CN104671709A - 一种利用工业废弃液态渣制备的外墙真石漆 - Google Patents
一种利用工业废弃液态渣制备的外墙真石漆 Download PDFInfo
- Publication number
- CN104671709A CN104671709A CN201510103601.XA CN201510103601A CN104671709A CN 104671709 A CN104671709 A CN 104671709A CN 201510103601 A CN201510103601 A CN 201510103601A CN 104671709 A CN104671709 A CN 104671709A
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid slag
- industrial waste
- waste liquid
- exterior wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于建筑外墙装饰环保新材料的研发技术领域,具体涉及一种利用工业废弃液态渣制备的外墙真石漆,该外墙真石漆由水、胶结剂、成膜助剂、杀菌剂、pH调节剂、功能型助剂、增稠剂、石英砂、液态渣及云母制成,其中,各原料所占重量份数为:水50~100份、胶结剂150~200份、成膜助剂5~10份、杀菌剂1~2份、pH调节剂1~1.5份、功能型助剂5~10份、增稠剂1.5~2份、石英砂300~700份、工业废弃液态渣20~350份、云母10~100份。本发明主要用于建筑外墙的装饰。
Description
技术领域
本发明属于建筑外墙装饰环保新材料的研发技术领域,具体涉及一种利用工业废弃液态渣制备的外墙真石漆。
背景技术
传统建筑外墙装饰材料主要采用涂料、乳胶漆、石材及瓷砖等材料。但是,随着人们对建筑外墙装饰材料的要求越来越高,涂料、乳胶漆存在易开裂、剥落、装饰效果单一等技术问题,石材、瓷砖存在质量重、高能耗及易掉落危险等技术问题。这些技术问题或者安全隐患导致人们需求物理性能优越、装饰效果好、质量轻、低能耗及安全的建筑外墙装饰材料。
目前,国内的真石漆类材料品种繁多,技术也较为成熟,但也存在一些问题,如:色彩单一,主要采用色浆调色;仿石不够逼真,不能突出石材的厚重感与立体感;耐候性能差,在如新疆等严酷地域环境一两年就会出现产品褪色、开裂、剥落的现象等。
本发明与专利申请公开文件CN02277059A具有类似内容,区别之一在于该专利骨料限定为石粉,未使用液态渣、未使用阿勒泰地区特有戈壁卵石破碎石英砂、未使用天然有色云母;区别之二在于该专利未使用pH调节剂;区别之三在于该专利胶结剂只限定为硅丙乳液,未使用纯丙乳液;区别之四在于该专利功能型助剂限定为丙二醇,未使用乙二醇。
本发明申请与专利申请公开文件CN102558973A具有类似内容,区别之一在于该专利使用了消泡剂;区别之二在于该专利未使用功能型助剂乙二醇或丙二醇;区别之三在于该专利未使用液态渣、未使用阿勒泰地区特有戈壁卵石破碎石英砂、未使用天然有色云母。
发明内容
本发明的目的在于:提供一种利用工业废弃液态渣制备的外墙真石漆,这种外墙真石漆可大量利用工业废弃液态渣作为部分骨料,具有节能环保的有益效果;利用新疆阿勒泰当地戈壁卵石破碎的石英砂作为部分骨料,可以使真石漆焕发出石材的厚重感与立体感;利用天然有色云母作为真石漆色源,可以使真石漆的仿石效果更加逼真、自然等。同时,本外墙真石漆具有物理性能优越、装饰效果好、质量轻、低能耗及环保安全等特点。
本发明技术方案如下:一种利用工业废弃液态渣制备的外墙真石漆,该外墙真石漆由水、胶结剂、成膜助剂、杀菌剂、pH调节剂、功能型助剂、增稠剂、石英砂、液态渣及云母制成,其中,各原料所占重量份数为:水50~100份、胶结剂150~200份、成膜助剂5~10份、杀菌剂1~2份、pH调节剂1~1.5份、功能型助剂5~10份、增稠剂1.5~2份、石英砂300~700份、工业废弃液态渣20~350份、云母10~100份。所述的胶结剂为纯丙聚合物乳液或硅丙聚合物乳液的任意一种。所述的成膜助剂为醇酯十二,美国伊斯曼公司生产市售。所述的杀菌剂为520杀菌剂,南京维高化工有限公司生产市售。所述的pH调节剂为AMP-95,南京维高化工有限公司生产市售。所述的功能型助剂为乙二醇或丙二醇的任意一种。所述的增稠剂为羟乙基纤维素,粘度为30000mpa·s。所述的石英砂为新疆阿勒泰地区戈壁卵石破碎石英砂,粒径为:20目~40目占10%~20%,40目~80目占80%~90%。所述的工业废弃液态渣为发电厂燃煤废弃的液态渣经破碎、清洗、烘干、筛分得到的液态渣,其粒径为:20目~40目占10%~20%,40目~80目占80%~90%。所述的云母为天然有色云母,其粒径为6目~10目。
本发明的有益效果:1、性能优异:本产品未使用苯丙乳液,而使用了纯丙乳液或硅丙乳液,纯丙乳液呈硅丙乳液具有非常优异的耐候性、耐沾污性、耐水性、优良的拉伸粘结强度等,能够赋予真石漆非常优异的物理性能,使得真石漆在使用过程中更有保障。本产品不使用色浆调色,利用工业废弃液态渣作为仿石黑色色相,液态渣黑色相耐紫外线照射极好,利用新疆阿勒泰当地戈壁卵石破碎的石英砂作为仿石点缀色相,天然石英砂耐紫外线照射极好,利用天然有色云母作为真石漆主要色相,天然有色云母色彩虽然不如色浆丰富,但因为云母为天然矿物色相,耐紫外线照射极好,所以,真石漆不会出现掉色、褪色等现象。
2、仿石逼真:本成品利用大量工业废弃液态渣作为部分骨料,由于液态渣玻璃相含量在95%以上,颗粒结构完整坚固,不会吸水,不用担心生产过程中破碎,并且具有一定玻璃光泽,在阳光照射下会反射光线,使真石漆具有类岩石矿物结晶反射效果,比传统真石漆更具有逼真的仿石效果。同时,本成品还利用新疆阿勒泰当地戈壁卵石破碎的石英砂作为部分骨料,这种石英砂以白色为主,少量含量天然红色、黄色、黑色,具有天然岩石美感,并且这种石英砂具有一定的透光性,在阳光照射下会反射出石英砂中所含的各种天然色泽,使得真石漆具有岩石的立体观感,而不是传统真石漆的平面观感。不使用色浆调色,利用天然有色云母作为真石漆主要色相,天然有色云母有黑色、金黄色、墨绿色、银白色等,由于这些颜色以及云母的高光泽性本身就属于岩石矿物所具有的特性,用在真石漆中所表现出的颜色更加像石材,是传统真石漆无法比拟的。
3、环保:本成品利用大量工业废弃液态渣作为部分骨料,液态渣为电厂燃煤排放废渣,由于液态渣排放量大、利用率低,对环境造成巨大危害。本成品利用液态渣作为真石漆部分骨料,可提高液态渣的废物利用率,降低天然石英砂的用量,如配制“金刚黑”真石漆,液态渣的取代天然石英砂用量超过50%,具有明显的社会效益。
4、低成本:本成品利用大量工业废弃液态渣作为部分骨料,由于液态渣为电厂燃煤排放废渣,成本为30元/吨,天然石英砂成本为360元/吨,按液态渣在真石漆中用量200公斤/吨,每吨真石漆成本可节约66元,能产生极为良好的经济效益。
具体实施方式
为了更好地理解本发明,下面结合实施例进一步阐明本发明的内容,但本发明的内容不仅仅局限于下面的实施例。
实施例1:本利用工业废弃液态渣制备的外墙真石漆的原料组成配比按重量份数计为:水50份、纯丙聚合物乳液200份、成膜助剂10份、杀菌剂1份、pH调节剂1.5份、乙二醇10份、增稠剂2份、石英砂700份、液态渣20份、云母(银白色)10。经刮涂成型仿芝麻灰。实施性能见表1。
实施例2:本利用工业废弃液态渣制备的外墙真石漆的原料组成配比按重量份数计为:水100份、硅丙聚合物乳液150份、成膜助剂5份、杀菌剂2份、pH调节剂1份、丙二醇5份、增稠剂1.5份、石英砂300份、液态渣350份、云母(黑色)100份。经刮涂成型仿金刚黑。实施性能见表1。
实施例3:本利用工业废弃液态渣制备的外墙真石漆的原料组成配比按重量份数计为:水80份、纯丙聚合物乳液170份、成膜助剂8份、杀菌剂1.5份、pH调节剂1.2份、乙二醇8份、增稠剂18份、石英砂600份、液态渣100份、云母(金黄色)50份。经刮涂成型仿卡拉麦利金。实施性能见表1。
表1 实施例所得利用工业废弃液态渣制备的外墙真石漆性能测试结果
Claims (10)
1.一种利用工业废弃液态渣制备的外墙真石漆,其特征在于:该外墙真石漆由水、胶结剂、成膜助剂、杀菌剂、pH调节剂、功能型助剂、增稠剂、石英砂、液态渣及云母制成,其中,各原料所占重量份数为:水50~100份、胶结剂150~200份、成膜助剂5~10份、杀菌剂1~2份、pH调节剂1~1.5份、功能型助剂5~10份、增稠剂1.5~2份、石英砂300~700份、工业废弃液态渣20~350份、云母10~100份。
2.根据权利要求1所述的利用工业废弃液态渣制备的外墙真石漆,其特征在于:所述的胶结剂为纯丙聚合物乳液或硅丙聚合物乳液的任意一种。
3.根据权利要求1所述的利用工业废弃液态渣制备的外墙真石漆,其特征在于:所述的成膜助剂为醇酯十二,美国伊斯曼公司生产市售。
4.根据权利要求1所述的利用工业废弃液态渣制备的外墙真石漆,其特征在于:所述的杀菌剂为520杀菌剂,南京维高化工有限公司生产市售。
5.根据权利要求1所述的利用工业废弃液态渣制备的外墙真石漆,其特征在于:所述的pH调节剂为AMP-95,南京维高化工有限公司生产市售。
6.根据权利要求1所述的利用工业废弃液态渣制备的外墙真石漆,其特征在于:所述的功能型助剂为乙二醇或丙二醇的任意一种。
7.根据权利要求1所述的利用工业废弃液态渣制备的外墙真石漆,其特征在于:所述的增稠剂为羟乙基纤维素,粘度为30000mpa·s。
8.根据权利要求1所述的利用工业废弃液态渣制备的外墙真石漆,其特征在于:所述的石英砂为新疆阿勒泰地区戈壁卵石破碎石英砂,粒径为:20目~40目占10%~20%,40目~80目占80%~90%。
9.根据权利要求1所述的利用工业废弃液态渣制备的外墙真石漆,其特征在于:所述的工业废弃液态渣为发电厂燃煤废弃的液态渣经破碎、清洗、烘干、筛分得到的液态渣,其粒径为:20目~40目占10%~20%,40目~80目占80%~90%。
10.根据权利要求1所述的利用工业废弃液态渣制备的外墙真石漆,其特征在于:所述的云母为天然有色云母,其粒径为6目~10目。