CN104494262B - Coextru-lamination barrier packaging film - Google Patents
Coextru-lamination barrier packaging film Download PDFInfo
- Publication number
- CN104494262B CN104494262B CN201410817531.XA CN201410817531A CN104494262B CN 104494262 B CN104494262 B CN 104494262B CN 201410817531 A CN201410817531 A CN 201410817531A CN 104494262 B CN104494262 B CN 104494262B
- Authority
- CN
- China
- Prior art keywords
- film
- barrier
- packaging
- packaging film
- coextru
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Coextru-lamination barrier packaging film, belongs to field of packaging material. The present invention is to solve that existing co-extrusion film intermediate layer water absorption is higher, barrier layer barrier declines, effective shelf-life of product is short, simultaneously because the structure of the single barrier layer of co-extrusion film intermediate layer PA and both sides thereof is arranged, it is impossible to realize packaging film high obstructing performance and the problem of high co-extrusion ductility simultaneously. Packaging film includes BOPET biaxial stretching polyester film, APET photomask, a PE polyethylene film, a PET mylar, the first EVOH barrier layer, PVDC gas barrier film, the second EVOH barrier layer, the 2nd PET mylar and the 2nd PE polyethylene film; Described BOPET biaxial stretching polyester film, APET photomask, a PE polyethylene film, a PET mylar, the first EVOH barrier layer, PVDC gas barrier film, the second EVOH barrier layer, the 2nd PET mylar and the 2nd PE polyethylene film coextru-lamination from outside to inside constitute packaging film. The packaging film of the present invention is especially suitable for the packaging of fresh seafood, beef and dried tofu.
Description
Technical field
The present invention relates to a kind of co-extrusion packaging film, be specifically related to a kind of coextru-lamination barrier packaging film, belong to field of packaging material.
Background technology
At present, numerous Aquatic product companies outlet seafood uses co-extrusion film vacuum packaging. But, when packing content and being the bigger seafood product of humidity, due to co-extrusion film intermediate layer PA(nylon) water absorption higher, and barrier layer EVOH(ethylene/vinyl alcohol copolymer) when high humility, barrier sharply declines, thus having had a strong impact on the barrier property that packaging is overall, substantially reduce effective shelf-life of product, simultaneously because co-extrusion film intermediate layer PA(nylon) and the single barrier layer EVOH(ethylene/vinyl alcohol copolymer of both sides) structure arrange, it is impossible to realize the high obstructing performance of packaging film and the high co-extrusion ductility of packaging film simultaneously. It would therefore be highly desirable to design a kind of packaging film with high barrier and high co-extrusion ductility.
Summary of the invention
It is an object of the invention to provide a kind of coextru-lamination barrier packaging film, water absorption to solve existing co-extrusion film intermediate layer PA is higher, barrier layer EVOH barrier sharply declines, shorten effective shelf-life of product, simultaneously because the structure of the single barrier layer of co-extrusion film intermediate layer PA and both sides thereof is arranged, it is impossible to realize packaging film high obstructing performance and the problem of packaging film high co-extrusion ductility simultaneously.
The present invention is to solve that above-mentioned technical problem is adopted the technical scheme that:
The coextru-lamination barrier packaging film of the present invention, including BOPET biaxial stretching polyester film, APET photomask, a PE polyethylene film, a PET mylar, the first EVOH barrier layer, PVDC gas barrier film, the second EVOH barrier layer, the 2nd PET mylar and the 2nd PE polyethylene film;Described BOPET biaxial stretching polyester film, APET photomask, a PE polyethylene film, a PET mylar, the first EVOH barrier layer, PVDC gas barrier film, the second EVOH barrier layer, the 2nd PET mylar and the 2nd PE polyethylene film coextru-lamination from outside to inside constitute packaging film.
PA film as core structural layer, by the stepped construction of the film that changes package, is replaced with PVDC gas barrier film, enhances the barrier property of packaging film, owing to PVDC has stronger shrinkage, thus also enhancing the ductility of packaging film by the present invention. In order to make packaging film have stronger barrier property and ductility, the present invention, except arranging EVOH barrier layer in the both sides of core structural layer PVDC gas barrier film, also add PET mylar. Furthermore present invention also adds BOPET biaxial stretching polyester film as printing basement membrane, it is simple to follow-up printing labeling. Finally present invention also adds photomask, for preventing article in packaging bag from occurring rotten because of reasons such as illumination.
Preferred: on a described PET mylar and the 2nd PET mylar, all processing has mesh. So arrange, while ensureing packaging film entirety barrier, further increase the ductility of packaging film.
Preferred: described mesh be shaped as rhombus. So arranging, the integral extension of packaging film is higher.
Preferred: the thickness of described coextru-lamination barrier packaging film is 540 ~ 560 ��m. So arrange, meet the requirement of strength of packaging film.
Preferred: the thickness of described PVDC gas barrier film is 70 ~ 90 ��m. So arranging, while meeting gas barrier property, ductility is better.
The present invention compared with prior art has the effect that the stepped construction by the film that changes package of the present invention, PA film as core structural layer is replaced with PVDC gas barrier film, enhance the barrier property of packaging film, owing to PVDC has stronger shrinkage, thus also enhancing the ductility of packaging film. In order to make packaging film have stronger barrier property and ductility, the present invention, except arranging EVOH barrier layer in the both sides of core structural layer PVDC gas barrier film, also add PET mylar. Furthermore present invention also adds BOPET biaxial stretching polyester film as printing basement membrane, it is simple to follow-up printing labeling. Finally present invention also adds photomask, for preventing article in packaging bag from occurring rotten because of reasons such as illumination. It has good contractility, gas barrier property, water preventing ability, is mainly used in the packaging of fresh seafood, beef and dried tofu etc. (gas barrier properties does not change with the change of humidity to utilize its gas barrier property, even if high humidity environment is rotten without causing product), the generation of Food Oxidation denaturalization phenomenon can be delayed, it is greatly prolonged the product shelf phase, simultaneously it can be avoided that the fragrance of content scatters and disappears and prevents the intrusion of outside bad smell; The resistance utilizing packaging film is moist, it is possible to prevent the phenomenon of product generation dehydration exsiccation, taste bad, will not damage packaging prototype because of product water suction, it is prevented that quantitatively goods generation natural wastage (weightlessness); Utilize packaging film hypotonicity, can prevent loss of aroma, and not absorption of residual residual air taste and off-taste, it is ensured that the integrity (this point is particularly important when packing low fat or high-protein food) of abnormal smells from the patient. The packaging film of the present invention at 100 DEG C, can bear the heating duration of 10 minutes, has flexibility good, and heat sealability is excellent, nonpoisonous and tasteless, and oil resistivity is good, the advantage of good corrosion resistance.The packaging film of the present invention is especially suitable for the packaging of fresh seafood, beef and dried tofu.
Accompanying drawing explanation
Fig. 1 is the structure chart of coextru-lamination barrier packaging film of the present invention.
In figure: 1-BOPET biaxial stretching polyester film; 2-APET photomask; 3-the oneth PE polyethylene film; 4-the oneth PET mylar; 5-the first EVOH barrier layer; 6-PVDC gas barrier film; 7-the second EVOH barrier layer; 8-the 2nd PET mylar; 9-the 2nd PE polyethylene film.
Detailed description of the invention
The preferred embodiment of the present invention is elaborated below according to accompanying drawing.
As it is shown in figure 1, coextru-lamination barrier packaging film of the present invention includes BOPET biaxial stretching polyester film 1, APET photomask the 2, the oneth PE polyethylene film the 3, the oneth PET mylar the 4, first EVOH barrier layer 5, PVDC gas barrier film the 6, second EVOH barrier layer the 7, the 2nd PET mylar 8 and the 2nd PE polyethylene film 9; Described BOPET biaxial stretching polyester film 1, APET photomask the 2, the oneth PE polyethylene film the 3, the oneth PET mylar the 4, first EVOH barrier layer 5, PVDC gas barrier film the 6, second EVOH barrier layer the 7, the 2nd PET mylar 8 and the 2nd PE polyethylene film 9 coextru-lamination from outside to inside constitute packaging film. On a described PET mylar 4 and the 2nd PET mylar 8, all processing has mesh. Described mesh be shaped as rhombus. The thickness of coextru-lamination barrier packaging film is 540 ~ 560 ��m. The thickness of PVDC gas barrier film is 70 ~ 90 ��m.
PA film as core structural layer, by the stepped construction of the film that changes package, is replaced with PVDC gas barrier film, enhances the barrier property of packaging film, owing to PVDC has stronger shrinkage, thus also enhancing the ductility of packaging film by the present invention. In order to make packaging film have stronger barrier property and ductility, the present invention, except arranging EVOH barrier layer in the both sides of core structural layer PVDC gas barrier film, also add PET mylar. Furthermore present invention also adds BOPET biaxial stretching polyester film as printing basement membrane, it is simple to follow-up printing labeling. Finally present invention also adds photomask, for preventing article in packaging bag from occurring rotten because of reasons such as illumination. This packaging film is resistant to 100 DEG C of decocting in water, can not high temperature steaming. Its tensile property of this packaging film is better, is suitable to the packaging of large volume, can be used for striking out the mould of content shape, and not with other materials compound tense, deep drawn is up to 16cm; Compound CPP(cast polypropylene) time, it is possible to do the shallow stretching of 2cm.
Present embodiment is the exemplary illustration to this patent, does not limit its protection domain, and its local can also be changed by those skilled in the art, as long as no the spirit beyond this patent, all in the protection domain of this patent.
Claims (5)
1. coextru-lamination barrier packaging film, it is characterised in that: include BOPET biaxial stretching polyester film (1), APET photomask (2), a PE polyethylene film (3), a PET mylar (4), the first EVOH barrier layer (5), PVDC gas barrier film (6), the second EVOH barrier layer (7), the 2nd PET mylar (8) and the 2nd PE polyethylene film (9); Described BOPET biaxial stretching polyester film (1), APET photomask (2), a PE polyethylene film (3), a PET mylar (4), the first EVOH barrier layer (5), PVDC gas barrier film (6), the second EVOH barrier layer (7), the 2nd PET mylar (8) and the 2nd PE polyethylene film (9) coextru-lamination from outside to inside constitute packaging film.
2. coextru-lamination barrier packaging film according to claim 1, it is characterised in that: on a described PET mylar (4) and the 2nd PET mylar (8), all processing has mesh.
3. coextru-lamination barrier packaging film according to claim 2, it is characterised in that: described mesh be shaped as rhombus.
4. coextru-lamination barrier packaging film according to claim 3, it is characterised in that: the thickness of described coextru-lamination barrier packaging film is 540 ~ 560 ��m.
5. coextru-lamination barrier packaging film according to claim 4, it is characterised in that: the thickness of described PVDC gas barrier film is 70 ~ 90 ��m.