CN104530905A - Antistatic coating - Google Patents
Antistatic coating Download PDFInfo
- Publication number
- CN104530905A CN104530905A CN201410791784.4A CN201410791784A CN104530905A CN 104530905 A CN104530905 A CN 104530905A CN 201410791784 A CN201410791784 A CN 201410791784A CN 104530905 A CN104530905 A CN 104530905A
- Authority
- CN
- China
- Prior art keywords
- parts
- conductive
- conductive filler
- filler material
- dispersion agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antistatic coating prepared from the following components in parts by mass: 45-80 parts of epoxy resin, 20-30 parts of silicon micro powder, 2-8 parts of titanium dioxide, 1-2 parts of organic bentonite, 10-30 parts of a conductive filler, 3-8 parts of ethanol, 1-2 parts of n-butyl alcohol, 5-10 parts of a diluent, 1-5 parts of a dispersant and 2-3 parts of a pigment. The antistatic coating disclosed by the invention is excellent in wear resistance and electrical conductivity, and a lacquer film is high in compactness and long in service life.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of Antistatic Paint.
Background technology
Oil tank static conductive coating is the one of petrochemical industry storage tin paint, is the special coating kind having traditional Corrosion Protection and special electrostatic-proof function concurrently.Liquid petroleum product (particularly lightweight oils), under the situations such as flowing, mixing, stirring, can produce static charge because of friction.When the static charge speed produced is greater than its derivation speed, gathering of static charge will be caused, static voltage is constantly raised, finally leads to point discharge.When within the scope of the explosive limits of mixture that the static charge discharge energy gathered is in flammable oil product steam and air, the harm of static electric fire and blast may be there is at any time.In technology today, the conducting medium in static conductive coating mostly is graphitized carbon black or Graphite Powder 99.Because the electropotential of graphitized carbon black or Graphite Powder 99 is higher than steel, when directly contacting with steel, form galvanic corrosion, make iron and steel accelerated corrosion as anode; And due to its oil number high, when conduction needs height, add-on is comparatively large, and paint film is more loose, and shielding, permeability resistance decline, and cause underfilm corrosion, rust-preventing characteristic is not good.And the coating made thus, preservative property and electroconductibility can not be taken into account, and work-ing life is short.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of Antistatic Paint efficiently.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is:
Thering is provided a kind of Antistatic Paint, is be prepared from by the composition of following mass fraction: epoxy resin 45 ~ 80 parts, silicon powder 20 ~ 30 parts, titanium dioxide 2 ~ 8 parts, organobentonite 1 ~ 2 part, conductive filler material 10 ~ 30 parts, ethanol 3 ~ 8 parts, propyl carbinol 1 ~ 2 part, thinner 5 ~ 10 parts, dispersion agent 1 ~ 5 part and pigment 2 ~ 3 parts.
In a preferred embodiment of the present invention, described conductive filler material is conductive mica powder, conductive titanate dioxide or conductive zinc oxide.
In a preferred embodiment of the present invention, described dispersion agent is polyethylene wax.
In a preferred embodiment of the present invention, be prepared from by the composition of following mass fraction: epoxy resin 65 parts, silicon powder 25 parts, titanium dioxide 5 parts, organobentonite 1.5 parts, conductive filler material 20 parts, ethanol 6 parts, propyl carbinol 1.5 parts, thinner 7.5 parts, dispersion agent 3.5 parts and pigment 2 parts.
The invention has the beneficial effects as follows: a kind of Antistatic Paint of the present invention, the antiseptic property of the Antistatic Paint that this formula is prepared from and conductivity superior, the compactness of paint film is high, long service life.
Embodiment
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
Embodiment 1:
A kind of Antistatic Paint is be prepared from by the composition of following mass fraction: epoxy resin 65 parts, silicon powder 25 parts, titanium dioxide 5 parts, organobentonite 1.5 parts, conductive filler material 20 parts, ethanol 6 parts, propyl carbinol 1.5 parts, thinner 7.5 parts, dispersion agent 3.5 parts and pigment 2 parts.
Wherein, described conductive filler material is conductive mica powder, and described dispersion agent is polyethylene wax.
Embodiment 2:
A kind of Antistatic Paint is be prepared from by the composition of following mass fraction: epoxy resin 80 parts, silicon powder 28 parts, titanium dioxide 4 parts, organobentonite 1 part, conductive filler material 20 parts, ethanol 5 parts, propyl carbinol 2 parts, thinner 8 parts, dispersion agent 4 parts and pigment 2.5 parts.
Wherein, described conductive filler material is conductive titanate dioxide, and described dispersion agent is polyethylene wax.
Embodiment 3:
A kind of Antistatic Paint is be prepared from by the composition of following mass fraction: epoxy resin 50 parts, silicon powder 30 parts, titanium dioxide 8 parts, organobentonite 2 parts, conductive filler material 30 parts, ethanol 4 parts, propyl carbinol 2 parts, thinner 10 parts, dispersion agent 3 parts and pigment 3 parts.
Wherein, described conductive filler material is conductive zinc oxide, and described dispersion agent is polyethylene wax.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (4)
1. an Antistatic Paint, it is characterized in that, be prepared from by the composition of following mass fraction: epoxy resin 45 ~ 80 parts, silicon powder 20 ~ 30 parts, titanium dioxide 2 ~ 8 parts, organobentonite 1 ~ 2 part, conductive filler material 10 ~ 30 parts, ethanol 3 ~ 8 parts, propyl carbinol 1 ~ 2 part, thinner 5 ~ 10 parts, dispersion agent 1 ~ 5 part and pigment 2 ~ 3 parts.
2. Antistatic Paint according to claim 1, is characterized in that, described conductive filler material is conductive mica powder, conductive titanate dioxide or conductive zinc oxide.
3. Antistatic Paint according to claim 1, is characterized in that, described dispersion agent is polyethylene wax.
4. according to the Antistatic Paint one of claim 1 ~ 3 Suo Shu, it is characterized in that, be prepared from by the composition of following mass fraction: epoxy resin 65 parts, silicon powder 25 parts, titanium dioxide 5 parts, organobentonite 1.5 parts, conductive filler material 20 parts, ethanol 6 parts, propyl carbinol 1.5 parts, thinner 7.5 parts, dispersion agent 3.5 parts and pigment 2 parts.