CN104629545A - High-altitude mark paint and preparation method thereof - Google Patents
High-altitude mark paint and preparation method thereof Download PDFInfo
- Publication number
- CN104629545A CN104629545A CN201510031398.XA CN201510031398A CN104629545A CN 104629545 A CN104629545 A CN 104629545A CN 201510031398 A CN201510031398 A CN 201510031398A CN 104629545 A CN104629545 A CN 104629545A
- Authority
- CN
- China
- Prior art keywords
- preparation
- parts
- altitude signal
- component
- signal paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-altitude mark paint. The paint is prepared from the following raw materials in parts by mass: 20-35 parts of chlorosulfonated polyethylene resin, 5-15 parts of synthesized resin, 10-20 parts of weather-resistance filler, 1-5 parts of a vulcanizing agent, 10-20 parts of a curing agent, 1-5 parts of accelerant and 100-150 parts of active solvent. The high-altitude mark paint has the characteristics of strong atmospheric aging resistance, good resistance to acid, alkali and salt.
Description
Technical field
The present invention relates to a kind of high-altitude signal paint and preparation method thereof, be applied to paint.
Background technology
The structural mark protection of the concrete such as concrete chimney, power transmission rod is owing to being in high-altitude, and atmospheric aging phenomenon is serious, and is usually subject to the corrosion of sour environment, and its surface corrosion, attaching organism and filthy corrosion phenomenon are very serious, easily cause danger.When general antifouling paste is used for the concrete such as concrete chimney, power transmission rod structure, film forming is thin, and sticking power is low, surface treatment requires strict, complicated construction technique, the technical barrier such as have atomospheric corrosion, environmental pollution serious and life-span short, is not well positioned to meet the demand in market.
Summary of the invention
The present invention is the weak point for avoiding existing for above-mentioned prior art, provide that a kind of resistance to weathering is strong, acid-and base-resisting, a kind of high-altitude signal paint that salt corrosion performance is good and preparation method thereof, its preparation method is simple, easy to operate.
Object of the present invention is achieved through the following technical solutions: a kind of high-altitude signal paint, obtained by mass parts by following raw material:
Chlorosulfonated polyethylene resin 20-35 part;
Synthetic resins 5-15 part;
Weather-proof filler 10-20 part;
Vulcanizing agent 1-5 part;
Solidifying agent 10-20 part;
Promotor 1-5 part;
Strong solvent 100-150 part.
A preparation method for high-altitude signal paint, the preparation process of the method is as follows:
The preparation of component A: get 70-100 part strong solvent, be heated to 45-55 DEG C, stirring active solvent limit, limit adds the chlorosulfonated polyethylene resin, the synthetic resins that take by proportioning, proceeds in stirred vessel after making it miscible, keeps rotating speed 1000-1500r/min, after fully miscible, add weather-proof filler, keep rotating speed 1300-1800 r/min to continue to stir 20-30min, leave standstill, filter, obtain component A;
The preparation of B component: take vulcanizing agent by proportioning, solidifying agent, promotor is dissolved in 30-50 part strong solvent, obtain B component.
Wherein, synthetic resins is modified epoxy.
Wherein, weather-proof filler is calcium carbonate, calcium phosphate, mica, barium sulfate, talcum powder and diatomite.
Wherein, vulcanizing agent is fatty ether polysulfide, thiadiazoles derivative, 4,4 '-dimorpholinyl disulfide.
Wherein, solidifying agent is two chlorine Ammonia, imidazoles, modified aliphatic amines.
Wherein, promotor is thiazoles, thiurams, sulfonamides.
Wherein, strong solvent is epoxy propane butyl ether.
The present invention compared with prior art has the following advantages:
A kind of high-altitude provided by the invention signal paint and preparation method thereof, this high-altitude signal paint has good resistance to weathering, excellent acid-and base-resisting, salt corrosion performance; Perviousness is strong, can low-temperature construction, reduces difficulty of construction; Paint film is bright in colour, and guarantor's light tint retention is excellent; Be exclusively used in the concrete such as concrete chimney, power transmission rod structure, suitability is strong, long service life.
embodiment:
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment of the present invention is:
Embodiment 1:
A kind of high-altitude signal paint, obtained by mass parts by following raw material:
Chlorosulfonated polyethylene resin 20 parts;
Synthetic resins 5 parts;
Weather-proof filler 10 parts;
Vulcanizing agent 1 part;
10 parts, solidifying agent;
Promotor 1 part;
Strong solvent 100 parts.
The preparation process of the preparation method of a kind of high-altitude signal paint is as follows:
The preparation of component A: get 70 parts of strong solvents, be heated to 50 DEG C, stirring active solvent limit, limit adds the chlorosulfonated polyethylene resin, the synthetic resins that take by proportioning, proceeds in stirred vessel after making it miscible, keeps rotating speed 1200r/min, after fully miscible, add weather-proof filler, keep rotating speed 1500r/min to continue to stir 20min, leave standstill, filter, obtain component A;
The preparation of B component: take vulcanizing agent by proportioning, solidifying agent, promotor is dissolved in 30 parts of strong solvents, obtain B component.
Embodiment 2:
A kind of high-altitude signal paint, obtained by mass parts by following raw material:
Chlorosulfonated polyethylene resin 25 parts;
Synthetic resins 8 parts;
Weather-proof filler 13 parts;
Vulcanizing agent 2 parts;
13 parts, solidifying agent;
Promotor 2 parts;
Strong solvent 100 parts.
The preparation process of the preparation method of a kind of high-altitude signal paint is as follows:
The preparation of component A: get 70 parts of strong solvents, be heated to 50 DEG C, stirring active solvent limit, limit adds the chlorosulfonated polyethylene resin, the synthetic resins that take by proportioning, proceeds in stirred vessel after making it miscible, keeps rotating speed 1200r/min, after fully miscible, add weather-proof filler, keep rotating speed 1500 r/min to continue to stir 20min, leave standstill, filter, obtain component A;
The preparation of B component: take vulcanizing agent by proportioning, solidifying agent, promotor is dissolved in 30 parts of strong solvents, obtain B component.
Embodiment 3:
A kind of high-altitude signal paint, obtained by mass parts by following raw material:
Chlorosulfonated polyethylene resin 25 parts;
Synthetic resins 8 parts;
Weather-proof filler 15 parts;
Vulcanizing agent 3 parts;
13 parts, solidifying agent;
Promotor 3 parts;
Strong solvent 120 parts.
The preparation process of the preparation method of a kind of high-altitude signal paint is as follows:
The preparation of component A: get 80 parts of strong solvents, be heated to 50 DEG C, stirring active solvent limit, limit adds the chlorosulfonated polyethylene resin, the synthetic resins that take by proportioning, proceeds in stirred vessel after making it miscible, keeps rotating speed 1500r/min, after fully miscible, add weather-proof filler, keep rotating speed 1800 r/min to continue to stir 20min, leave standstill, filter, obtain component A;
The preparation of B component: take vulcanizing agent by proportioning, solidifying agent, promotor is dissolved in 40 parts of strong solvents, obtain B component.
Embodiment 4:
A kind of high-altitude signal paint, obtained by mass parts by following raw material:
Chlorosulfonated polyethylene resin 30 parts;
Synthetic resins 10 parts;
Weather-proof filler 15 parts;
Vulcanizing agent 3 parts;
15 parts, solidifying agent;
Promotor 3 parts;
Strong solvent 130 parts.
The preparation process of the preparation method of a kind of high-altitude signal paint is as follows:
The preparation of component A: get 90 parts of strong solvents, be heated to 50 DEG C, stirring active solvent limit, limit adds the chlorosulfonated polyethylene resin, the synthetic resins that take by proportioning, proceeds in stirred vessel after making it miscible, keeps rotating speed 1200r/min, after fully miscible, add weather-proof filler, keep rotating speed 1600 r/min to continue to stir 20min, leave standstill, filter, obtain component A;
The preparation of B component: take vulcanizing agent by proportioning, solidifying agent, promotor is dissolved in 40 parts of strong solvents, obtain B component.
Embodiment 5:
A kind of high-altitude signal paint, obtained by mass parts by following raw material:
Chlorosulfonated polyethylene resin 30 parts;
Synthetic resins 10 parts;
Weather-proof filler 15 parts;
Vulcanizing agent 4 parts;
15 parts, solidifying agent;
Promotor 4 parts;
Strong solvent 130 parts.
The preparation process of the preparation method of a kind of high-altitude signal paint is as follows:
The preparation of component A: get 90 parts of strong solvents, be heated to 50 DEG C, stirring active solvent limit, limit adds the chlorosulfonated polyethylene resin, the synthetic resins that take by proportioning, proceeds in stirred vessel after making it miscible, keeps rotating speed 1200r/min, after fully miscible, add weather-proof filler, keep rotating speed 1500 r/min to continue to stir 20min, leave standstill, filter, obtain component A;
The preparation of B component: take vulcanizing agent by proportioning, solidifying agent, promotor is dissolved in 40 parts of strong solvents, obtain B component.
Embodiment 6:
A kind of high-altitude signal paint, obtained by mass parts by following raw material:
Chlorosulfonated polyethylene resin 35 parts;
Synthetic resins 15 parts;
Weather-proof filler 20 parts;
Vulcanizing agent 5 parts;
20 parts, solidifying agent;
Promotor 5 parts;
Strong solvent 150 parts.
The preparation process of the preparation method of a kind of high-altitude signal paint is as follows:
The preparation of component A: get 100 parts of strong solvents, be heated to 50 DEG C, stirring active solvent limit, limit adds the chlorosulfonated polyethylene resin, the synthetic resins that take by proportioning, proceeds in stirred vessel after making it miscible, keeps rotating speed 1500r/min, after fully miscible, add weather-proof filler, keep rotating speed 1800 r/min to continue to stir 20min, leave standstill, filter, obtain component A;
The preparation of B component: take vulcanizing agent by proportioning, solidifying agent, promotor is dissolved in 50 parts of strong solvents, obtain B component.
Component A and B component mix by the volume ratio of 10:1 by the present invention before use, re-use.
The foregoing is only explanation embodiments of the present invention; be not limited to the present invention, for a person skilled in the art, within the spirit and principles in the present invention all; any amendment of doing, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (8)
1. a high-altitude signal paint, is characterized in that: obtained by mass parts by following raw material:
Chlorosulfonated polyethylene resin 20-35 part;
Synthetic resins 5-15 part;
Weather-proof filler 10-20 part;
Vulcanizing agent 1-5 part;
Solidifying agent 10-20 part;
Promotor 1-5 part;
Strong solvent 100-150 part.
2., according to the preparation method of a kind of high-altitude signal paint described in claim 1, it is characterized in that the preparation process of the method is as follows:
The preparation of component A: get 70-100 part strong solvent, be heated to 45-55 DEG C, stirring active solvent limit, limit adds the chlorosulfonated polyethylene resin, the synthetic resins that take by proportioning, proceeds in stirred vessel after making it miscible, keeps rotating speed 1000-1500r/min, after fully miscible, add weather-proof filler, keep rotating speed 1300-1800 r/min to continue to stir 20-30min, leave standstill, filter, obtain component A;
The preparation of B component: take vulcanizing agent by proportioning, solidifying agent, promotor is dissolved in 30-50 part strong solvent, obtain B component.
3. the preparation method of a kind of high-altitude signal paint according to claim 1 or 2, is characterized in that:
Described synthetic resins is modified epoxy.
4. the preparation method of a kind of high-altitude signal paint according to claim 1 or 2, is characterized in that:
Described weather-proof filler is calcium carbonate, calcium phosphate, mica, barium sulfate, talcum powder and diatomite.
5. the preparation method of a kind of high-altitude signal paint according to claim 1 or 2, is characterized in that:
Described vulcanizing agent is fatty ether polysulfide, thiadiazoles derivative, 4,4 '-dimorpholinyl disulfide.
6. the preparation method of a kind of high-altitude signal paint according to claim 1 or 2, is characterized in that: described solidifying agent is two chlorine Ammonia, imidazoles, modified aliphatic amine.
7. the preparation method of a kind of high-altitude signal paint according to claim 1 or 2, is characterized in that: described promotor is thiazoles, thiurams, sulfonamides.
8. the preparation method of a kind of high-altitude signal paint according to claim 1 or 2, is characterized in that: described strong solvent is epoxy propane butyl ether.