CN104450045A - 一种耐腐蚀脂型防锈油及其制备方法 - Google Patents
一种耐腐蚀脂型防锈油及其制备方法 Download PDFInfo
- Publication number
- CN104450045A CN104450045A CN201410626813.1A CN201410626813A CN104450045A CN 104450045 A CN104450045 A CN 104450045A CN 201410626813 A CN201410626813 A CN 201410626813A CN 104450045 A CN104450045 A CN 104450045A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- grease type
- stir
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐腐蚀脂型防锈油，其特征在于，由下列重量份的原料制成：n32机械油16-20、灯用煤油12-15、十二烯基丁二酸4-6、二壬基萘磺酸钡3-5.5、聚甲基丙烯酸十四酯1-3、聚乙烯粉末2.5-3.5、凡士林48-55、二甲硅油12-14、橄榄油2-4、尼泊金丁酯1-1.5、对氨基苯磺酸钠1-2、乙二醇脂肪酸酯1-2、保护剂5-7；本发明通过特殊工艺将多种防锈成分制成脂型，防锈效果显著，而且添加尼泊金丁酯，耐腐蚀，品质稳定，耐久性好；添加保护剂，具有良好的防水润滑效果，能够在金属表面形成牢固的疏水膜，防止水和氧的侵蚀导致生锈；本发明可用作金属的长期封存或者金属紧固件防锈，使用方便。
Description
技术领域
本发明涉及防锈液领域，特别是一种耐腐蚀脂型防锈油及其制备方法。
背景技术
如今的防锈油的种类很多，但是也存在的问题，比如耐腐蚀、耐久性、粘着性不好，容易出现变硬、脱落、开裂的现象，因此不断提高防锈油的综合质量对于社会发展也具有很好的促进意义。为保护金属不受环境中的腐蚀介质腐蚀，工程建设中通常使用防锈脂使金属表面与腐蚀介质隔离。使用防锈脂作为暂时性防护是一种较理想、有效的防腐方法，具有效果好、使用方便、成本低廉、操作简便和易去除的优点。
本发明通过研究，生产中一种脂型防锈油，通过添加特制的保护剂，具有良好的防水润滑效果，能够在金属表面形成牢固的疏水膜，防止水和氧的侵蚀导致生锈；而且配方采用防腐配方，使用寿命长，不会造成因自身腐败对金属造成锈蚀，而且防锈时间长，而且使用方便，冷涂、热涂均可。
发明内容
本发明的目的是提供一种耐腐蚀脂型防锈油及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种耐腐蚀脂型防锈油，由下列重量份的原料制成：n32机械油16-20、灯用煤油12-15、十二烯基丁二酸4-6、二壬基萘磺酸钡3-5.5、聚甲基丙烯酸十四酯1-3、聚乙烯粉末2.5-3.5、凡士林48-55、二甲硅油12-14、橄榄油2-4、尼泊金丁酯1-1.5、对氨基苯磺酸钠1-2、乙二醇脂肪酸酯1-2、保护剂5-7；
所述的保护剂由以下重量份的原料制备而成：聚羟乙基硅氧烷乳液8-11、聚乙烯醇缩丁醛3-5、天然胶乳5-7、石墨乳3-5、有机膨润土2-4、氢化蓖麻油4-6、十二烷基聚氧乙烯醚 2-3、E-12环氧树脂19-22、苯甲醇4-6、尿素2-3、棕榈酸异丙酯3-4、亚油酸钠1-2；制备方法是首先将石墨乳与有机膨润土混合后加入氢化蓖麻油，搅拌研磨60-80分钟，形成分散体；然后将E-12环氧树脂、苯甲醇、尿素、天然胶乳混合，加热至85℃-110℃搅拌反应2-3小时，再降温至60℃-70℃，加入其余剩余成分，以300-500转/分的速度搅拌20-30分钟；最后冷却至室温，加入分散体，充分搅拌均匀即得保护剂。
本发明所述一种耐腐蚀脂型防锈油，由以下具体步骤制成：
（1）将n32机械油、灯用煤油放在研钵中，加入二甲硅油、橄榄油，分次加入凡士林，研磨均匀形成糊状物；
（2）聚甲基丙烯酸十四酯、聚乙烯粉末混合，加热至90℃-110℃，保温20-30分钟，然后降温至65℃-75℃，加入十二烯基丁二酸、二壬基萘磺酸钡，继续搅拌15-25分钟；
（3）将步骤（1）糊状物与步骤（2）混合，加入保护剂，以200-300转/分的速度搅拌30-40分钟，然后加入其余剩余成分，加热至60℃-80℃，继续搅拌1.5-2小时，然后冷去至室温即得本发明防锈脂。
本发明的优异效果是：本发明通过特殊工艺将多种防锈成分制成脂型，防锈效果显著，而且添加尼泊金丁酯，耐腐蚀，品质稳定，耐久性好；添加保护剂，具有良好的防水润滑效果，能够在金属表面形成牢固的疏水膜，防止水和氧的侵蚀导致生锈；本发明可用作金属的长期封存或者金属紧固件防锈，使用方便。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种耐腐蚀脂型防锈油，由下列重量份（公斤）的原料制成：n32机械油16、灯用煤油12、十二烯基丁二酸4、二壬基萘磺酸钡3、聚甲基丙烯酸十四酯1、聚乙烯粉末2.5、凡士林48、二甲硅油12、橄榄油2、尼泊金丁酯1、对氨基苯磺酸钠1、乙二醇脂肪酸酯1、保护剂5；
所述的保护剂由以下重量份（公斤）的原料制备而成：聚羟乙基硅氧烷乳液8、聚乙烯醇缩丁醛3、天然胶乳5、石墨乳3、有机膨润土2、氢化蓖麻油4、十二烷基聚氧乙烯醚 2、E-12环氧树脂19、苯甲醇4、尿素2、棕榈酸异丙酯3、亚油酸钠1；制备方法是首先将石墨乳与有机膨润土混合后加入氢化蓖麻油，搅拌研磨60-80分钟，形成分散体；然后将E-12环氧树脂、苯甲醇、尿素、天然胶乳混合，加热至85℃-110℃搅拌反应2-3小时，再降温至60℃-70℃，加入其余剩余成分，以300-500转/分的速度搅拌20-30分钟；最后冷却至室温，加入分散体，充分搅拌均匀即得保护剂。
本发明所述一种耐腐蚀脂型防锈油，由以下具体步骤制成：
（1）将n32机械油、灯用煤油放在研钵中，加入二甲硅油、橄榄油，分次加入凡士林，研磨均匀形成糊状物；
（2）聚甲基丙烯酸十四酯、聚乙烯粉末混合，加热至90℃-110℃，保温20-30分钟，然后降温至65℃-75℃，加入十二烯基丁二酸、二壬基萘磺酸钡，继续搅拌15-25分钟；
（3）将步骤（1）糊状物与步骤（2）混合，加入保护剂，以200-300转/分的速度搅拌30-40分钟，然后加入其余剩余成分，加热至60℃-80℃，继续搅拌1.5-2小时，然后冷去至室温即得本发明防锈脂。
本发明制成的脂型防锈油外观为光滑均匀的油膏，可以室温涂覆或加热涂覆，耐盐雾实验：在温度为35℃，经过150 小时，45#钢无腐蚀 ；耐湿热实验：在温度为50℃，经过700小时，45#钢无腐蚀。
Claims (2)
1.一种耐腐蚀脂型防锈油，其特征在于，由下列重量份的原料制成：n32机械油16-20、灯用煤油12-15、十二烯基丁二酸4-6、二壬基萘磺酸钡3-5.5、聚甲基丙烯酸十四酯1-3、聚乙烯粉末2.5-3.5、凡士林48-55、二甲硅油12-14、橄榄油2-4、尼泊金丁酯1-1.5、对氨基苯磺酸钠1-2、乙二醇脂肪酸酯1-2、保护剂5-7；
所述的保护剂由以下重量份的原料制备而成：聚羟乙基硅氧烷乳液8-11、聚乙烯醇缩丁醛3-5、天然胶乳5-7、石墨乳3-5、有机膨润土2-4、氢化蓖麻油4-6、十二烷基聚氧乙烯醚 2-3、E-12环氧树脂19-22、苯甲醇4-6、尿素2-3、棕榈酸异丙酯3-4、亚油酸钠1-2；制备方法是首先将石墨乳与有机膨润土混合后加入氢化蓖麻油，搅拌研磨60-80分钟，形成分散体；然后将E-12环氧树脂、苯甲醇、尿素、天然胶乳混合，加热至85℃-110℃搅拌反应2-3小时，再降温至60℃-70℃，加入其余剩余成分，以300-500转/分的速度搅拌20-30分钟；最后冷却至室温，加入分散体，充分搅拌均匀即得保护剂。
2.根据权利要求1所述一种耐腐蚀脂型防锈油，其特征在于，由以下具体步骤制成：
（1）将n32机械油、灯用煤油放在研钵中，加入二甲硅油、橄榄油，分次加入凡士林，研磨均匀形成糊状物；
（2）聚甲基丙烯酸十四酯、聚乙烯粉末混合，加热至90℃-110℃，保温20-30分钟，然后降温至65℃-75℃，加入十二烯基丁二酸、二壬基萘磺酸钡，继续搅拌15-25分钟；
（3）将步骤（1）糊状物与步骤（2）混合，加入保护剂，以200-300转/分的速度搅拌30-40分钟，然后加入其余剩余成分，加热至60℃-80℃，继续搅拌1.5-2小时，然后冷去至室温即得本发明防锈脂。