CN104783715A - Toilet paper easily dissolving in water - Google Patents
Toilet paper easily dissolving in water Download PDFInfo
- Publication number
- CN104783715A CN104783715A CN201510227274.9A CN201510227274A CN104783715A CN 104783715 A CN104783715 A CN 104783715A CN 201510227274 A CN201510227274 A CN 201510227274A CN 104783715 A CN104783715 A CN 104783715A
- Authority
- CN
- China
- Prior art keywords
- toilet paper
- water
- cornstarch
- absorbent resin
- super absorbent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a toilet paper easily dissolving in water. The toilet paper forms a coiling block without length limit by pressing a super absorbent resin layer in the upper layer and a brown algae film impervious layer in the lower layer. Ripples are formed in the toilet paper. The super absorbent resin layer is prepared through film formation of corn starch acrylic acid graft copolymer. The proportion of all components in the brown algae film impervious layer is, by weight, 12% of brown algae, 3% of glycerinum, 2% of calcium chloride and 83% of water. The toilet paper easily dissolving in water has the advantages that the cleaning effect is notable; the toilet paper after being used can be thrown into a sewer directly and the sewer cannot be blocked due to the fact the toilet paper is easy to dissolve in water, a big pollution source in the rest room is removed, and sanitation in the rest room is facilitated.
Description
Technical field
The present invention relates to amenities technical field, especially a kind of toilet paper soluble in water.
Background technology
Toilet paper is manufactured by wood pulp usually.Because the fiber in wood pulp is water insoluble, toilet paper with after very easily cause sewer blockage.In order to prevent blocking sewer, people usually by with after toilet paper throw away in dustbin, and to be deposited in dustbin the large pollution sources that the toilet paper do not removed in time becomes toilet.
Summary of the invention
Not only cleaning effect is remarkable to the object of this invention is to provide one, and is conducive to the toilet paper of toilet health.
Technical scheme of the present invention is: a kind of toilet paper soluble in water, and described toilet paper forms by the super absorbent resin layer on upper strata and the Alginate Film impervious barrier pressing of lower floor the reel that length do not limit.
Described toilet paper is provided with ripple.
Described super absorbent resin layer adopts cornstarch acrylic acid graft copolymer film forming to obtain, the preparation technology of described cornstarch acrylic acid graft copolymer is: add in reactor by cornstarch 85 parts and 800 parts, water, be heated to 80 DEG C under nitrogen flowing, stir 1h, after making cornstarch gel, be cooled to 30 DEG C, add 120 parts, acrylic acid and by 30% hydrogen peroxidase 10 .2 part, after the polymerization catalyst of L-AA 0.1 part composition, polyase 13 h is stirred at 40 DEG C, then 30% sodium hydroxide solution 120 parts is added, a night is placed at 30 DEG C, drying under reduced pressure at 60 DEG C again, pulverize, obtained cornstarch acrylic acid graft copolymer.
Each component of described Alginate Film impervious barrier by weight formula rate is: algin 12%, glycerine 3%, calcium chloride 2%, water 83%, adds up to 100%.
Described toilet paper adopts existing equipment and technique obtained super absorbent resin layer and Alginate Film impervious barrier respectively, upper and lower two-layer pressing is formed the reel that length is not limit.
The water absorbing capacity of super absorbent resin can reach more than 250 times of deadweight.Meanwhile, the water sorption of super absorbent resin is different from physics water suction, even if the gel pressurization be swelled into after water suction is also not easily oozed out, water-retaining property is extremely strong.Super absorbent resin also has extremely strong suction ammonia ability, fully its significant deodorizing effect of display.Due to these superior character of super absorbent resin, be highly suitable for the processing of paper nappy and sanitary napkin.The present invention adopts super absorbent resin lamination to be combined in the top of Alginate Film impervious barrier, can absorb water fast and deodorizing, with after throw into sewer time soluble in water, dissolved completely in 15 minutes, can not sewer blockage be caused.
Algin is the sizing material extracting with sea-tangle, bulk kelp or horse hair algae brown alga for raw material, obtain, and main component is water-soluble sodium alginate, has good filming performance, the timbering materials such as the food additives that Chang Zuowei eats and medical capsulae enterosolubilis.The structure of Alginate Film densification makes it have higher water preventing ability, and water droplet penetration time is at more than 800min.The present invention adopts Alginate Film impervious barrier liner in the below of super absorbent resin layer, has good anti-seepage effect, with after throw into sewer time then soluble in water, dissolved completely in 45 minutes, can not sewer blockage be caused.
The present invention not only cleaning effect is remarkable, and due to soluble in water, with after can throw into sewer, can not cause sewer blockage, large pollution sources of elimination toilet, are conducive to toilet health.
Accompanying drawing explanation
Concrete structure of the present invention is provided by following embodiment and accompanying drawing thereof.
Fig. 1 is the structural representation of concrete structure of the toilet paper a kind of soluble in water proposed according to the present invention.
In figure, (1) is reel, and (2) are super absorbent resin layer, and (3) are Alginate Film impervious barrier.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further.
Embodiment: as shown in Figure 1, a kind of toilet paper soluble in water, toilet paper forms the reel (1) of length 200 meters by the super absorbent resin layer (2) on upper strata and Alginate Film impervious barrier (3) pressing of lower floor.
Toilet paper is provided with ripple.
Super absorbent resin layer (2) adopts cornstarch acrylic acid graft copolymer film forming to obtain, the preparation technology of cornstarch acrylic acid graft copolymer is: add in reactor by cornstarch 85 kg and water 800 kg, be heated to 80 DEG C under nitrogen flowing, stir 1h, after making cornstarch gel, be cooled to 30 DEG C, add acrylic acid 120 kg and by 30% hydrogen peroxidase 10 .2 kg, after the polymerization catalyst that L-AA 0.1 kg forms, polyase 13 h is stirred at 40 DEG C, then 30% sodium hydroxide solution 120kg is added, a night is placed at 30 DEG C, drying under reduced pressure at 60 DEG C again, pulverize, obtained cornstarch acrylic acid graft copolymer.
Each component of Alginate Film impervious barrier (3) by weight formula rate is: algin 12%, glycerine 3%, calcium chloride 2%, water 83%, adds up to 100%.
Toilet paper adopts existing equipment and technique obtained super absorbent resin layer (2) and Alginate Film impervious barrier (3) respectively, upper and lower two-layer pressing is formed the reel (1) of length 200 meters.
Claims (5)
1. a toilet paper soluble in water, is characterized in that: described toilet paper forms by the super absorbent resin layer (2) on upper strata and Alginate Film impervious barrier (3) pressing of lower floor the reel (1) that length do not limit.
2. a kind of toilet paper soluble in water according to claim 1, it is characterized in that, described toilet paper is provided with ripple.
3. a kind of toilet paper soluble in water according to claim 1, it is characterized in that, described super absorbent resin layer (2) adopts cornstarch acrylic acid graft copolymer film forming to obtain, the preparation technology of described cornstarch acrylic acid graft copolymer is: add in reactor by cornstarch 85 parts and 800 parts, water, be heated to 80 DEG C under nitrogen flowing, stir 1h, after making cornstarch gel, be cooled to 30 DEG C, add 120 parts, acrylic acid and by 30% hydrogen peroxidase 10 .2 part, after the polymerization catalyst of L-AA 0.1 part composition, polyase 13 h is stirred at 40 DEG C, then 30% sodium hydroxide solution 120 parts is added, a night is placed at 30 DEG C, drying under reduced pressure at 60 DEG C again, pulverize, obtained cornstarch acrylic acid graft copolymer.
4. a kind of toilet paper soluble in water according to claim 1, is characterized in that, each component of described Alginate Film impervious barrier (3) by weight formula rate is: algin 12%, glycerine 3%, calcium chloride 2%, water 83%, adds up to 100%.
5. a kind of toilet paper soluble in water according to claim 1, it is characterized in that, described toilet paper adopts existing equipment and technique obtained super absorbent resin layer (2) and Alginate Film impervious barrier (3) respectively, upper and lower two-layer pressing is formed the reel (1) that length is not limit.