CN104616920B - The method for improving insulated tension pole external insulation performance - Google Patents
The method for improving insulated tension pole external insulation performance Download PDFInfo
- Publication number
- CN104616920B CN104616920B CN201510064817.XA CN201510064817A CN104616920B CN 104616920 B CN104616920 B CN 104616920B CN 201510064817 A CN201510064817 A CN 201510064817A CN 104616920 B CN104616920 B CN 104616920B
- Authority
- CN
- China
- Prior art keywords
- weight
- silicon rubber
- pole
- parts
- silicone oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
One method for improving insulated tension pole external insulation performance, comprises the following steps pole is 1. fixed on into insulating sleeve with vacuum switch tube, 2. pours into a mould hard silicon rubber with the cavity between vacuum switch tube and insulating sleeve in pole;3. positioning spacer is set between the end of vacuum switch tube and insulating sleeve in pole, the cavity between pole vacuum switch tube and insulating sleeve is closed;4. pole vacuum switch tube is connected with insulated tension pole component by being flexible coupling, 5. the cavity being flexible coupling, between insulated tension pole component and insulating sleeve pours into a mould soft silicon rubber;This method can greatly improve insulated tension pole external insulation performance.
Description
Technical field
It is more particularly to a kind of to improve insulated tension pole external insulation performance the present invention relates to a kind of technical field of power equipment
Method.
Background technology
Currently used for driving, the insulation mode between the insulated tension pole and moving contact of the motion of vacuum interrupter moving contact is general
There are the insulation modes such as air insulation, oil-insulation, SF6 gas-insulateds, insulating properties respectively have quality.As air insulation volume is big, exhausted
Edge poor performance, easily influenceed to cause apparatus insulated puncture by outdoor environment;SF6 gas-insulateds may not apply to plateau, extremely tremble with fear ground
Area, insulation decline easily causes equipment explosion after the leakage of SF6 gases, and SF6 belongs to greenhouse gases, not environmentally, is not easily recycled;Oil
Insulation complex manufacturing, influenceed to easily cause oil leak by outdoor environment and apparatus insulated performance reduction is caused equipment explosion;
And insulating oil is not environmentally, is not easily recycled.Therefore a kind of method of good raising insulated tension pole external insulation performance is found, is lifting
The only way which must be passed of middle voltage electrical equipment performance.
The content of the invention
To solve the above problems, the present invention provides a kind of method for improving insulated tension pole external insulation performance.
The technical scheme is that:A kind of method for improving insulated tension pole external insulation performance, comprises the following steps
1. pole is fixed on insulating sleeve with vacuum switch tube,
2. in pole with hard silicon rubber is poured into a mould in the cavity between vacuum switch tube and insulating sleeve, the hard silicon such as stand
Cure of Rubber;
3. positioning spacer is set between the end of vacuum switch tube and insulating sleeve in pole, pole is used
Cavity closing between vacuum switch tube and insulating sleeve;
4. pole vacuum switch tube is connected with insulated tension pole component by being flexible coupling,
5. the cavity being flexible coupling, between insulated tension pole component and insulating sleeve pours into a mould soft silicon rubber;
6. after soft silicon rubber is poured by flexible sealing barrier film by lock sleeve and lock sleeve, be separately fixed at insulation draw
In bar assembly and on insulating sleeve.
The present invention is realized using following technical measures:
Pole is fixed in insulating sleeve with vacuum switch tube, one end of insulated tension pole by pole with using true
The moving contact of empty switching tube is rigidly connected, and the location of pole vacuum switch tube and insulated tension pole are divided into two
Not connected space,
Soft silicon rubber is poured into a mould around insulated tension pole, the soft silicon rubber has a good electrical insulation properties, and can be with
Connection is glued well with other materials, electricity is climbed so as to block, and plays a part of sealed insulation pull bar, so that it is no longer by the external world
The influence of environment.By being sealed by the good soft silicon rubber of electrical insulation properties around insulated tension pole, so its external form
Size by air insulation just without being considered, so that its overall dimensions is greatly reduced.
By the viscosity for adjusting soft silicon rubber so that insulated tension pole can obtain certain damped coefficient when moving, from
And good second order velocity and acceleration response curve is obtained, shock loading of the closing process to arc-chutes is reduced, is improved
The life-span of arc-chutes;Separating brake overshoot is reduced to the shock loading of mechanism, the life-span of mechanism is improved.
In order to ensure that soft silicon rubber glues connection well with insulating cylinder, insulated tension pole, insulating cylinder and insulated tension pole are used and sprayed
The process of surface treatment of sand and ball blast, makes its rough surface, be more conducive to and soft silicon rubber combination.
Use vacuum casting process when pouring into a mould soft silicon rubber, and remove moisture removal, it is ensured that it is poured be poured in after, it is whole as one
The excellent interior insulation performance of body.
Brief description of the drawings
Fig. 1 be improve insulated tension pole external insulation performance method after the completion of pole structure chart.
1. insulating sleeves in figure, 2. pole vacuum switch tubes, 3. be flexible coupling, 4. insulated tension pole components, 5. barrier films
Pump diaphragm, 6. lock sleeves, 7. lock sleeves, 8. soft silicon rubber, 9. positioning spacers, 10. hard silicon rubber.
Embodiment
Referring to Fig. 1, a kind of method for improving insulated tension pole external insulation performance, comprises the following steps in figure
1. pole is fixed on insulating sleeve with vacuum switch tube,
2. in pole with hard silicon rubber is poured into a mould in the cavity between vacuum switch tube and insulating sleeve, the hard silicon such as stand
Cure of Rubber;
3. positioning spacer is set between the end of vacuum switch tube and insulating sleeve in pole, pole is used
Cavity closing between vacuum switch tube and insulating sleeve;
4. pole vacuum switch tube is connected with insulated tension pole component by being flexible coupling,
5. the cavity being flexible coupling, between insulated tension pole component and insulating sleeve pours into a mould soft silicon rubber;
6. after soft silicon rubber is poured by flexible sealing barrier film by lock sleeve and lock sleeve, be separately fixed at insulation draw
In bar assembly and on insulating sleeve.
The formula of described soft silicon rubber, includes by weight
Silicone rubber material:50-90, diluent:20-30, coupling agent:2-3, chain extender:3-5, vulcanizing agent:3-5, catalysis
Agent:4-10, tackifier:5-10.
Described vulcanizing agent be si28, si32, si40, tetrabutyl titanate it is therein a kind of or at least two compound.
Described diluent is that dimethicone, 203 silicone oil, polyhydroxy silicon, epoxy radicals silicone oil are therein a kind of or at least
Two kinds of mixture.
Described coupling agent be KH560, KH550, KH792, KH602 it is therein a kind of or at least two mixture.
Described chain extender:Dimethyl diethoxy siloxanes, containing hydrogen silicone oil, the butanone oximino silane of dimethyl two are therein
It is a kind of or at least two mixture.
Described catalyst:The complex compound of the metals such as lawrencium, palladium, nickel, platinum it is therein a kind of or at least two mixture.
Described tackifier:Boric acid, KH560, KH792, titanium complex it is therein a kind of or at least two mixture.
The preparation method of the soft silicon rubber carried out according to foregoing formula, comprises the following steps:
(1), silicone rubber material, diluent, chain extender, catalyst are added in blender and stirred 20-30 minutes, it is ensured that is filled
Divide well mixed;
(2), silicone rubber material, diluent, vulcanizing agent, coupling agent, tackifier are added in blender and stirred 15-20 minutes
Ensure to be sufficiently mixed uniformly;
(3), by step 1) and step 2) press 1:1 is mixed evenly, 1.5-2 hour of vacuumizing and defoaming, you can embedding;
(4), normal temperature embedding has started to glue after 1 hour, and solidify afterwards are complete within 24 hours;Or be heated under 80 degree -150 degree
Solidification, the completion of cure in -1 hour 20 minutes.
The formula of described hard silicon rubber, following raw material and proportioning silicon rubber are at least included according to parts by weight:30-50 weights
Measure part, vulcanizing agent:2-5 parts by weight, diluent:4-8 parts by weight, aerosil:2-5 parts by weight, fire retardant:20-40 weights
Measure part, silica flour:20-40 parts by weight, silicone oil:4-8 parts by weight, organotin:0.5-2 parts by weight, coupling agent:2-5 parts by weight, two
Titanium oxide:1-3 parts by weight, carbon black:0.1-1 parts by weight.
Described vulcanizing agent be si28, si32, si40, tetrabutyl titanate it is therein a kind of or at least two compound;
Vulcanizing agent increase solidification intensity, curing rate;
Described diluent is that dimethicone, 203 silicone oil, polyhydroxy silicon, epoxy radicals silicone oil are therein a kind of or at least
Two kinds of mixture;Diluent being capable of speedup deaeration;
Described fire retardant be aluminium hydroxide, deca-BDE, antimony oxide it is therein a kind of or at least two it is mixed
Compound;
Described silicone oil be dimethicone, 203 silicone oil, hydroxy silicon oil it is therein a kind of or at least two mixture;
Silicone oil is nertralizer, for reconcile silicon rubber proportioning;
Described organotin is stannous octoate, dibutyl tin laurate, titanium complex one kind therein or at least two
Mixture;Organotin can increase silicon rubber curing rate;
Described coupling agent be KH560, KH550, KH792, KH602 it is therein a kind of or at least two mixture.It is even
Connection agent can increase caking property.
Described aerosil is used to lift caking property, and titanium dioxide is used to brighten.
The preparation method of hard silicon rubber is made using foregoing formula, step is as follows:
(1), by silicone rubber material, diluent, aerosil, fire retardant, silica flour, titanium dioxide by a certain percentage
Add in banbury and stir 20-30 minutes, it is ensured that be uniform, then heat to 120-150 degree, vacuumize dehydration 1.5-2 small
When, it is ensured that solid material fully infiltrates;
(2), silicone oil, coupling agent, organotin, carbon black are put into agitator in proportion, stirred evenly 5-10 minutes;
(3) raw material in step (1), is cooled to normal temperature, vulcanizing agent is added, stirred 10-20 minutes in agitator;
(4) 7-11 parts by weight, will be taken in step (3), then in step (2) 0.8-1 parts by weight will be taken fully to stir evenly, deaeration,
Addition need to be poured into a mould in product, then deaeration 15-30 minutes under vacuo.
(5), quiet to put by embedding container, 1-2 hour thickening, quiet put reaches surface cure for 24 hours, production is reached after 7 days
Product are fully cured.
Claims (1)
1. a kind of method for improving insulated tension pole external insulation performance, comprises the following steps
1. pole is fixed on insulating sleeve with vacuum switch tube,
2. in pole with hard silicon rubber is poured into a mould in the cavity between vacuum switch tube and insulating sleeve, the hard silicon rubber such as stand
Solidification;
3. positioning spacer is set between the end of vacuum switch tube and insulating sleeve in pole, by pole vacuum
Cavity closing between switching tube and insulating sleeve;
4. pole vacuum switch tube is connected with insulated tension pole component by being flexible coupling,
5. the cavity being flexible coupling, between insulated tension pole component and insulating sleeve pours into a mould soft silicon rubber;
6. after soft silicon rubber is poured by flexible sealing barrier film by lock sleeve and lock sleeve, be separately fixed at insulated tension pole group
On part and on insulating sleeve;
The formula of described soft silicon rubber, includes by weight
Silicone rubber material:50-90, diluent:20-30, coupling agent:2-3, chain extender:3-5, vulcanizing agent:3-5, catalyst:4-
10th, tackifier:5-10;
Described vulcanizing agent be si28, si32, si40, tetrabutyl titanate it is therein a kind of or at least two compound;
Described diluent is dimethicone, 203 silicone oil, polyhydroxy silicon, epoxy radicals silicone oil one kind therein or at least two
Mixture;
Described coupling agent be KH560, KH550, KH792, KH602 it is therein a kind of or at least two mixture;
Described chain extender:Dimethyl diethoxy siloxanes, containing hydrogen silicone oil, the butanone oximino silane one kind therein of dimethyl two
Or at least two mixture;
Described catalyst:Lawrencium, palladium, nickel, platinum complex compound it is therein a kind of or at least two mixture;
Described tackifier:Boric acid, KH560, KH792, titanium complex it is therein a kind of or at least two mixture;
The preparation method of the soft silicon rubber carried out according to foregoing formula, comprises the following steps:
(1), silicone rubber material, diluent, chain extender, catalyst are added in blender and stirred 20-30 minutes, it is ensured that be fully mixed
Close uniform;
(2), add to stir in blender by silicone rubber material, diluent, vulcanizing agent, coupling agent, tackifier ensures for 15-20 minutes
It is sufficiently mixed uniform;
(3), by step 1) and step 2) press 1:1 is mixed evenly, 1.5-2 hour of vacuumizing and defoaming, you can embedding;
(4), normal temperature embedding has started to glue after 1 hour, and solidify afterwards are complete within 24 hours;Or be heated to solidify under 80 degree -150 degree,
The completion of cure in -1 hour 20 minutes;
The formula of described hard silicon rubber, following raw material and proportioning silicon rubber are at least included according to parts by weight:30-50 weight
Part, vulcanizing agent:2-5 parts by weight, diluent:4-8 parts by weight, aerosil:2-5 parts by weight, fire retardant:20-40 weight
Part, silica flour:20-40 parts by weight, silicone oil:4-8 parts by weight, organotin:0.5-2 parts by weight, coupling agent:2-5 parts by weight, dioxy
Change titanium:1-3 parts by weight, carbon black:0.1-1 parts by weight;
Described vulcanizing agent be si28, si32, si40, tetrabutyl titanate it is therein a kind of or at least two compound;Vulcanization
Agent increase solidification intensity, curing rate;
Described diluent is dimethicone, 203 silicone oil, polyhydroxy silicon, epoxy radicals silicone oil one kind therein or at least two
Mixture;Diluent being capable of speedup deaeration;
Described fire retardant be aluminium hydroxide, deca-BDE, antimony oxide it is therein a kind of or at least two mixture;
Described silicone oil be dimethicone, 203 silicone oil, hydroxy silicon oil it is therein a kind of or at least two mixture;Silicone oil
For nertralizer, for reconciling silicon rubber proportioning;
Described organotin be stannous octoate, dibutyl tin laurate, titanium complex it is therein a kind of or at least two it is mixed
Compound;Organotin can increase silicon rubber curing rate;
Described coupling agent be KH560, KH550, KH792, KH602 it is therein a kind of or at least two mixture;Coupling agent
Caking property can be increased;
Described aerosil is used to lift caking property, and titanium dioxide is used to brighten;
The preparation method of hard silicon rubber is made using foregoing formula, step is as follows:
(1), silicone rubber material, diluent, aerosil, fire retardant, silica flour, titanium dioxide are added by a certain percentage
Stirred 20-30 minutes in banbury, it is ensured that uniform, then heat to 120-150 degree, vacuumize 1.5-2 hour of dehydration, really
Solid material is protected fully to infiltrate;
(2), silicone oil, coupling agent, organotin, carbon black are put into agitator in proportion, stirred evenly 5-10 minutes;
(3) raw material in step (1), is cooled to normal temperature, vulcanizing agent is added, stirred 10-20 minutes in agitator;
(4) 7-11 parts by weight, will be taken in step (3), then in step (2) 0.8-1 parts by weight will be taken fully to stir evenly, deaeration is added
It need to pour into a mould in product, then deaeration 15-30 minutes under vacuo;
(5), quiet to put by embedding container, 1-2 hour thickening, quiet put reaches surface cure for 24 hours, reaches that product is complete after 7 days
All solidstate.