CN104680216B - Two-dimensional code anti-counterfeiting label and its printing process - Google Patents
Two-dimensional code anti-counterfeiting label and its printing process Download PDFInfo
- Publication number
- CN104680216B CN104680216B CN201510026612.2A CN201510026612A CN104680216B CN 104680216 B CN104680216 B CN 104680216B CN 201510026612 A CN201510026612 A CN 201510026612A CN 104680216 B CN104680216 B CN 104680216B
- Authority
- CN
- China
- Prior art keywords
- microballon
- pearly
- lustre
- code
- dimensional code
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to field of anti-counterfeit technology, and in particular to a kind of two-dimensional code anti-counterfeiting label and its printing process.Two-dimensional code anti-counterfeiting label is made by following methods:1. the pearly-lustre microballon of different colours is prepared, the particle diameter of pearly-lustre microballon is 0.1 3 millimeters, 2. step 1. obtained pearly-lustre microballon is added in using resin as the ink of main component, the ink special for printing two-dimensional code anti-counterfeiting label is obtained after mixing, the usage amount of pearly-lustre microballon is the 5 80% of weight resin, pearly-lustre microballon selects more than three kinds colors, 3. pattern in 2 D code is printed using above-mentioned ink special on the product or label paper for need to print Quick Response Code, make no more than 1 pearly-lustre microballon of printing in each cell of Quick Response Code, the pearly-lustre microballon of more than three kinds colors is randomly formed specific pattern in 2 D code.The two-dimensional code anti-counterfeiting label of the present invention can not almost be repeated, and the probability repeated is less than 1/100000000th, even if repeating, can be excluded by detecting system.
Description
Technical field
The invention belongs to field of anti-counterfeit technology, and in particular to a kind of two-dimensional code anti-counterfeiting label and its printing process.
Background technology
Low-quality goods is always the formidable enemy of proper enterprise, and there are currently no a simple Antiforge system veritably can be of poor quality
Product differentiation is gone out, even multilayer laser anti-counterfeit label, it is also possible to which the imitation of similar technology comes out.Low-quality goods possesses oneself
Circulation systems, particularly Internet era, circulation duct is more complicated, by controlling circulation duct to be that to be unable to reach elimination pseudo-
Bad product is in the circulation in market, and unique feasible is that consumer's self-authentication certified products rejects low-quality goods.Quick Response Code can pass through
Network is used for linking up with businessman, but can not be not unique for false proof, because Quick Response Code can be replicated particularly simple
Property, not reproducible then to can be a security code with almost unique and uncertain Quick Response Code, this code is taken the photograph by possessing
The life experience of product can be confirmed perfectly safely as the database of function smart mobile phone and network and producer is compared.Can not simply it answer
System means the printing of unavailable ordinary numbers printer, and its color and luster is not unique reproducible, if just possess can not for a mess code
Predictability, possesses intimate uniqueness, the arrangement summation of 400 bits of such as one four color is 10 if its excursion is huge
240 powers.So the invention provides the material for producing not reproducible huge two-dimentional mess code production and typography.
The content of the invention
The present invention provides a kind of two-dimensional code anti-counterfeiting label of not reproducible high uniqueness.
The present invention also provides a kind of printing process of the two-dimensional code anti-counterfeiting label.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of two-dimensional code anti-counterfeiting label, it is made by following methods:
1. the pearly-lustre microballon of different colours is prepared, the particle diameter of pearly-lustre microballon is 0.1-3 millimeters,
2. step 1. obtained pearly-lustre microballon is added in using resin as the ink of main component, obtains being used to print after mixing
The ink special of brush two-dimensional code anti-counterfeiting label, the usage amount of pearly-lustre microballon is the 5-80% of weight resin, and pearly-lustre microballon selects three kinds
Above color,
3. pattern in 2 D code is printed using above-mentioned ink special on the product or label paper for need to print Quick Response Code, makes two dimension
No more than 1 pearly-lustre microballon of printing in each cell of code, the pearly-lustre microballon of more than three kinds colors is randomly formed specific two
Tie up code pattern.The pattern in 2 D code is random generation, it is ensured that uniqueness.
Preferably, the pearly-lustre microballon is selected from metal microbead, the coated microballon in surface or polymethacrylates microballon.
Preferably, the particle diameter of pearly-lustre microballon is 0.3-1 millimeters.
Preferably, the pearly-lustre microballon of each color accounts for the overall accumulated amount more than 5% of pearly-lustre microballon.
Preferably, for four color systems, it is 20-60% that the pearly-lustre microballon of each color, which accounts for the overall accumulated amount of pearly-lustre microballon,.
A kind of printing process of described two-dimensional code anti-counterfeiting label, this method comprises the following steps:
1. the pearly-lustre microballon of different colours is prepared, the particle diameter of pearly-lustre microballon is 0.1-3 millimeters,
2. step 1. obtained pearly-lustre microballon is added in using resin as the ink of main component, obtains being used to print after mixing
The ink special of brush two-dimensional code anti-counterfeiting label, the usage amount of pearly-lustre microballon is the 5-80% of weight resin, and pearly-lustre microballon selects three kinds
Above color,
3. pattern in 2 D code is printed using above-mentioned ink special on the product or label paper for need to print Quick Response Code, makes two dimension
No more than 1 pearly-lustre microballon of printing in each cell of code, the pearly-lustre microballon of more than three kinds colors is randomly formed specific two
Tie up code pattern.
Preferably, described printing uses silk-screen printing, the size of pearly-lustre microballon close to silk-screen printing net hole size,
Each net hole is set to stamp a pearly-lustre microballon.
The present invention is made up of 2 parts:1)The synthesis of special three-dimensional pearlescent pigment, and 2)The production and printing of ink and
Record.
The present invention produces not reproducible high uniqueness 2 using method for printing and the spherical color pigment of special 3-dimensional and ties up colored mess code,
The mess code can be tested as antifalsification label by having the mobile phone of camera function and corresponding software and internet to be used for linking up with businessman
Demonstrate,prove the true and false and sequence number of product.Ink formulations are resin, solvent, pigment, pearly-lustre microballon and various auxiliary agents comprising binding agent.Printing
Pattern is that another is designed to increase uniqueness, standard and specification except meeting Quick Response Code, and other is all variable part.Root
QR codes of pattern such as standard according to user's design Quick Response Code etc. or completely non-standard pattern, in principle for
It is colour code, and is colored mess code, its information content is the several times of black and white code, for example totally 4 color(Including background color), its information content
It is 4 times of standard, if 8 color information content are 32 times.When Quick Response Code prints, using the different colours that color aberration is larger, example
As reddish yellow is bluish-green.
The production of Part I pearly-lustre microballon
The present invention at least production 3-8 kind different colours suitable silk-screen printing three-dimensional pearly-lustre microballon, pearly-lustre microballon it is big
The small size close to silk-screen printing net hole, makes each net hole to stamp a pearly-lustre microballon, and microballon particle diameter is 0.1-3 millimeters,
The too small more difficult display 3-dimensional third dimension of microballon and camera can not differentiate each colour cell, easily come off greatly very much, what is be more suitable for is big
It is small to be less than more than 0.3 millimeter between 1 millimeter, although other method for printing can also be used, such as intaglio plate and letterpress, silk screen
Printing is more suitable for.The net hole of silk screen should be slightly bigger than microballon, but can not be too big, and the position deviation for netting the too big microballon in hole is big, also has
The microballon that may have two different colours in same net hole causes print to read error.
Pearly-lustre microballon can be produced with various methods, below 2 simply wherein feasible lower cost method.Except following
Method and raw material, metal microbead can be used, the coated microballon in surface, pearly-lustre toner coloring epoxy resin microballon etc..
The production technology one of pearly-lustre microballon:Liquid epoxies comminution granulation
1. pearly-lustre toner and liquid epoxies mixed at high speed are obtained into uniform sizing material;
Pearly-lustre toner:Particle size select within pearly-lustre bead diameter, preferably pearly-lustre bead diameter ten/
Within one, such as 200 mesh, 325 mesh etc.;The addition of pearly-lustre toner is the 0.1-50% of weight epoxy, face during less than 0.1%
Color is too light, and viscosity is too high during more than 50%, it is difficult to mix.
Magnetic powder, warm variable pigments are also may be optionally added in above-mentioned slurry, to increase extra antiforge function.Magnetic powder is selected from carbonyl
Base iron nickel powder, carbonyl nickel powder, carbonyl iron dust, ferrite powder;Warm variable pigments show different colors warm temperature is upper and lower;
Liquid epoxies:Bisphenol-A, Bisphenol F or solid epoxy are dissolved in the liquid of solvent,
Rate of dispersion:More than 3000rpm or other process for dispersing pearly-lustre toner can be made uniformly to be mixed with epoxy resin, point
The time of dissipating requires to adjust according to fineness of dispersion, and granularity should be less than 30 microns.
2. a water miscible epoxy curing agent is poured into water and adds surfactant
Deionized water:It is(Epoxy resin+toner)1.5-20 times, less than 1.5 times epoxy resin balls may be bonded in
Together, more than 20 times low production efficiencies.
Water soluble solid agent:For example in ethylenediamine, diethylenetriamine, water concentration is 1-20%, according to epoxy resin equivalent and
Resin concentration is calculated.
Surfactant:Some curing agent have surfactant effect, can be in order to avoid few usage amount that adds deduct;Any species
Surfactant, as long as non-toxic and corrosivity, have no adverse reaction with curing agent;Concentration is 0.0-5%, more than 5%
Produce too many foam and to subsequent technique and using there may be ill effect.
Rate of dispersion:Middle low speed, not produce a large amount of foams as index.
3. the epoxy resin of toner is mixed with to add dissolved with the water of curing agent and stirring makes epoxy resin turn into little particle;
Rate of dispersion:Adjusted according to required granular size, not produce a large amount of foams as index.
4. persistently stirring and being heated for a period of hours until epoxy resin cure, the speed and temperature of stirring determine pearly-lustre microballon
Size, high-speed and high-temperature obtains small microballon, and low speed low temperature obtains big microballon, and relatively low temperature needs the longer reaction time.
Reaction temperature:15-90 DEG C, less than 15 DEG C reactions are slow, need to add substantial amounts of catalyst, higher than 90 DEG C, the evaporation of water
Comparatively fast, the stability of surfactant may go wrong.
Reaction time:0.1-24 hours, less than 0.1 hour too short solidification was not exclusively and reaction is difficult to control to, more than 24
Hour, low production efficiency does not conform to cost.
5. an obtained circular granular washing and drying, screening removes larger and less particle and is classified by granular size standby
With.
Wash and dry:Washed 3 times to 5 times with the deionization of the volume of about 3 times of particles, shower WATER-WASHING METHOD can also be used,
With screen cloth separation water and pearly-lustre bead particles, 20-80 DEG C of aeration-drying temperature to moisture is less than 5%, more preferably less than 1%.
Classification:For example screen cloth vibrations classification is divided into required series, such as 4 grades, 6 grades, 8 grades etc. from 10 mesh to 150 mesh;Greatly
Removed in 10 mesh less than 150 mesh.Also other partition methods, such as centrifugal separation etc. can be used.
The production technology two of pearly-lustre microballon:Microballon method
1. a glass microballoon for meeting size is washed successively with the processing of bronsted lowry acids and bases bronsted lowry liquid;
Pickling:Isometric 1N sulfuric acid washes glass microballoon, and screen filtration falls acid solution,
Alkali cleaning:Isometric 1N alkali lye(NaOH, KOH etc.)The glass microballoon of pickling is washed, screen filtration falls alkali lye,
Washing:The washed glass microballoon of deionized water soda, screen filtration falls water;
2. a ferric sulfate or titanium chloride can form the salt of other colors and dissolve in water, treated microballon is added, is stirred
Mix;
Salt amount:According to the color and the size of microballon and amount formed, the amount of salt needed for calculating, with deionized water formation about
0.1-10N solution, concentration is too low, and reaction efficiency is low, and too high reaction is uneven,
Mixing speed:The speed for adding microballon stirring ensures that microballon is not sunk to the bottom, and reaction is uniform;
The pH of bead solution is set to reach 6-13 3. adding alkali lye with measuring pump constant speed, and sustained response 2-24 hours, make iron
Or the compound precipitation of titanium etc. color on glass microballoon and needed for producing, the thickness of compound determines the difference of color, then
Weakly acidic pH is washed with deionized water;
Alkali lye:0.5-10N alkali lye is formed with deionized water, such as sodium hydroxide and potassium hydroxide solution, concentration are too low, instead
Answer efficiency low, too high reaction is uneven;
4. filtering, is dried, high temperature sintering obtains the microballon of pearly-lustre color;
Oxide is sintered to obtain in screen filtration, 60-180 DEG C of ventilation stirring drying, 400-800 DEG C of stirring sintering, air,
Sintered in nitrogen, molysite can obtain magnetic ferrites.
The Printing ink producing 1. of Part II microballon containing pearly-lustre is solvent, thickener, pigment and dyestuff, and levelling agent etc. is added
Simultaneously high-speed stirred obtains coloured or transparent resin solution to resin, and its granularity should be less than 20 microns.
Resin:Any kind of resin, one pack system, bi-component, heat curing-type, thermoplastics type, as long as being adapted to silk-screen printing,
Such as polymethacrylates, epoxy resin, polyurethane, polyester etc.;Account for the 10-90% of integral formula weight.
Solvent:It should be matched with resin, ethylbenzene, dimethyl benzene, methylisobutylketone, alcohols, etc.;Account for integral formula weight
5-90%。
Pigment and dyestuff:The color of change resin, such as iron oxide red, iron oxide yellow, titanium dioxide, etc., account for integral formula weight
0-30%。
Additive:Change manufacturability and feature, such as thickener, levelling agent etc., account for the 0-10% of integral formula weight.
Rate of dispersion:More than 3000rpm or other process for dispersing toner can be made uniformly to be mixed with resin, its granularity reaches
Less than 20 microns.
2. assorted pearly-lustre microballon needed for adding, mixed on low speed is uniform, ink is obtained, its viscosity is adapted to silk-screen printing, if viscous
Du Taigao, can be turned down with solvent.Range of viscosities 100-10000cP, more preferably scope 500-3000cP.
Various colored nacreous microballons:The part by weight of pearly-lustre microballon total amount and resin solution is 5-80:100, according to resin
Concentration regulation;Resin concentration is high, and pearly-lustre microballon can be added more, otherwise adds less, the ratio of pearly-lustre microballon can change blank
Ratio.
The ratio of various pearly-lustre microballons:5-90%, any of which microballon is difficult to form stable polychrome ideal less than 5%
Scrambling code combination;Ideal range for the various microballons of four color systems is 20-60%, and 4 color systems use the pearly-lustre microballon of 3 kinds of colors,
Background color is also a kind of color, i.e. the code without pearly-lustre microballon.
3. curing agent is added print if needed before and is stirred.
The printing of Part III two-dimensional code anti-counterfeiting label
Method for printing selection silk screen, intaglio plate or relief printing plate etc., silk-screen printing is best suitable for ideal 2 needed for providing and ties up mess code pattern.
The part by weight of chromatic colour pearly-lustre microballon in the formula of ink special, microballon total amount and resin solution is from 5:100 to 80:100,
Microballon should be greater than 0.1 millimeter and be less than 3 millimeters, and more preferably size range is between 0.3 to 1 millimeter, can to use in market
Satisfactory microballon, adhesive strength and durability are met as long as not specially required for resin and being adapted to printing.
Pearly-lustre microballon must size uniform be that diameter distribution is narrow, the hole of silk screen slightly larger than maximum microballon but can not
To accommodate in 2 minimum pearly-lustre microballons, i.e., each silk screen hole in printing, including each only one of which pearly-lustre microballon.Print
Map brushing case can be any shape, itself also possess the false proof function in part or the different product of difference and sequence number etc., its
It is interior to possess the uniqueness that enough holes meet mess code, i.e., should more than 100 holes, the colour for obtaining more than 100 is single
Member, 1.6x10 can be formed for 4 colour codings60Possible mess code arrangement, 6.7x10 can be obtained preferably over 400 units240Possible mess code
Arrangement, in 1,000,000,000 mess codes of printing, one of 20 powers of its recurrence probability less than 10(1/1020), to the Quick Response Code of printing
Carry out image scanning coding to achieve, the mess code of any repetition is destroyed at once, the present invention can also be used in combination with other method for anti-counterfeit.
The ink that silk-screen printing is best suitable for the present invention forms required mess code, and net hole is slightly larger than pearly-lustre microballon, it is ensured that pearly-lustre
Microballon can be by netting hole, and intaglio plate and letterpress may also be used for printing required mess code, due to the position error of pearly-lustre microballon
Greatly, the possibility that error code is misread is higher, and the pattern of required Quick Response Code should design the QR codes of such as standard according to user's request, can
To be complete non-standard pattern, it can also be used in conjunction with the Quick Response Code of standard, i.e., the printed color mess code in the Quick Response Code of standard.For
Production efficiency is improved, continuous silk-screen printing and infrared heating should be used to solidify.Impressing pattern is encoded through camera-shooting scanning on production line
Achieve, coding method can at once be destroyed using color 2 D code standard, assorted aberration is analyzed, made to duplication code
Recorded for extra false proof information.It is used in conjunction with standard two-dimensional code with embedded pattern etc., should first prints plane pattern, 3 are finally printed again
The colored mess code of dimension.The present invention can also be used in combination with other method for anti-counterfeit, for example laser anti-counterfeit label, magnetic ink printing etc..
The two-dimentional mess code can be printed directly on product, can also be imprinted in the materials such as paper as label that to be bonded at its first-class
Deng.Two-dimensional color mess code reaches non-reproduction and high uniqueness, utilizes internet and cell-phone camera function and the data of manufacturer
Storehouse contrast confirmation is printed on this authenticity of products and production batch and sequence number.This product production cost is low, can be with other false proof sides
Method and with improve anti-counterfeit capability, it is easy to promote.
The beneficial effects of the invention are as follows:The two-dimensional code anti-counterfeiting label of the present invention is by using special 3-dimensional ink and special print
Brush technology produces the two-dimentional mess code of polychrome, and the polychrome Quick Response Code that this method is produced can not almost be repeated, and the probability repeated is less than hundred million points
One of, even if repeating, it can be excluded by detecting system.This Quick Response Code is 3 D multi-colour pearly-lustre, and digital printer can not be produced
This three-dimensional pearly-lustre color and luster.As long as consumer scans this Quick Response Code and feeds back to businessman, just may know that product the true and false and batch and
Sequence number.The false proof degree of increase, the low suitable large-scale production of cost can be used in conjunction in this technology with other anti-counterfeiting technologies.
Brief description of the drawings
Fig. 1-5 is the impressing pattern design drawing of the two-dimentional mess code of 4 colors, and 3 colors add basic stimulus totally 4 color, 3 kinds of different figures in figure
The circle of case represents the ball of 3 kinds of colors;Fig. 1 is square 20x20 units Unit totally 400;Fig. 2 is non-squared design;Fig. 3 is client's figure
Case is embedded;Fig. 4 and Fig. 5 are two kinds of compound cases with QR codes.
Embodiment
Below by specific embodiment, technical scheme is described in further detail.It should be appreciated that this hair
Bright implementation is not limited to the following examples, and any formal accommodation and/or change made to the present invention will all fall
Enter the scope of the present invention.
In the present invention, if not refering in particular to, all part, percentage are unit of weight, equipment and raw material for being used etc.
It is commercially available or commonly used in the art.Method in following embodiments, is the normal of this area unless otherwise instructed
Rule method.
Pearly-lustre microballon of the present invention can be produced with various methods, and as use case, there is provided polymerization of epoxy resins
Method, glass microballoon coating method, the specific formula of ink, but this not limits to this patent using and selecting and weighing to raw material
Power scope.The microballon of the present invention can increase extra antiforge function, such as magnetic, temperature change, etc..
Embodiment 1:The production of pearly-lustre microballon --- liquid epoxies comminution granulation
1. a 10% golden yellow pearly-lustre toner of 325 mesh and the liquid bisphenol F epoxy resin of molecular weight 500 or so exist
High speed dispersion mixing obtains uniform sizing material under 8000rpm speed, jitter time 1 hour, and granularity is less than 30 microns;
2. the weight diethylenetriamine of a water solubility 10% is mixed with deionized water, obtain mixed liquor and add mixed liquor weight
0.2% neopelex surfactant, the consumption of deionized water is(Epoxy resin+pearly-lustre toner)3 times, point
Scattered speed is middle low speed, not produce a large amount of foams as index;
3. material that a step 2 is obtained is added dissolved with the water of curing agent and stirring makes epoxy resin cure turn into small
Grain, rate of dispersion about 1200rpm;
4. being persistently stirred and heated to 60 DEG C reacts 4 hours until epoxy resin cure;
5. an obtained circular granular is washed 3 times with the deionization of about 3 times of particle volumes, 60 DEG C of warm air dryings are few to humidity
In 2%, vibration screening removes the particle below 32 mesh and more than 80 mesh and by the classification of following Taylor's mesh number.
It is classified mesh number scope:
1)32 [0.5mm] -35 [0.425mm],
2)35 [0.425mm] -42 [0.355mm],
3)42 [0.355mm] -48 [0.3mm],
4)48 [0.3mm] -60 [0.25mm],
5)60[0.25mm]-80[0.18mm].
Embodiment 2:The production of pearly-lustre microballon --- microballon method
1. the isometric 1N sodium hydroxide lyes processing after being washed with isometric 1N sulfuric acid of the glass microballoon between a 32-35 mesh,
Finally it is washed with deionized water, screen filtration falls water.
2. adding 2N ferric sulfate aqueous solutions in the microballon after step 1 processing, the weight of ferric sulfate aqueous solution is microballon weight
2 times, the speed of stirring ensures that microballon is not sunk to the bottom, and makes reaction uniform.
The pH of bead solution is set to reach 9 3. adding 2N sodium hydroxide lyes with measuring pump constant speed, pump speed is to add institute in 4 hours
Need alkali lye, and sustained response 5 hours, then wash weakly acidic pH with deionized water.
4. the microballon that step 3 is obtained is through screen filtering and dewatering, 80 DEG C of ventilations are stirred to be sintered in dryings, 600 DEG C of stirring nitrogen,
Obtain the magnetic micro-beads of pearly-lustre color and luster.
The Printing ink producing technique of embodiment 3
The polymethacrylates of 20% weight is dissolved in the dimethyl benzene and methylisobutylketone of 80% weight with 1:1 weight ratio
In the solvent of mixing, high-speed stirred dissolving stands a night de-bubbled and obtains transparent resin solution;
3 color pearly-lustre microballons needed for adding, bead size is 32-35 mesh, and pearly-lustre microballon total amount is resin solution gross weight
30%, the volume ratio of various colored nacreous microballons is 1:1:1.Mixed on low speed is uniform, obtains ink, if viscosity is too high, can be with molten
Agent is turned down, and the scope of viscosity is 1000-2000cP.
The typography of embodiment 4
Required mess code is formed using silk-screen printing, the mesh net of Taylor 28 is used for forming 0.6mm nets hole, slightly larger than 32 mesh
(0.5mm)Pearly-lustre microballon, it is ensured that microballon can be by netting hole, and the pattern of Quick Response Code is the design 1 in Fig. 1, and size is
20x20mm.Other designs in Fig. 1 can be printed as pattern, to form new two-dimension code label.
Embodiment 5
A kind of printing process of two-dimensional code anti-counterfeiting label, this method comprises the following steps:
1. the pearly-lustre microballon of different colours is prepared, the particle diameter of pearly-lustre microballon is 1 millimeter,
2. step 1. obtained pearly-lustre microballon is added in using resin as the ink of main component, obtains being used to print after mixing
The ink special of brush two-dimensional code anti-counterfeiting label, the usage amount of pearly-lustre microballon is the 40% of weight resin, and pearly-lustre microballon selects three kinds of face
Color, the volume ratio of the pearly-lustre microballon of each color is 1:1:2;
3. pattern in 2 D code is printed using above-mentioned ink special on the product or label paper for need to print Quick Response Code, makes two dimension
1 pearly-lustre microballon of printing in each cell of code, the pearly-lustre microballon of different colours is randomly formed specific pattern in 2 D code.This
Embodiment uses silk-screen printing, and the size of pearly-lustre microballon makes each net hole to stamp one close to the size in silk-screen printing net hole
Individual pearly-lustre microballon.
Embodiment 6
A kind of printing process of two-dimensional code anti-counterfeiting label, this method comprises the following steps:
1. the pearly-lustre microballon of different colours is prepared, the particle diameter of pearly-lustre microballon is 0.3 millimeter,
2. step 1. obtained pearly-lustre microballon is added in using resin as the ink of main component, obtains being used to print after mixing
The ink special of brush two-dimensional code anti-counterfeiting label, the usage amount of pearly-lustre microballon is the 20% of weight resin, and pearly-lustre microballon selects 4 kinds of face
Color, the volume ratio of the pearly-lustre microballon of each color is 1:1:1:1;
3. pattern in 2 D code is printed using above-mentioned ink special on the product or label paper for need to print Quick Response Code, makes two dimension
1 pearly-lustre microballon of printing in each cell of code, the pearly-lustre microballon of different colours is randomly formed specific pattern in 2 D code.This
Embodiment uses 42 mesh silk-screen printings, and the size of pearly-lustre microballon makes each net hole to print close to the size in silk-screen printing net hole
A upper pearly-lustre microballon.
Embodiment described above is a kind of preferably scheme of the present invention, not makees any formal to the present invention
Limitation, also has other variants and remodeling on the premise of without departing from the technical scheme described in claim.
Claims (6)
1. a kind of two-dimensional code anti-counterfeiting label, it is characterised in that it is made by following methods:
1. the pearly-lustre microballon of different colours is prepared, the particle diameter of pearly-lustre microballon is 0.1-3 millimeters,
2. step 1. obtained pearly-lustre microballon is added in using resin as the ink of main component, obtains being used to print two after mixing
The ink special of code antifalsification label is tieed up, the usage amount of pearly-lustre microballon is the 5-80% of weight resin, and pearly-lustre microballon selects more than three kinds
Color,
3. pattern in 2 D code is printed using above-mentioned ink special on the product or label paper for need to print Quick Response Code, makes Quick Response Code
No more than 1 pearly-lustre microballon of printing in each cell, the pearly-lustre microballon of more than three kinds colors is randomly formed specific Quick Response Code
Pattern;The pattern in 2 D code is random generation, it is ensured that uniqueness.
2. two-dimensional code anti-counterfeiting label according to claim 1, it is characterised in that:The pearly-lustre microballon be selected from metal microbead,
The coated microballon in surface or pearly-lustre toner coloring epoxy resin microballon.
3. two-dimensional code anti-counterfeiting label according to claim 1, it is characterised in that:The particle diameter of pearly-lustre microballon is 0.3-1 millimeters.
4. two-dimensional code anti-counterfeiting label according to claim 1, it is characterised in that:It is micro- that the pearly-lustre microballon of each color accounts for pearly-lustre
Pearl totality accumulated amount more than 5%.
5. two-dimensional code anti-counterfeiting label according to claim 1, it is characterised in that:For four color systems, the pearl of each color
It is 20-60% that light microballon, which accounts for the overall accumulated amount of pearly-lustre microballon,.
6. two-dimensional code anti-counterfeiting label according to claim 1, it is characterised in that:Described printing uses silk-screen printing, pearl
The size of light microballon makes each net hole to stamp a pearly-lustre microballon close to the size in silk-screen printing net hole.