CN104774480A - Vegetable fiber product and manufacturing method thereof - Google Patents

Abstract

The invention relates to a vegetable fiber product and a manufacturing method thereof. The vegetable fiber product is prepared from 40-60wt% of bamboo powder, 20-30wt% of urea-formaldehyde molding powder, 6-10wt% of corn starch, 6-10wt% of powdered steatile, 0.5-0.8wt% of water, 0.001-0.03wt% of an organic dye, 3-5wt% of flour and 0.3-0.5wt% of zinc stearate. The vegetable fiber product has a wide source, saves sources, is environmentally friendly, has a low cost, can be recycled and naturally degraded after use, and does not produce pollutants.

Description

A kind of plant fiber products and preparation method thereof

Technical field

The present invention relates to a kind of plant fiber products and preparation method thereof.

Background technology

Along with improving constantly of people's living standard, the demand of mineral products and natural resources is also got more and more, exacerbate the in short supply of all kinds of resource, its cost is also constantly soaring, and a lot of resource all can cause certain pollution in exploitation, production, use procedure, therefore some countries are all focusing on recycling and the exploitation of some wastes and agricultural byproducts.

In life, we can often touch some plastics and paper product.In short supply due to petroleum resources, oil price constantly goes up, cause the cost of some plastics constantly to rise, simultaneously because plastics also cannot cause very large pollution to environment by natural degradation, therefore the plastics of a big chunk have the trend replaced by other materials goods.And the goods that paper using makes, need paper to do raw material, the manufacture of paper must be fallen trees again, damages not only to ecological natural environment, and papermaking also can produce a large amount of sewage, causes secondary pollution to environment, is unfavorable for environmental protection; Meanwhile, the goods that paper using makes, complex process, production efficiency is low, and cost is high; Larger defect is also in use, and due to the climate change such as temperature, humidity, its working strength exists very large problem, and meeting deliquescing that humidity is high, increases the also corresponding increase of thickness cost, and the goods that therefore paper using makes receive the restriction of arriving very much in use.

Summary of the invention

For the deficiencies in the prior art, the present invention aims to provide a kind of plant fiber products and preparation method thereof, its not only raw material sources extensively, save, environmental protection, making method is simple, cost is low, and can also reclaim after obtained product abandonment and do recycle, simultaneously these goods discarded after can natural degradation, pollution-free.

In order to solve the problem, the invention provides following technical scheme:

A kind of plant fiber products, described plant fiber products is made by the raw material of following weight percents: bamboo powder: 40% ~ 60%, urea-formaldehyde moulding powder: 20% ~ 30%, W-Gum: 6% ~ 10%, talcum powder: 6% ~ 10%, water: 0.5% ~ 0.8%, organic dye: 0.001% ~ 0.03%, flour 3% ~ 5%, Zinc Stearate 3% ~ 5%.

A making method for plant fiber products, the first step, puts into high-speed mixer and stirs 3 minutes by bamboo powder, urea-formaldehyde moulding powder, starch, talcum powder, organic dye, flour and Zinc Stearate;

Second step, after the first step completes, in high-speed mixer stirs, family adds water continuation stirring 2 minutes;

3rd step, then after second step completes, compound is poured in product mold, and places it on vulcanizing press, heat to 180 DEG C until products solidifying is shaping;

4th step, after the 3rd step completes, by the moulding product demoulding.

Beneficial effect: the present invention not only raw material sources extensively, save, environmental protection, making method is simple, and cost is low, and can also reclaim after obtained product abandonment and do recycle, simultaneously these goods discarded after can natural degradation, pollution-free.

Embodiment

A kind of plant fiber products, described plant fiber products is made by the raw material of following weight percents: bamboo powder: 40% ~ 60%, urea-formaldehyde moulding powder: 20% ~ 30%, W-Gum: 6% ~ 10%, talcum powder: 6% ~ 10%, water: 0.5% ~ 0.8%, organic dye: 0.001% ~ 0.03%, flour 3% ~ 5%, Zinc Stearate 0.3% ~ 0.5%.

A making method for plant fiber products, the first step, puts into high-speed mixer stir bamboo powder, urea-formaldehyde moulding powder, starch, talcum powder, organic dye, flour 3 minutes; Second step, after the first step completes, in high-speed mixer stirs, family adds water continuation stirring 2 minutes; 3rd step, then after second step completes, compound is poured in product mold, and places it on vulcanizing press, heat to 180 DEG C until products solidifying is shaping; 4th step, after the 3rd step completes, by the moulding product demoulding.

The above, it is only preferred embodiment of the present invention, not any restriction is made to technical scope of the present invention, thus every above embodiment is done according to technical spirit of the present invention any trickle amendment, equivalent variations and modification, all still belong in the scope of technical scheme of the present invention.

Claims (2)

1. a plant fiber products, it is characterized in that: described plant fiber products is made by the raw material of following weight percents: bamboo powder: 40% ~ 60%, urea-formaldehyde moulding powder: 20% ~ 30%, W-Gum: 6% ~ 10%, talcum powder: 6% ~ 10%, water: 0.5% ~ 0.8%, organic dye: 0.001% ~ 0.03%, flour 3% ~ 5%, Zinc Stearate 0.3% ~ 0.5%.

2. the making method of a kind of plant fiber products according to claim 1, is characterized in that: the first step, bamboo powder, urea-formaldehyde moulding powder, starch, talcum powder, organic dye, flour and Zinc Stearate is put into high-speed mixer and stirs 3 minutes;

Second step, after the first step completes, in high-speed mixer stirs, family adds water continuation stirring 2 minutes;

3rd step, then after second step completes, compound is poured in product mold, and places it on vulcanizing press, heat to 180 DEG C until products solidifying is shaping;

4th step, after the 3rd step completes, by the moulding product demoulding.