CN104529482A - High temperature resistant functional material adhesive - Google Patents
High temperature resistant functional material adhesive Download PDFInfo
- Publication number
- CN104529482A CN104529482A CN201410736381.XA CN201410736381A CN104529482A CN 104529482 A CN104529482 A CN 104529482A CN 201410736381 A CN201410736381 A CN 201410736381A CN 104529482 A CN104529482 A CN 104529482A
- Authority
- CN
- China
- Prior art keywords
- high temperature
- parts
- temperature resistant
- resistant functional
- functional materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Relating to the technical field of high temperature materials and metallurgy, the invention discloses a high temperature resistant functional material adhesive, which comprises the following raw materials by mass: 0.9-1.2 parts of phenolic resin, 0.4-0.8 part of a curing agent, 1.8-2.2 parts of magnesia fine powder, and 1.8-2.2 parts of industrial alcohol. The high temperature resistant functional material adhesive provided by the invention has the advantages of reasonable formula, simple making method and strong adhesion, bonds split type high temperature resistant functional materials into a whole, prevents a lot of slits after installation from causing "gas connection" accidents, reduces abnormal production halt, and promotes metallurgical continuity.
Description
Technical field
The present invention relates to high-temperature material and metallurgical technology field, refer more particularly to a kind of high temperature resistant functional materials caking agent.
Background technology
Efficiently, safety, intensive manufacture be the direction of metallurgical industry development, is also the important technical improving high temperature material enterprise's existence and development and the market competitiveness.But, along with metallurgical serialization flatly improves, due to the singularity that ladle functional materials uses, monoblock type function brick difficult forming in traditional mode, makes the higher bottleneck becoming restriction enterprise of die cost, especially after most of function brick is installed, gap is more, when ladle bottom is by gas permeable brick winding-up argon gas, between function brick, gap produces and collaborates, and continuity is smelted in impact, and labour intensity is large when changing, elapsed time is long.Therefore, a kind of desirable bonding way is found imperative in functional materials is produced, cause material shrinkage to peel off to stop using thus reduce cylinder-packing work-ing life, minimizing manual work, change the masonry way of traditional split type functional materials, improve installation rate to greatest extent and save labor force.
Summary of the invention
Technical problem to be solved by this invention is to provide the high temperature resistant functional materials caking agent that one is simple to operate, raw materials cost is low, can effectively prevent " gas leakage " accident from occurring, to overcome the irrational defect of existing split type high temperature resistant functional materials.
For solving the problems of the technologies described above, the present invention is part by the following technical solutions,
A kind of high temperature resistant functional materials caking agent, is characterized in that, comprise following raw material part, resol, solidifying agent, magnesia powder and industrial spirit; The mass fraction of described raw material is respectively part, 0.9-1.2 parts, resol, 0.4-0.8 part, solidifying agent, magnesia powder 1.8-2.2 parts, industrial spirit 1.8-2.2 parts.
Preferably, the mass fraction of described raw material is respectively part, 1-1.2 parts, resol, 0.5-0.8 part, solidifying agent, magnesia powder 1.9-2.1 parts, industrial spirit 1.9-2.1 parts.
Preferably, the mass fraction of described raw material is respectively part, 1-1.1 parts, resol, 0.5-0.7 part, solidifying agent, magnesia powder 2-2.1 parts, industrial spirit 1.9-2 parts.
Preferably, the mass fraction of described raw material is respectively part, 1 part, resol, 0.5 part, solidifying agent, magnesia powder 2 parts, industrial spirit 2 parts.
Described high temperature resistant functional materials caking agent to be made part by following steps, takes raw material in described ratio, stirs 5 minutes to evenly after mixing.
The present invention has the following advantages part,
(1) the present invention fills a prescription rationally, and making method is simple, and cohesiveness is very strong, by integrally bonding for split type high temperature resistant functional materials, avoid installing rear gap more, causes " collaborating " accident, reduce improper stopping production, promote metallurgical continuity;
(2) what the present invention adopted is by shaping split type functional materials, smear caking agent by needing the position of docking then to combine, then low temperature 200 DEG C baking, this eliminates the making of integral special-shaped mould, make processing and manufacturing more simple, also thus reduce costs;
(3) what the present invention adopted is the raw material close with high temperature material material, by not changing the character of material after bonding for original split type functional materials, avoiding the generation of " going bad ", making functional materials more safe and reliable in applied at elevated temperature.
Accompanying drawing explanation
Fig. 1 wants by the present invention the sectional view of bonding split type functional materials;
Fig. 2 is whole result schematic diagram of the present invention.
Part in figure, 1-upper brick cup, 2-lower brick cup, 3-adhesive coating.
Embodiment
Below in conjunction with the drawings and specific embodiments, technical scheme of the present invention is further described in detail.
Embodiment one:
A kind of preparation method of high temperature resistant functional materials caking agent: resol, solidifying agent, magnesia powder and industrial spirit are stirred 5 minutes to even according to the mass ratio of 1:0.5:2:2.
As shown in Figure 1, a kind of ladle metallurgy is high temperature resistant functional materials, comprises brick cup 1, lower brick cup 2.
As shown in Figure 2, add binding agent at upper brick cup and lower brick cup, after upper and lower brick cup is bonding, caking agent is filled with the gap between brick cup, avoids the generation of " collaborating ", makes split type functional materials become as a whole, has ensured the security of metallurgical production.
Embodiment two:
A kind of preparation method of high temperature resistant functional materials caking agent: resol, solidifying agent, magnesia powder and industrial spirit are stirred 5 minutes to even according to the mass ratio of 1.2:0.8:2.2:2.2.
Embodiment three:
A kind of preparation method of high temperature resistant functional materials caking agent: resol, solidifying agent, magnesia powder and industrial spirit are stirred 5 minutes to even according to the mass ratio of 0.9:0.4:1.8:1.8.
Embodiment four:
A kind of preparation method of high temperature resistant functional materials caking agent: resol, solidifying agent, magnesia powder and industrial spirit are stirred 5 minutes to even according to the mass ratio of 1.1:0.6:1.9:1.9.
Embodiment five:
A kind of preparation method of high temperature resistant functional materials caking agent: resol, solidifying agent, magnesia powder and industrial spirit are stirred 5 minutes to even according to the mass ratio of 1:0.7:2.1:2.1
The present invention has the following advantages:
(1) the present invention fills a prescription rationally, and making method is simple, and cohesiveness is very strong, by integrally bonding for split type high temperature resistant functional materials, avoid installing rear gap more, causes " collaborating " accident, reduce improper stopping production, promote metallurgical continuity;
(2) what the present invention adopted is by shaping split type functional materials, smear caking agent by needing the position of docking then to combine, then low temperature 200 degrees Celsius baking, this eliminates the making of integral special-shaped mould, make processing and manufacturing more simple, also thus reduce costs;
(3) what the present invention adopted is the raw material close with high temperature material material, by not changing the character of material after bonding for original split type functional materials, avoiding the generation of " going bad ", making functional materials more safe and reliable in applied at elevated temperature.
It should be noted last that, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted, although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to technical scheme of the present invention or equivalent replacement, and not departing from the spirit and scope of technical solution of the present invention, it all should be encompassed in the middle of right of the present invention.
Claims (5)
1. a high temperature resistant functional materials caking agent, is characterized in that, comprises following raw material: resol, solidifying agent, magnesia powder and industrial spirit; The mass fraction of described raw material is respectively: 0.9-1.2 parts, resol, 0.4-0.8 part, solidifying agent, magnesia powder 1.8-2.2 parts, industrial spirit 1.8-2.2 parts.
2. high temperature resistant functional materials caking agent according to claim 1, it is characterized in that, the mass fraction of described raw material is respectively: 1-1.2 parts, resol, 0.5-0.8 part, solidifying agent, magnesia powder 1.9-2.1 parts, industrial spirit 1.9-2.1 parts.
3. high temperature resistant functional materials caking agent according to claim 1, it is characterized in that, the mass fraction of described raw material is respectively: 1-1.1 parts, resol, 0.5-0.7 part, solidifying agent, magnesia powder 2-2.1 parts, industrial spirit 1.9-2 parts.
4. high temperature resistant functional materials caking agent according to claim 1, it is characterized in that, the mass fraction of described raw material is respectively: 1 part, resol, 0.5 part, solidifying agent, magnesia powder 2 parts, industrial spirit 2 parts.
5. high temperature resistant functional materials caking agent according to claim 1, is characterized in that, be made by following steps: take resol, solidifying agent, magnesia powder, industrial spirit in described ratio, stirs 5 minutes to even after mixing.