CN104801892A - Manufacturing process of welding wire for welding process - Google Patents
Manufacturing process of welding wire for welding process Download PDFInfo
- Publication number
- CN104801892A CN104801892A CN201510199120.3A CN201510199120A CN104801892A CN 104801892 A CN104801892 A CN 104801892A CN 201510199120 A CN201510199120 A CN 201510199120A CN 104801892 A CN104801892 A CN 104801892A
- Authority
- CN
- China
- Prior art keywords
- parts
- welding
- welding wire
- manufacturing process
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing process of a welding wire for a welding process. The manufacturing process comprises the following steps that (1) the following ingredients including 18 parts of Zr, 20 parts of Nb, 5 parts of C, 6 parts of Mn, 7 parts of Si, 8 parts of B, 2 parts of V, 3 parts of Ni, 4.5 parts of Cu, 1.5 parts of Cr, 0.05 part of S, 0.12 part of P and 15 parts of Fe are proportioned in parts by weight; (2) all ingredients are proportioned according to the corresponding weight parts, and are then melted and smelted in a metal smelting furnace, a welding wire mold is used, and the required welding wire is prepared. The manufacturing process of the welding wire for the welding process can overcome the defects of unreasonable proportion, poor stability, weak bearing force and the like in the prior art for realizing the advantages of reasonable proportion, good stability and strong bearing force.
Description
Technical field
The present invention relates to welding technique field in mechanical engineering, particularly, relate to a kind of manufacture craft of welding procedure welding wire.
Background technology
Welding, connects also referred to as welding, Rong, be a kind of with the mode jointing metal of heating, high temperature or high pressure or other thermoplastics as the manufacturing process of plastics and technology.
The energy source of welding has a variety of, comprises gas flame, electric arc, laser, electron beam, friction and ultrasonic wave etc.Except using in the factory, welding can also be carried out in a variety of contexts, as field, under water and space.No matter wherein, welding all may bring danger to operator, so must take suitable safeguard procedures when welding.Welding the injury that may cause to human body, to comprise burn, electric shock, inpairment of vision, suction toxic gas, Ultraviolet radiation excessive etc.
But current welding wire, plasticity and the toughness of weld seam are low, cause the increase of Welding Structure crack sensitivity, bearing capacity decline.
Realizing in process of the present invention, inventor finding at least to exist in prior art that proportioning is unreasonable, poor stability and the defect such as bearing capacity is weak.
Summary of the invention
The object of the invention is to, for the problems referred to above, propose a kind of manufacture craft of welding procedure welding wire, to realize the strong advantage of reasonable mixture ratio, good stability and bearing capacity.
For achieving the above object, the technical solution used in the present invention is: a kind of manufacture craft of welding procedure welding wire, comprising:
(1) by each component of following parts by weight proportioning:
Zirconium Zr:18 part;
Niobium Nb:20 part;
Carbon C:5 part;
Manganese Mn:6 part;
Silicon Si:7 part;
Boron: 8 parts;
Vanadium V:2 part;
Nickel: 3 parts;
Copper Cu:4.5 part;
Chromium Cr:1.5 part;
Sulphur S:0.05 part;
Touch P:0.12 part;
Iron Fe:15 part;
(2), after each component being pressed corresponding parts by weight proportioning, in metal smelting furnace after fusion smelting, use the obtained required welding wire of welding wire mould.
The manufacture craft of the welding procedure welding wire of various embodiments of the present invention, owing to comprising: (1) by each component of following parts by weight proportioning: zirconium Zr:18 part; Niobium Nb:20 part; Carbon C:5 part; Manganese Mn:6 part; Silicon Si:7 part; Boron: 8 parts; Vanadium V:2 part; Nickel: 3 parts; Copper Cu:4.5 part; Chromium Cr:1.5 part; Sulphur S:0.05 part; Touch P:0.12 part; Iron Fe:15 part; (2), after each component being pressed corresponding parts by weight proportioning, in metal smelting furnace after fusion smelting, use the obtained required welding wire of welding wire mould; Thus can overcome that proportioning in prior art is unreasonable, poor stability and the weak defect of bearing capacity, to realize the strong advantage of reasonable mixture ratio, good stability and bearing capacity.
Other features and advantages of the present invention will be set forth in the following description, and, partly become apparent from description, or understand by implementing the present invention.
Below by embodiment, technical scheme of the present invention is described in further detail.
Detailed description of the invention
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
According to the embodiment of the present invention, provide a kind of manufacture craft of welding procedure welding wire, comprising:
(1) by each component of following parts by weight proportioning:
Zirconium Zr:18 part;
Niobium Nb:20 part;
Carbon C:5 part;
Manganese Mn:6 part;
Silicon Si:7 part;
Boron: 8 parts;
Vanadium V:2 part;
Nickel: 3 parts;
Copper Cu:4.5 part;
Chromium Cr:1.5 part;
Sulphur S:0.05 part;
Touch P:0.12 part;
Iron Fe:15 part;
(2), after each component being pressed corresponding parts by weight proportioning, in metal smelting furnace after fusion smelting, use the obtained required welding wire of welding wire mould.
Through lot of experiments checking, use technical scheme resulting materials of the present invention to weld, the stability of welding material is high, reduces tendency of hardenability and the crack sensitivity of weld seam.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (1)
1. a manufacture craft for welding procedure welding wire, is characterized in that, comprising:
(1) by each component of following parts by weight proportioning:
Zirconium Zr:18 part;
Niobium Nb:20 part;
Carbon C:5 part;
Manganese Mn:6 part;
Silicon Si:7 part;
Boron: 8 parts;
Vanadium V:2 part;
Nickel: 3 parts;
Copper Cu:4.5 part;
Chromium Cr:1.5 part;
Sulphur S:0.05 part;
Touch P:0.12 part;
Iron Fe:15 part;
(2), after each component being pressed corresponding parts by weight proportioning, in metal smelting furnace after fusion smelting, use the obtained required welding wire of welding wire mould.