CN104497779A - Temperature-variable leather - Google Patents

Temperature-variable leather Download PDF

Info

Publication number
CN104497779A
CN104497779A CN201510005423.7A CN201510005423A CN104497779A CN 104497779 A CN104497779 A CN 104497779A CN 201510005423 A CN201510005423 A CN 201510005423A CN 104497779 A CN104497779 A CN 104497779A
Authority
CN
China
Prior art keywords
weight part
temperature
parts
resin
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510005423.7A
Other languages
Chinese (zh)
Inventor
胡文摇
蔡振聪
蔡祥林
汪炳安
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shishi Longxiang Leather Co Ltd
Original Assignee
Shishi Longxiang Leather Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shishi Longxiang Leather Co Ltd filed Critical Shishi Longxiang Leather Co Ltd
Priority to CN201510005423.7A priority Critical patent/CN104497779A/en
Publication of CN104497779A publication Critical patent/CN104497779A/en
Pending legal-status Critical Current

Abstract

The invention discloses temperature-variable leather, which sequentially comprises a base layer, a resin layer, a temperature-variable layer and a transparent membrane layer from inside to outside; the temperature-variable layer is prepared by mixing the following raw materials in parts by weight: 40-60 parts of petroleum resin, 20-30 parts of dimethylbenzene, 30-35 parts of DMF, 15-25 parts of butyl ester, 20-30 parts of acetone, 2-5 parts of stressed color-changing wax powder, 1-3 parts of silica extinction powder, 1-3 parts of modified organosilicon, 1-3 parts of liquid paraffin, 2-5 parts of polyurethane nanofibers, and 2-6 parts of modified polytetrafluoroethylene color-changing paraffin powder. All components of the temperature-variable layer are harmonized and combined for action, so that the touch feeling is fine and comfortable, the true leather feeling is strong, and the temperature-variable leather has good temperature resistance property, color grading characteristic is natural and rich in fashion and artistic expressive force, and the temperature-variable leather can be used in boxes, shoes, garments, interior decoration leather, especially children shoes and outdoor sports.

Description

A kind of temperature is changed
Technical field
A kind of leatheroid of the present invention, be specially a kind of can the synthetic leather that becomes of temperature.
Background technology
At present, synthetic leather has been widely used in producing the product such as case and bag, clothes, footwear, and synthetic leather has good, the resistance to complications of physical property, pliability is good, tensile strength is large feature, and has ventilation property.
Therefore synthetic leather is widely used in the position that the fabric of footwear or case and bag bear weight.
Along with growth in the living standard, people require also more outstanding to the quality and performance of leatherware, and the temperature that can send different lights along with the change of temperature changes the interest having caused human consumer.
Particularly in children's footwear and outdoor activity, temperature is changed and is had huge market.Temperature is changed does not need battery, and can emit light along with temperature variation, the color of leather surface can change according to temperature variation, and this will break the static color system of leather products, make leather products have magnificent outward appearance.
Summary of the invention
The technical problem to be solved in the present invention is the defect overcoming prior art, provides a kind of temperature sending out novel to change.
In order to solve the problems of the technologies described above, the invention provides following technical scheme:
A kind of temperature is changed, and comprises basic unit, resin layer, warm change layer and transparent film layer from inside to outside successively; Described temperature change layer is by petroleum resin 40 ~ 60 weight part, dimethylbenzene 20 ~ 30 weight part, DMF 30 ~ 35 weight part, butyl ester 15 ~ 25 weight part, acetone 20 ~ 30 weight part, stress discoloration wax powder 2 ~ 5 weight part, silicon-dioxide flatting silica 1 ~ 3 weight part, modified organic silicon 1 ~ 3 weight part, whiteruss 1 ~ 3 weight part, polyurethane nanofiber 2 ~ 5 weight part, 2 ~ 6 parts, modified Teflon discoloration wax powder mixes.
Further, described temperature change layer by petroleum resin 40 ~ 50 weight part, dimethylbenzene 24 ~ 30 weight part, DMF 30 ~ 34 weight part, butyl ester 18 ~ 22 weight part, acetone 22 ~ 27 weight part, stress discoloration wax powder 3 ~ 5 weight part, silicon-dioxide flatting silica 2 weight part, modified organic silicon 2 ~ 3 weight part, whiteruss 2 ~ 3 weight part, polyurethane nanofiber 2 ~ 4 weight part, 3 ~ 6 parts, modified Teflon discoloration wax powder mixes.
Preferably, described temperature change layer by petroleum resin 46 weight part, dimethylbenzene 26 weight part, DMF 33 weight part, butyl ester 20 weight part, acetone 25 weight part, stress discoloration wax powder 5 weight part, silicon-dioxide flatting silica 2 weight part, modified organic silicon 3 weight part, whiteruss 2 weight part, polyurethane nanofiber 3 weight part, 6 parts, modified Teflon discoloration wax powder mixes.
Change to make temperature and have better corium texture and feel, described temperature change layer also can comprise flow agent 1 ~ 3 weight part, erucicamide 1 ~ 3 weight part.
In actual fabrication, basic unit can be cloth, nonwoven cloth, synthetic leather or ox-hide layer, and resin layer can be PU, PVC, PC, vinylformic acid or nitro-resin.Petroleum resin are polyamide, epoxy resin, polyurethane resin or modified, high temperature resistant urethane resin.Preferably, described petroleum resin are aliphatic modified High-temperature-respolyurethane polyurethane resin, and its Young's modulus is 40GPa ~ 80GPa.
Temperature of the present invention is changed, each component of temperature change layer is coordinated mutually, acting in conjunction, adding of polyurethane nanofiber, the leather surface after process is made to have unique fine hair, sense of touch exquisiteness is comfortable, flow agent and adding of erucicamide make leather surface soft, gloss is soft, kishke feel is strong, adding of modified, high temperature resistant urethane resin and modified, high temperature resistant tetrafluoroethylene discoloration wax powder, the synthetic leather after process is made to have good heat resistance, temperature of the present invention is changed can not only in stretching, fold under waiting external stress effect and present colour-change, and leather surface also has corresponding colour-change when outside temperature changes to some extent, color gradient feature nature, be imbued with fashion and artistic expression, can be used for case and bag, footwear, dress ornament and upholstery leather etc. are especially in children's footwear and outdoor activity.
Embodiment
Should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
embodiment 1
A kind of temperature is changed, and comprises ox-hide layer basic unit, PU resin layer, warm change layer and transparent film layer from inside to outside successively; Described temperature change layer is aliphatic modified High-temperature-respolyurethane polyurethane resin 40 weight part of 40GPa by Young's modulus, dimethylbenzene 20 weight part, DMF 35 weight part, butyl ester 25 weight part, acetone 20 weight part, stress discoloration wax powder 2 weight part, silicon-dioxide flatting silica 3 weight part, modified organic silicon 3 weight part, whiteruss 1 weight part, polyurethane nanofiber 2 weight part, 6 parts, modified Teflon discoloration wax powder mixes.
embodiment 2
A kind of temperature is changed, and comprises nonwoven cloth basic unit, nitro-resin, warm change layer and transparent film layer from inside to outside successively; Described temperature change layer by polyurethane resin 60 weight part, dimethylbenzene 30 weight part, DMF 30 weight part, butyl ester 15 weight part, acetone 30 weight part, stress discoloration wax powder 5 weight part, silicon-dioxide flatting silica 1 weight part, modified organic silicon 1 weight part, whiteruss 3 weight part, polyurethane nanofiber 5 weight part, 2 parts, modified Teflon discoloration wax powder, flow agent 1 weight part, erucicamide 3 weight part mixes.
embodiment 3
A kind of temperature is changed, and comprises basic unit, resin layer, warm change layer and transparent film layer from inside to outside successively; Described temperature change layer by polyamide 50 weight part, dimethylbenzene 24 weight part, DMF34 weight part, butyl ester 18 weight part, acetone 22 weight part, stress discoloration wax powder 3 weight part, silicon-dioxide flatting silica 2 weight part, modified organic silicon 1 ~ 3 weight part, whiteruss 2 weight part, polyurethane nanofiber 4 weight part, 3 parts, modified Teflon discoloration wax powder, flow agent 3 weight part, erucicamide 1 weight part.
embodiment 4
A kind of temperature is changed, and comprises synthetic leather basic unit, synthetic leather resin layer, warm change layer and transparent film layer from inside to outside successively; Described temperature change layer is by aliphatic modified High-temperature-respolyurethane polyurethane resin 46 weight part, dimethylbenzene 26 weight part, DMF 33 weight part, butyl ester 20 weight part, acetone 25 weight part, stress discoloration wax powder 5 weight part, silicon-dioxide flatting silica 2 weight part, modified organic silicon 3 weight part, whiteruss 2 weight part, polyurethane nanofiber 3 weight part, 6 parts, modified Teflon discoloration wax powder mixes.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.

Claims (8)

1. a temperature is changed, and it is characterized in that, comprises basic unit, resin layer, warm change layer and transparent film layer from inside to outside successively; Described temperature change layer is by petroleum resin 40 ~ 60 weight part, dimethylbenzene 20 ~ 30 weight part, DMF 30 ~ 35 weight part, butyl ester 15 ~ 25 weight part, acetone 20 ~ 30 weight part, stress discoloration wax powder 2 ~ 5 weight part, silicon-dioxide flatting silica 1 ~ 3 weight part, modified organic silicon 1 ~ 3 weight part, whiteruss 1 ~ 3 weight part, polyurethane nanofiber 2 ~ 5 weight part, 2 ~ 6 parts, modified Teflon discoloration wax powder mixes.
2. a kind of temperature as claimed in claim 1 is changed, and it is characterized in that, described temperature change layer is by petroleum resin 40 ~ 50 weight part, dimethylbenzene 24 ~ 30 weight part, DMF 30 ~ 34 weight part, butyl ester 18 ~ 22 weight part, acetone 22 ~ 27 weight part, stress discoloration wax powder 3 ~ 5 weight part, silicon-dioxide flatting silica 2 weight part, modified organic silicon 2 ~ 3 weight part, whiteruss 2 ~ 3 weight part, polyurethane nanofiber 2 ~ 4 weight part, 3 ~ 6 parts, modified Teflon discoloration wax powder mixes.
3. a kind of temperature as claimed in claim 1 is changed, and it is characterized in that, described temperature change layer is by petroleum resin 46 weight part, dimethylbenzene 26 weight part, DMF 33 weight part, butyl ester 20 weight part, acetone 25 weight part, stress discoloration wax powder 5 weight part, silicon-dioxide flatting silica 2 weight part, modified organic silicon 3 weight part, whiteruss 2 weight part, polyurethane nanofiber 3 weight part, 6 parts, modified Teflon discoloration wax powder mixes.
4. the one temperature as described in any one of claim 1-3 is changed, and it is characterized in that, described described temperature change layer also comprises flow agent 1 ~ 3 weight part, erucicamide 1 ~ 3 weight part.
5. the one temperature as described in claim 1 or 4 is changed, and it is characterized in that, described basic unit is cloth, nonwoven cloth, synthetic leather or ox-hide layer.
6. the one temperature as described in claim 1 or 4 is changed, and it is characterized in that, described resin layer is PU, PVC, PC, vinylformic acid or nitro-resin.
7. the one temperature as described in claim 1 or 4 is changed, and it is characterized in that, described petroleum resin are polyamide, epoxy resin, polyurethane resin or modified, high temperature resistant urethane resin.
8. the one temperature as described in claim 1 or 4 is changed, and it is characterized in that, described petroleum resin are aliphatic modified High-temperature-respolyurethane polyurethane resin, and its Young's modulus is 40GPa ~ 80GPa.
CN201510005423.7A 2015-01-07 2015-01-07 Temperature-variable leather Pending CN104497779A (en)