CN104479413A - Preparation method of coating superfine heavy calcium carbonate - Google Patents
Preparation method of coating superfine heavy calcium carbonate Download PDFInfo
- Publication number
- CN104479413A CN104479413A CN201410748314.XA CN201410748314A CN104479413A CN 104479413 A CN104479413 A CN 104479413A CN 201410748314 A CN201410748314 A CN 201410748314A CN 104479413 A CN104479413 A CN 104479413A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- heavy calcium
- grinding
- preparation
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of coating superfine heavy calcium carbonate. The preparation method is characterized by comprising the following steps: feeding a calcium carbonate coarse material with the diameter of less than 1cm into a flour mill; in weight percentage of heavy calcium carbonate coarse powder, adding 1-3% of sodium carbonate and 1-3% of dodecyl dimethyl benzyl ammonium chloride respectively; grinding to 5-10 microns at 85-95 DEG C, and then adding water to prepare a slurry with the solid content of 70-80%; in weight percentage of heavy calcium carbonate powder, adding 1-5% of a modifier; and driving the slurry into a wet method stirring grinding machine by virtue of a pump valve, and grinding in a grinding medium to obtain modified superfine calcium carbonate powder with the particle size of 0.1-1 micron. The preparation method has the advantages of scientific and reasonable design, simple process, safety, reliability, easiness in control, convenience in operation, suitability for large-scale production, low production cost and the like.
Description
Technical field
The invention belongs to a kind of production method of calcium carbonate powder.
Background technology
At present, calcium carbonate is widely used in papermaking, plastics, plastics film, chemical fibre, rubber, tackiness agent, sealing agent, daily-use chemical industry, makeup, building materials, coating, paint, ink, putty, sealing wax, putty, carpet veneer is packed, medicine, food is (as chewing gum, chocolate), in feed, its effect has: increase small product size, reduce costs, improve processing characteristics (as adjusting viscosity, rheological property, curability), improve dimensional stability, reinforcement or half reinforcement, improve printing performance, improve physicals (as thermotolerance, extinction, wear resistance, flame retardant resistance, whiteness, glossiness) etc.The technological process of production of water-ground limestone has two kinds.Dry technology for production flow process: the first calcite, Wingdale, chalk, shell etc. that ship from stone quarry of picking, to remove gangue; Then with crusher, coarse breaking is carried out to Wingdale, cover that (pendulum-type) abrasive dust is broken obtains microlith limestone flour again with thunder, finally carry out classification with grading machine to abrasive dust, the powder meeting granularity requirements is put in storage as the packing of product, otherwise returns pulverizing mill abrasive dust again.Wet process technique flow process: first dry method fine powder is made suspension and be placed in grinding machine and pulverize further, just obtained superfine heavy calcium carbonate after dehydration, drying.
Retrieve through Chinese publication, find calcium carbonate application for a patent for invention 53; Do not find the scheme identical with present patent application.
Summary of the invention
The object of the invention is to; A kind of preparation method of coating superfine heavy calcium carbonate is proposed.
The preparation method of coating superfine heavy calcium carbonate of the present invention, comprises stone fragmentation, pulverizing, grinding, screening, activation, drying, classification, and product-collecting is packed, it is characterized in that: calcium carbonate coarse fodder diameter being less than 1 centimetre, send in pulverizing mill, with the weight percent meter of coarse heavy calcium carbonate powder, add 1-3% sodium carbonate respectively, 1-3% dodecyl benzyl dimethyl ammonium chloride, after at 85 ~ 95 DEG C, grinding causes 5-10 micron, add water and be made into the slurry that solid content is 70% ~ 80%, with the weight percent meter of heavy calcium carbonate, add 1-5% and add properties-correcting agent, by pump valve, slurry is squeezed into wet method and stir disintegrating machine, grind in grinding medium, obtain the modified superfine Paris white that obtained particle diameter is 0.1 ~ 1 micron, described auxiliary agent, by weight, by 6-γ-(2,3-epoxy third oxygen) propyl trimethoxy silicane 1-3 part, ethylene glycol 3-4 part, Sodium hexametaphosphate 99 3-4 part, vinylformic acid-cationic acrylate multipolymer 3-5 part composition.
The present invention compared with prior art its beneficial effect is: have design science reasonable, and technique is simple, safe reliability, is easy to control, easy to operate, is applicable to scale operation, the advantages such as production cost is low.
Embodiment
Below in conjunction with embodiment, the invention will be further described, but embodiments of the present invention are not limited thereto.
Embodiment 1
The preparation method of coating superfine heavy calcium carbonate of the present invention, comprises stone fragmentation, pulverizing, grinding, screening, activation, drying, classification, and product-collecting is packed, it is characterized in that: calcium carbonate coarse fodder diameter being less than 1 centimetre, send in pulverizing mill, with the weight percent meter of coarse heavy calcium carbonate powder, add 1-3% sodium carbonate respectively, 1-3% dodecyl benzyl dimethyl ammonium chloride, after at 85 ~ 95 DEG C, grinding causes 5-10 micron, add water and be made into the slurry that solid content is 70% ~ 80%, with the weight percent meter of heavy calcium carbonate, add 1-5% and add properties-correcting agent, by pump valve, slurry is squeezed into wet method and stir disintegrating machine, grind in grinding medium, obtain the modified superfine Paris white that obtained particle diameter is 0.1 ~ 1 micron, described auxiliary agent, by weight, by 6-γ-(2,3-epoxy third oxygen) propyl trimethoxy silicane 1-3 part, ethylene glycol 3-4 part, Sodium hexametaphosphate 99 3-4 part, vinylformic acid-cationic acrylate multipolymer 3-5 part composition.
Embodiment 2
The preparation method of coating superfine heavy calcium carbonate of the present invention, comprises stone fragmentation, pulverizing, grinding, screening, activation, drying, classification, and product-collecting is packed, it is characterized in that: calcium carbonate coarse fodder diameter being less than 1 centimetre, send in pulverizing mill, with the weight percent meter of coarse heavy calcium carbonate powder, add 1-3% sodium carbonate respectively, 1-3% dodecyl benzyl dimethyl ammonium chloride, after at 85 ~ 95 DEG C, grinding causes 5-10 micron, add water and be made into the slurry that solid content is 70% ~ 80%, with the weight percent meter of heavy calcium carbonate, add 1-5% and add properties-correcting agent, by pump valve, slurry is squeezed into wet method and stir disintegrating machine, grind in grinding medium, obtain the modified superfine Paris white that obtained particle diameter is 0.1 ~ 1 micron, described auxiliary agent, by weight, by 6-γ-(2,3-epoxy third oxygen) propyl trimethoxy silicane 1 part, ethylene glycol 4 parts, Sodium hexametaphosphate 99 3 parts, vinylformic acid-cationic acrylate multipolymer 5 parts composition.
Embodiment 3
The preparation method of coating superfine heavy calcium carbonate of the present invention, comprises stone fragmentation, pulverizing, grinding, screening, activation, drying, classification, and product-collecting is packed, it is characterized in that: calcium carbonate coarse fodder diameter being less than 1 centimetre, send in pulverizing mill, with the weight percent meter of coarse heavy calcium carbonate powder, add 1-3% sodium carbonate respectively, 1-3% dodecyl benzyl dimethyl ammonium chloride, after at 85 ~ 95 DEG C, grinding causes 5-10 micron, add water and be made into the slurry that solid content is 70% ~ 80%, with the weight percent meter of heavy calcium carbonate, add 1-5% and add properties-correcting agent, by pump valve, slurry is squeezed into wet method and stir disintegrating machine, grind in grinding medium, obtain the modified superfine Paris white that obtained particle diameter is 0.1 ~ 1 micron, described auxiliary agent, by weight, by 6-γ-(2,3-epoxy third oxygen) propyl trimethoxy silicane 3 parts, ethylene glycol 3 parts, Sodium hexametaphosphate 99 4 parts, vinylformic acid-cationic acrylate multipolymer 3 parts composition.
Claims (1)
1. a preparation method for coating superfine heavy calcium carbonate, comprises stone fragmentation, pulverizing, grinding, screening, activation, drying, classification, and product-collecting is packed, it is characterized in that: calcium carbonate coarse fodder diameter being less than 1 centimetre, send in pulverizing mill, with the weight percent meter of coarse heavy calcium carbonate powder, add 1-3% sodium carbonate respectively, 1-3% dodecyl benzyl dimethyl ammonium chloride, after at 85 ~ 95 DEG C, grinding causes 5-10 micron, add water and be made into the slurry that solid content is 70% ~ 80%, with the weight percent meter of heavy calcium carbonate, add 1-5% and add properties-correcting agent, by pump valve, slurry is squeezed into wet method and stir disintegrating machine, grind in grinding medium, obtain the modified superfine Paris white that obtained particle diameter is 0.1 ~ 1 micron, described auxiliary agent, by weight, by 6-γ-(2,3-epoxy third oxygen) propyl trimethoxy silicane 1-3 part, ethylene glycol 3-4 part, Sodium hexametaphosphate 99 3-4 part, vinylformic acid-cationic acrylate multipolymer 3-5 part composition.