CN104451316A - 高塑性锻压用镁合金材料及其制备方法 - Google Patents

高塑性锻压用镁合金材料及其制备方法 Download PDF

Info

Publication number
CN104451316A
CN104451316A CN201410843599.5A CN201410843599A CN104451316A CN 104451316 A CN104451316 A CN 104451316A CN 201410843599 A CN201410843599 A CN 201410843599A CN 104451316 A CN104451316 A CN 104451316A
Authority
CN
China
Prior art keywords
forging
magnesium alloy
ductility
preparation
stamping
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410843599.5A
Other languages
English (en)
Other versions
CN104451316B (zh
Inventor
翟慎宝
孙启明
柴韶春
王鲁东
石宪柱
岳明
吕丽丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZIBO HONGTAI ANTISEPTIC CO Ltd
Original Assignee
ZIBO HONGTAI ANTISEPTIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZIBO HONGTAI ANTISEPTIC CO Ltd filed Critical ZIBO HONGTAI ANTISEPTIC CO Ltd
Priority to CN201410843599.5A priority Critical patent/CN104451316B/zh
Publication of CN104451316A publication Critical patent/CN104451316A/zh
Application granted granted Critical
Publication of CN104451316B publication Critical patent/CN104451316B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高塑性锻压用镁合金材料及其制备方法，高塑性锻压用镁合金材料的化学成份如下：Y:1-2％，Zn:1-3％，Nd：0.3-1％，Zr:0.1-0.5％，Fe<0.01，Si<0.02，Cu<0.01，Ni<0.001，余量为镁。本发明所述的高塑性锻压用镁合金材料及其制备方法，具有高塑性、易锻压的特性，大大降低了镁合金在锻压过程中的成本投入。

Description

高塑性锻压用镁合金材料及其制备方法
技术领域
本发明涉及一种高塑性锻压用镁合金材料及其制备方法。
发明背景
镁合金是较轻的金属结构材料，具有较高的比轻度和比刚度，良好的阻尼、电磁屏蔽和尺寸稳定性，易加工、可回收。近年来，镁合金在汽车、3C、交通运输、家用电器等方面应用增长迅速。
锻造镁合金与传统的铸造镁合金相比，有更高的强度、更好的延展性和更多样化的力学性能。但是，近年来，镁合金的锻压产品进用在很少的几个方面，主要原因是镁合金的自身塑变特性决定其难以锻造成型，制造成本高，价格昂贵。锻压用镁合金的研究越来越受重视。发明内容
本发明所述的高塑性锻压用镁合金材料及其制备方法，具有高塑性、易锻压的特性，大大降低了镁合金在锻压过程中的成本投入。
高塑性锻压用镁合金材料的化学成份如下：
Y:1-2％，Zn:1-3％，Nd：0.3-1％，Zr:0.1-0.5％，Fe<0.01，Si<0.02，Cu<0.01，Ni<0.001，余量为镁。
高塑性锻压用镁合金材料的制备方法，取镁锭熔化，将温度控制在690‐700℃，加入总重1‐3％的纯锌，充分搅拌，然后调节温度至720‐750℃，加入总重0.5‐2％的Mg‐Zr中间合金，然后将温度调节为720‐730℃，加入总重5‐10％的Mg‐Y中间合金和总重1‐5％的Mg‐Nd中间合金，充分搅拌后，保温40min‐1h，然后将温度调整为690‐710℃，除渣后浇铸。
Mg‐Zr中间合金中Zr的质量含量为30％。
Mg‐Y中间合金中Y的质量含量为30％。
Mg‐Nd中间合金中Nd的质量含量为30％。
高塑性锻压用镁合金材料铸锭的力学性能如下：
抗拉强度260-340Mpa，断后延伸率20-30％，晶粒度<30μm。
与现有技术相比，本发明具有以下有益效果：
本发明所述的高塑性锻压用镁合金材料及其制备方法，具有高塑性、易锻压的特性，大大降低了镁合金在锻压过程中的成本投入。
具体实施方式
下面结合实施例对本发明做进一步的说明。
实施例1
高塑性锻压用镁合金材料的制备方法：
取牌号为Mg99.85(符合GB5153)的镁锭，熔化，将温度控制在690-700℃，加入总重2％的纯锌，充分搅拌，然后调节温度至740±3℃，加入总重0.5％的Mg-Zr中间合金(Zr质量含量为30％)然后将温度调节为720±3℃，加入总重10％的Mg-Y中间合金(Y质量含量为30％)和总重1％的Mg-Nd中间合金(Nd质量含量为30％)，充分搅拌后，保温50min，然后将温度调整为710±3℃，除渣后开始浇铸。
实施例2
高塑性锻压用镁合金材料的制备方法：
取牌号为Mg99.85(符合GB5153)的镁锭，熔化，将温度控制在690-700℃，加入总重3％的纯锌，充分搅拌，然后调节温度至720±3℃，加入总重2％的Mg-Zr中间合金(Zr质量含量为30％)然后将温度调节为730±3℃，加入总重5％的Mg-Y中间合金(Y质量含量为30％)和总重1％的Mg-Nd中间合金(Nd质量含量为30％)，充分搅拌后，保温1h，然后将温度调整为700±3℃，除渣后开始浇铸。
实施例3
高塑性锻压用镁合金材料的制备方法：
取牌号为Mg99.85(符合GB5153)的镁锭，熔化，将温度控制在690-700℃，加入总重2％的纯锌，充分搅拌，然后调节温度至750±3℃，加入总重1％的Mg-Zr中间合金(Zr质量含量为30％)然后将温度调节为725±3℃，加入总重8％的Mg-Y中间合金(Y质量含量为30％)和总重1-5％的Mg-Nd中间合金(Nd质量含量为30％)，充分搅拌后，保温40min，然后将温度调整为690±3℃，除渣后开始浇铸。
实施例1-3的高塑性锻压用镁合金材料的化学成份如下：
Y:1-2％，Zn:1-3％，Nd：0.3-1％，Zr:0.1-0.5％，Fe<0.01，Si<0.02，Cu<0.01，Ni<0.001，余量为镁。
高塑性锻压用镁合金材料铸锭的力学性能如下：
抗拉强度260-340Mpa，断后延伸率20-30％，晶粒度<30μm。

Claims (6)

1.一种高塑性锻压用镁合金材料，其特征在于，原料化学成份重量百分比如下：
Y:1-2％，Zn:1-3％，Nd：0.3-1％，Zr:0.1-0.5％，Fe<0.01，Si<0.02，Cu<0.01，Ni<0.001，余量为镁。
2.根据权利要求1所述的高塑性锻压用镁合金材料，其特征在于，高塑性锻压用镁合金材料铸锭的力学性能如下：
抗拉强度260-340Mpa，断后延伸率20-30％，晶粒度<30μm。
3.一种权利要求1所述的高塑性锻压用镁合金材料的制备方法，其特征在于，取镁锭熔化，将温度控制在690-700℃，加入总重1-3％的纯锌，充分搅拌，然后调节温度至720-750℃，加入总重0.5-2％的Mg-Zr中间合金，然后将温度调节为720-730℃，加入总重5-10％的Mg-Y中间合金和总重1-5％的Mg-Nd中间合金，充分搅拌后，保温40min-1h，然后将温度调整为690-710℃，除渣后浇铸。
4.根据权利要求3所述的高塑性锻压用镁合金材料的制备方法，其特征在于，Mg-Zr中间合金中Zr的质量含量为30％。
5.根据权利要求3所述的高塑性锻压用镁合金材料的制备方法，其特征在于，Mg-Y中间合金中Y的质量含量为30％。
6.根据权利要求3所述的高塑性锻压用镁合金材料的制备方法，其特征在于，Mg-Nd中间合金中Nd的质量含量为30％。
CN201410843599.5A 2014-12-30 2014-12-30 高塑性锻压用镁合金材料及其制备方法 Active CN104451316B (zh)