CN104513499A - Preparation method of silicon dioxide/ammonium polyphosphate composite flame retardant - Google Patents
Preparation method of silicon dioxide/ammonium polyphosphate composite flame retardant Download PDFInfo
- Publication number
- CN104513499A CN104513499A CN201310444576.2A CN201310444576A CN104513499A CN 104513499 A CN104513499 A CN 104513499A CN 201310444576 A CN201310444576 A CN 201310444576A CN 104513499 A CN104513499 A CN 104513499A
- Authority
- CN
- China
- Prior art keywords
- ammonium polyphosphate
- preparation
- flame retardant
- silicon dioxide
- gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a silicon dioxide/ammonium polyphosphate composite flame retardant. The preparation method comprises the following steps: adding ammonium polyphosphate into waterless ethanol, evenly stirring, dropwise adding n-ethyl silicate, adding oxalic acid, stirring to carry out reactions for 12 minutes, dropwise adding ammonia water, adding waterless ethanol after gelation; then soaking the gel into a mixed solution of hexamethyl disilazane and n-hexane for 24 hours at a temperature of 50 DEG C, drying, and then grinding the gel so as to obtain the silicon dioxide/ammonium polyphosphate composite flame retardant. The provided preparation method has the advantage of simple and convenient synthesis route. The synthesized compound has a uniform particle size, and moreover, the flame retardant property of the compound is prominently improved compared with those of silicon dioxide and ammonium polyphosphate.
Description
Technical field
The present invention relates to a kind of preparation method of fire retardant, be specifically related to a kind of preparation method of composite flame-retardant agent.
Background technology
Ammonium polyphosphate is one of most important kind in current inorganic phosphorus flame retardant, its phosphorus content and nitrogen content are all very high, there is again N-P synergistic effect between them, thus there is good flame retardant properties, but due to himself chemical structure, also there is a lot of problem in actual applications in it, as poor water resistance, easily reunite, the bad dispersibility in polymkeric substance body, and very easily ooze out to material surface migration when high temperature, high humidity, reduce the comprehensive effectiveness especially flame retardant properties of material.
Summary of the invention
The object of the invention is to, a kind of preparation method of silicon-dioxide/ammonium polyphosphate compound fire retardant is provided, improve oxygen index, the horizontal firing grade of material, reduce heat release rate, improve the carbon yield after material combustion, improve flame retardant effect.
A preparation method for silicon-dioxide/ammonium polyphosphate compound fire retardant, it comprises the following steps:
One, ammonium polyphosphate is joined in dehydrated alcohol, stir, drip tetraethoxy, stir, add oxalic acid, stirring reaction 12h, drip ammoniacal liquor, after gel, add dehydrated alcohol;
Two, immersed by gel in hexamethyldisilazane and normal hexane mixing solutions, at 50 DEG C of temperature, insulation 24h, dry, pulverize, obtain silicon-dioxide/ammonium polyphosphate compound fire retardant; The volume ratio of described hexamethyldisilazane and normal hexane is 1:4.
The preparation method of silicon-dioxide/ammonium polyphosphate compound fire retardant provided by the invention, its beneficial effect is, simple synthetic method, quick, the compound uniform particle sizes of synthesis, and its flame retardant properties is compared with silicon-dioxide with ammonium polyphosphate, obtain obvious improvement.
Embodiment
Below in conjunction with an embodiment, the preparation method of silicon-dioxide/ammonium polyphosphate compound fire retardant provided by the invention is described in detail.
Embodiment
One, the ammonium polyphosphate of 5g is joined in 10ml dehydrated alcohol, be placed in after high-shear whipping appts fully disperses, dropwise add 10ml tetraethoxy, add the oxalic acid 2.5ml of an acidic catalyst 0.008mol/L under magnetic stirring, at 60 DEG C of temperature, be transferred to after stirring reaction 12h in beaker, drip the ammoniacal liquor 0.2ml of basic catalyst 0.05ml/L, after gel, add a certain amount of dehydrated alcohol immediately;
Two, immersed by the wet gel after aging in the hexamethyldisilazane that volume ratio is 1:4 and normal hexane mixing solutions, carry out surface modification at 50 DEG C of temperature, modification 24h, dry, pulverize, and obtains silicon-dioxide/ammonium polyphosphate compound fire retardant.
Claims (1)
1. a preparation method for silicon-dioxide/ammonium polyphosphate compound fire retardant, is characterized in that: it comprises the following steps:
One, ammonium polyphosphate is joined in dehydrated alcohol, stir, drip tetraethoxy, stir, add oxalic acid, stirring reaction 12h, drip ammoniacal liquor, after gel, add dehydrated alcohol;
Two, immersed by gel in hexamethyldisilazane and normal hexane mixing solutions, at 50 DEG C of temperature, insulation 24h, dry, pulverize, obtain silicon-dioxide/ammonium polyphosphate compound fire retardant; The volume ratio of described hexamethyldisilazane and normal hexane is 1:4.