CN104693569A - Insulating plastic for electronic products - Google Patents
Insulating plastic for electronic products Download PDFInfo
- Publication number
- CN104693569A CN104693569A CN201310653615.XA CN201310653615A CN104693569A CN 104693569 A CN104693569 A CN 104693569A CN 201310653615 A CN201310653615 A CN 201310653615A CN 104693569 A CN104693569 A CN 104693569A
- Authority
- CN
- China
- Prior art keywords
- electronic products
- plastics
- insulating plastic
- insulating plastics
- plastics according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to insulating plastic for electronic products and belongs to the field of plastic products. The insulating plastic for electronic products is prepared from polyether-ether-ketone, high density polyethylene, epoxy resin, polyethylene glycol, a surfactant, a polymerization initiator, a pigment and a styrene-maleic anhydride copolymer. The insulating plastic has low conductivity and environmental protection and self-cleaning functions.
Description
Technical field
The present invention relates to a kind of use for electronic products insulating plastics, belong to field of plastic products.
Background technology
Along with the development of science and technology, the life of people is more and more convenient, especially in office, along with various office appliance easily occurs, as computer, fax, phone, printer, staff can process a large amount of things in office, and the time of these office appliances of worker exposure is also more and more longer thus, and the security of electronic product is also more and more subject to people's attention.Insulating plastics is more and more subject to people's attention for sheating material as substantially all electronic products, and the quality of insulating property determines the security feature of product.
Summary of the invention
The object of this invention is to provide a kind of use for electronic products insulating plastics, this insulating plastics has the low feature of specific conductivity, and has environmental protection self-cleaning function simultaneously.
A kind of use for electronic products insulating plastics, described plastics, by mass parts, prepare gained by following raw material:
The preferred described plastics of use for electronic products insulating plastics of the present invention, by mass parts, prepare gained by following raw material:
The molecular weight of the preferred described high density polyethylene(HDPE) of use for electronic products insulating plastics of the present invention is 500000 ~ 2000000.
The polymerization degree of the preferred described styrene-maleic anhydride copolymer of use for electronic products insulating plastics of the present invention is 100000 ~ 5000000.
The preferred described tensio-active agent of use for electronic products insulating plastics of the present invention is sodium laurylsulfonate.
The preferred described polymerization starter of use for electronic products insulating plastics of the present invention is di-isopropylbenzene hydroperoxide.
A kind of preparation method of use for electronic products insulating plastics, ether ether ketone, high density polyethylene(HDPE), epoxy resin, polyoxyethylene glycol, colorant, styrene-maleic anhydride copolymer are incubated 0.1 ~ 0.5h at being placed in reactor 180 ~ 240 DEG C, after add tensio-active agent and polymerization starter, insulation 2 ~ 24h at 200 ~ 300 DEG C after mixing, cooling both obtained.
The invention has the beneficial effects as follows: use for electronic products insulating plastics of the present invention is obtained by following material: polyether-ether-ketone, high density polyethylene(HDPE), epoxy resin, polyoxyethylene glycol, tensio-active agent, polymerization starter, colorant, styrene-maleic anhydride copolymer.Insulating plastics of the present invention has the low feature of specific conductivity, and has environmental protection self-cleaning function simultaneously.
Embodiment
Following non-limiting example can make the present invention of those of ordinary skill in the art's comprehend, but does not limit the present invention in any way.
Embodiment 1
A kind of preparation method of use for electronic products insulating plastics, ether ether ketone, high density polyethylene(HDPE), epoxy resin, polyoxyethylene glycol, colorant are incubated 0.1h at being placed in reactor 200 DEG C, after add tensio-active agent and polymerization starter, 10h is incubated at mixing latter 265 DEG C, cooling both obtained, raw material, by mass parts, is made up of following component:
Embodiment 2
A kind of preparation method of use for electronic products insulating plastics, ether ether ketone, high density polyethylene(HDPE), epoxy resin, polyoxyethylene glycol, colorant, styrene-maleic anhydride copolymer are incubated 0.1h at being placed in reactor 220 DEG C, after add tensio-active agent and polymerization starter, be incubated 8h at mixing latter 280 DEG C, cooling both obtained.
Claims (6)
1. a use for electronic products insulating plastics, is characterized in that: described plastics, by mass parts, prepares gained by following raw material:
2. plastics according to claim 1, is characterized in that: described plastics, by mass parts, prepare gained by following raw material:
3. plastics according to claim 1, is characterized in that: the molecular weight of described high density polyethylene(HDPE) is 500000 ~ 2000000.
4. plastics according to claim 1, is characterized in that: the polymerization degree of described styrene-maleic anhydride copolymer is 100000 ~ 5000000.
5. plastics according to claim 1, is characterized in that: described tensio-active agent is sodium laurylsulfonate.
6. plastics according to claim 1, is characterized in that: described polymerization starter is di-isopropylbenzene hydroperoxide.