CN104786608A

CN104786608A - Flame-retardant high-usability fabric

Info

Publication number: CN104786608A
Application number: CN201510174907.4A
Authority: CN
Inventors: 黄磊
Original assignee: Jiangsu Hongliu Bedsheet Ltd Co
Current assignee: Jiangsu Hongliu Bedsheet Ltd Co
Priority date: 2015-04-15
Filing date: 2015-04-15
Publication date: 2015-07-22

Abstract

The invention relates to flame-retardant high-usability fabric which comprises an upper cotton cloth layer (1) and a lower cotton cloth layer (2), wherein a substrate (5) is compounded below the lower cotton cloth layer; an antistatic layer (3) is further arranged between the upper and lower cotton cloth layers, and is made from core-spun yarn fibers; each fiber comprises a yarn (3.1) and a metal wire (3.2); the metal wires (3.2) are wound on the yarns (3.1); the surface of the upper cotton cloth layer is covered with a layer of flame-retardant coating (4) which comprises a bottom flame-retardant polyurethane layer (4.1) and a top organic silicon oil layer (4.2); the substrate is made of a textile; wool fibers and coconut fibers are adopted as warps and wefts of the textile respectively; each wool fiber has a diameter of 9 [mu]m; each coconut fiber has a diameter of 10 [mu]m; the warp density of the textile is 26.6 per centimeter, and the weft density of the textile is 31.3 per centimeter. The fabric is lower in cost, bendable and variable; the adopted textile is reasonable in structure and high in usability.

Description

The good fabric of fire-retardant serviceability

Technical field

The present invention relates to the good fabric of a kind of fire-retardant serviceability.

Background technology

The good fabric of fire-retardant serviceability is as one of textile the most familiar in people's life, be widely used in the modern life, fire-retardant serviceability of the prior art good fabric many employings flame-retardant yarn weaves, but adopt the production cost of the good fabric of fire-retardant serviceability of flame-retardant yarn braiding higher, and technique is comparatively complicated; The good fabric of fire-retardant serviceability of the prior art adopts cheap simultaneously, the cotton fabric that its comfort is good, but the wrinkle resistance of this kind of cotton fabric product is with very may just as well poor.Also there is easy contracting, easily wrinkle, not well-pressed defect in pure cotton cloth simultaneously, and rigidity and the bendability of fabric are poor, therefore must often press before dress, and also not possessing antistatic, radioresistance etc. is conducive to healthy function simultaneously.

In addition, the fabric construction that traditional clothes adopt is unreasonable, and serviceability is bad.

Summary of the invention

The object of the invention is to overcome above-mentioned deficiency, provide a kind of cost lower, bending variable, and there is the good fabric of fire-retardant serviceability of antistatic, radiation-resisting functional.

The object of the present invention is achieved like this:

The good fabric of the fire-retardant serviceability of the present invention, comprise cotton layer and lower cotton layer, a basic unit is compounded with below described lower cotton layer, also antistatic backing is provided with between described upper cotton layer and lower cotton layer, this antistatic backing is made up of cored silk fiber, this fiber comprises yarn and wire, described wire is wrapped on yarn, the surface of described upper cotton layer is covered with one deck flame retardant coating, this flame retardant coating comprises the flame retardant polyurethane layer of bottom and the organosilicon oil reservoir at top, described cotton layer, lower cotton layer, bonded by glue between antistatic backing and the adjacent two layers of flame retardant coating, described basic unit is made up of fabric, the warp of described fabric and parallel adopt wool fiber and cocoanut fiber respectively, and wherein the diameter of wool fiber is 9 μm, and the diameter of cocoanut fiber is 10 μm, described fabric be 26.6/cm through density, weft density is 31.3/cm.

Compared with prior art, the invention has the beneficial effects as follows:

The good fabric of this fire-retardant serviceability, by arranging flame retardant coating on upper cotton layer surface, reaches fire-retardant effect, and this production technology is simple, reduces the production cost of enterprise, has met the level of consumption of ordinary populace; Form antistatic backing after yarn and wire composition cored silk simultaneously, make fabric have special rigidity, and bending variable, and third dimension is stronger, can various wrinkle effect be formed, not easily contract, not easily wrinkle, radiating metal gloss, feel is fine and smooth, has antistatic, radiation-resistant effect.

Fabric construction of the present invention is reasonable, and serviceability is good.

Accompanying drawing explanation

Fig. 1 is the structural representation of the good fabric of the fire-retardant serviceability of the present invention.

Fig. 2 is the structural representation of antistatic backing in Fig. 1.

Wherein: upper cotton layer 1, lower cotton layer 2, antistatic backing 3, flame retardant coating 4, flame retardant polyurethane layer 4.1, organosilicon oil reservoir 4.2, basic unit 5.

Detailed description of the invention

See Fig. 1 and Fig. 2, the present invention relates to the good fabric of a kind of fire-retardant serviceability, it comprises cotton layer 1 and lower cotton layer 2, described lower cotton layer 2 is compounded with a basic unit 5 below, antistatic backing 3 is also provided with between described upper cotton layer 1 and lower cotton layer 2, this antistatic backing 3 is made up of cored silk fiber, this fiber comprises yarn 3.1 and wire 3.2, described wire 3.2 is wrapped on yarn 3.1, the surface of described upper cotton layer 1 is covered with one deck flame retardant coating 4, this flame retardant coating 4 comprises the flame retardant polyurethane layer 4.1 of bottom and the organosilicon oil reservoir 4.2 at top, the fire resistance of flame retardant polyurethane layer 4.1 is good, be applicable to the use to the high occasion of flame-retardancy requirements, organosilicon oil reservoir 4.2 makes web surface smooth, be not clamminess, add the flexibility of fabric, described cotton layer 1, lower cotton layer 2, bonded by glue between the adjacent two layers of antistatic backing 3 and flame retardant coating 4.

Described basic unit is made up of fabric, the warp of described fabric and parallel adopt wool fiber and cocoanut fiber respectively, and wherein the diameter of wool fiber is 9 μm, and the diameter of cocoanut fiber is 10 μm, described fabric be 26.6/cm through density, weft density is 31.3/cm.

Claims

1. the good fabric of fire-retardant serviceability, it is characterized in that: it comprises cotton layer (1) and lower cotton layer (2), described lower cotton layer (2) is compounded with a basic unit (5) below, antistatic backing (3) is also provided with between described upper cotton layer (1) and lower cotton layer (2), this antistatic backing (3) is made up of cored silk fiber, this fiber comprises yarn (3.1) and wire (3.2), described wire (3.2) is wrapped on yarn (3.1), the surface of described upper cotton layer (1) is covered with one deck flame retardant coating (4), this flame retardant coating (4) comprises the flame retardant polyurethane layer (4.1) of bottom and the organosilicon oil reservoir (4.2) at top, described cotton layer (1), lower cotton layer (2), bonded by glue between the adjacent two layers of antistatic backing (3) and flame retardant coating (4), described basic unit is made up of fabric, the warp of described fabric and parallel adopt wool fiber and cocoanut fiber respectively, and wherein the diameter of wool fiber is 9 μm, and the diameter of cocoanut fiber is 10 μm, described fabric be 26.6/cm through density, weft density is 31.3/cm.