CN104795123A - 镍层镀锡铜包钢线 - Google Patents

镍层镀锡铜包钢线 Download PDF

Info

Publication number
CN104795123A
CN104795123A CN201410025904.XA CN201410025904A CN104795123A CN 104795123 A CN104795123 A CN 104795123A CN 201410025904 A CN201410025904 A CN 201410025904A CN 104795123 A CN104795123 A CN 104795123A
Authority
CN
China
Prior art keywords
copper
tinning
nickel coating
layer
layers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410025904.XA
Other languages
English (en)
Inventor
谢科科
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Electronic Material Factory Of Yuyao City Htc
Original Assignee
Electronic Material Factory Of Yuyao City Htc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Electronic Material Factory Of Yuyao City Htc filed Critical Electronic Material Factory Of Yuyao City Htc
Priority to CN201410025904.XA priority Critical patent/CN104795123A/zh
Publication of CN104795123A publication Critical patent/CN104795123A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种镍层镀锡铜包钢线,包括线芯,所述线芯外侧包覆有铜层,所述铜层外侧设有镀锡层;所述铜层与所述镀锡层之间还设有镀镍层。本发明提供的镍层镀锡铜包钢线在原有的基础在大胆创新,又在铜层与镀锡层之间增加了一道镀镍层,主要是起封闭隔绝的作用,再增加一道镍层能使产品99.9%的长时间隔绝铁离子与铜离子穿透锡层到达产品表面。

Description

镍层镀锡铜包钢线
技术领域
本发明涉及镀锡铜包钢线,具体是一种镍层镀锡铜包钢线。
背景技术
随着市场上有色金属价格持续上升,纯铜、纯铝产品价格飞速上涨,新产品镀锡铜包钢线(CP线)应运而生,镀锡铜包钢线是以优质低碳钢为芯线,经采用机械方法均匀包覆无氧铜层,然后镀上(一般分为冷镀、热镀)纯锡层的新型复合材料,相较于纯铜线具有价格低、强度高、韧性好、重量轻、焊接性能良好等特点,是传统纯铜线的更新换代产品。
为了延长镀锡铜包钢线的使用寿命,通常采用将钢材线芯镀铜后再镀锡构成,然而,上述镀锡铜包钢线的抗氧化性能比较薄弱,产品基层的铁离子会随着时长而穿透铜层穿透锡层到达产品表面,从而使产品表面出现氧化发黑现象,使产品出现次品。
发明内容
本发明的首要目的在于提供一种使用寿命更长的镍层镀锡铜包钢线,为实现上述目的本发明的具体方案如下:
一种镍层镀锡铜包钢线,包括线芯,所述线芯外侧包覆有铜层,所述铜层外侧设有镀锡层;
所述铜层与所述镀锡层之间还设有镀镍层。
优选的,所述线芯与所述铜层之间也设有镀镍层。
本发明提供的镍层镀锡铜包钢线在原有的基础在大胆创新,又在铜层与镀锡层之间增加了一道镀镍层,主要是起封闭隔绝的作用,再增加一道镍层能使产品99.9%的长时间隔绝铁离子与铜离子穿透锡层到达产品表面。
附图说明
此处所说明的附图用来提供对本发明的进一步理解,构成本申请的一部分,并不构成对本发明的不当限定,在附图中:
图1为本发明实施例结构示意图;
图2为传统镀锡铜包钢线EDS分析图;
图3~图7为图2中001~005位置的EDS测试能谱图;
图8为本发明实施例EDS分析图;
图9~图12为图8中001~004位置的EDS测试能谱图。
具体实施方式
下面将结合附图以及具体实施例来详细说明本发明,在此本发明的示意性实施例以及说明用来解释本发明,但并不作为对本发明的限定。
实施例
如图1所示,一种镍层镀锡铜包钢线,包括优质低碳钢线芯1,所述线芯1外侧包覆有铜层2,所述铜层2外侧设有镀锡层3;所述铜层2与所述镀锡层3之间还设有镀镍层4。
作为上述实施例方案的优选方案,所述线芯1与所述铜层2之间也设有镀镍层4。
传统镀锡铜包钢线受电镀本身的工艺局限性所制,几种不同的材料混合在一起,不一定可以使用,发明人在无意中通过测试得知铜层2与镍层的结合力要比铁层与镍层的结合力要好的多,通过上述实施例方案,把铁离子、铜离子都控制在镍层内部,不会穿透到锡层表面,使表面锡层上没有其他离子产品,这样对产品的焊接性与保存时间有很大好处。
图2为传统镀锡铜包钢线EDS分析图
图3~图7为图2中001~005位置的EDS测试能谱图
传统镀锡铜包钢线EDS测试结果如下(表1):
Spectrum C O Fe Cu Sn Total
001 1.57 0.95 0.77 0.53 96.18 100
002 2.49 0.75 0.51 35.21 61.05 100
003 3.61 0.42 1.75 9422 / 100
004 29.52 8.51 0.40 0.70 60.87 100
0二05 4.10 1.25 1.12 75.08 18.45 100
图8为本发明实施例EDS分析图;
图9~图12为图8中001~004位置的EDS测试能谱图
本发明实施例EDS测试结果如下(表2):
Spectrum C O Fe Ni Cu Sn lotal
001 1.22 1.23 / / 1.65 95.91 100
002 5.15 0.62 1.11 90.03 / 3.09 100
003 4.36 / 1.59 / 94.05 / 100
004 6.24 1.20 / / 92.55 / 100
通过表1可以得知,001为锡层,002与005是铜与锡之间的一层,003是铜层2,001锡层上有大量FE铁离子与铜离子,003的铜层2上也有铁离子,说明电镀层没有一个很好的保护性,内部的铁、铜离子都随着时间的推移穿透到表面。
通过表2可以得知,同样001锡层,002是镍,004是铜,003完全是铜层2,001中分析表面锡层上只有大量的锡层与少量的铜离子,002是有镍的成分,但是有少量的铁离子,这就很好的说明镍有封闭作用,而且能控制大部分的其他离子层。
以上对本发明实施例所提供的技术方案进行了详细介绍,本文中应用了具体个例对本发明实施例的原理以及实施方式进行了阐述,以上实施例的说明只适用于帮助理解本发明实施例的原理;同时,对于本领域的一般技术人员,依据本发明实施例,在具体实施方式以及应用范围上均会有改变之处,综上所述,本说明书内容不应理解为对本发明的限制。

Claims (2)

1.一种镍层镀锡铜包钢线,其特征在于:
包括线芯,所述线芯外侧包覆有铜层,所述铜层外侧设有镀锡层;所述铜层与所述镀锡层之间还设有镀镍层。
2.如权利要求1所述的镍层镀锡铜包钢线,其特征在于:
所述线芯与所述铜层之间也设有镀镍层。
CN201410025904.XA 2014-01-21 2014-01-21 镍层镀锡铜包钢线 Pending CN104795123A (zh)