CN104629618A - High-friction-resistance paint and preparation method thereof - Google Patents
High-friction-resistance paint and preparation method thereof Download PDFInfo
- Publication number
- CN104629618A CN104629618A CN201510107257.1A CN201510107257A CN104629618A CN 104629618 A CN104629618 A CN 104629618A CN 201510107257 A CN201510107257 A CN 201510107257A CN 104629618 A CN104629618 A CN 104629618A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- crocking resistance
- paint
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-friction-resistance paint and a preparation method thereof. The high-friction-resistance paint is prepared from the following raw materials in parts by mass: 85 parts of epoxy modified organic silicon resin, 38 parts of bisphenol A epoxy resin, 13 parts of castor oil, 24 parts of graphite powder, 13 parts of chromium powder, 8 parts of defoaming agent, 65 parts of solvent, 12 parts of pearl powder, 8 parts of pigment, 10 parts of silane coupling agent, 7 parts of additive and 4 parts of reinforcing agent. The invention also discloses a preparation method of the paint. The paint has the advantages of high friction resistance, favorable adhesion property, low shedding tendency, small surface friction coefficient, diversified colors and long service life, and can not have the problem of blistering, cracking, whitening, shedding or the like after life-time service. The paint can be used in severe environments, and thus, has wide application range. The paint has environment-friendly effect and lowers the cost.
Description
Technical field
The present invention relates to a kind of coating, coating that a kind of crocking resistance is high specifically and preparation method thereof.
Background technology
At present, the coating that crocking resistance is high can be widely used in the industries such as electrical equipment, metallurgy, oil, aviation field, chemical industry, medicine, food various in, but the crocking resistance of the coating of equipment surface does not still reach requirement, and due to the friction between equipment component, coating is caused to drop, damage equipment surface, reduces its work-ing life, increases cost.
Summary of the invention
Technical problem to be solved by this invention is, for the shortcoming of above prior art, high coating of a kind of crocking resistance and preparation method thereof is proposed, this coating not only crocking resistance is strong, and adhesivity is good, difficult drop-off, this coating surface frictional coefficient is little, rub resistance, and color is various, long service life, this coating life-time service can not bubble, chap, whiten the problems such as even delamination, and can use under rugged environment, and use range is wide, and there is environment protecting, reduce costs.
In order to solve the problems of the technologies described above, technical scheme of the present invention is achieved in the following ways: the coating that a kind of crocking resistance is high, and the coating that crocking resistance is high is following raw material according to the mass fraction:
Epoxy modified silicone resin: 82-85 part
Bisphenol A epoxide resin: 30-38 part
Viscotrol C: 11-13 part
Graphite Powder 99: 18-24 part
Chromium powder: 10-13 part
Defoamer: 5-8 part
Solvent: 60-65 part
Pearlescence: 10-12 part
Pigment: 5-8 part
Silane coupling agent: 8-12 part
Additive: 5-8 part
Strengthening agent: 3-5 part;
And use following method to obtain this coating:
Step (1): by raw material: epoxy modified silicone resin, bisphenol A epoxide resin and Viscotrol C are first put into stirring tank and mixed, temperature in control stirring tank is at 30-32 DEG C, setting stirring velocity 620-630r/min, churning time 20-25min, then mix putting into Graphite Powder 99, chromium powder, defoamer and solvent successively, stirring velocity is 730-750 r/min, keeps 35-45min;
Step (2): then by raw material: pearlescence, pigment, silane coupling agent, additive and strengthening agent are put into stirring tank and mixed, setting stirring velocity is 820-850r/min, churning time is 55-60min, can obtain the coating that described crocking resistance is high.
The technical scheme that the present invention limits further is:
The coating that aforesaid crocking resistance is high, defoamer is polydimethylsiloxane.
The coating that aforesaid crocking resistance is high, solvent is the mixture in hexone, toluene, ketone and butanone, wherein: the ratio between the mixture in hexone, toluene, ketone and butanone is: 1:3:2.
The coating that aforesaid crocking resistance is high, pigment is any one in Rutile type Titanium Dioxide, deep chrome yellow.
The coating that aforesaid crocking resistance is high, silane coupling agent is KH550.
The coating that aforesaid crocking resistance is high, additive is that releasing agent Lay mattress falls apart.
The coating that aforesaid crocking resistance is high, strengthening agent is thermals MT.
The invention has the beneficial effects as follows: by technical scheme of the present invention, not only toxicity is little, and surface tension is little, and surfactivity is high, and cost is low; This coating can keep for a long time non-foaming, non-corrosive, colour-fast, not mildew spot, do not come off; And all have good adhesion property to various material, smooth, outward appearance is beautiful, has good rub resistance and corrosion resistance nature, and production technique is simple, easy construction, easy handling, and short construction period is environment friendly and pollution-free.
Embodiment
The present invention is described in further detail below:
embodiment 1
Coating that a kind of crocking resistance that the present embodiment provides is high and preparation method thereof, the coating that crocking resistance is high is following raw material according to the mass fraction:
Epoxy modified silicone resin: 82 parts
Bisphenol A epoxide resin: 30 parts
Viscotrol C: 11 parts
Graphite Powder 99: 18 parts
Chromium powder: 10 parts
Defoamer: 5 parts
Solvent: 60 parts
Pearlescence: 10 parts
Pigment: 5 parts
Silane coupling agent: 8 parts
Additive: 5 parts
Strengthening agent: 3 parts; And use following method to obtain this coating:
Step (1): by raw material: epoxy modified silicone resin, bisphenol A epoxide resin and Viscotrol C are first put into stirring tank and mixed, temperature in control stirring tank is at 30 DEG C, setting stirring velocity 620r/min, churning time 20min, then mix putting into Graphite Powder 99, chromium powder, defoamer and solvent successively, stirring velocity is 730 r/min, keeps 35min;
Step (2): then by raw material: pearlescence, pigment, silane coupling agent, additive and strengthening agent are put into stirring tank and mixed, setting stirring velocity is 820r/min, and churning time is 55min, can obtain the coating that described crocking resistance is high.
embodiment 2
The preparation method of the coating that a kind of crocking resistance that the present embodiment provides is high, the coating that crocking resistance is high is following raw material according to the mass fraction:
Epoxy modified silicone resin: 85 parts
Bisphenol A epoxide resin: 38 parts
Viscotrol C: 13 parts
Graphite Powder 99: 24 parts
Chromium powder: 13 parts
Defoamer: 8 parts
Solvent: 65 parts
Pearlescence: 12 parts
Pigment: 8 parts
Silane coupling agent: 10 parts
Additive: 7 parts
Strengthening agent: 4 parts; And use following method to obtain this coating:
Step (1): by raw material: epoxy modified silicone resin, bisphenol A epoxide resin and Viscotrol C are first put into stirring tank and mixed, temperature in control stirring tank is at 31 DEG C, setting stirring velocity 625/min, churning time 22min, then mix putting into Graphite Powder 99, chromium powder, defoamer and solvent successively, stirring velocity is 740 r/min, keeps 38min;
Step (2): then by raw material: pearlescence, pigment, silane coupling agent, additive and strengthening agent are put into stirring tank and mixed, setting stirring velocity is 828r/min, and churning time is 58min, can obtain the coating that described crocking resistance is high.
embodiment 3
The preparation method of the coating that a kind of crocking resistance that the present embodiment provides is high, the coating that crocking resistance is high is following raw material according to the mass fraction:
Epoxy modified silicone resin: 84 parts
Bisphenol A epoxide resin: 36 parts
Viscotrol C: 12 parts
Graphite Powder 99: 22 parts
Chromium powder: 12 parts
Defoamer: 6 parts
Solvent: 63 parts
Pearlescence: 11 parts
Pigment: 7 parts
Silane coupling agent: 12 parts
Additive: 8 parts
Strengthening agent: 5 parts; And use following method to obtain this coating:
Step (1): by raw material: epoxy modified silicone resin, bisphenol A epoxide resin and Viscotrol C are first put into stirring tank and mixed, temperature in control stirring tank is at 32 DEG C, setting stirring velocity 630r/min, churning time 25min, then mix putting into Graphite Powder 99, chromium powder, defoamer and solvent successively, stirring velocity is 750 r/min, keeps 45min;
Step (2): then by raw material: pearlescence, pigment, silane coupling agent, additive and strengthening agent are put into stirring tank and mixed, setting stirring velocity is 850r/min, and churning time is 60min, can obtain the coating that described crocking resistance is high.
Like this by technical scheme of the present invention, this coating not only crocking resistance is strong, and adhesivity is good, difficult drop-off, this coating surface frictional coefficient is little, rub resistance, and color is various, long service life, this coating life-time service can not bubble, chap, whiten the problems such as even delamination, and can use under rugged environment, and use range is wide, and there is environment protecting, reduce costs.
Above embodiment is only and technological thought of the present invention is described, can not limit protection scope of the present invention with this, and every technological thought proposed according to the present invention, any change that technical scheme basis is done, all falls within scope.
Claims (8)
1. the coating that crocking resistance is high, is characterized in that: the coating that described crocking resistance is high is following raw material according to the mass fraction:
Epoxy modified silicone resin: 82-85 part
Bisphenol A epoxide resin: 30-38 part
Viscotrol C: 11-13 part
Graphite Powder 99: 18-24 part
Chromium powder: 10-13 part
Defoamer: 5-8 part
Solvent: 60-65 part
Pearlescence: 10-12 part
Pigment: 5-8 part
Silane coupling agent: 8-12 part
Additive: 5-8 part
Strengthening agent: 3-5 part.
2. the coating that crocking resistance according to claim 1 is high, is characterized in that: described defoamer is polydimethylsiloxane.
3. the coating that crocking resistance according to claim 1 is high, it is characterized in that: described solvent is the mixture in hexone, toluene, ketone and butanone, wherein: the ratio between the mixture in hexone, toluene, ketone and butanone is: 1:3:2.
4. the coating that crocking resistance according to claim 1 is high, is characterized in that: described pigment is any one in Rutile type Titanium Dioxide, deep chrome yellow.
5. the coating that crocking resistance according to claim 1 is high, is characterized in that: described silane coupling agent is KH550.
6. the coating that crocking resistance according to claim 1 is high, is characterized in that: described additive is that releasing agent Lay mattress falls apart.
7. the coating that crocking resistance according to claim 1 is high, is characterized in that: described strengthening agent is thermals MT.
8. a preparation method for the coating that crocking resistance is high, is characterized in that: the method is carried out according to the following steps:
Step (1): by raw material: epoxy modified silicone resin, bisphenol A epoxide resin and Viscotrol C are first put into stirring tank and mixed, temperature in control stirring tank is at 30-32 DEG C, setting stirring velocity 620-630r/min, churning time 20-25min, then mix putting into Graphite Powder 99, chromium powder, defoamer and solvent successively, stirring velocity is 730-750 r/min, keeps 35-45min;
Step (2): then by raw material: pearlescence, pigment, silane coupling agent, additive and strengthening agent are put into stirring tank and mixed, setting stirring velocity is 820-850r/min, churning time is 55-60min, can obtain the coating that described crocking resistance is high.