CN104558763A - Film for food and production method thereof - Google Patents
Film for food and production method thereof Download PDFInfo
- Publication number
- CN104558763A CN104558763A CN201410735256.7A CN201410735256A CN104558763A CN 104558763 A CN104558763 A CN 104558763A CN 201410735256 A CN201410735256 A CN 201410735256A CN 104558763 A CN104558763 A CN 104558763A
- Authority
- CN
- China
- Prior art keywords
- parts
- density polyethylene
- food grade
- mixed solution
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a film for food, which comprises the following components in parts by weight: 70-80 parts of high density polyethylene, 5-10 parts of metallocene linear low density polyethylene, 10-20 parts of polyethylene resin, 10-20 parts of dioctyl epoxy tetrahydrophthalate, 5-20 parts of high-speed heat-sealing copolymer polypropylene, 1-10 parts of multi-component co-polypropylene, 0.1-1 part of titanium dioxide and 1-5 parts of filler. The film for food disclosed by the invention has good barrier property and air tightness as well as good anti-pollution property and high strength. A preparation method is simple and easy to operate while the investment cost is low and large-scale production is facilitated.
Description
Technical field
The present invention relates to packing film field, particularly a kind of food grade film and production method thereof.
Background technology
Current food packaging industry says that the packaging base material film quantity needed is large, kind is many, adopts the film of single raw material production to be difficult to adapt to the packing instructions of Special food.Trace it to its cause, although producer's production technique of mainly respectively producing plastic raw materials is each has something to recommend him, often kind of raw material has its weak point, so the film produced is difficult to the demand meeting various situation.Although also there are the way adopting different material used in combination in some companies, owing to lacking necessary testing installation and the testing program of test set and system, its effect is unsatisfactory.
The information being disclosed in this background technology part is only intended to increase the understanding to general background of the present invention, and should not be regarded as admitting or imply in any form that this information structure has been prior art that persons skilled in the art are known.
Summary of the invention
In order to overcome prior art Problems existing, the object of the present invention is to provide the food grade film of a kind of high barrier, high-air-tightness, high strength.
For achieving the above object, the invention provides a kind of food grade film, meter comprises following component by weight: the adjacent stupid dioctyl phthalate dioctyl ester 10 ~ 20 parts of high density polyethylene(HDPE) 70 ~ 80 parts, metallocene linear-low density polyethylene 5 ~ 10 parts, polyethylene resin 10 ~ 20 parts, epoxy tetrahydrochysene, at a high speed heat-sealing copolymerized type propene polymer 5 ~ 20 parts, multi-component copolymer polypropylene 1 ~ 10 part, titanium dioxide 0.1 ~ 1 part, filler 1 ~ 5 part.
Preferably, in technique scheme, described food grade film, meter comprises following component by weight: the adjacent stupid dioctyl phthalate dioctyl ester 17 parts of high density polyethylene(HDPE) 75 parts, metallocene linear-low density polyethylene 7 parts, polyethylene resin 15 parts, epoxy tetrahydrochysene, at a high speed heat-sealing copolymerized type propene polymer 13 parts, multi-component copolymer polypropylene 5 parts, titanium dioxide 0.5 part, filler 4 parts.
Preferably, in technique scheme, described filler is fabric fibre.
A preparation method for food grade film, comprises the following steps:
(1) raw material needed for production is taken on demand;
(2) raw material is mixed, adopt back the mode of heating up in a steamer, control temperature 150 ~ 200 DEG C, stir material with the speed that rotating speed is 80 ~ 100r/min, material is thoroughly dissolved, obtains mixed solution;
(3) mixed solution is left standstill 1 ~ 2 hour at 100 ~ 130 DEG C, pour the advection mould being preheated to 90 ~ 100 DEG C into, curtain coating, on the mirror steel plate of room temperature, makes the rapid gel of mixed solution chilling, and it is peeled off obtained high-temp liquid plastics film from steel plate.
Compared with prior art, the present invention has following beneficial effect: food grade film of the present invention, barrier and resistance to air loss good, there is good resistance to crocking, and intensity is high.Preparation method is simple, and easy handling, cost of investment is low, is beneficial to scale operation.
Embodiment
Below in conjunction with specific embodiment, the specific embodiment of the present invention is described in detail, but is to be understood that protection scope of the present invention not by the restriction of embodiment.
Embodiment 1
A preparation method for food grade film, comprises the following steps:
(1) take the raw material needed for production on demand, meter comprises following component by weight: the adjacent stupid dioctyl phthalate dioctyl ester 17 parts of high density polyethylene(HDPE) 75 parts, metallocene linear-low density polyethylene 7 parts, polyethylene resin 15 parts, epoxy tetrahydrochysene, at a high speed heat-sealing copolymerized type propene polymer 13 parts, multi-component copolymer polypropylene 5 parts, titanium dioxide 0.5 part, filler 4 parts;
(2) raw material is mixed, adopt back the mode of heating up in a steamer, control temperature 180 DEG C, be that the speed of 90r/min stirs material with rotating speed, material thoroughly dissolved, obtains mixed solution;
(3) mixed solution is left standstill 1 hour at 110 DEG C, pour the advection mould being preheated to 100 DEG C into, curtain coating, on the mirror steel plate of room temperature, makes the rapid gel of mixed solution chilling, and it is peeled off obtained high-temp liquid plastics film from steel plate.
Embodiment 2
A preparation method for food grade film, comprises the following steps:
(1) take the raw material needed for production on demand, meter comprises following component by weight: the adjacent stupid dioctyl phthalate dioctyl ester 10 parts of high density polyethylene(HDPE) 70 parts, metallocene linear-low density polyethylene 5 parts, polyethylene resin 10 parts, epoxy tetrahydrochysene, at a high speed heat-sealing copolymerized type propene polymer 5 parts, multi-component copolymer polypropylene 1 part, titanium dioxide 0.1 part, filler 1 part;
(2) raw material is mixed, adopt back the mode of heating up in a steamer, control temperature 150 DEG C, be that the speed of 80r/min stirs material with rotating speed, material thoroughly dissolved, obtains mixed solution;
(3) mixed solution is left standstill 1 hour at 100 DEG C, pour the advection mould being preheated to 90 DEG C into, curtain coating, on the mirror steel plate of room temperature, makes the rapid gel of mixed solution chilling, and it is peeled off obtained high-temp liquid plastics film from steel plate.
Embodiment 3
A preparation method for food grade film, comprises the following steps:
(1) take the raw material needed for production on demand, meter comprises following component by weight: the adjacent stupid dioctyl phthalate dioctyl ester 20 parts of high density polyethylene(HDPE) 80 parts, metallocene linear-low density polyethylene 10 parts, polyethylene resin 20 parts, epoxy tetrahydrochysene, at a high speed heat-sealing copolymerized type propene polymer 20 parts, multi-component copolymer polypropylene 10 parts, titanium dioxide 1 part, filler 5 parts;
(2) raw material is mixed, adopt back the mode of heating up in a steamer, control temperature 200 DEG C, be that the speed of 100r/min stirs material with rotating speed, material thoroughly dissolved, obtains mixed solution;
(3) mixed solution is left standstill 2 hours at 130 DEG C, pour the advection mould being preheated to 100 DEG C into, curtain coating, on the mirror steel plate of room temperature, makes the rapid gel of mixed solution chilling, and it is peeled off obtained high-temp liquid plastics film from steel plate.
The aforementioned description to concrete exemplary of the present invention is to illustrate and the object of illustration.These descriptions not want the present invention to be defined as disclosed precise forms, and obviously, according to above-mentioned instruction, can much change and change.The object selected exemplary embodiment and describe is to explain certain principles of the present invention and practical application thereof, thus those skilled in the art can be realized and utilize various different exemplary of the present invention and various different selection and change.Scope of the present invention is intended to limited by claims and equivalents thereof.
Claims (4)
1. a food grade film, it is characterized in that, meter comprises following component by weight: the adjacent stupid dioctyl phthalate dioctyl ester 10 ~ 20 parts of high density polyethylene(HDPE) 70 ~ 80 parts, metallocene linear-low density polyethylene 5 ~ 10 parts, polyethylene resin 10 ~ 20 parts, epoxy tetrahydrochysene, at a high speed heat-sealing copolymerized type propene polymer 5 ~ 20 parts, multi-component copolymer polypropylene 1 ~ 10 part, titanium dioxide 0.1 ~ 1 part, filler 1 ~ 5 part.
2. food grade film according to claim 1, it is characterized in that, meter comprises following component by weight: the adjacent stupid dioctyl phthalate dioctyl ester 17 parts of high density polyethylene(HDPE) 75 parts, metallocene linear-low density polyethylene 7 parts, polyethylene resin 15 parts, epoxy tetrahydrochysene, at a high speed heat-sealing copolymerized type propene polymer 13 parts, multi-component copolymer polypropylene 5 parts, titanium dioxide 0.5 part, filler 4 parts.
3. food grade film according to claim 1, is characterized in that, described filler is fabric fibre.
4. a preparation method for food grade film according to claim 1, is characterized in that, comprise the following steps:
(1) raw material needed for production is taken on demand;
(2) raw material is mixed, adopt back the mode of heating up in a steamer, control temperature 150 ~ 200 DEG C, stir material with the speed that rotating speed is 80 ~ 100r/min, material is thoroughly dissolved, obtains mixed solution;
(3) mixed solution is left standstill 1 ~ 2 hour at 100 ~ 130 DEG C, pour the advection mould being preheated to 90 ~ 100 DEG C into, curtain coating, on the mirror steel plate of room temperature, makes the rapid gel of mixed solution chilling, and it is peeled off obtained high-temp liquid plastics film from steel plate.