CN104497521A - Composite material used for LED lampshades - Google Patents
Composite material used for LED lampshades Download PDFInfo
- Publication number
- CN104497521A CN104497521A CN201410690184.9A CN201410690184A CN104497521A CN 104497521 A CN104497521 A CN 104497521A CN 201410690184 A CN201410690184 A CN 201410690184A CN 104497521 A CN104497521 A CN 104497521A
- Authority
- CN
- China
- Prior art keywords
- parts
- matrix material
- led lamp
- lamp cover
- cover according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A disclosed composite material used for LED lampshades is composed of the following compositions in parts by weight: 50-80 parts of PC (polycarbonate), 10-30 parts of nanometer TiO2, 0.2-0.5 part of a flexibilizer, 0.5-2 parts of an anti-oxidant, 1-3 parts of a light diffusion agent, 0.1-2 parts of an ultraviolet ray absorber, and 5-10 parts of a blending agent. The composite material is formed by improving a PC material, possesses good light-ageing resistance, possesses various physical mechanical performances and thermodynamic properties which are basically not influenced, and has wide application prospect.
Description
Technical field
The present invention relates to a kind of matrix material for LED lamp cover, belong to technical field of polymer materials.
Background technology
PC (polycarbonate) has excellent shock resistance, creep resistance, dimensional stability and electric insulating quality, a kind of engineering plastics of superior performance, be widely used in the fields such as mechanical means, electronic product, automobile making, but also there is poor fluidity, easily stress cracking, the easily aging and shortcoming such as to wear no resistance, its application is in a lot of fields restricted.In recent years, along with expanding economy, plasticity and the chemical stability of PC engineering plastics are relatively good, but, when being used as LED lamp cover, owing to being subject to the irradiation of light for a long time, easily causing aging, the demand in market can not be met.
Summary of the invention
For solving the deficiencies in the prior art, the object of the invention is to the defect overcoming prior art, providing a kind of aging-resistant for the matrix material of LED lamp cover.
In order to realize above-mentioned target, the present invention adopts following technical scheme: a kind of matrix material for LED lamp cover, is characterized in that, comprises following component and the parts by weight of each component are:
PC 50-80 part;
Nano-TiO
210-30 part;
Toughner 0.2-0.5 part;
Oxidation inhibitor 0.5-2 part;
Light diffusing agent 1-3 part;
UV light absorber 0.1-2 part;
Alloying agent 5-10 part.
Aforesaid a kind of matrix material for LED lamp cover, is characterized in that, described nano-TiO
2for rutile type nano TiO
2.
Aforesaid a kind of matrix material for LED lamp cover, is characterized in that, described toughner is MBS, MMB or ASA.
Aforesaid a kind of matrix material for LED lamp cover, is characterized in that, the Hinered phenols antioxidant 1010 of described oxidation inhibitor to be mass ratio be 1:1 and phosphite kind antioxidant 168.
Aforesaid a kind of matrix material for LED lamp cover, it is characterized in that, described UV light absorber is selected from UV-3853, one or both mixtures in UV-2908.
Aforesaid a kind of matrix material for LED lamp cover, is characterized in that, described alloying agent is linear low density polyethylene.
Beneficial effect of the present invention is: the present invention improves PC material, and not only have good anti-light aging performance, every physical and mechanical property of material and thermomechanical property are substantially unaffected, have broad application prospects.
embodiment:
Below in conjunction with specific embodiment, the present invention is described further.
The proportioning of each component of table 1 embodiment 1-4 and comparative example
Wherein, described nano-TiO
2for rutile type nano TiO
2.
Described toughner is MBS, MMB or ASA.
The Hinered phenols antioxidant 1010 of described oxidation inhibitor to be mass ratio be 1:1 and phosphite kind antioxidant 168.
Described UV light absorber is selected from UV-3853, one or both mixtures in UV-2908.
Described alloying agent is linear low density polyethylene.
The performance test results of each embodiment of table 2 and comparative example
Note: reference standard is: GB13525/T-92 and UL94.
As can be seen from Table 2, nano-TiO is added
2, significantly improve the photostabilization grade of PC matrix material, improve the anti-light aging performance of PC matrix material, every physical and mechanical property of material and thermomechanical property are substantially unaffected, have broad application prospects.
More than show and describe ultimate principle of the present invention, principal character and advantage.The technician of the industry should understand, and above-described embodiment does not limit the present invention in any form, the technical scheme that the mode that all employings are equal to replacement or equivalent transformation obtains, and all drops in protection scope of the present invention.
Claims (6)
1. for a matrix material for LED lamp cover, it is characterized in that, comprise following component and the parts by weight of each component are:
PC 50-80 part;
Nano-TiO
210-30 part;
Toughner 0.2-0.5 part;
Oxidation inhibitor 0.5-2 part;
Light diffusing agent 1-3 part;
UV light absorber 0.1-2 part;
Alloying agent 5-10 part.
2. a kind of matrix material for LED lamp cover according to claim 1, is characterized in that, described nano-TiO
2for rutile type nano TiO
2.
3. a kind of matrix material for LED lamp cover according to claim 1, is characterized in that, described toughner is MBS, MMB or ASA.
4. a kind of matrix material for LED lamp cover according to claim 1, is characterized in that, the Hinered phenols antioxidant 1010 of described oxidation inhibitor to be mass ratio be 1:1 and phosphite kind antioxidant 168.
5. a kind of matrix material for LED lamp cover according to claim 1, it is characterized in that, described UV light absorber is selected from UV-3853, one or both mixtures in UV-2908.
6. a kind of matrix material for LED lamp cover according to claim 1, is characterized in that, described alloying agent is linear low density polyethylene.