CN104629656A - Special binder for wooden windows - Google Patents
Special binder for wooden windows Download PDFInfo
- Publication number
- CN104629656A CN104629656A CN201510044284.9A CN201510044284A CN104629656A CN 104629656 A CN104629656 A CN 104629656A CN 201510044284 A CN201510044284 A CN 201510044284A CN 104629656 A CN104629656 A CN 104629656A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- present
- sodium
- emulsifying agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a special binder for wooden windows. The binder is prepared from the following components in parts by weight: 700-1,050 parts of polyvinyl acetate, 300-350 parts of vinyl acetate, 120-145 parts of polyvinyl alcohol, 60-100 parts of dibutyl phthalate, 20-40 parts of diethylene glycol dibenzoate, 10-15 parts of octanol, 30-45 parts of isopropanol, 10-25 parts of allyl methacrylate, 5-10 parts of glycol dimethacrylate, 3-7 parts of toluene diisocyanate, 35-50 parts of sodium hydrogen carbonate, 1,400-1,500 parts of water, 35-48 parts of a compound emulsifier, 5-10 parts of an initiator, 20-32 parts of hydroxymethyl acrylamide, 10-15 parts of waxy maize starch and 2-7 parts of sodium hypochlorite. The special binder for wooden windows has excellent comprehensive properties and can meet the strict requirements for quality of high-grade wooden windows.
Description
Technical field
The present invention relates to chemical material technical field, particularly relate to a kind of timber window adhesive special.
Background technology
At present, the threshold industry of door and window is lower, and industry competition is more chaotic, for improving quality and the market competitiveness of product, needs constantly to improve.The energy-conservation wooden doors and windows of the top grade that external window of building engineering is widely used comprises: the large kind of pure Wood-door window, aluminium bag Wood-door window, wooden aluminium composite door and window three.And wooden aluminium composite door and window is because being heat insulated shape bar of aluminum alloy outside it, inner side is wooden decoration bar section, therefore more can adapt to southern rainy, high temperature, moist weather condition.The unreasonable structure of present domestic market processing and fabricating wood aluminium composite door and window, secondary processing is wanted in aluminium layering assembling, and in Wind-Pressure Resistance, resistance to air loss and sound insulation, the aspect of performance such as heat insulation neither be very desirable, still has the energy loss of considerable part.
Timber window is due to attractive in appearance, and the sensation got close to nature, has extraordinary market outlook, but because the environment for use of window is special, present rugged environment day by day in addition, as haze weather, cause the bad environments residing for timber window, if the quality of timber window does not pass a test, be easy to occur to ftracture between ligneous piece, connect undertighten, affect result of use, cause customer complaint, therefore, research and development can be suitable for boisterous timber window adhesive special and have huge market outlook.
Through finding the retrieval of prior art, Chinese invention patent application 02109653.8 (publication date on November 19th, 2003) discloses a kind of powerful white latex, specifically by polyvinyl alcohol, sodium hydroxide, starch, hydrochloric acid, formaldehyde, urea, water forms, and this white glue with vinyl frost resistance is good, not easily precipitates, not stratified, technique is simple.But this glue contains formaldehyde and urea, and environmental-protecting performance is poor.
Chinese invention patent application 201310012677.2 (publication date on January 14th, 2013) discloses a kind of modified latex, this modified latex comprises vinyl acetate, vinylformic acid, butyl acrylate, initiator and emulsifying agent, obtained modified polyvinyl acetate emulsion adhesive capacity is large, can at room temperature film forming, cohesive strength is large, water-tolerant.The vinyl acetate toxicity that this glue adopts is large, inadequate environmental protection.
Chinese invention patent application 201410004735.1 (publication date: on April 16th, 2014) discloses a kind of environmental Protection type white latex, and described glue comprises: PVAC polyvinylalcohol, vinyl acetate VAC, vinylformic acid AA, acrylamide AM, ammonium persulphate, anionic emulsifier A-102, alkyl polyoxyethylene ether LCN-287 nonionic emulsifying agent; W-Gum, transparent powder, softening agent, diethylene glycol dibenzoate DEDB, sanitas KSG-201, sodium hydroxide and methyl alcohol; But this glue still employs the virose vinyl acetate of tool, and environmental-protecting performance is poor.
Meanwhile, the associated adhesive agent disclosed in prior art over-all properties in result of use is also poor, and the method for there is no meets the related request of high-grade energy-conservation wooden doors and windows quality.
Summary of the invention
Provide hereinafter about brief overview of the present invention, to provide about the basic comprehension in some of the present invention.Should be appreciated that this general introduction is not summarize about exhaustive of the present invention.It is not that intention determines key of the present invention or integral part, and nor is it intended to limit the scope of the present invention.Its object is only provide some concept in simplified form, in this, as the preorder in greater detail discussed after a while.
The object of the invention is to overcome the deficiencies in the prior art, a kind of timber window adhesive special is provided; Binding agent environmental-protecting performance of the present invention is high, excellent combination property, can meet the related request of high-grade timber window completely.
The present invention relates to a kind of timber window adhesive special, described binding agent is made up of each component of following parts by weight:
Polyvinyl acetate (PVA) 700-1050,
Vinyl acetate 300-350,
Polyvinyl alcohol 120-145,
Dibutyl phthalate 60-100,
Diethylene glycol dibenzoate 20-40,
Octanol 10-15,
Virahol 30-45,
Allyl methacrylate(AMA) 10-25,
Ethyleneglycol dimethyacrylate 5-10,
Tolylene diisocyanate 3-7,
Sodium bicarbonate 35-50,
Water 1400-1500,
Compound emulsifying agent 35-48,
Initiator 5-10,
N-methylolacrylamide 20-32,
Waxy corn starch 10-15,
Clorox 2-7;
Described compound emulsifying agent is made up of each component of following part by weight: Sodium dodecylbenzene sulfonate, and fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, sodium dibutyl naphthalene sulfonate, Brij 35 sodium sulfate are (2-3): (1-3): (1-4): (2-5): (2-6).
Compared with existing, the present invention has following beneficial effect: timber window adhesive special of the present invention fundamentally improves the environmental-protecting performance of product; Simultaneously at thermal stability, just the dry time, water resistance, cohesive strength and set time etc., index had outstanding representation, and over-all properties is superior, can meet the strict demand of high-grade timber window quality.
Embodiment
Embodiments of the invention are described below.The element described in one embodiment of the invention and feature can combine with the element shown in one or more other embodiment and feature.It should be noted that for purposes of clarity, in explanation, eliminate expression and the description of unrelated to the invention, parts known to persons of ordinary skill in the art and process.
Embodiment 1
The present embodiment relates to a kind of timber window adhesive special and preparation method thereof; Described binding agent is made up of each component of following parts by weight:
Polyvinyl acetate (PVA) 700,
Vinyl acetate 300,
Polyvinyl alcohol 120,
Dibutyl phthalate 60,
Diethylene glycol dibenzoate 20,
Octanol 10,
Virahol 30,
Allyl methacrylate(AMA) 10,
Ethyleneglycol dimethyacrylate 5,
Tolylene diisocyanate 3,
Sodium bicarbonate 35,
Water 1400,
Compound emulsifying agent 35;
Initiator 5, initiator is ammonium persulphate;
N-methylolacrylamide 20,
Waxy corn starch 10,
Clorox 2;
Described compound emulsifying agent is made up of each component of following part by weight: Sodium dodecylbenzene sulfonate, and fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, sodium dibutyl naphthalene sulfonate, Brij 35 sodium sulfate are 2:1:1:2:2.
The each component related in the present embodiment all obtains by disclosed commercially available channel.In the present embodiment, preparation method's step of timber window adhesive special is as follows:
Step one, under agitation condition, gets water and the polyvinyl alcohol of 50-73% weight percent, and mixing, is warmed up to 88-95 degree, polyvinyl alcohol is dissolved completely, and be incubated 1 hour under 70-80 degree, adjustment pH is 8-9, obtains solution A;
Step 2, get the emulsifying agent of 30-40% weight percent, under agitation condition, described emulsifying agent and remaining water are joined in solution A, slowly add the vinyl acetate of 40-50% weight percent and the initiator of 40-50% weight percent again, be warming up to 88-95 degree, insulation 0.3-0.5 hour; Be cooled to 60-70 degree; Slowly add remaining vinyl acetate and remaining initiator more afterwards; Be warming up to 88-95 degree (DEG C), insulation 0.2-0.4 hour;
Step 3, adds emulsifying agent and the polyvinyl acetate (PVA) of 30-40% weight percent, is incubated 0.2-0.4 hour under 88-95 degree, be then cooled to 40-50 degree (DEG C);
Step 4, under agitation condition, adds sodium bicarbonate, dibutyl phthalate, diethylene glycol dibenzoate, octanol, Virahol, mixes, obtain solution B;
Step 5, remaining emulsifying agent is added, allyl methacrylate(AMA), ethyleneglycol dimethyacrylate in solution B, tolylene diisocyanate, n-methylolacrylamide, waxy corn starch, clorox, mix, 40-50 degree (DEG C) insulation 0.1-0.3 hour, is cooled to room temperature, obtains described timber window part connection glue.
Embodiment 2
The present embodiment relates to a kind of timber window adhesive special and preparation method thereof (preparation method is with embodiment 1); Described binding agent is made up of each component of following parts by weight:
Polyvinyl acetate (PVA) 1050,
Vinyl acetate 350,
Polyvinyl alcohol 145,
Dibutyl phthalate 100,
Diethylene glycol dibenzoate 40,
Octanol 15,
Virahol 45,
Allyl methacrylate(AMA) 25,
Ethyleneglycol dimethyacrylate 10,
Tolylene diisocyanate 7,
Sodium bicarbonate 50,
Water 1500,
Emulsifying agent 48;
Initiator 10, initiator is ammonium persulphate;
N-methylolacrylamide 32,
Waxy corn starch 15,
Clorox 7;
Described compound emulsifying agent is made up of each component of following part by weight: Sodium dodecylbenzene sulfonate, and fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, sodium dibutyl naphthalene sulfonate, Brij 35 sodium sulfate are 3:3:4:5:6.
Embodiment 3
The present embodiment relates to a kind of timber window adhesive special and preparation method thereof (preparation method is with embodiment 1); Described binding agent is made up of each component of following parts by weight:
Polyvinyl acetate (PVA) 800,
Vinyl acetate 315,
Polyvinyl alcohol 125,
Dibutyl phthalate 80,
Diethylene glycol dibenzoate 25,
Octanol 12,
Virahol 35,
Allyl methacrylate(AMA) 15,
Ethyleneglycol dimethyacrylate 7,
Tolylene diisocyanate 4,
Sodium bicarbonate 39,
Water 1450,
Emulsifying agent 40;
Initiator 6, initiator is Potassium Persulphate;
N-methylolacrylamide 25,
Waxy corn starch 12,
Clorox 4,
Described compound emulsifying agent is made up of each component of following part by weight: Sodium dodecylbenzene sulfonate, and fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, sodium dibutyl naphthalene sulfonate, Brij 35 sodium sulfate are 2.5:1.2:2:3:3.
Embodiment 4
The present embodiment relates to a kind of timber window adhesive special and preparation method thereof (preparation method is with embodiment 1); Described binding agent is made up of each component of following parts by weight:
Polyvinyl acetate (PVA) 950,
Vinyl acetate 335,
Polyvinyl alcohol 135,
Dibutyl phthalate 90,
Diethylene glycol dibenzoate 35,
Octanol 14,
Virahol 40,
Allyl methacrylate(AMA) 22,
Ethyleneglycol dimethyacrylate 9,
Tolylene diisocyanate 6,
Sodium bicarbonate 45,
Water 1480,
Emulsifying agent 45;
Initiator 9, initiator is Potassium Persulphate;
N-methylolacrylamide 29,
Waxy corn starch 14,
Clorox 6.
Described compound emulsifying agent is made up of each component of following part by weight: Sodium dodecylbenzene sulfonate, and fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, sodium dibutyl naphthalene sulfonate, Brij 35 sodium sulfate are 2.8:2.8:3:4:5.
Embodiment 5
The present embodiment relates to a kind of timber window adhesive special and preparation method thereof (preparation method is with embodiment 1); Described binding agent is made up of each component of following parts by weight:
Polyvinyl acetate (PVA) 900,
Vinyl acetate 330,
Polyvinyl alcohol 130,
Dibutyl phthalate 85,
Diethylene glycol dibenzoate 30,
Octanol 13,
Virahol 37,
Allyl methacrylate(AMA) 19,
Ethyleneglycol dimethyacrylate 8,
Tolylene diisocyanate 5,
Sodium bicarbonate 41,
Water 1460,
Emulsifying agent 43;
Initiator 8, initiator is Potassium Persulphate;
N-methylolacrylamide 27,
Waxy corn starch 13,
Clorox 5;
Described compound emulsifying agent is made up of each component of following part by weight: Sodium dodecylbenzene sulfonate, and fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, sodium dibutyl naphthalene sulfonate, Brij 35 sodium sulfate are 2.6:2.5:2.5:3.5:4.
Comparative example 1
In prior art, the customary preparation methods of glue comprises the steps: to get polyvinyl alcohol 300 parts, under agitation condition, adds Sodium dodecylbenzene sulfonate 40 parts, 800 parts, water, stirs 10-15 minute; Add vinyl acetate 450 parts, 10 parts of Potassium Persulphates, be incubated under 65-70 degree and wait basic disappearance of refluxing, be warmed up to 80-85 degree, add vinyl acetate 800 parts, 10 parts of Potassium Persulphates, be warmed up to 90-95 degree insulation 05-0.6 hour, be cooled to 50 degree, add dibutyl phthalate 50 parts, sodium bicarbonate 10 parts, stirs, cooling, obtains glue.
Implementation result
For verifying the implementation result of the present invention, carry out the test of following index:
1, environmental-protecting performance, the subjective feeling of production and user;
Whether 2, thermal stability determination: keep 6 days under 50-60 degree, observe and change, if appearance precipitates or gelatin phenomenon is more, then thermostability is poorer;
3, just dry timing: get ligneous piece, get 6g glue and be evenly coated in ligneous piece surface, observe its time of drying; Repeat, average for 5 times;
4, water tolerance measures: the ligneous piece of getting one group (2) same specification, 150g every square metre glue coating is pressed at the contact surface that each ligneous piece is corresponding, the specification of each contact surface is 100mm*30mm, afterwards by corresponding for the contact surface of Liang Ge ligneous piece superimposed compression, seasoning 12 hours, soak in 30-35 degree water, measure and come unglued the time; Repeat, average for 5 times;
5, cohesive strength measures: the ligneous piece of getting one group (2) same specification, 150g every square metre glue coating is pressed at the contact surface that each ligneous piece is corresponding, the specification of each contact surface is 100mm*30mm, afterwards by corresponding for the contact surface of Liang Ge ligneous piece superimposed compression, closed assembly time is no more than 10 minutes, and contact surface applies 1Mpa pressure, under room temperature, time of setting-up 12 hours, places 12 hours again after pressure relief, makes a strength test; Repeat, average for 5 times;
6, measure set time, get glue 10g, be positioned in beaker, heating in water bath under 50-55 degree, stir, measure its set time; Repeat, average for 5 times.
Table 1
Table 1 is the experiment effect of each embodiment and comparative example, as shown in Table 1, the glue environmental-protecting performance of embodiment of the present invention 1-5 is all better than comparative example 1, the equal tasteless of glue prepared by each embodiment, the subjective sensation of production and user is better, analyzes reason, and glue of the present invention is a large amount of consumption reducing vinyl acetate in component, replace vinyl acetate with nontoxic polyvinyl acetate (PVA), significantly improve the environmental-protecting performance of glue; Because polyvinyl acetate (PVA) is not identical with the character of vinyl acetate, for meeting the technology stability prepared in the performance of glue and preparation process, need to regulate and control the ratio of polyvinyl acetate (PVA) and vinyl acetate in an OK range, need emulsifying agent, the consumption of initiator also has specific requirement simultaneously; Glue of the present invention is by overall adjustment of formula, work in coordination with between each component, achieve while adopting polyvinyl acetate (PVA) and vinyl acetate enhancing ring guaranteed cost simultaneously, the unexpected technique effect of the remarkable lifting of glue over-all properties can also be realized, there is significant novelty.
Thermostability index, the thermal stability of embodiment of the present invention 1-5 is also all better than comparative example 1, experimental observation, there is not obvious sediment or gelatin phenomenon in glue prepared by embodiment 1-5, glue prepared by embodiment 1-5 has upper and lower two-layer emulsion phenomenon, and upper strata emulsion is more liquid, and lower floor's emulsion is gluing thick, mobility is slightly weak, and thermal stability is excellent; Review comparative example 1, in maintenance after 25 days, there is comparatively significantly gelatin phenomenon in glue, thermal stability is poor.
First dry time index, as shown in Table 1, the first dry time of embodiment of the present invention 1-5 is all shorter than comparative example 1, and just the dry time is shorter, illustrates that the performance of glue is more excellent; Comparative example 1 first dry for up to 50 minutes, just the dry time the longest is 32 minutes to the embodiment of the present invention, the shortlyest reaches 21 minutes, is much better than comparative example 1.
Water tolerance index, as shown in Table 1, the water tolerance that embodiment of the present invention 1-5 prepares glue is all better than comparative example 1, and water resistance at least improves more than 2 times, has significant technique effect.
Cohesive strength index, as shown in Table 1, the cohesive strength index that comparative example 1 prepares glue is 5.34Mp, and the present invention prepares the cohesive strength index of glue all at more than 9.11Mp, at least improve 70.6%, glue cohesive strength index prepared by the embodiment 5 that wherein performance is best reaches 9.90Mp, and performance boost, up to 85.4%, has the technique effect that purpose is not thought.
Set time index, as shown in Table 1, the set time that comparative example 1 prepares glue is 450 seconds, embodiment 1-5 prepares the set time of glue all within 415 seconds, glue prepared by embodiment 5 that the shortest is, foreshortens to 300 seconds set time, and be only that comparative example 1 prepares the glue curing time about 66.7%, significantly shorten the set time of glue, there is significant technical progress.
In summary it can be seen, glue performance prepared by embodiment of the present invention 1-5 not only environmental-protecting performance significantly promotes, and achieves the remarkable lifting of glue over-all properties simultaneously, has beyond thought technique effect.The indices embodied in his-and-hers watches 1 carries out global alignment, and applicant finds that the glue of embodiment 5 index all has the most excellent performance on indices, and embodiment 5 is most preferred embodiment of the present invention undoubtedly.
In conjunction with the excellent effect of the present invention, applicant sets forth component of the present invention and technique: glue of the present invention is enhancing ring guaranteed cost, have employed the consumption rationally reducing vinyl acetate, the technical thought of vinyl acetate is replaced with nontoxic polyvinyl acetate (PVA), because polyvinyl acetate (PVA) is not identical with the character of vinyl acetate, for meeting the technology stability prepared in the performance of glue and preparation process, need to regulate and control the ratio of polyvinyl acetate (PVA) and vinyl acetate, simultaneously must the selection of all the other components in concern system.Why applicant must use polyvinyl acetate (PVA) and vinyl acetate in same system, instead of abandon vinyl acetate completely, because generally adopt vinyl acetate as raw material production glue in prior art, the present invention retains use vinyl acetate and the technology of the present invention can be made to have very strong promotional value in system, existing glue production manufacturer can be made to be easy to accept the production technique of this improvement, but not brand-new production technique, make the technology of the present invention have good market using value; Take into account the consideration of production cost on the other hand.
Applicant is through great many of experiments, unexpected discovery, the weight ratio of polyvinyl acetate (PVA) and vinyl acetate is (700-1050): (300-350) just realizes the goal of the invention of the present invention, if the consumption of vinyl acetate exceeds this ratio, then the glue environmental-protecting performance of final preparation just cannot significantly promote, little with the common glue environmental-protecting performance difference of prior art, if the too high levels of polyvinyl acetate (PVA), preparation technology's reaction stability then can be caused to be deteriorated, wayward, glue over-all properties is deteriorated, and causes the over-all properties of final glue significantly to promote.
Dibutyl phthalate and diethylene glycol dibenzoate are softening agent, and the present invention is the reaction system adapting to compound material, have employed the way simultaneously adding dibutyl phthalate and diethylene glycol dibenzoate; Octanol and Virahol, can not only be used for dissolving dibutyl phthalate and diethylene glycol dibenzoate, is conducive to the degree of adhesion improving glue; Can also play the effect of a part of defoamer, what be conducive to time prepared by glue of the present invention is steady; The applicant thinks, dibutyl phthalate, diethylene glycol dibenzoate and octanol, Virahol four kinds of components constitute synergistic small system together, specificly can meet the particular requirement that polyvinyl acetate (PVA) and vinyl acetate react in conjunction with polyvinyl alcohol as compound material, not only achieve reaction system steady, do not use the remarkable efficacy of defoamer, effectively can also promote the bond properties of glue, for indexs such as promoting the cohesive strength of final glue and set time, there is direct action effect.
Allyl methacrylate(AMA), ethyleneglycol dimethyacrylate and tolylene diisocyanate have the effect of tackiness agent, applicant selects this 3 kinds of materials dexterously, in conjunction with specific ratio, form synergy system, add in preparation technology's system in the suitable time, very considerably enhance the over-all properties of final glue, and bad impact is not produced on the stability of glue, because the time joining reaction system is last, therefore do not make the preparation technology of glue become more complicated yet, there is significant technical progress.Meanwhile, this area general knowledge, under normal circumstances in rational scope, the higher then result of use of concentration of glue is better, and for reducing costs, glue concentration prepared by a lot of manufacturer is only about 40%, and should be normally about 50-60%; After glue dilution, its moisture content improves, and in use, the moisture that glue contains can infiltrate ligneous piece, and wood is expanded, and causing between ligneous piece cannot be in conjunction with, causes serious product quality problem generation.Therefore, for the object improving the market competitiveness, its result of use and like product can also be kept to maintain an equal level while rationally reducing finished product glue concentration, there is huge marketable value undoubtedly.Glue prepared by the present invention is when being diluted to the degree of market like product, relevant cohesive strength, set time, water tolerance etc. are known and are significantly better than like product, this improves the competitiveness of product in market of the present invention greatly, there is huge marketable value, applicant analyzes, this and in system of the present invention, employ " dibutyl phthalate, diethylene glycol dibenzoate and octanol, Virahol " and " allyl methacrylate(AMA), ethyleneglycol dimethyacrylate and tolylene diisocyanate " these 2 special synergistic combination have vital contact, these 2 collaboration systems not only can promote the adhesive property of glue respectively, combine, further delicate synergy can also be there is, the adhesive property of further raising glue, significantly increase the market competitiveness that the present invention prepares glue.
The experiment effect of associative list 1, although the indices of embodiment 1-5 is all better than comparative example 1, but also difference to some extent between embodiment 1-5, analysis is got off, implement the most preferred embodiment that 5 are the present invention, visible, the content of component selects also there is vital impact, so novelty of the present invention is also embodied in the content selection aspect of each component simultaneously for the final performance of index glue.
Certainly, because the mentality of designing of glue of the present invention and the requirement of goal of the invention, it is also non-obvious that all the other compositional selectings of the present invention and content are selected obviously, and those skilled in the art can expect easily in conjunction with prior art absolutely not.This has further embodiment in the preparation technology of glue of the present invention, can see in conjunction with embodiments of the invention, preparation method of the present invention adopts five steps to design, gradation adds raw material in batches, and the per-cent added has special scope, but not adopt disposable the adding of prior art routine, this technique adapts with the special proportioning of glue component of the present invention, only with adopting this technique, the smooth sequential of guarantee reaction system carries out, and guarantees the superior quality finally preparing glue.
The paste viscosity of waxy corn starch itself is higher, and mobility is poor, and usability is poor; The present invention adds waxy corn starch and clorox with suitable ratio simultaneously in the composition, utilizes hypochlorite oxidation waxy corn starch, forms Sumstar 190, and stick with paste viscosity and reduce, mobility improves; The present invention simultaneously with the addition of N hydroxymethyl acrylamide; Applicant finds, adds waxy corn starch simultaneously, after clorox and N hydroxymethyl acrylamide, significantly can promote the over-all properties of glue further, the cohesive strength of glue and set time index be significantly improved, over-all properties improves further; Applicant thinks, N hydroxymethyl acrylamide is rich in reactive methylol, effectively can promote the degree of adhesion of system; The Sumstar 190 that waxy corn starch changes into has good mobility and stronger anti-shear stability, can promote the fusion of N hydroxymethyl acrylamide in system of the present invention further, and then the lifting of Promotion system degree of adhesion; Meanwhile, Sumstar 190 itself also has sticks with paste viscosity preferably, also can play the effect of tamanori, promotes the adhesive capacity of system; In the process that Sumstar 190 and N hydroxymethyl acrylamide move in system, also can mutually bond, the adhesive capacity of further lifting system; Visible, the present invention is ingenious be make use of waxy corn starch and changes the characteristic that Sumstar 190 has into, not only achieve the effect of enhancing system bounding force, effectively can also promote effect of N hydroxymethyl acrylamide, also can occur to interact and bond with N hydroxymethyl acrylamide, the collaborative integrated bond ability improving system, achieves beyond thought technique effect.Because waxy corn starch itself is comparatively stable, therefore the present invention adopts waxy corn starch as raw material, is convenient to store and transport.
Those skilled in the art know, the use of emulsifying agent and selection, for the speed of response of system, the stability of system and the characteristics influence of product very large; The applicant is through great many of experiments, and unexpected discovery selects following compound emulsifying agent to have beyond thought technique effect; Compound emulsifying agent is made up of each component of following part by weight: Sodium dodecylbenzene sulfonate, and fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, sodium dibutyl naphthalene sulfonate, Brij 35 sodium sulfate are (2-3): (1-3): (1-4): (2-5): (2-6).Compared with independent emulsifying agent, the present invention adopts compound emulsifying agent effectively can improve the bounding force of glue, shortens the just dry time simultaneously significantly, set time index; Analyze its reason, applicant thinks to promote the feature of environmental protection of the present invention, the present invention adopts different material system in the past, have employed polyvinyl acetate (PVA) and vinyl acetate compound material, this causes whole system of the present invention to change, adopt the more difficult demand meeting system reaction of conventional emulsifying agent, the compound emulsifying agent that the present invention adopts can agree with system of the present invention; Further, relative to using single emulsifying agent, the consumption of compound emulsifying agent can decline to some extent.
In sum, timber window adhesive special of the present invention fundamentally improves the environmental-protecting performance of product; Simultaneously at thermal stability, just the dry time, water resistance, cohesive strength and set time etc., index had outstanding representation, and over-all properties is superior, can meet the strict demand of high-grade timber window quality.
Last it is noted that above embodiment is only in order to illustrate technical scheme of the present invention, be not intended to limit; Although with reference to previous embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that: it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature; And these amendments or replacement, do not make appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme for essence.
Claims (3)
1. a timber window adhesive special, is characterized in that, described binding agent is made up of each component of following parts by weight:
Polyvinyl acetate (PVA) 700-1050,
Vinyl acetate 300-350,
Polyvinyl alcohol 120-145,
Dibutyl phthalate 60-100,
Diethylene glycol dibenzoate 20-40,
Octanol 10-15,
Virahol 30-45,
Allyl methacrylate(AMA) 10-25,
Ethyleneglycol dimethyacrylate 5-10,
Tolylene diisocyanate 3-7,
Sodium bicarbonate 35-50,
Water 1400-1500,
Compound emulsifying agent 35-48,
Initiator 5-10,
N-methylolacrylamide 20-32,
Waxy corn starch 10-15,
Clorox 2-7;
Described compound emulsifying agent is made up of each component of following part by weight: Sodium dodecylbenzene sulfonate, and fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, sodium dibutyl naphthalene sulfonate, Brij 35 sodium sulfate are (2-3): (1-3): (1-4): (2-5): (2-6).
2. timber window adhesive special according to claim 1, is characterized in that, described binding agent is made up of each component of following parts by weight:
Polyvinyl acetate (PVA) 800-950,
Vinyl acetate 310-335,
Polyvinyl alcohol 125-135,
Dibutyl phthalate 80-90,
Diethylene glycol dibenzoate 25-35,
Octanol 12-14,
Virahol 35-40,
Allyl methacrylate(AMA) 15-22,
Ethyleneglycol dimethyacrylate 7-9,
Tolylene diisocyanate 4-6,
Sodium bicarbonate 39-45,
Water 1450-1480,
Compound emulsifying agent 40-45,
Initiator 6-9,
N-methylolacrylamide 25-29,
Waxy corn starch 12-14,
Clorox 4-6,
Described compound emulsifying agent is made up of each component of following part by weight: Sodium dodecylbenzene sulfonate, and fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, sodium dibutyl naphthalene sulfonate, Brij 35 sodium sulfate are (2.5-2.8): (1.2-2.8): (2-3): (3-4): (3-5).
3. timber window adhesive special according to claim 1, is characterized in that, described initiator is Potassium Persulphate or ammonium persulphate.