CN104745110A - 用于导电布的无卤阻燃热熔胶膜及其制备方法 - Google Patents

用于导电布的无卤阻燃热熔胶膜及其制备方法 Download PDF

Info

Publication number
CN104745110A
CN104745110A CN201510195982.9A CN201510195982A CN104745110A CN 104745110 A CN104745110 A CN 104745110A CN 201510195982 A CN201510195982 A CN 201510195982A CN 104745110 A CN104745110 A CN 104745110A
Authority
CN
China
Prior art keywords
parts
halogen
melt adhesive
free flame
conductive fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510195982.9A
Other languages
English (en)
Inventor
杜卫卫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510195982.9A priority Critical patent/CN104745110A/zh
Publication of CN104745110A publication Critical patent/CN104745110A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于导电布的无卤阻燃热熔胶膜及其制备方法，其特征在于：它是主要由以下重量份的原料组成的：聚酯热熔胶25～50份；十二碳醇酯23～38份；可膨胀石墨10～17份；单季戊四醇10～35份；双氰胺5～13份。本发明具有耐寒耐湿，阻燃效果好，无毒无二次危害，粘结度好的优点。

Description

用于导电布的无卤阻燃热熔胶膜及其制备方法
技术领域：
    本发明涉及一种用于导电布的无卤阻燃热熔胶膜及其制备方法，具体地说是一种化工热熔胶膜材料。
背景技术：
热熔胶是一种可塑性的粘合剂，在一定温度范围内其物理状态随温度改变而改变，而化学特性不变，其无毒无味，属环保型化学产品。因其产品本身系固体，便于包装、运输、存储、无溶剂、无污染、无毒型；以及生产工艺简单，高附加值，黏合强度大、速度快等优点而备受青睐。
而热熔胶胶膜是一种带离型纸或不带离型纸的膜类产品，可以方便地进行连续或间歇操作。传统的热熔胶胶膜为含卤阻燃热熔胶膜，而含卤阻燃材料在阻燃过程中会产生大量的烟雾和有毒的腐蚀性卤化氢气体，造成成二次危害，这已经不符合国际环保要求了，故此新型环保无卤阻燃热熔胶膜急需发展。
发明内容：
本发明的目的是为了提供一种耐寒耐湿，阻燃效果好，无毒无二次危害，粘结度好的环保型的用于导电布的无卤阻燃热熔胶膜及其制备方法，制备方法简单方便。
    本发明的目的通过以下技术方案来实现：一种用于导电布的无卤阻燃热熔胶膜，它是主要由以下重量份的原料组成的：
聚酯热熔胶25～50份；
十二碳醇酯23～38份；
可膨胀石墨10～17份；
单季戊四醇10～35份；
双氰胺5～13份。
用于导电布的无卤阻燃热熔胶膜的制备方法，具体制作步骤如下：将所述的聚酯热熔胶与十二碳醇酯、可膨胀石墨、单季戊四醇和双氰胺在温度230-280℃下进行混合，反应时间2.5-3h之后用常规的离型纸刮膜工艺即可得到用于导电布的无卤阻燃热熔胶膜。
本发明有益效果为：
本发明包含了聚酯热熔胶，聚酯PET是主链中含有酯基—COO—的聚合物的总称，由于其是由二元酸和二元醇或醇酸缩聚而成，聚酯热熔胶具有优异的电绝缘性和较好的粘结强度，耐冲击性、耐水、耐寒、耐介质及弹性都较好。
本发明包含了十二碳醇酯，其可以降低成膜温度，成膜速度加快。
本发明包含了可膨胀石墨、单季戊四醇和双氰胺，可膨胀石墨膨胀的初始温度为220C左右，一般在220C开始轻微膨胀230-280C迅速膨胀，之后体积可达原来的100多倍，甚至280倍。可膨胀石墨在阻燃过程中主要起到以下作用：在高聚物表面形成坚韧的炭层，将可燃物与热源隔开；在膨胀过程中大量吸热，降低了体系的温度；在膨胀过程中释放夹层中的酸根离子，促进脱水碳化，并能结合单季戊四醇和双氰胺燃烧产生的自由基从而中断链反应。
本发明无卤，在阻燃过程中不会产生大量的烟雾和有毒的腐蚀性卤化氢气体，不会造成成二次危害，符合国际环保要求。
具体实施方式：
    为了加深对本发明的理解，下面将结合实例对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
本发明实施方式为：
实施例1：
    一种用于导电布的无卤阻燃热熔胶膜，它是主要由以下重量份的原料组成的：
聚酯热熔胶25份；
十二碳醇酯35份；
可膨胀石墨10份；
单季戊四醇25份；
双氰胺5份。
用于导电布的无卤阻燃热熔胶膜的制备方法，具体制作步骤如下：将上述的聚酯热熔胶与十二碳醇酯、可膨胀石墨、单季戊四醇和双氰胺在温度230℃下进行混合，反应时间2.5h之后用常规的离型纸刮膜工艺即可得到用于导电布的无卤阻燃热熔胶膜。
实施例2：
    一种用于导电布的无卤阻燃热熔胶膜，它是主要由以下重量份的原料组成的：
聚酯热熔胶24份；
十二碳醇酯23份；
可膨胀石墨13份；
单季戊四醇30份；
双氰胺10份。
    用于导电布的无卤阻燃热熔胶膜的制备方法，具体制作步骤如下：将上述的聚酯热熔胶与十二碳醇酯、可膨胀石墨、单季戊四醇和双氰胺在温度280℃下进行混合，反应时间3h之后用常规的离型纸刮膜工艺即可得到用于导电布的无卤阻燃热熔胶膜。
    实施例3：
   一种用于导电布的无卤阻燃热熔胶膜，它是主要由以下重量份的原料组成的：
聚酯热熔胶22份；
十二碳醇酯38份；
可膨胀石墨10份；
单季戊四醇17份；
双氰胺13份。
    用于导电布的无卤阻燃热熔胶膜的制备方法，具体制作步骤如下：将上述的聚酯热熔胶与十二碳醇酯、可膨胀石墨、单季戊四醇和双氰胺在温度250℃下进行混合，反应时间2.5h之后用常规的离型纸刮膜工艺即可得到用于导电布的无卤阻燃热熔胶膜。
    实施例4：
一种用于导电布的无卤阻燃热熔胶膜，它是主要由以下重量份的原料组成的：
聚酯热熔胶50份；
十二碳醇酯23份；
可膨胀石墨10份；
单季戊四醇10份；
双氰胺7份。
用于导电布的无卤阻燃热熔胶膜的制备方法，具体制作步骤如下：将上述的聚酯热熔胶与十二碳醇酯、可膨胀石墨、单季戊四醇和双氰胺在温度240℃下进行混合，反应时间3h之后用常规的离型纸刮膜工艺即可得到用于导电布的无卤阻燃热熔胶膜。
实施例5:
    一种用于导电布的无卤阻燃热熔胶膜，它是主要由以下重量份的原料组成的：
聚酯热熔胶45份；
十二碳醇酯23份；
可膨胀石墨12份；
单季戊四醇13份；
双氰胺7份。
用于导电布的无卤阻燃热熔胶膜的制备方法，具体制作步骤如下：将上述的聚酯热熔胶与十二碳醇酯、可膨胀石墨、单季戊四醇和双氰胺在温度260℃下进行混合，反应时间2.5h之后用常规的离型纸刮膜工艺即可得到用于导电布的无卤阻燃热熔胶膜。
实施例6：
一种用于导电布的无卤阻燃热熔胶膜，它是主要由以下重量份的原料组成的：
聚酯热熔胶30份；
十二碳醇酯25份；
可膨胀石墨15份；
单季戊四醇20份；
双氰胺10份。
用于导电布的无卤阻燃热熔胶膜的制备方法，具体制作步骤如下：将上述的聚酯热熔胶与十二碳醇酯、可膨胀石墨、单季戊四醇和双氰胺在温度270℃下进行混合，反应时间3h之后用常规的离型纸刮膜工艺即可得到用于导电布的无卤阻燃热熔胶膜。
以上所述仅为发明本发明的实施方式，并不用于限制本发明，对于本领域的技术人员来说，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (2)

1.一种用于导电布的无卤阻燃热熔胶膜，其特征在于：它是主要由以下重量份的原料组成的：
聚酯热熔胶25～50份；
十二碳醇酯23～38份；
可膨胀石墨10～17份；
单季戊四醇10～35份；
双氰胺5～13份。
2.根据权利要求1所述的用于导电布的无卤阻燃热熔胶膜的制备方法，其特征在于：具体制作步骤如下：将所述的聚酯热熔胶与十二碳醇酯、可膨胀石墨、单季戊四醇和双氰胺在温度230-280℃下进行混合，反应时间2.5-3h之后用常规的离型纸刮膜工艺即可得到用于导电布的无卤阻燃热熔胶膜。
CN201510195982.9A 2015-04-23 2015-04-23 用于导电布的无卤阻燃热熔胶膜及其制备方法 Pending CN104745110A (zh)