CN104610796B - A kind of king joins the system of selection of filler - Google Patents
A kind of king joins the system of selection of filler Download PDFInfo
- Publication number
- CN104610796B CN104610796B CN201410476486.6A CN201410476486A CN104610796B CN 104610796 B CN104610796 B CN 104610796B CN 201410476486 A CN201410476486 A CN 201410476486A CN 104610796 B CN104610796 B CN 104610796B
- Authority
- CN
- China
- Prior art keywords
- filler
- king
- selection
- joins
- accurate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of king and join the system of selection of filler, this system of selection comprises the following steps: (1) takes the graduated cylinder of a 250ml, scale is accurate to 1ml, add and become owner of filler at 130 160ml, add at technical grade solvent DBE to 160 200ml, stir evenly with Glass rod, extremely emerge without steam bubble in standing graduated cylinder, the heap volume reading main filler is d1, is accurate to 0.2ml；(2) in above sample, add 8 12ml flour fillers to be selected, stir evenly with Glass rod, stand to emerging without steam bubble, read total filler heap volume d2；(3) calculating d2 d1, when the value of d2 d1 is between 12, then this filler is that the king of main filler joins filler.Beneficial effect: this method can effectively be selected king by simple method and join filler, time saving and energy saving.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of king and join the system of selection of filler.
Background technology
Filler plays a very important role in coating.When a kind of coating of research and development have selected a main filler, this filler
Space can also fill with a kind of thinner filler, so can save resin in a large number, to save solvent, thus reduce painting
The carbon emission amount of material, and improve the performance of coating.And the one selected in this process is most preferably arranged in pairs or groups, filler, referred to as king are joined
Filler.
At present in the development process of coating, the selection to filler is unable to reach most preferably, accordingly, it would be desirable to a kind of new technology
Scheme solves the problems referred to above.
Summary of the invention
The present invention provides a kind of king effective, convenient to join the system of selection of filler.
The technical solution used in the present invention: a kind of king joins the system of selection of filler and comprises the following steps: (1) takes one
The graduated cylinder of 250ml, scale is accurate to 1ml, adds and becomes owner of filler at 130-160ml, adds technical grade solvent DBE extremely
At 160-200ml, stirring evenly with Glass rod, extremely emerge without steam bubble in standing graduated cylinder, the heap volume reading main filler is d1, essence
Really to 0.2ml；(2) in above sample, add 8-12ml flour filler to be selected, stir evenly with Glass rod, stand to emitting without steam bubble
Go out, read total filler heap volume d2；(3) d2-d1 is calculated, when the value of d2-d1 is between 1-2, then this filler is
The king of main filler joins filler.
If d2-d1 is more than 2, then select the filler above step that mesh number is bigger；If d2-d1 is less than 1, then select mesh number more
Little filler repeats above step.
Beneficial effects of the present invention: this method can effectively be selected king by simple method and join filler to save a large amount of tree
Fat, such that it is able to save solvent, reduces the carbon emission amount of coating, it is also possible to improve the performance of coating.
Detailed description of the invention
Embodiment 1
A kind of king joins the system of selection of filler and comprises the following steps；(1) taking the graduated cylinder of a 250ml, scale is accurate to
1ml, adds and becomes owner of filler at 130ml, add technical grade solvent DBE to 160ml place, stir evenly with Glass rod, standing amount
To emerging without steam bubble in cylinder, the heap volume reading main filler is d1, is accurate to 0.2ml；(2) add in above sample
8ml flour filler to be selected, stirs evenly with Glass rod, stands to emerging without steam bubble, reads total filler heap volume d2；(3) d2-is calculated
D1, when the value of d2-d1 is between 1-2, then this filler is that the king of main filler joins filler.
If d2-d1 is more than 2, then select the filler above step that mesh number is bigger；If d2-d1 is less than 1, then select mesh number more
Little filler repeats above step and joins filler until selecting king.
Embodiment 2
A kind of king joins the system of selection of filler and comprises the following steps: (1) takes the graduated cylinder of a 250ml, and scale is accurate to
1ml, adds and becomes owner of filler at 140ml, add technical grade solvent DBE to 170ml place, stir evenly with Glass rod, standing amount
To emerging without steam bubble in cylinder, the heap volume reading main filler is d1, is accurate to 0.2ml；(2) add in above sample
10ml flour filler to be selected, stirs evenly with Glass rod, stands to emerging without steam bubble, reads total filler heap volume d2；(3) calculate
D2-d1, when the value of d2-d1 is between 1-2, then this filler is that the king of main filler joins filler.
If d2-d1 is more than 2, then select the filler above step that mesh number is bigger；If d2-d1 is less than 1, then select mesh number more
Little filler repeats above step and joins filler until selecting king.
Embodiment 3
A kind of king joins the system of selection of filler and comprises the following steps: (1) takes the graduated cylinder of a 250ml, and scale is accurate to
1ml, adds and becomes owner of filler at 150ml, add technical grade solvent DBE to 180ml place, stir evenly with Glass rod, standing amount
To emerging without steam bubble in cylinder, the heap volume reading main filler is d1, is accurate to 0.2ml；(2) add in above sample
10ml flour filler to be selected, stirs evenly with Glass rod, stands to emerging without steam bubble, reads total filler heap volume d2；(3) calculate
D2-d1, when the value of d2-d1 is between 1-2, then this filler is that the king of main filler joins filler.
If d2-d1 is more than 2, then select the filler above step that mesh number is bigger；If d2-d1 is less than 1, then select mesh number less
Filler repeat above step join filler until selecting king.
Embodiment 4
A kind of king joins the system of selection of filler and comprises the following steps: (1) takes the graduated cylinder of a 250ml, and scale is accurate to
1ml, adds and becomes owner of filler at 160ml, add technical grade solvent DBE to 200ml place, stir evenly with Glass rod, standing amount
To emerging without steam bubble in cylinder, the heap volume reading main filler is d1, is accurate to 0.2ml；(2) add in above sample
12ml flour filler to be selected, stirs evenly with Glass rod, stands to emerging without steam bubble, reads total filler heap volume d2；(3) calculate
D2-d1, when the value of d2-d1 is between 1-2, then this filler is that the king of main filler joins filler.
If d2-d1 is more than 2, then select the filler above step that mesh number is bigger；If d2-d1 is less than 1, then select mesh number less
Filler repeat above step join filler until selecting king.
Claims (2)
1. a king joins the system of selection of filler, it is characterised in that this system of selection comprises the following steps:
(1) taking the graduated cylinder of a 250ml, scale is accurate to 1ml, adds and becomes owner of filler at 130-160ml, adds industry
Level solvent DBE to 160-200ml place, stirs evenly with Glass rod, extremely emerges without steam bubble, read the heap of main filler in standing graduated cylinder
Volume is d1, is accurate to 0.2ml；
(2) in above sample, add 8-12ml flour filler to be selected, stir evenly with Glass rod, stand to emerging without steam bubble, read
Total filler heap volume d2；
(3) calculating d2-d1, when the value of d2-d1 is between 1-2, then this filler is that the king of main filler joins filler.
2. the system of selection of filler is joined according to a kind of king described in claim 1, it is characterised in that: if d2-d1 is more than 2,
The filler that mesh number is bigger is then selected to repeat above step；If d2-d1 is less than 1, then select more than the filler repetition that mesh number is less
Step.