CN104496194A - Preparation method of glass for video screen - Google Patents
Preparation method of glass for video screen Download PDFInfo
- Publication number
- CN104496194A CN104496194A CN201410700104.3A CN201410700104A CN104496194A CN 104496194 A CN104496194 A CN 104496194A CN 201410700104 A CN201410700104 A CN 201410700104A CN 104496194 A CN104496194 A CN 104496194A
- Authority
- CN
- China
- Prior art keywords
- glass
- preparation
- mixed solution
- screen
- video screen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of glass for a video screen. The preparation method comprises the following steps of mixing ammonium hydrofluoride, ammonium sulfate, barium sulfate, oxalic acid, glycerin and deionized water to obtain a uniform mixed solution with corrosion effects, heating common glass by fire, immersing the glass in the mixed solution for a certain time, taking out the glass, and carrying out cleaning to obtain the glass for a video screen. The preparation method adopts the common easily-available raw materials and can be popularized. The glass reaches to the foreign country enterprise standard level, has invariable transmittance, can be installed on the video screen, produces imaging effects the same as those of the common screen glass and doses not produce viewer inverted images.
Description
Technical field
The present invention relates to a kind of preparation method of glass, particularly relate to a kind of preparation method of the glass in TV screen.
Background technology
Sheet glass is namely without the plate glass of other processing, sheet glass be in modern glass turnout maximum, use maximum one, being mainly used in door and window, as long as have daylighting, go along with sb. to guard him, be incubated, the effect such as sound insulation, is also former that is processed into other technologies glass further.As sheet glass can use as the starting material of the glass in TV screen, but existing glass ubiquity on the tv screen has the problem of inverted image, people sees TV before being sitting in televisor, except the program of viewing can be seen, also can see the inverted image of oneself and surrounding environment, affect the viewing effect of people, thus affect the vision performance of people.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of preparation method of the glass in TV screen, and this preparation method can obtain the good glass of viewing effect.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: the preparation method providing a kind of glass in TV screen, and comprising step is:
(1) hydrofluoric acid ammonium, ammonium sulfate, barium sulfate, oxalic acid, glycerine and deionized water are mixed the mixed solution obtaining having corrosive effect;
(2) simple glass fire is warmed, then put into described mixed solution and soak, take out after soaking certain hour and clean up, obtaining the glass in TV screen.
In a preferred embodiment of the present invention, described in step (1), the component of mixed solution is: by percentage to the quality, hydrofluoric acid ammonium 8-11%, ammonium sulfate 3-5%, barium sulfate 7-9%, oxalic acid 6-7%, glycerine 2-4%, deionized water surplus.
In a preferred embodiment of the present invention, described in step (2), the temperature of mixed solution is 50-65 DEG C.
In a preferred embodiment of the present invention, described in step (2), soak time is 10-15 hour.
The invention has the beneficial effects as follows: the preparation method of the glass in TV screen of the present invention, the raw material that this preparation method adopts is conventional raw material, simple and easy to get, can apply, the glass obtained can reach the level of foreign enterprise standard, transmitance is constant, and the glass imaging effect be installed in TV screen is identical with common screen glass effect, can not produce the inverted image of beholder simultaneously.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment one:
There is provided a kind of preparation method of the glass in TV screen, comprising step is:
(1) hydrofluoric acid ammonium, ammonium sulfate, barium sulfate, oxalic acid, glycerine and deionized water are mixed the mixed solution obtaining having corrosive effect, the component of wherein said mixed solution is: by percentage to the quality, hydrofluoric acid ammonium 11%, ammonium sulfate 4%, barium sulfate 9%, oxalic acid 7%, glycerine 2%, deionized water surplus;
(2) simple glass fire is warmed, then to put into temperature be that the described mixed solution of 55 DEG C soaks, soak and to take out after 15 hours and to clean up, obtain the glass in TV screen.
Embodiment two:
There is provided a kind of preparation method of the glass in TV screen, comprising step is:
(1) hydrofluoric acid ammonium, ammonium sulfate, barium sulfate, oxalic acid, glycerine and deionized water are mixed the mixed solution obtaining having corrosive effect, the component of wherein said mixed solution is: by percentage to the quality, hydrofluoric acid ammonium 8%, ammonium sulfate 3%, barium sulfate 8%, oxalic acid 6%, glycerine 4%, deionized water surplus;
(2) simple glass fire is warmed, then to put into temperature be that the described mixed solution of 65 DEG C soaks, soak and to take out after 10 hours and to clean up, obtain the glass in TV screen.
Embodiment three:
There is provided a kind of preparation method of the glass in TV screen, comprising step is:
(1) hydrofluoric acid ammonium, ammonium sulfate, barium sulfate, oxalic acid, glycerine and deionized water are mixed the mixed solution obtaining having corrosive effect, the component of wherein said mixed solution is: by percentage to the quality, hydrofluoric acid ammonium 10%, ammonium sulfate 5%, barium sulfate 7%, oxalic acid 6%, glycerine 3%, deionized water surplus;
(2) simple glass fire is warmed, then to put into temperature be that the described mixed solution of 60 DEG C soaks, soak and to take out after 12 hours and to clean up, obtain the glass in TV screen.
The invention has the beneficial effects as follows:
One, the raw material that the preparation method adopted adopts is conventional raw material, simple and easy to get, can apply;
Two, the glass obtained can reach the level of foreign enterprise standard, and transmitance is constant;
Three, the glass imaging effect be installed in TV screen is identical with common screen glass effect, can not produce the inverted image of beholder simultaneously.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (4)
1. a preparation method for the glass in TV screen, is characterized in that, comprises step to be:
(1) hydrofluoric acid ammonium, ammonium sulfate, barium sulfate, oxalic acid, glycerine and deionized water are mixed the mixed solution obtaining having corrosive effect;
(2) simple glass fire is warmed, then put into described mixed solution and soak, take out after soaking certain hour and clean up, obtaining the glass in TV screen.
2. the preparation method of the glass in TV screen according to claim 1, it is characterized in that, described in step (1), the component of mixed solution is: by percentage to the quality, hydrofluoric acid ammonium 8-11%, ammonium sulfate 3-5%, barium sulfate 7-9%, oxalic acid 6-7%, glycerine 2-4%, deionized water surplus.
3. the preparation method of the glass in TV screen according to claim 1, is characterized in that, described in step (2), the temperature of mixed solution is 50-65 DEG C.
4. the preparation method of the glass in TV screen according to claim 1, is characterized in that, described in step (2), soak time is 10-15 hour.