CN104497252A - Polyurethane for making solid tires and preparation method thereof - Google Patents
Polyurethane for making solid tires and preparation method thereof Download PDFInfo
- Publication number
- CN104497252A CN104497252A CN201410757937.3A CN201410757937A CN104497252A CN 104497252 A CN104497252 A CN 104497252A CN 201410757937 A CN201410757937 A CN 201410757937A CN 104497252 A CN104497252 A CN 104497252A
- Authority
- CN
- China
- Prior art keywords
- component
- solid tyre
- making solid
- parts
- urethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention aims to provide a polyurethane for making solid tires, which is composed of a component A and a component B. The component A is composed of the following ingredients in parts by weight: 80-90 parts of polyether glycol 1, 10-20 parts of polyether glycol 2, 0.1-0.2 part of foam stabilizer, 0.3-0.40 part of amine catalyst, 0.05-0.10 part of metal catalyst, 3-5 parts of crosslinking agent, 5-7 parts of chain extender 1, 10-12 parts of chain extender 2 and 5-10 parts of physical foaming agent. The component B is composed of 100-110 parts by weight of modified black material. The invention also provides a preparation method of the polyurethane for making solid tires. The solid tire made from the polyurethane has the advantages of small environmental pollution, high carrying capacity and favorable wear resistance. The preparation method is easy to implement and high in production efficiency.
Description
Technical field
The present invention relates to a kind of urethane and preparation method thereof, particularly relate to a kind of making solid tyre urethane and preparation method thereof, belong to chemical field.
Background technology
In use, the materials such as the polycyclic aromatic hydrocarbons in tyre surface and carbon black can be dispersed in air and soil rubber tyre, serious environment pollution, and it is large that junked tire recycles difficulty, expends more manpower, financial resources and material resources.
Its recycling of polyurethane material is easier than rubber, adopts physical method to reclaim and may be used for the less demanding polyurethane product of production performance, adopts chemical process to reclaim and can obtain pure starting monomer, as polyvalent alcohol, isocyanic ester, amine etc.
Summary of the invention
For the shortcoming of rubber tyre, the object of the present invention is to provide a kind of urethane, for making solid tyre; The tire adopting urethane of the present invention to make have environmental pollution little, reclaim easily, and the advantage such as wear resistance is good, tear strength is high, bearing capacity is strong; The present invention also provides the preparation method of described urethane, the method easy enforcement simple to operate, and production efficiency is high, energy consumption is low.
A kind of making solid tyre urethane, be made up according to following weight part of component A and B component:
Component A:
B component:
100 ~ 110 parts, the black material of modification.
It is 3 that described polyether glycol 1 chooses functionality, and molecular weight is the polyether glycol of 6000, the polyether glycol DEP-330G that the federal chemical Industrial Co., Ltd of preferred Zibo moral letter produces; The advantages such as it is good that the goods using this kind of polyvalent alcohol to do have surface skining, and demould time is fast.
It is 3 that described polyether glycol 2 chooses functionality, molecular weight is the grafted polyether polyol of 8000, the polyether glycol POP-93/28 that preferred Zibo federal chemical Industrial Co., Ltd of moral letter produces, the advantages such as the goods using this kind of polyvalent alcohol to do have good hand touch, and hardness is large.
Described suds-stabilizing agent preferred foams stablizer Y-10366, has stable foam and regulates abscess, the effect of emulsification foam material.
Described amine catalyst preferred amines catalyst A 33, mainly utilizes its high reactivity, plays stronger katalysis to gel reaction and foamable reaction.
The preferred tin catalyst T12 of described metal catalyst, adopts Cang Zhoudong to mould the T12 of chemical company's production, mainly utilizes its strong gel active, play stronger katalysis to gel reaction.
The preferred diethanolamine of described linking agent, produces certain katalysis to polyurethane reaction while stable foam structure.
Described chainextender 1 is ethylene glycol preferably, hard for the molecular chain in reaction section is strengthened, improves the hardness of goods.
Described chainextender 2 is BDO preferably, and the molecular chain in reaction is expanded further, increases the snappiness of goods.
Described whipping agent preferably adopts pneumatogen or chemical foaming agent; Pneumatogen optimization cyclopentane, chemical foaming agent preferably water.
The black material of modification that-NCO mass content is 16-22% chosen by the black material of described modification, and preferably-NCO mass content is 19%;
Further, the black material of described modification selects functionality to be 2, and molecular weight is that the polyether glycol of 2000 and the black material PM200 of Yantai ten thousand China production react generation; The goods adopting the black material of modification to make as raw material have smooth surface, good toughness, the advantages such as intensity is large.
The preparation method of making solid tyre urethane of the present invention, comprises the following steps:
(1) each for component A raw material is added agitator to mix, adjustment material temperature is also constant in 25 ± 2 DEG C, constant temperature 1-2 hour; Adjustment B component material temperature is also constant in 25 ± 2 DEG C, constant temperature 1-2 hour;
(2) regulate agitator speed to 4000-5000r/min, B component is poured in component A be uniformly mixed stand-by.
When making solid tyre, after the A in step (2), B component mixture are stirred 15-25s, pour in the mould being preheated to 40 ± 5 DEG C, the demoulding after 5-10min, obtains solid tyre.
Compared with prior art, the present invention has following beneficial effect:
(1) solid tyre adopting urethane of the present invention to make, environmental pollution is little, recovery is easy, and tire capacity is high, wear resistance is good, tear strength is high, application prospect is good, the industrial vehicle used under the special conditions such as be applicable to manufacture high loading, energy-conservation, condition of road surface is severe or operating environment requirements is clean or truck tyre.
(2) preparation method of making solid tyre urethane of the present invention is simple and easy to enforcement, production efficiency is high, energy consumption is low.
Embodiment
Below in conjunction with embodiment, the present invention is set forth further.
Embodiment 1
Component A: polyether glycol 1:82 part, polyether glycol 2:15 part, suds-stabilizing agent Y-10366:0.1 part, amine catalyst A33:0.3 part, tin catalyst T12:0.05 part, diethanolamine: 3 parts, ethylene glycol: 5 parts, BDO: 10 parts and pentamethylene: 6 parts.
B component: the black material of modification: 100 parts.
In said components: polyether glycol 1 adopts functionality to be 3, and molecular weight is the polyether glycol of 6000; Polyether glycol 2 adopts functionality to be 3, and molecular weight is the grafted polyether polyol of 8000; The black material of modification is 2 for selecting functionality, and molecular weight is that the polyether glycol of 2000 and the black material PM200 of Yantai ten thousand China production react the black material of the modification that-NCO mass content generated is 19%.
Make the preparation method of solid tyre urethane, comprise the following steps:
(1) each for component A raw material is added agitator to mix, adjustment material temperature is also constant in 25 ± 2 DEG C, constant temperature 1.5 hours; Adjustment B component material temperature is also constant in 25 ± 2 DEG C, constant temperature 1 hour;
(2) regulate agitator speed to 4200r/min, B component is poured in component A be uniformly mixed stand-by.
When making solid tyre, after the A in step (2), B component mixture are stirred 20s, pour in the mould being preheated to 40 DEG C, the demoulding after 6min, obtains solid tyre.
Embodiment 2
Component A: polyether glycol DEP-330G:85 part, polyether glycol POP-36/28:15 part, suds-stabilizing agent Y-10366:0.15 part, amine catalyst A33:0.35 part, tin catalyst T12:0.05 part, diethanolamine: 4 parts, ethylene glycol: 6 parts, BDO: 11 parts and water: 8 parts.
B component: the black material of modification: 105 parts.
The black material of above-mentioned modification is 2 for selecting functionality, and molecular weight is that the polyether glycol of 2000 and the black material PM200 of Yantai ten thousand China production react the black material of the modification that-NCO mass content generated is 20%.
Make the preparation method of solid tyre urethane, comprise the following steps:
(1) each for component A raw material is added agitator to mix, adjustment material temperature is also constant in 25 ± 2 DEG C, constant temperature 1.5 hours; Adjustment B component material temperature is also constant in 25 ± 2 DEG C, constant temperature 1.5 hours;
(2) regulate agitator speed to 4500r/min, B component is poured in component A be uniformly mixed stand-by.
When making solid tyre, after the A in step (2), B component mixture are stirred 20s, pour in the mould being preheated to 42 DEG C, the demoulding after 8min, obtains solid tyre.
Embodiment 3
Component A: polyether glycol DEP-330G:90 part, polyether glycol POP-36/28:20 part, suds-stabilizing agent Y-10366:0.2 part, amine catalyst A33:0.4 part, tin catalyst T12:0.1 part, diethanolamine: 5 parts, ethylene glycol: 7 parts, BDO: 12 parts and pentamethylene: 10 parts.
B component: the black material of modification: 110 parts.
The black material of above-mentioned modification is 2 for selecting functionality, and molecular weight is that the polyether glycol of 2000 and the black material PM200 of Yantai ten thousand China production react the black material of the modification that-NCO mass content generated is 22%.
Make the preparation method of solid tyre urethane, comprise the following steps:
(1) each for component A raw material is added agitator to mix, adjustment material temperature is also constant in 25 ± 2 DEG C, constant temperature 2 hours; Adjustment B component material temperature is also constant in 25 ± 2 DEG C, constant temperature 1.5 hours;
(2) regulate agitator speed to 5000r/min, B component is poured in component A be uniformly mixed stand-by.
When making solid tyre, after the A in step (2), B component mixture are stirred 25s, pour in the mould being preheated to 45 DEG C, the demoulding after 10min, obtains solid tyre.
Claims (10)
1. make a solid tyre urethane, it is characterized in that, be made up according to following weight part of component A and B component:
Component A:
B component:
100 ~ 110 parts, the black material of modification.
2. making solid tyre urethane according to claim 1, is characterized in that, described polyether glycol 1 adopts functionality to be 3, and molecular weight is the polyether glycol of 6000; Described polyether glycol 2 adopts functionality to be 3, and molecular weight is the grafted polyether polyol of 8000.
3. making solid tyre urethane according to claim 1, it is characterized in that, suds-stabilizing agent Y-10366 chosen by described suds-stabilizing agent.
4. making solid tyre urethane according to claim 1, it is characterized in that, described amine catalyst chooses amine catalyst A33, and tin catalyst T12 chosen by metal catalyst.
5. making solid tyre urethane according to claim 1, it is characterized in that, diethanolamine chosen by described linking agent.
6. making solid tyre urethane according to claim 1, is characterized in that, ethylene glycol chosen by described chainextender 1, and BDO chosen by chainextender 2.
7. making solid tyre urethane according to claim 1, is characterized in that, described whipping agent adopts pneumatogen or chemical foaming agent, and pneumatogen chooses pentamethylene, and chemical foaming agent chooses water.
8. making solid tyre urethane according to claim 1, is characterized in that, the black material of modification that-NCO mass content is 16-22% chosen by the black material of described modification, and preferably-NCO mass content is 19%.
9. making solid tyre urethane according to claim 8, is characterized in that, the black material of described modification selects functionality to be 2, and molecular weight is polyether glycol and the black material PM200 reaction generation of 2000.
10., according to a preparation method for the arbitrary described making solid tyre urethane of claim 1-8, it is characterized in that, comprise the following steps:
(1) each for component A raw material is added agitator to mix, adjustment material temperature is also constant in 25 ± 2 DEG C, constant temperature 1-2 hour; Adjustment B component material temperature is also constant in 25 ± 2 DEG C, constant temperature 1-2 hour;
(2) regulate agitator speed to 4000-5000r/min, B component is poured in component A be uniformly mixed stand-by.