CN104530300A - Synthesis method of biaxially orientated polyester film - Google Patents
Synthesis method of biaxially orientated polyester film Download PDFInfo
- Publication number
- CN104530300A CN104530300A CN201410594366.6A CN201410594366A CN104530300A CN 104530300 A CN104530300 A CN 104530300A CN 201410594366 A CN201410594366 A CN 201410594366A CN 104530300 A CN104530300 A CN 104530300A
- Authority
- CN
- China
- Prior art keywords
- reaction
- polyester film
- initiator
- ethyl propenoate
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a synthesis method of a biaxially orientated polyester film. The synthesis method comprises the following steps: carrying out reduced pressure distillation on methyl methacrylate, ethyl acrylate, ethanol and benzoyl peroxide for refining, wherein the benzoyl peroxide is dissolved in chloroform, filtered, recrystallized in methanol and repeatedly processed for standby application; sequentially adding reaction monomers including methyl methacrylate, the ethyl acrylate and an initiator to a four-mouth flask equippted with a stirrer, a temperature gauge, a condenser pipe and an N2 ingress pipe; dropwise adding mixed liquid of the ethyl acrylate and the ethanol to the reaction flask by a dropping funnel, replenishing the initiator, and carrying out reaction at constant temperature; dropwise adding ammonium hydroxide under fiercely stirring to neutralize reaction liquid and adding an appropriate amount of water for dilution to obtain semitransparent blue-suffused hydrosol; and taking out a part of the hydrosol and drying for later use and adding water to a part of the hydrosol to dilute film to obtain the biaxially orientated polyester film. The synthesis method is simple and is low in cost. The synthesized biaxially orientated polyester film is strong in designability, good in stability, high in transparency and good in rheological property.
Description
Technical field
The present invention relates to organic coating synthesis technical field, particularly relate to a kind of biaxially oriented polyester film synthetic method.
Background technology
Biaxial stretching polyester (BOPET) film is that a kind of thin-film material of excellent performance is widely used in the fields such as packaging, printing, the BOPET film tension of non-modified is lower in use exists aluminium coated or the caducous phenomenon of ink cannot meet the requirement of high-grade packaging therefore must carry out surface modification to it, coating modification is a kind of easy industrialized method of stable performance, and coated with resins is the key that this method is implemented.Along with the enhancing non-solvent water-borne coatings of environmental consciousness has better competitiveness.Resin for water-borne coatings mainly contains aqueous epoxy resins, vibrin, acrylic resin, urethane resin etc.Wherein aqueous polyacrylamide acid resin has the advantages such as designability is strong, good stability, transparency are high, rheological is good and is subject to people's attention.
Summary of the invention
It is simple that technical problem to be solved by this invention is to provide a kind of method, with low cost, the synthetic method that synthesized biaxially oriented polyester film designability is strong, good stability, transparency are high, rheological is good.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: a kind of biaxially oriented polyester film synthetic method, comprises the steps:
By methyl methacrylate, ethyl propenoate, ethanol, benzoyl peroxide carry out underpressure distillation refine, wherein, by benzoyl peroxide with chloroform dissolve, filter, and in methyl alcohol recrystallization, repeatedly process for subsequent use;
Agitator, thermometer, prolong, N are being housed
2the four-hole bottle of ingress pipe adds reaction monomers methyl methacrylate, ethyl propenoate and initiator successively;
Ethyl propenoate and alcohol mixeding liquid are passed through dropping funnel dropwise reaction bottle, and adds initiator, isothermal reaction;
Drip ammonia neutralization reaction solution with vigorous stirring, and add appropriate water and dilute, obtain the water-sol of translucent blueing light;
Taking-up partially desiccated is stand-by, and part thin up film obtains biaxially oriented polyester film.
On the basis of technique scheme, the present invention can also do following improvement.
Further, described agitator, thermometer, prolong, N are being housed
2the four-hole bottle of ingress pipe adds being implemented as follows of reaction monomers methyl methacrylate, ethyl propenoate and initiator step successively:
Agitator, thermometer, prolong, N are being housed
2the four-hole bottle of ingress pipe adds reaction monomers methyl methacrylate, ethyl propenoate and 2/3 initiator successively, is warming up to 60 ~ 100 DEG C.
Further, described by ethyl propenoate and alcohol mixeding liquid by dropping funnel dropwise reaction bottle, and add initiator, being implemented as follows of isothermal reaction step:
Ethyl propenoate and 1/2 alcohol mixeding liquid are added dropwise to reaction flask by dropping funnel at 1 ~ 1.5h, and residue ethanol dropwises at 1 ~ 1.5h, and adds 1/3 initiator, cools to 40 ~ 60 DEG C after isothermal reaction 2 ~ 4h.
Further, describedly drip ammonia neutralization reaction solution with vigorous stirring, and add appropriate water and dilute, obtain being implemented as follows of the water-sol step of translucent blueing light:
Drip ammonia neutralization reaction solution with vigorous stirring, and the water adding 1 ~ 10L dilutes, and obtains the water-sol of translucent blueing light.
The invention has the beneficial effects as follows: method is simple, with low cost, synthesized biaxially oriented polyester film designability is strong, good stability, transparency are high, rheological good.
Embodiment
Be described principle of the present invention and feature below in conjunction with example, example, only for explaining the present invention, is not intended to limit scope of the present invention.
A kind of biaxially oriented polyester film synthetic method, comprises the steps:
By methyl methacrylate, ethyl propenoate, ethanol, benzoyl peroxide carry out underpressure distillation refine, wherein, by benzoyl peroxide with chloroform dissolve, filter, and in methyl alcohol recrystallization, repeatedly process for subsequent use;
Agitator, thermometer, prolong, N are being housed
2the four-hole bottle of ingress pipe adds reaction monomers methyl methacrylate, ethyl propenoate and initiator successively;
Ethyl propenoate and alcohol mixeding liquid are passed through dropping funnel dropwise reaction bottle, and adds initiator, isothermal reaction;
Drip ammonia neutralization reaction solution with vigorous stirring, and add appropriate water and dilute, obtain the water-sol of translucent blueing light;
Taking-up partially desiccated is stand-by, and part thin up film obtains biaxially oriented polyester film.
Embodiment 1:
By methyl methacrylate, ethyl propenoate, ethanol, benzoyl peroxide carry out underpressure distillation refine, wherein, by benzoyl peroxide with chloroform dissolve, filter, and in methyl alcohol recrystallization, repeatedly process for subsequent use; Agitator, thermometer, prolong, N are being housed
2the four-hole bottle of ingress pipe adds reaction monomers methyl methacrylate, ethyl propenoate and 2/3 initiator successively, is warming up to 60 DEG C; Ethyl propenoate and 1/2 alcohol mixeding liquid are added dropwise to reaction flask by dropping funnel at 1h, and residue ethanol dropwises at 1h, and adds 1/3 initiator, cools to 40 DEG C after isothermal reaction 2h; Drip ammonia neutralization reaction solution with vigorous stirring, and the water adding 1L dilutes, and obtains the water-sol of translucent blueing light.
Embodiment 2:
By methyl methacrylate, ethyl propenoate, ethanol, benzoyl peroxide carry out underpressure distillation refine, wherein, by benzoyl peroxide with chloroform dissolve, filter, and in methyl alcohol recrystallization, repeatedly process for subsequent use; Agitator, thermometer, prolong, N are being housed
2the four-hole bottle of ingress pipe adds reaction monomers methyl methacrylate, ethyl propenoate and 2/3 initiator successively, is warming up to 80 DEG C; Ethyl propenoate and 1/2 alcohol mixeding liquid are added dropwise to reaction flask by dropping funnel at 1.2h, and residue ethanol dropwises at 1.3h, and adds 1/3 initiator, cools to 50 DEG C after isothermal reaction 3h; Drip ammonia neutralization reaction solution with vigorous stirring, and the water adding 5L dilutes, and obtains the water-sol of translucent blueing light.
Embodiment 3:
By methyl methacrylate, ethyl propenoate, ethanol, benzoyl peroxide carry out underpressure distillation refine, wherein, by benzoyl peroxide with chloroform dissolve, filter, and in methyl alcohol recrystallization, repeatedly process for subsequent use; Agitator, thermometer, prolong, N are being housed
2the four-hole bottle of ingress pipe adds reaction monomers methyl methacrylate, ethyl propenoate and 2/3 initiator successively, is warming up to 100 DEG C; Ethyl propenoate and 1/2 alcohol mixeding liquid are added dropwise to reaction flask by dropping funnel at 1.5h, and residue ethanol dropwises at 1.5h, and adds 1/3 initiator, cools to 60 DEG C after isothermal reaction 4h; Drip ammonia neutralization reaction solution with vigorous stirring, and the water adding 10L dilutes, and obtains the water-sol of translucent blueing light.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (4)
1. a biaxially oriented polyester film synthetic method, is characterized in that, comprises the steps:
By methyl methacrylate, ethyl propenoate, ethanol, benzoyl peroxide carry out underpressure distillation refine, wherein, by benzoyl peroxide with chloroform dissolve, filter, and in methyl alcohol recrystallization, repeatedly process for subsequent use;
Agitator, thermometer, prolong, N are being housed
2the four-hole bottle of ingress pipe adds reaction monomers methyl methacrylate, ethyl propenoate and initiator successively;
Ethyl propenoate and alcohol mixeding liquid are passed through dropping funnel dropwise reaction bottle, and adds initiator, isothermal reaction;
Drip ammonia neutralization reaction solution with vigorous stirring, and add appropriate water and dilute, obtain the water-sol of translucent blueing light;
Taking-up partially desiccated is stand-by, and part thin up film obtains biaxially oriented polyester film.
2. a kind of biaxially oriented polyester film synthetic method according to claim 1, is characterized in that, described agitator, thermometer, prolong, N is being housed
2the four-hole bottle of ingress pipe adds being implemented as follows of reaction monomers methyl methacrylate, ethyl propenoate and initiator step successively:
Agitator, thermometer, prolong, N are being housed
2the four-hole bottle of ingress pipe adds reaction monomers methyl methacrylate, ethyl propenoate and 2/3 initiator successively, is warming up to 60 ~ 100 DEG C.
3. a kind of biaxially oriented polyester film synthetic method according to claim 1, is characterized in that, described by ethyl propenoate and alcohol mixeding liquid by dropping funnel dropwise reaction bottle, and add initiator, being implemented as follows of isothermal reaction step:
Ethyl propenoate and 1/2 alcohol mixeding liquid are added dropwise to reaction flask by dropping funnel at 1 ~ 1.5h, and residue ethanol dropwises at 1 ~ 1.5h, and adds 1/3 initiator, cools to 40 ~ 60 DEG C after isothermal reaction 2 ~ 4h.
4. a kind of biaxially oriented polyester film synthetic method according to claim 1, it is characterized in that, describedly drip ammonia neutralization reaction solution with vigorous stirring, and add appropriate water and dilute, obtain being implemented as follows of the water-sol step of translucent blueing light:
Drip ammonia neutralization reaction solution with vigorous stirring, and the water adding 1 ~ 10L dilutes, and obtains the water-sol of translucent blueing light.