CN104478485A - Opal glaze formula for electrical ceramics - Google Patents
Opal glaze formula for electrical ceramics Download PDFInfo
- Publication number
- CN104478485A CN104478485A CN201410688842.0A CN201410688842A CN104478485A CN 104478485 A CN104478485 A CN 104478485A CN 201410688842 A CN201410688842 A CN 201410688842A CN 104478485 A CN104478485 A CN 104478485A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- formula
- opal
- porcelain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an opal glaze formula for trical ceramics. The opal glaze comprises the following components in parts by weight: 41-43 parts of chinastone, 17-21 parts of zircon sand, 6-7 parts of aluminum oxide, 10-12 parts of talc, 4-8 parts of construction oil, 3-5 parts of calcium fluoride, 5-6 parts of barium carbonate and 16-18 parts of opacifier. The high-strength electrical ceramic glaze prepared by adopting the formula is high in whiteness, high in breaking strength, good in cold and hot surging resistance and stable in performance and is applied to various electricity industries.
Description
Technical field
The present invention relates to electroceramics technical field, more specifically, relate to a kind of opal glaze for electric porcelain formula.
Background technology
Electroceramics is mainly used in the transmitting line of various voltage range in power system, substation, electrical equipment, and other some special industries are as in the power system of track traffic, the conductor of different potentials or parts is connected and plays insulation and supporting function.As for the cap and pin type suspension insulator of high-voltage line tension or pendency and long rod insulator, for the solid core post insulator that substation bus bar or equipment are supported, for the hollow insulator etc. of transformer bushing, switching device, electrical condenser or mutual inductor, because relating to power industry, there is higher requirement to its mechanical property, electric property, environmental resistance (cold and hot, anti-pollution, aging etc.) and stability etc.
Summary of the invention
The object of this invention is to provide a kind of opal glaze for electric porcelain formula, the electrotechnical porcelain product stable performance that it prepares, is applicable to various power industry.
The object of the invention is achieved by the following technical programs:
A kind of opal glaze for electric porcelain formula is provided, is made up of each component of following weight fraction: porcelain stone 41 ~ 43 parts, zircon sand 17 ~ 21 parts, 6 ~ 7 parts, aluminum oxide, 10 ~ 12 parts, talcum, builds 4 ~ 8 parts, soil, 3 ~ 5 parts, Calcium Fluoride (Fluorspan), barium carbonate 5 ~ 6 parts, opacifying agent 16 ~ 18 parts.
Preferably, described opal glaze for electric porcelain formula is made up of each component of following weight fraction: porcelain stone 42 parts, zircon sand 19 parts, 6.5 parts, aluminum oxide, 11 parts, talcum, builds 6 parts, soil, 4 parts, Calcium Fluoride (Fluorspan), barium carbonate 5.5 parts, opacifying agent 17 parts.
Preferably, described opacifying agent is weisspiessglanz or titanium dioxide.
The preparation method of opaque glaze of the present invention is: take starting material by formula, to expect: water: ball=1:1:1.5 enters ball milling 8 ~ 10h, obtains glaze slip, and glaze slip fineness controls to tail over 0.03% ~ 0.06% at 325 mesh sieves.
The using method of opaque glaze of the present invention is: adopt leaching glaze mode to be blank glazing, glazed thickness controls at 0.4 ~ 0.5mm, enters after klining becomes and obtains opaque glaze electrotechnical porcelain product.
Compared with prior art, the present invention has following beneficial effect:
The invention provides a kind of opal glaze for electric porcelain formula, the opaque glaze glaze for electric porcelain colourless degree produced by this formula is greater than 75, and folding strength is greater than 160 MPa, and cold-hot shock property is greater than 240 DEG C, stable performance, is applicable to various power industry.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of opal glaze for electric porcelain formula, be made up of each component of following weight fraction: porcelain stone 42 parts, zircon sand 19 parts, 6.5 parts, aluminum oxide, 11 parts, talcum, build 6 parts, soil, 4 parts, Calcium Fluoride (Fluorspan), barium carbonate 5.5 parts, weisspiessglanz 17 parts.
Starting material are taken by formula, with material: water: ball=1:1:1.5 enters ball milling 8h, obtain glaze slip, glaze slip fineness controls to tail over 0.04% at 325 mesh sieves, adopts leaching glaze mode to be blank glazing, glazed thickness controls at 0.4mm, enter klining, obtain opaque glaze electrotechnical porcelain product, its glaze paint whiteness is 78, folding strength is 165 MPa, and cold-hot shock property is 245 DEG C.
Embodiment 2
Present embodiment discloses a kind of opal glaze for electric porcelain formula, be made up of each component of following weight fraction: porcelain stone 41 parts, zircon sand 17 parts, 7 parts, aluminum oxide, 12 parts, talcum, build 5 parts, soil, 3 parts, Calcium Fluoride (Fluorspan), barium carbonate 6 parts, weisspiessglanz 18 parts.
Starting material are taken by formula, with material: water: ball=1:1:1.5 enters ball milling 10h, obtain glaze slip, glaze slip fineness controls to tail over 0.06% at 325 mesh sieves, adopts leaching glaze mode to be blank glazing, glazed thickness controls at 0.5mm, enter klining, obtain opaque glaze electrotechnical porcelain product, its glaze paint whiteness is 76, folding strength is 162 MPa, and cold-hot shock property is 248 DEG C.
Embodiment 3
Present embodiment discloses a kind of opal glaze for electric porcelain formula, be made up of each component of following weight fraction: porcelain stone 43 parts, zircon sand 21 parts, 6 parts, aluminum oxide, 10 parts, talcum, build 4 parts, soil, 5 parts, Calcium Fluoride (Fluorspan), barium carbonate 5 parts, titanium dioxide 16 parts.
Starting material are taken by formula, with material: water: ball=1:1:1.5 enters ball milling 9h, obtain glaze slip, glaze slip fineness controls to tail over 0.03% at 325 mesh sieves, adopts leaching glaze mode to be blank glazing, glazed thickness controls at 0.45mm, enter klining, obtain opaque glaze electrotechnical porcelain product, its glaze paint whiteness is 77, folding strength is 161 MPa, and cold-hot shock property is 250 DEG C.
Embodiment 4
Present embodiment discloses a kind of opal glaze for electric porcelain formula, be made up of each component of following weight fraction: porcelain stone 41 parts, zircon sand 18 parts, 6 parts, aluminum oxide, 12 parts, talcum, build 7 parts, soil, 4 parts, Calcium Fluoride (Fluorspan), barium carbonate 6 parts, titanium dioxide 167 parts.
Starting material are taken by formula, with material: water: ball=1:1:1.5 enters ball milling 8h, obtain glaze slip, glaze slip fineness controls to tail over 0.05% at 325 mesh sieves, adopts leaching glaze mode to be blank glazing, glazed thickness controls at 0.4mm, enter klining, obtain opaque glaze electrotechnical porcelain product, its glaze paint whiteness is 76, folding strength is 162MPa, and cold-hot shock property is 246 DEG C.
Obviously, the above embodiment of the present invention is only for example of the present invention is clearly described, and is not the restriction to embodiments of the present invention.For those of ordinary skill in the field, can also make other changes in different forms on the basis of the above description.Here exhaustive without the need to also giving all embodiments.All any amendments done within the spirit and principles in the present invention, equivalent to replace and improvement etc., within the protection domain that all should be included in the claims in the present invention.
Claims (3)
1. an opal glaze for electric porcelain formula, is characterized in that, is made up of each component of following weight fraction: porcelain stone 41 ~ 43 parts, zircon sand 17 ~ 21 parts, 6 ~ 7 parts, aluminum oxide, 10 ~ 12 parts, talcum, builds 4 ~ 8 parts, soil, 3 ~ 5 parts, Calcium Fluoride (Fluorspan), barium carbonate 5 ~ 6 parts, opacifying agent 16 ~ 18 parts.
2. according to the opal glaze for electric porcelain formula described in claim 1, it is characterized in that, be made up of each component of following weight fraction: porcelain stone 42 parts, zircon sand 19 parts, 6.5 parts, aluminum oxide, 11 parts, talcum, builds 6 parts, soil, 4 parts, Calcium Fluoride (Fluorspan), barium carbonate 5.5 parts, opacifying agent 17 parts.
3. the opal glaze for electric porcelain formula according to claim 1 or 2, is characterized in that, described opacifying agent is weisspiessglanz or titanium dioxide.