CN104497945A - Adhesive oil glue for cloth bonding - Google Patents
Adhesive oil glue for cloth bonding Download PDFInfo
- Publication number
- CN104497945A CN104497945A CN201410754531.XA CN201410754531A CN104497945A CN 104497945 A CN104497945 A CN 104497945A CN 201410754531 A CN201410754531 A CN 201410754531A CN 104497945 A CN104497945 A CN 104497945A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- adhesive oil
- oil glue
- factice
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses adhesive oil glue for cloth bonding, which consists of the following raw materials in parts by weight: 100 parts of polyurethane resin, 40-55 parts of butanone, 1-3 parts of an accelerant and 10-15 parts of a bridging agent. With perfect bonding strength, the adhesive oil glue disclosed by the invention can effectively enhance the stability of the product and improve the properties of the product; meanwhile, the operation is simple, and the production cost is reduced; and the adhesive oil glue meets the operation requirements in relatively extreme or hostile environment, has good toughness and can be widely applied to the field of spinning.
Description
Technical field
The present invention relates to textile technology field, be specially a kind of cloth pasting factice glue.
Background technology
The title that adhesive fabric is formally put should be composite material or laminated fabric.Exactly by two kinds of fabrics or the novel fabric having both advantages concurrently that a kind of film and fabric are combined with each other and obtain.Polyurethane adhesive is mainly at present for the tackiness agent of fitting, polyurethane adhesive is an important component part in the urethane resin developed rapidly at present, have excellent performance, being widely used in many aspects, is one of important kind in synthetic adhesive.Polyurethane adhesive possesses excellent shear strength and impact property, is applicable to various structural bonding field, and possesses excellent flexible nature.The gluing stick of urethane possesses excellent rubber property, can adapt to the bonding of different heat expansion coefficient base material, and it is formed between base material has soft-hard transition layer, and not only bonding force is strong, also has excellent buffering, shock-absorbing function simultaneously.The low temperature of the gluing stick of urethane and very low temperature performance exceed the tackiness agent of every other type.
Now composite adhesive is commercially polyurethane adhesive is subsequent reactions type, polyurethane adhesive is after adding a certain proportion of bridging agent, coating is fallen solvent evaporates through high temperature, enclose rolling after matrix material, namely be work in-process, place 7 days in room temperature or place 3 days at the temperature of 50 degree, allow the active group of bridging agent and the active group of tackiness agent fully react, the matrix material of required adhesion strength will be obtained.Its reaction times is long, affects production efficiency, and required adhesion strength is not easy to control.
Therefore, for the problems referred to above, the present invention proposes a kind of new technical scheme.
Summary of the invention
The object of this invention is to provide a kind of adhesion strength high, the cloth pasting factice glue that stability is strong.
The present invention is achieved through the following technical solutions:
A kind of cloth pasting factice glue, counts by weight, comprises following raw material composition:
Urethane resin 100 parts;
Butanone 40 ~ 55 parts;
Promotor 1 ~ 3 part;
Bridging agent 10 ~ 15 parts.
Further, described promotor is the mixture of toluene and triethylene diamine, and described toluene and triethylene diamine weight ratio are 9:1.
Further, described bridging agent is ethyl acetate and polyisocyanates, and described ethyl acetate and polyisocyanates weight ratio are 1:3.
The invention has the beneficial effects as follows: the present invention has good cohesive strength, effectively can increase the stability of product, improve the performance of product, simultaneously simple to operate, reduce production cost, and meet in the service requirements relatively extremely or under rugged environment, good toughness, can be widely used in field of textiles.
Embodiment
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
A kind of cloth pasting factice glue, counts by weight, comprises following raw material composition:
Urethane resin 100 parts;
Butanone 40 parts;
Toluene 0.9 part;
Triethylene diamine 0.1 part;
Ethyl acetate 2.5 parts;
Polyisocyanates 7.5 parts.
Embodiment 2
A kind of cloth pasting factice glue, counts by weight, comprises following raw material composition:
Urethane resin 100 parts;
Butanone 50 parts;
Toluene 1.8 parts;
Triethylene diamine 0.2 part;
Ethyl acetate 3 parts;
Polyisocyanates 9 parts.
Embodiment 3
A kind of cloth pasting factice glue, counts by weight, comprises following raw material composition:
Urethane resin 100 parts;
Butanone 55 parts;
Toluene 2.7 parts;
Triethylene diamine 0.3 part;
Ethyl acetate 3.75 parts;
Polyisocyanates 11.25 parts.
The present invention has good cohesive strength, effectively can increase the stability of product, improves the performance of product, simultaneously simple to operate, reduce production cost, and meet in the service requirements relatively extremely or under rugged environment, good toughness, can be widely used in field of textiles.
The above is only embodiments of the invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (3)
1. a cloth pasting factice glue, is characterized in that: count by weight, comprises following raw material composition:
Urethane resin 100 parts;
Butanone 40 ~ 55 parts;
Promotor 1 ~ 3 part;
Bridging agent 10 ~ 15 parts.
2. a kind of cloth pasting factice glue according to claim 1, it is characterized in that: described promotor is the mixture of toluene and triethylene diamine, described toluene and triethylene diamine weight ratio are 9:1.
3. a kind of cloth pasting factice glue according to claim 1, it is characterized in that: described bridging agent is ethyl acetate and polyisocyanates, described ethyl acetate and polyisocyanates weight ratio are 1:3.