CN104625581A - Zinc white copper wire production technology - Google Patents
Zinc white copper wire production technology Download PDFInfo
- Publication number
- CN104625581A CN104625581A CN201310551844.0A CN201310551844A CN104625581A CN 104625581 A CN104625581 A CN 104625581A CN 201310551844 A CN201310551844 A CN 201310551844A CN 104625581 A CN104625581 A CN 104625581A
- Authority
- CN
- China
- Prior art keywords
- annealing
- production technology
- wire production
- copper wire
- zinc white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a zinc white copper wire production technology. A zinc white copper wire production technology with more than 25% of Ni comprises the steps of horizontal continuous casting, hot extrusion, cold rolling, low oxygen annealing, continuous drawing and planing, low oxygen annealing, diluted acid washing, multi-die stretching, straightening, and inspecting and packing. A zinc white copper wire production technology with less than 25% of Ni comprises the steps of horizontal continuous casting, cold rolling, low oxygen annealing, drawing and planing, low oxygen annealing, diluted acid washing, multi-die stretching, cover annealing, and inspecting and packing. The zinc white copper wire production technology has the advantages of being smooth and clean in the surface of a product, good in corrosion resistance and abrasion resistance, good in welding property, casting property and mechanical property, simpler in technology, easy in process control, low in production cost, and high in production efficiency.
Description
Technical field
The invention belongs to copper alloy wire production technology, be specifically related to a kind of Nickel-silver Wire production technology.
Background technology
The main application fields of copper alloy wire is zipper fabrication industry, valve inside, bar cap line manufacturing industry, solder manufacturing industry, spectacle-frame manufacturing industry, connector manufacturing industry, gadget, button, watchmaking and auto manufacturing etc.Packfong has the advantages such as corrosion resisting property is good, any surface finish, attractive in appearance, intensity is medium above, good springiness, easily weldering, can be used as structure, securing member, flexible member, connector etc., be widely used in the industries such as glasses accessory, the auxiliary material of clothes, precision instrument, instrument, medicine equipment and communication.Along with China's expanding economy, its consumption increases year by year.
Summary of the invention
The object of the invention is to, a kind of Nickel-silver Wire production technology is provided, easy to operate.
Nickel-silver Wire production technology provided by the invention, comprises horizontal casting → hot extrude → cold rolling → hypoxemia annealing → Lian Lalian plane → hypoxemia annealing → Diluted Acid Washing → multimode stretching → aligning → test package containing more than Ni25% Nickel-silver Wire production technology; Nickel-silver Wire production technology containing below Ni25% comprises horizontal casting → cold rolling → hypoxemia and to anneal → draw plane → hypoxemia annealing → Diluted Acid Washing → multimode stretching → bell-type annealing → test package; Casting temperature l160 DEG C ~ 1250 DEG C, casting speed 0.8 ~ 1.6 m/min, pickling adopts concentration to be the dilution heat of sulfuric acid of 5 ~ 20%; pickling temperature 40 ~ 85 DEG C; annealing adds nitrogen and makes protection gas, annealing temperature 390 ~ 410 DEG C, temperature retention time 90 ~ 120 minutes.
Nickel-silver Wire production technology provided by the invention, its beneficial effect is, product surface is bright and clean, corrosion-resistant, rub resistance good, and welding performance, casting character, mechanicalness are excellent, and technique is relatively simple, and flow process is easy to control, and production cost is low, and production efficiency is high.
Detailed description of the invention
Below in conjunction with an embodiment, Nickel-silver Wire production technology provided by the invention is described in detail.
Embodiment
Horizontal casting → hot extrude → cold rolling → hypoxemia annealing → Lian Lalian plane → hypoxemia annealing → Diluted Acid Washing → multimode stretching → aligning → test package is comprised containing more than Ni25% Nickel-silver Wire production technology; Casting temperature l160 DEG C ~ 1250 DEG C, casting speed 0.8 ~ 1.6 m/min, pickling adopts concentration to be the dilution heat of sulfuric acid of 5 ~ 20%; pickling temperature 40 ~ 85 DEG C; annealing adds nitrogen and makes protection gas, annealing temperature 390 ~ 410 DEG C, temperature retention time 90 ~ 120 minutes.
Claims (1)
1. a Nickel-silver Wire production technology, is characterized in that: comprise horizontal casting → hot extrude → cold rolling → hypoxemia annealing → Lian Lalian plane → hypoxemia annealing → Diluted Acid Washing → multimode stretching → aligning → test package containing more than Ni25% Nickel-silver Wire production technology; Nickel-silver Wire production technology containing below Ni25% comprises horizontal casting → cold rolling → hypoxemia and to anneal → draw plane → hypoxemia annealing → Diluted Acid Washing → multimode stretching → bell-type annealing → test package; Wherein, casting temperature l160 DEG C ~ 1250 DEG C, casting speed 0.8 ~ 1.6 m/min; pickling adopts concentration to be the dilution heat of sulfuric acid of 5 ~ 20%, pickling temperature 40 ~ 85 DEG C, and annealing adds nitrogen and makes protection gas; annealing temperature 390 ~ 410 DEG C, temperature retention time 90 ~ 120 minutes.