CN104788809A - Woven bag and preparation method thereof - Google Patents
Woven bag and preparation method thereof Download PDFInfo
- Publication number
- CN104788809A CN104788809A CN201510147044.1A CN201510147044A CN104788809A CN 104788809 A CN104788809 A CN 104788809A CN 201510147044 A CN201510147044 A CN 201510147044A CN 104788809 A CN104788809 A CN 104788809A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven bag
- polyethylene
- titanium dioxide
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a woven bag and a preparation method. The woven bag comprises raw materials of PP, an antioxidant, calcium carbonate, polyethylene, polyethylene wax, titanium dioxide, chlorinated paraffin, modified starch, iso-octyl acrylate and organic nano-montmorillonite. The product has impact strength of 23 to 27kJ/m<2>, bending elastic modulus of 115 to 125MPa, tensile strength of 35 to 55 MPa, breaking elongation of 30 to 50 percent, bending strength of 50 to 70MPa, bending modulus of 2,000 to 3,000MPa and impact strength of 65 to 85J/m, is low in density, high in toughness, abrasion resistance, heat resistance and flowability and strong in tensile strength, and can be widely produced and continuously used instead of the conventional material, the raw materials are simple and readily available, and the preparation method is simple.
Description
Technical field
The present invention relates to field of packaging material, particularly relate to a kind of woven bag and preparation method thereof.
Background technology
Woven bag, also known as snakeskin bag.Be the one of plastics, packaging, its raw material is generally the various Xylonite raw material such as polyethylene, polypropylene.Knitting tightness refers in 100mm × 100mm cloth, through the radical of weft yarn.Specify in standard GB/T/T8946-1998, " bag is shakeout, upper at sack, lower two diagonal angles place delineation 100mm × 100mm two square; outside square with bag sideline at a distance of 100mm, the warp of range estimation square, latitude radical; average, during counting when settled point last less than one time, by one." define knitting tightness in national standard while, define density tolerances.Knitting tightness depends primarily on wrapped product, is determined by user.
External production main raw material is polyethylene (PE), and domestic production is mainly polypropylene (PP), is that ethene is through being polymerized obtained a kind of thermoplastic resin.Industrially, the multipolymer of ethene and a small amount of alpha-olefin is also comprised.Polyethylene odorless, nontoxic, feel ceraceous, there is excellent resistance to low temperature (minimum use temperature can reach-70 ~-100 DEG C), chemical stability is good, and the erosion (the not resistance to acid with oxidizing property) of the most of soda acid of ability, is insoluble to common solvent under normal temperature, water-absorbent is little, and electrical insulation capability is excellent; But polyethylene is very sensitive for environmental stress (chemistry and mechanical effect), and heat-resistant aging is poor.Poly character is different because of kind, depends primarily on molecular structure and density.Adopt different production methods can obtain different densities (0.91 ~ 0.96g/cm
3) product.Polyethylene can be processed with the forming method of general thermoplastics (see plastic working).Purposes is very extensive, is mainly used to manufacture film, container, pipeline, monofilament, electric wire, daily necessities etc., and can be used as the high-frequency insulation material of TV, radar etc.Along with the development of petrochemical complex, polyethylene production is developed rapidly, and output accounts for 1/4 of plastics ultimate production.Nineteen eighty-three, polyethylene overall throughput in the world's was 24.65Mt, was 3.16Mt building device capability.
A kind of thermoplastic resin obtained by propylene polymerization.Have isotactic thing, random thing and rule thing three kinds of configurations, Industrial products with isotactic thing for main component.Polypropylene also comprises the multipolymer of propylene and a small amount of ethene.Be generally translucent colorless solid, odorless is nontoxic.The highly crystallized due to compound with regular structure, therefore fusing point is up to 167 DEG C, heat-resisting, the sterilization of goods used vapour is its outstanding advantages.Density 0.90g/cm
3, be the lightest general-purpose plastics.Corrosion-resistant, tensile strength 30MPa, intensity, rigidity and the transparency are all good than polyethylene.Shortcoming is that low-temperature impact resistance is poor, more aging, but can be overcome respectively by modification and interpolation oxidation inhibitor.
Due to goods resource and price problem, there are 6,000,000,000 woven bags in China every year for cement packing, account for more than 85% of bulk cement packaging. along with the Application and Development of flexible container bag, the pack of plastic knitting collection dress is widely used in sea, communications and transportation sacker agricultural prods, in agricultural product packaging, Polywoven Bag has been widely used in fishery products packaging, bird feed is packed, the covering material of plant, the sunshade of proportion of crop planting, windproof, the materials such as hail suppression canopy. usual products: feed woven bag, chemical industry woven bag, putty powder woven bag, urea woven bag, vegetables mesh pocket, fruit mesh pocket etc.
Makeshift tent in tourism, parasols, various traveling bag, travelling bag, plastic braid is had to apply, the covering material that various tarpaulin is widely used in transport and stores, instead of the cotton being easy to go rotten heaviness and knits tarpaulin. and the fence in construction, guard etc. are also widely used in plastic braid. common are: logistics bag, logistics packaging bag, shipping bag, freight transport packing bag etc.
Since developing geotextile from the eighties, widen the Application Areas of plastic braid, be widely used in little water conservancy, electric power, highway, railway, harbour, mine construction, in military engineering construction. in these engineerings, geosynthetics has filtration, draining, strengthens, isolation, the functions such as antiseepage, plastic civil engineering cloth is exactly the one of Geosynthetics.
Polywoven Bag is configured to Polypropylene Bag, polyethylene bag by main raw; Bag at the bottom of seam end bag, tape edge is divided into by method of sewing.Be widely used in a kind of wrapping material of the article such as fertilizer, Chemicals at present.Its main production utilizes plastic raw materials to be flat filament through extrusion film, cutting, unilateral stretching, through obtaining product through knitting device, is commonly referred to as woven bag.
Summary of the invention
The invention provides a kind of pull-off force and the high woven bag of tensile strength and preparation method thereof, solve existing woven bag pull-off force and the technical problem such as tensile strength is low.
The present invention is by the following technical solutions: a kind of woven bag, it is as follows that mass fraction proportioning pressed by its raw material: PP100 part, oxidation inhibitor 0.1-0.2 part, calcium carbonate 20-40 part, polyethylene 10-30 part, polyethylene wax 1-20 part, titanium dioxide 10-30 part, clorafin 5-25 part, treated starch 5-10 part, Isooctyl acrylate monomer 6-10 part, nano organic montmorillonite 2-8 part.
As a preferred technical solution of the present invention: it is as follows that mass fraction proportioning pressed by the raw material of described woven bag: PP100 part, oxidation inhibitor 0.12-0.18 part, calcium carbonate 25-35 part, polyethylene 15-25 part, polyethylene wax 5-15 part, titanium dioxide 15-25 part, clorafin 10-20 part, treated starch 6-8 part, Isooctyl acrylate monomer 7-9 part, nano organic montmorillonite 4-6 part.
As a preferred technical solution of the present invention: it is as follows that mass fraction proportioning pressed by the raw material of described woven bag: PP100 part, 0.15 part, oxidation inhibitor, 30 parts, calcium carbonate, polyethylene 20 parts, polyethylene wax 10 parts, titanium dioxide 20 parts, clorafin 15 parts, treated starch 8 parts, Isooctyl acrylate monomer 8 parts, nano organic montmorillonite 5 parts.
As a preferred technical solution of the present invention: described oxidation inhibitor adopts irgasfos 168 or antioxidant 1010.
Prepare a method for described woven bag, step is:
The first step: take PP, oxidation inhibitor, calcium carbonate, polyethylene, polyethylene wax, titanium dioxide, clorafin, treated starch, Isooctyl acrylate monomer and nano organic montmorillonite according to mass fraction proportioning;
Second step: all raw materials are dropped in high-speed mixer and mixes, mixing machine temperature 55-75 DEG C, mixing 20-30min;
3rd step: mixed material drops in twin screw extruder, extruder temperature 180-190 DEG C, 190-200 DEG C, 200-210 DEG C, 210-220 DEG C, 220-240 DEG C, head temperature 240-280 DEG C, water solution temperature 20-40 DEG C, first draw speed 1450-1500r/min, the second draw speed 1400-1450r/min.
beneficial effect
A kind of woven bag of the present invention and preparation method thereof adopts above technical scheme compared with prior art, has following technique effect: 1, product shock strength 23-27kJ/m
2, bending elastic modulus 115-125MPa; 2, density is little, good toughness, wear resistance are good, and tensile strength is high, tensile strength 35-55MPa, elongation at break 30-50%; 3, product good heat resistance, good fluidity, raw material is simple and easy to get, and preparation method is simple, flexural strength 50-70MPa, modulus in flexure 2000-3000MPa, shock strength 65-85J/m, the widespread production not division of history into periods can replace current material.
Embodiment
Below in conjunction with example, the invention will be further described, and embodiment, only for the present invention will be described, does not form the restriction to right, and other alternative means that it may occur to persons skilled in the art that, all within the scope of the claims in the present invention.
Embodiment 1:
The first step: take PP100 part according to mass fraction proportioning, antioxidant 1010 is 0.1 part, 20 parts, calcium carbonate, polyethylene 10 parts, polyethylene wax 1 part, titanium dioxide 10 parts, clorafin 5 parts, treated starch 5 parts, Isooctyl acrylate monomer 6 parts, nano organic montmorillonite 2 parts.
Second step: all raw materials are dropped in high-speed mixer and mixes, mixing machine temperature 55 DEG C, mixing 20min.
3rd step: mixed material drops in twin screw extruder, extruder temperature 180 DEG C, 190 DEG C, 200 DEG C, 210 DEG C, 220 DEG C, head temperature 240 DEG C, water solution temperature 20 DEG C, the first draw speed 1450r/min, the second draw speed 1400r/min.
Product shock strength 23kJ/m
2, bending elastic modulus 115MPa; Density is little, good toughness, wear resistance are good, and tensile strength is high, tensile strength 35MPa, elongation at break 30%; Product good heat resistance, good fluidity, raw material is simple and easy to get, and preparation method is simple, flexural strength 50MPa, modulus in flexure 2000MPa, shock strength 65J/m.
Embodiment 2:
The first step: take PP100 part according to mass fraction proportioning, antioxidant 1010 is 0.2 part, 40 parts, calcium carbonate, polyethylene 30 parts, polyethylene wax 20 parts, titanium dioxide 30 parts, clorafin 25 parts, treated starch 10 parts, Isooctyl acrylate monomer 10 parts, nano organic montmorillonite 8 parts.
Second step: all raw materials are dropped in high-speed mixer and mixes, mixing machine temperature 75 DEG C, mixing 30min.
3rd step: mixed material drops in twin screw extruder, extruder temperature 190 DEG C, 200 DEG C, 210 DEG C, 220 DEG C, 240 DEG C, head temperature 280 DEG C, water solution temperature 40 DEG C, the first draw speed 1500r/min, the second draw speed 1450r/min.
Product shock strength 24kJ/m
2, bending elastic modulus 118MPa; Density is little, good toughness, wear resistance are good, and tensile strength is high, tensile strength 40MPa, elongation at break 35%; Product good heat resistance, good fluidity, raw material is simple and easy to get, and preparation method is simple, flexural strength 55MPa, modulus in flexure 2200MPa, shock strength 70J/m.
Embodiment 3:
The first step: take PP100 part according to mass fraction proportioning, irgasfos 168 is 0.12 part, 25 parts, calcium carbonate, polyethylene 15 parts, polyethylene wax 5 parts, titanium dioxide 15 parts, clorafin 10 parts, treated starch 6 parts, Isooctyl acrylate monomer 7 parts, nano organic montmorillonite 4 parts.
Second step: all raw materials are dropped in high-speed mixer and mixes, mixing machine temperature 55 DEG C, mixing 20min.
3rd step: mixed material drops in twin screw extruder, extruder temperature 180 DEG C, 190 DEG C, 200 DEG C, 210 DEG C, 220 DEG C, head temperature 240 DEG C, water solution temperature 20 DEG C, the first draw speed 1450r/min, the second draw speed 1400r/min.
Product shock strength 25kJ/m
2, bending elastic modulus 120MPa; Density is little, good toughness, wear resistance are good, and tensile strength is high, tensile strength 45MPa, elongation at break 40%; Product good heat resistance, good fluidity, raw material is simple and easy to get, and preparation method is simple, flexural strength 60MPa, modulus in flexure 2500MPa, shock strength 75J/m.
Embodiment 4:
The first step: take PP100 part according to mass fraction proportioning, irgasfos 168 is 0.18 part, 35 parts, calcium carbonate, polyethylene 25 parts, polyethylene wax 15 parts, titanium dioxide 25 parts, clorafin 20 parts, treated starch 8 parts, Isooctyl acrylate monomer 9 parts, nano organic montmorillonite 6 parts.
Second step: all raw materials are dropped in high-speed mixer and mixes, mixing machine temperature 75 DEG C, mixing 30min.
3rd step: mixed material drops in twin screw extruder, extruder temperature 190 DEG C, 200 DEG C, 210 DEG C, 220 DEG C, 240 DEG C, head temperature 280 DEG C, water solution temperature 40 DEG C, the first draw speed 1500r/min, the second draw speed 1450r/min.
Product shock strength 26kJ/m
2, bending elastic modulus 123MPa; Density is little, good toughness, wear resistance are good, and tensile strength is high, tensile strength 50MPa, elongation at break 45%; Product good heat resistance, good fluidity, raw material is simple and easy to get, and preparation method is simple, flexural strength 65MPa, modulus in flexure 2800MPa, shock strength 80J/m.
Embodiment 5:
The first step: take PP100 part according to mass fraction proportioning, irgasfos 168 is 0.15 part, 30 parts, calcium carbonate, polyethylene 20 parts, polyethylene wax 10 parts, titanium dioxide 20 parts, clorafin 15 parts, treated starch 8 parts, Isooctyl acrylate monomer 8 parts, nano organic montmorillonite 5 parts.
Second step: all raw materials are dropped in high-speed mixer and mixes, mixing machine temperature 65 DEG C, mixing 25min.
3rd step: mixed material drops in twin screw extruder, extruder temperature 185 DEG C, 195 DEG C, 205 DEG C, 215 DEG C, 230 DEG C, head temperature 260 DEG C, water solution temperature 30 DEG C, the first draw speed 1480r/min, the second draw speed 1420r/min.
Product shock strength 27kJ/m
2, bending elastic modulus 125MPa; Density is little, good toughness, wear resistance are good, and tensile strength is high, tensile strength 55MPa, elongation at break 50%; Product good heat resistance, good fluidity, raw material is simple and easy to get, and preparation method is simple, flexural strength 70MPa, modulus in flexure 3000MPa, shock strength 85J/m.
Claims (5)
1. a woven bag, it is characterized in that, it is as follows that mass fraction proportioning pressed by the raw material of described woven bag: PP100 part, oxidation inhibitor 0.1-0.2 part, calcium carbonate 20-40 part, polyethylene 10-30 part, polyethylene wax 1-20 part, titanium dioxide 10-30 part, clorafin 5-25 part, treated starch 5-10 part, Isooctyl acrylate monomer 6-10 part, nano organic montmorillonite 2-8 part.
2. a kind of woven bag according to claim 1, it is characterized in that, it is as follows that mass fraction proportioning pressed by the raw material of described woven bag: PP100 part, oxidation inhibitor 0.12-0.18 part, calcium carbonate 25-35 part, polyethylene 15-25 part, polyethylene wax 5-15 part, titanium dioxide 15-25 part, clorafin 10-20 part, treated starch 6-8 part, Isooctyl acrylate monomer 7-9 part, nano organic montmorillonite 4-6 part.
3. a kind of woven bag according to claim 2, it is characterized in that, it is as follows that mass fraction proportioning pressed by the raw material of described woven bag: PP100 part, 0.15 part, oxidation inhibitor, 30 parts, calcium carbonate, polyethylene 20 parts, polyethylene wax 10 parts, titanium dioxide 20 parts, clorafin 15 parts, treated starch 8 parts, Isooctyl acrylate monomer 8 parts, nano organic montmorillonite 5 parts.
4. a kind of woven bag according to claim 1, is characterized in that: described oxidation inhibitor adopts irgasfos 168 or antioxidant 1010.
5. make a method for woven bag according to claim 1, it is characterized in that, comprise the steps:
The first step: take PP, oxidation inhibitor, calcium carbonate, polyethylene, polyethylene wax, titanium dioxide, clorafin, treated starch, Isooctyl acrylate monomer and nano organic montmorillonite according to mass fraction proportioning;
Second step: all raw materials are dropped in high-speed mixer and mixes, mixing machine temperature 55-75 DEG C, mixing 20-30min;
3rd step: mixed material drops in twin screw extruder, extruder temperature 180-190 DEG C, 190-200 DEG C, 200-210 DEG C, 210-220 DEG C, 220-240 DEG C, head temperature 240-280 DEG C, water solution temperature 20-40 DEG C, first draw speed 1450-1500r/min, the second draw speed 1400-1450r/min.