs after being warmed to 108 DEG C again and be cooled to 55 DEG C of dischargings;
Step 3, material mixed in advance to be joined in forcing machine through processes such as melting, plasticizing, mixing from the continuous extruded material of head, be PVC material.
Embodiment 2
A kind of PVC tubing is made up of the raw material of following parts by weight: polyvinyl chloride (PVC) RESINS 50 parts, acrylic elastomer 10 parts, acrylonitrile-styrene 9.5 parts, calcium stearate 10 parts, polyethylene wax 15.5 parts, acrylic acid esters co-polymer 13.5 parts, titanium dioxide 13.5 parts, organo-tin het stabilizer 8.5 parts, toughner 7 parts, tribasic lead sulfate 9 parts, lubricant 5 parts.
The preparation method of above-mentioned PVC tubing, comprises the following steps:
Step one, by ready polyvinyl chloride (PVC) RESINS and other auxiliary agents, according to polyvinyl chloride (PVC) RESINS 50 parts, acrylic elastomer 10 parts, calcium stearate .5 part, titanium dioxide 13.5 parts, toughner 7 parts, the amount that tribasic lead sulfate is 9 parts adds in mixing machine and mixes, and is then heated to 80 DEG C;
Step 2, continue to stir the material in mixing machine, and add acrylonitrile-styrene 10 parts successively, acrylic acid esters co-polymer 13.5 parts, polyethylene wax 15.5 parts, organo-tin het stabilizer 8.5 parts carry out stirring and add after lubricant 5 parts stirs after being warmed to 110 DEG C again and be cooled to 55 DEG C of dischargings;
Step 3, material mixed in advance to be joined in forcing machine through processes such as melting, plasticizing, mixing from the continuous extruded material of head, be PVC material.
The invention has the beneficial effects as follows: a kind of PVC tubing of the present invention, its tensile strength and notch strength increase more than 2 times than general PVC, and 99% of elongation at break raising, fusion time decreases 165S, is applicable to the PVC of two-way stretch.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. a PVC tubing, it is characterized in that, be made up of the raw material of following parts by weight: polyvinyl chloride (PVC) RESINS 35-65 part, acrylic elastomer 6-10 part, acrylonitrile-styrene 7-11 part, calcium stearate 6-11 part, polyethylene wax 9-18 part, acrylic acid esters co-polymer 10-15 part, titanium dioxide 10-15 part, organo-tin het stabilizer 5-10 part, toughner 5-9 part, tribasic lead sulfate 7-12 part, lubricant 2 ~ 5 parts.
2. PVC tubing according to claim 1, it is characterized in that, be made up of the raw material of following parts by weight: polyvinyl chloride (PVC) RESINS 45-60 part, acrylic elastomer 8-10 part, acrylonitrile-styrene 8-11 part, calcium stearate 9-11 part, polyethylene wax 12-18 part, acrylic acid esters co-polymer 12-15 part, titanium dioxide 12-15 part, organo-tin het stabilizer 7-9 part, toughner 6-9 part, tribasic lead sulfate 8-10 part, lubricant 3 ~ 5 parts.
3. PVC tubing according to claim 1, it is characterized in that, be made up of the raw material of following parts by weight: polyvinyl chloride (PVC) RESINS 55 parts, acrylic elastomer 9.5 parts, acrylonitrile-styrene 10.5 parts, calcium stearate 10 parts, polyethylene wax 15 parts, acrylic acid esters co-polymer 13 parts, titanium dioxide 14 parts, organo-tin het stabilizer 8 parts, toughner 8 parts, tribasic lead sulfate 8.5 parts, lubricant 4.5 parts.
4. PVC tubing according to claim 1, is characterized in that, described toughner is ACR core-shell structure copolymer toughner.
5. a preparation method for PVC tubing, is characterized in that, comprises the following steps:
Step one, by ready polyvinyl chloride (PVC) RESINS and other auxiliary agents, according to polyvinyl chloride (PVC) RESINS 55 parts, acrylic elastomer 9.5 parts, calcium stearate 10 parts, titanium dioxide 14 parts, toughner 8 parts, the amount that tribasic lead sulfate is 8.5 parts adds in mixing machine and mixes, and is then heated to 75 ~ 85 DEG C;
Step 2, continue to stir the material in mixing machine, and add acrylonitrile-styrene 10.5 parts successively, acrylic acid esters co-polymer 13 parts, polyethylene wax 15 parts, organo-tin het stabilizer 8 parts carry out stirring and add after lubricant 4.5 parts stirs after being warmed to 105 ~ 110 DEG C again and be cooled to 55 DEG C of dischargings;
Step 3, material mixed in advance to be joined in forcing machine through processes such as melting, plasticizing, mixing from the continuous extruded material of head, be PVC material.