CN104479362A - Rubber roller for coiling metallized film - Google Patents
Rubber roller for coiling metallized film Download PDFInfo
- Publication number
- CN104479362A CN104479362A CN201410697022.8A CN201410697022A CN104479362A CN 104479362 A CN104479362 A CN 104479362A CN 201410697022 A CN201410697022 A CN 201410697022A CN 104479362 A CN104479362 A CN 104479362A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- carbon black
- white carbon
- micro mist
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rubber roller for coiling a metallized film. The rubber roller is prepared from the following components in parts by weight: 80-100 parts of raw methyl vinyl silicone rubber, 10-20 parts of white carbon black, 5-8 parts of methylsiloxane, 10-15 parts of silicon rubber micro powder, 1-3 parts of 1-bromopentane, 0.5-1.5 parts of tributyl borate, 2-4 parts of calcium lactate, 1-2 parts of nepeta oil and 0.5-1 part of butanone. The components are simple, the preparation process is simple and convenient to operate, and the prepared product has high quality and good use effect and meets the requirement of the use environment of a capacitor metal film rubber roller.
Description
Technical field
The present invention relates to rubber item technical field, be specifically related to a kind of metallizing film winding rubber roll.
Background technology
Silicon rubber, point heat vulcanization type (high temperature vulcanized silica gel HTV), room temperature vulcanized (RTV), wherein room temperature vulcanized divides again polycondensation reaction type and addition reaction-type.High temperature silicone rubber is mainly for the manufacture of various silastic product, and room temperature silicon rubber then mainly uses as caking agent, Embedding Material or mould.Heat vulcanization type consumption is maximum, and heat vulcanization type divides again methyl silicone rubber, methyl vinyl silicone rubber, methyl vinyl phenyl silicon rubber, and other also have eyeball silicon rubber, trifluoropropyl siloxane etc.In numerous synthetic rubber, silicon rubber is outstanding person wherein.It has tasteless nontoxic, is not afraid of high temperature and the feature resisting severe cold, and " keeping cool ", " remaining calm " when 300 degrees Celsius and subzero 90 degrees Celsius, still do not lose original intensity and elasticity.Silicon rubber also has good electrical insulating property, oxytolerant resistance to deterioration, fast light resistance to deterioration and mildew resistance, chemical stability etc.Owing to being provided with the performance of these excellences, silicon rubber is made extensively to have played vital role in modern medicine.In recent years, by hospital, R&D institution and factory's collaborate, multiple silicon rubber medical treatment product are trial-produceed successfully.The materials such as the terpolymer EP rubber that paper-feed roll uses frictional coefficient higher than silicon rubber usually, poly-propylhomoserin rubber make.Along with the development of technology, the temperature tolerance, photostabilization etc. of rubber roll are had higher requirement.
Summary of the invention
It is simple that technical problem to be solved by this invention is to provide a kind of composition, the metallizing film winding rubber roll that cost is low.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of metallizing film winding rubber roll, is made up of the component of following parts by weight: methyl vinyl silicon kautschuk 80-100 part, white carbon black 10-20 part, methylsiloxane 5-8 part, silicon rubber micro mist 10-15 part, bromo pentane 1-3 part, tributyl borate 0.5-1.5 part, calcium lactate 2-4 part, nepeta oil 1-2 part, butanone 0.5-1 part;
The better parts by weight of above-mentioned each component are: methyl vinyl silicon kautschuk 90 parts, white carbon black 15 parts, methylsiloxane 7 parts, silicon rubber micro mist 12 parts, bromo pentane 2 parts, tributyl borate 1 part, calcium lactate 3 parts, nepeta oil 1.5 parts, butanone 0.8 part;
Preparation method is as follows:
1) in methyl vinyl silicone rubber, thermal silica and methylsiloxane is added in rubber, in kneader mixing 30 minutes;
2) then within thermal treatment 3-4 hour at 170 DEG C, add silicon rubber micro mist at twice again, to continue in kneader mixing 30 minutes;
3) add bromo pentane, tributyl borate, calcium lactate, nepeta oil and butanone again in kneader mixing 30 minutes, be made into sizing material.
Described white carbon black is specific surface area is 200m
2the Meteorological Act white carbon black of/g.
Described silicon rubber micro mist is the Spherical silicone rubber micro mist of median size 10um.
The invention has the beneficial effects as follows: instant component is simple, preparation technology is simple, and convenient operation, the quality product of preparation is high, and result of use is good, meets the requirement of capacitor metal film rubber roll environment for use.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of metallizing film winding rubber roll, is made up of the component of following parts by weight: methyl vinyl silicon kautschuk 90 parts, white carbon black 15 parts, methylsiloxane 7 parts, silicon rubber micro mist 12 parts, bromo pentane 2 parts, tributyl borate 1 part, calcium lactate 3 parts, nepeta oil 1.5 parts, butanone 0.8 part;
Preparation method is as follows:
1) in methyl vinyl silicone rubber, thermal silica and methylsiloxane is added in rubber, in kneader mixing 30 minutes;
2) then within thermal treatment 3-4 hour at 170 DEG C, add silicon rubber micro mist at twice again, to continue in kneader mixing 30 minutes;
3) add bromo pentane, tributyl borate, calcium lactate, nepeta oil and butanone again in kneader mixing 30 minutes, be made into sizing material.
Described white carbon black is specific surface area is 200m
2the Meteorological Act white carbon black of/g.
Described silicon rubber micro mist is the Spherical silicone rubber micro mist of median size 10um.
Embodiment 2
A kind of metallizing film winding rubber roll, is made up of the component of following parts by weight: methyl vinyl silicon kautschuk 100 parts, white carbon black 10 parts, methylsiloxane 8 parts, silicon rubber micro mist 10 parts, bromo pentane 3 parts, tributyl borate 0.5 part, calcium lactate 4 parts, nepeta oil 1 part, butanone 1 part;
Preparation method is as follows:
1) in methyl vinyl silicone rubber, thermal silica and methylsiloxane is added in rubber, in kneader mixing 30 minutes;
2) then within thermal treatment 3-4 hour at 170 DEG C, add silicon rubber micro mist at twice again, to continue in kneader mixing 30 minutes;
3) add bromo pentane, tributyl borate, calcium lactate, nepeta oil and butanone again in kneader mixing 30 minutes, be made into sizing material.
Described white carbon black is specific surface area is 200m
2the Meteorological Act white carbon black of/g.
Described silicon rubber micro mist is the Spherical silicone rubber micro mist of median size 10um.
Embodiment 3
A kind of metallizing film winding rubber roll, is made up of the component of following parts by weight: methyl vinyl silicon kautschuk 80 parts, white carbon black 20 parts, methylsiloxane 5 parts, silicon rubber micro mist 15 parts, bromo pentane 1 part, tributyl borate 1.5 parts, calcium lactate 2 parts, nepeta oil 2 parts, butanone 0.5 part;
Preparation method is as follows:
1) in methyl vinyl silicone rubber, thermal silica and methylsiloxane is added in rubber, in kneader mixing 30 minutes;
2) then within thermal treatment 3-4 hour at 170 DEG C, add silicon rubber micro mist at twice again, to continue in kneader mixing 30 minutes;
3) add bromo pentane, tributyl borate, calcium lactate, nepeta oil and butanone again in kneader mixing 30 minutes, be made into sizing material.
Described white carbon black is specific surface area is 200m
2the Meteorological Act white carbon black of/g.
Described silicon rubber micro mist is the Spherical silicone rubber micro mist of median size 10um.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (3)
1. a metallizing film winding rubber roll, it is characterized in that, be made up of the component of following parts by weight: methyl vinyl silicon kautschuk 80-100 part, white carbon black 10-20 part, methylsiloxane 5-8 part, silicon rubber micro mist 10-15 part, bromo pentane 1-3 part, tributyl borate 0.5-1.5 part, calcium lactate 2-4 part, nepeta oil 1-2 part, butanone 0.5-1 part.
2. metallizing film winding rubber roll according to claim 1, is characterized in that: described white carbon black is specific surface area is 200m
2the Meteorological Act white carbon black of/g.
3. metallizing film winding rubber roll according to claim 1, is characterized in that: described silicon rubber micro mist is the Spherical silicone rubber micro mist of median size 10um.