CN104710784A - Socket prepared from nylon material with long service life - Google Patents
Socket prepared from nylon material with long service life Download PDFInfo
- Publication number
- CN104710784A CN104710784A CN201510071448.7A CN201510071448A CN104710784A CN 104710784 A CN104710784 A CN 104710784A CN 201510071448 A CN201510071448 A CN 201510071448A CN 104710784 A CN104710784 A CN 104710784A
- Authority
- CN
- China
- Prior art keywords
- nylon
- parts
- service life
- socket
- long service
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a socket prepared from a nylon material with a long service life. The socket is prepared from the following raw material in parts by weight: 65-85 parts of nylon 66 resin, 15-20 parts of MC nylon, 3-5 parts of PP, 4-6 parts of POE, 0.3-0.5 part of zinc naphthenate, 1.1-2.3 parts of sodium sulfide, 30-40 parts of chopped glass fiber, 30-40 parts of a sintering packing, 3-5 parts of ethoxylation wool fat, 3-7 parts of calcium stearate, 2-4 parts of zinc stearate, 0.1-0.2 part of hydroxypropyl methyl cellulose, 0.3-0.5 part of triethanolamine oleate and 0.5-1 part of an antioxidant BHT. As the nylon material, PP and the like are taken as main raw materials, the socket is long in service life, environment-friendly, wearing resisting, high in strength, simple to prepare and convenient to use.
Description
Technical field
The present invention relates to field of plastic products, is exactly socket prepared by a kind of long service life nylon material.
Background technology
Plastics be adopt plastics be main raw material process daily necessities, industrial goods general designation.Comprise the goods of all technique such as injection moulding, plastic uptake there to be raw material with plastics.Plastic cement is that a class has plastic synthesized polymer material.
Tynex is commonly called as nylon (Nylon), English name Polyamide(is called for short PA), density 1.15g/cm3, be on molecular backbone chain containing recurring amide radical group-[NHCO]-thermoplastic resin general name, comprise aliphatics PA, fat-aromatic series PA and aromatic series PA.Wherein aliphatics PA is wide in variety, and output is large, and be widely used, its name is determined by the carbonatoms that synthon is concrete.Invented by famous American chemist Tomas Carothers and his computer MSR Information system.Nylon is a kind of saying of tynex (polyamide fibre), can be made into long fine or short fiber.
Summary of the invention
The object of the present invention is to provide socket prepared by a kind of long service life nylon material.
Above-mentioned purpose is realized by following scheme:
A socket prepared by long service life nylon material, is characterized in that: it is obtained by the raw material of following weight parts:
Nylon 66 65-85, MC nylon 15-20, PP3-5, POE4-6, zinc naphthenate 0.3-0.5, sodium sulphite 1.1-2.3, short glass fiber 30-40, sintering filler 30-40, ethoxylated lanolin 3-5, calcium stearate 3-7, Zinic stearas 2-4, Vltra tears 0.1-0.2, triethanolamine oleate 0.3-0.5, antioxidant BHT 0.5-1;
Sintering filler is obtained by the raw material of following weight parts:
Sepiolite powder 8-10, boehmite powder 1.3-2.5, polyacrylamide 0.5-1.2, calcium metasilicate 2-4, gypsum 0.1-0.3, stearic acid 1-1.2, lithium chloride 0.6-0.8, magnesium nitrate 0.1-0.3, butyl acrylate 1.2-2.6, concentration are that hydrochloric acid 1-3, the oleic acid 0.3-0.4 of 3-5%, carob bean gum 0.5-0.8, deionized water are appropriate;
The preparation method of sintering filler is:
Magnesium nitrate, butyl acrylate, concentration be the hydrochloric acid of 3-5%, oleic acid, carob bean gum, deionized water and stirring evenly after, add boehmite powder again, 60-80 rev/min is stirred 20-30 minute, water-bath 30-40min at 60-80 DEG C again, adds all the other raw materials again after taking out cooling, stirs 10-20min under 100-200 rev/min, after gained raw material drying, 4-7 minute is sintered again, grinding, after crossing 100-200 mesh sieve and get final product at 180-220 DEG C.
Socket prepared by described a kind of long service life nylon material, is characterized in that:
Preparation method comprises the following steps:
(1), after Nylon 66, MC nylon, PP, POE, zinc naphthenate, sodium sulphite, short glass fiber, sintering filler, ethoxylated lanolin being mixed, at 140-150 DEG C, 10-13min mediated by kneader, obtains mixing materials for subsequent use;
(2) surplus stock is stirred 50-60min at 55-65 rev/min of lower 50-60 DEG C, obtain compound;
(3), after being mixed with mixing materials by gained compound, after melt extruding granulation at 150-155 DEG C on the twin screw extruder, namely material is obtained,
(4) by after gained material forming, to obtain final product.
Beneficial effect of the present invention is: nylon material of the present invention and PP etc. are main raw material, and the material lifetime of preparation is long, environmental protection, wear-resisting, and intensity is high, and preparation is simple, easy to use.
Embodiment
A socket prepared by long service life nylon material, it is obtained by the raw material of following weight (kg):
Nylon 66 83, MC nylon 15, PP5, POE6, zinc naphthenate 0.3, sodium sulphite 1.3, short glass fiber 40, sintering filler 30, ethoxylated lanolin 5, calcium stearate 3, Zinic stearas 2, Vltra tears 0.2, triethanolamine oleate 0.5, antioxidant BHT 0.5;
Sintering filler is obtained by the raw material of following weight (kg):
Sepiolite powder 8, boehmite powder 1.5, polyacrylamide 1.2, calcium metasilicate 2, gypsum 0.1, stearic acid 1, lithium chloride 0.6, magnesium nitrate 0.1, butyl acrylate 1.6, concentration be 5% hydrochloric acid 3, oleic acid 0.4, carob bean gum 0.8, deionized water appropriate;
The preparation method of sintering filler is:
Magnesium nitrate, butyl acrylate, concentration be 5% hydrochloric acid, oleic acid, carob bean gum, deionized water and stirring evenly after, add boehmite powder again, 60 revs/min are stirred 30 minutes, water-bath 40min at 70 DEG C again, adds all the other raw materials again after taking out cooling, stirs 15min under 150 revs/min, after gained raw material drying, at 220 DEG C, sinter 5 minutes again, grinding, cross after 200 mesh sieves and get final product.
Socket prepared by described a kind of long service life nylon material,
Preparation method comprises the following steps:
(1), after Nylon 66, MC nylon, PP, POE, zinc naphthenate, sodium sulphite, short glass fiber, sintering filler, ethoxylated lanolin being mixed, at 143 DEG C, 10min mediated by kneader, obtains mixing materials for subsequent use;
(2) surplus stock is stirred 60min at 57 revs/min lower 60 DEG C, obtain compound;
(3), after being mixed with mixing materials by gained compound, after melt extruding granulation at 155 DEG C on the twin screw extruder, namely material is obtained,
(4) by after gained material forming, to obtain final product.
The performance detection data of the socket that the present embodiment obtains sees the following form:
Claims (2)
1. the socket prepared of long service life nylon material, is characterized in that: it is obtained by the raw material of following weight parts:
Nylon 66 65-85, MC nylon 15-20, PP3-5, POE4-6, zinc naphthenate 0.3-0.5, sodium sulphite 1.1-2.3, short glass fiber 30-40, sintering filler 30-40, ethoxylated lanolin 3-5, calcium stearate 3-7, Zinic stearas 2-4, Vltra tears 0.1-0.2, triethanolamine oleate 0.3-0.5, antioxidant BHT 0.5-1;
Sintering filler is obtained by the raw material of following weight parts:
Sepiolite powder 8-10, boehmite powder 1.3-2.5, polyacrylamide 0.5-1.2, calcium metasilicate 2-4, gypsum 0.1-0.3, stearic acid 1-1.2, lithium chloride 0.6-0.8, magnesium nitrate 0.1-0.3, butyl acrylate 1.2-2.6, concentration are that hydrochloric acid 1-3, the oleic acid 0.3-0.4 of 3-5%, carob bean gum 0.5-0.8, deionized water are appropriate;
The preparation method of sintering filler is:
Magnesium nitrate, butyl acrylate, concentration be the hydrochloric acid of 3-5%, oleic acid, carob bean gum, deionized water and stirring evenly after, add boehmite powder again, 60-80 rev/min is stirred 20-30 minute, water-bath 30-40min at 60-80 DEG C again, adds all the other raw materials again after taking out cooling, stirs 10-20min under 100-200 rev/min, after gained raw material drying, 4-7 minute is sintered again, grinding, after crossing 100-200 mesh sieve and get final product at 180-220 DEG C.
2. the socket prepared of a kind of long service life nylon material according to claim 1, is characterized in that:
Preparation method comprises the following steps:
(1), after Nylon 66, MC nylon, PP, POE, zinc naphthenate, sodium sulphite, short glass fiber, sintering filler, ethoxylated lanolin being mixed, at 140-150 DEG C, 10-13min mediated by kneader, obtains mixing materials for subsequent use;
(2) surplus stock is stirred 50-60min at 55-65 rev/min of lower 50-60 DEG C, obtain compound;
(3), after being mixed with mixing materials by gained compound, after melt extruding granulation at 150-155 DEG C on the twin screw extruder, namely material is obtained,
(4) by after gained material forming, to obtain final product.