CN104450005A - Castor-based biodegradable plastic composite lithium base lubricating grease composition - Google Patents
Castor-based biodegradable plastic composite lithium base lubricating grease composition Download PDFInfo
- Publication number
- CN104450005A CN104450005A CN201410653255.8A CN201410653255A CN104450005A CN 104450005 A CN104450005 A CN 104450005A CN 201410653255 A CN201410653255 A CN 201410653255A CN 104450005 A CN104450005 A CN 104450005A
- Authority
- CN
- China
- Prior art keywords
- castor
- oil plant
- base
- plastic cement
- degradable plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a castor-based biodegradable plastic composite lithium base lubricating grease composition. Poly-internal-olefin and castor-based diisodecyl sebacate are compounded to serve as base oil, and multiple composite additives including 12-hydroxystearic acid, an antioxidant, aids, lithium hydrate, a viscosity-temperature characteristic modifier, a light stabilizer, a mildew preventive, an antistatic agent, a light screener and a reinforcing agent are also used. The lubricating grease composition disclosed by the invention has good compatibility with plastic products, lubricating property, stability, durability, low diffusivity, stability and wide application temperature range, does not corrode metal materials, and does not cause bad contact of contact points.
Description
Technical field
The invention belongs to lubricating grease field, particularly a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite.
Background technology
The features such as plastics and matrix material tool light weight, inexpensive, rotational noise is little, production process is few, its intensity, close to metallic substance, can substitute non-ferrous metal and alloy use under many circumstances.Compared with common metal, plastics have special rubbing characteristics.Because the mechanical property variation range of plastics is very wide, and with intensity, rate of deformation and the failure procedure susceptibility to envrionment conditions, therefore comparatively metal is much complicated for the wear process of plastics.The interaction process of this complexity it has been generally acknowledged that: adhesive wear, chemical abrasion, abrasive wear and fatigue wear.Plastics also have certain self-lubricating property.The self-lubricating theory of engineering plastics has fully been confirmed and has been applied in engineering practice.But at present in the application scenario of many oil-free lubricatoins, engineering plastics exist that some are significantly not enough.As plastic gear mechanism etc. often cannot reach the work-ing life of expection, thus have impact on the application of plastic paste.This selection mainly due to plastic paste is improper, or lubricating grease select improper caused by.Plastic friction pair nearly all except only a few special plastic needs proper lubrication material to lubricate, otherwise the serious wearing and tearing of generation is even lost efficacy.Therefore, use lubricating grease to be harmful to very much indiscriminately.Therefore, be necessary to develop a kind of have good with plasthetics consistency, oilness, stability, weather resistance, low diffustivity, stability, wider use temperature scope, the castor-oil plant base degradable plastic cement compound lithium base grease composite of the loose contact corrosion-free to metallic substance, point of contact can not be caused.
Summary of the invention
The technical problem to be solved in the present invention be to provide a kind of have good with plasthetics consistency, oilness, stability, weather resistance, low diffustivity, stability, wider use temperature scope, the castor-oil plant base degradable plastic cement compound lithium base grease composite of the loose contact corrosion-free to metallic substance, point of contact can not be caused.
For solving the problems of the technologies described above, the present invention adopts following technical scheme:
A kind of castor-oil plant base degradable plastic cement compound lithium base grease composite, adopt oil based on poly-internal olefin and castor-oil plant base DI(2ETHYLHEXYL)SEBACATE compound, coordinate multiple composite additive, the mass percent of its each component is:
Component | Mass percent content |
Base oil | Surplus |
12-oxystearic acid | 12.0% |
Oxidation inhibitor | 1.5%~2.0% |
Auxiliary agent | 2.5%~4.0% |
Lithium hydroxide | 15.0%~17.0% |
Viscosity-temperature characteristics improving agent | 3.0%~4.0% |
Photostabilizer | 0.1%~0.5% |
Mould inhibitor | 0.1%~0.3% |
Static inhibitor | 0.1%~1.0% |
Photomask agent | 1.0%~3.0% |
Strengthening agent | 0.1%~0.3% |
Base oil is poly-internal olefin and 50% ~ 30% castor-oil plant base DI(2ETHYLHEXYL)SEBACATE compound of mass ratio 50% ~ 70%.The phenyl-a-naphthylamine of oxidation inhibitor mass ratio 60% ~ 50% and the 2,4,6-trimethyl phenol compound of 40% ~ 50%.Auxiliary agent is castor-oil plant base sebacic acid; Lithium hydroxide is Lithium Hydroxide Monohydrate, and molecular formula is LiOHH
2o.Viscosity-temperature characteristics improving agent is polyisobutene.Photostabilizer is 2-hydroxyl-4-octyloxybenzophenone.Mould inhibitor is copper 8-quinolinolate.Static inhibitor is alkyl imidazoline.Photomask agent is titanium white.Strengthening agent is Sodium Nitrite.
Remarkable advantage of the present invention has: good with plasthetics consistency, oilness, stability, weather resistance, low diffustivity, stability, wider use temperature scope, the loose contact corrosion-free to metallic substance, point of contact can not be caused.
Embodiment
Embodiment 1:
Each component of following masses percentage ratio is in harmonious proportion and forms:
Component | Content (mass percent) |
The poly-internal olefin of mass ratio 50% and 50% castor-oil plant base DI(2ETHYLHEXYL)SEBACATE compound | 64.6% |
12-oxystearic acid | 12.0% |
The phenyl-a-naphthylamine of mass ratio 60% and the 2,4,6-trimethyl phenol compound of 40% | 1.5% |
Castor-oil plant base sebacic acid | 2.5% |
Lithium Hydroxide Monohydrate, molecular formula is LiOHH 2O | 15.0% |
Polyisobutene | 3.0% |
2-hydroxyl-4-octyloxybenzophenone (uv-531) | 0.1% |
Copper 8-quinolinolate | 0.1% |
Alkyl imidazoline | 0.1% |
Titanium white | 1.0% |
Sodium Nitrite | 0.1% |
Embodiment 2:
Each component of following masses percentage ratio is in harmonious proportion and forms:
Component | Content (mass percent) |
The poly-internal olefin of mass ratio 60% and 40% castor-oil plant base DI(2ETHYLHEXYL)SEBACATE compound | 60.05% |
12-oxystearic acid | 12.0% |
The phenyl-a-naphthylamine of mass ratio 55% and the 2,4,6-trimethyl phenol compound of 45% | 1.75% |
Castor-oil plant base sebacic acid | 3.5% |
Lithium Hydroxide Monohydrate, molecular formula is LiOHH 2O | 16.0% |
Polyisobutene | 3.5% |
2-hydroxyl-4-octyloxybenzophenone (uv-531) | 0.3% |
Copper 8-quinolinolate | 0.2% |
Alkyl imidazoline | 0.5% |
Titanium white | 2.0% |
Sodium Nitrite | 0.2% |
Embodiment 3:
Each component of following masses percentage ratio is in harmonious proportion and forms:
Component | Content (mass percent) |
The poly-internal olefin of mass ratio 70% and 30% castor-oil plant base DI(2ETHYLHEXYL)SEBACATE compound | 55.9% |
12-oxystearic acid | 12.0% |
The phenyl-a-naphthylamine of mass ratio 50% and the 2,4,6-trimethyl phenol compound of 50% | 2.0% |
Castor-oil plant base sebacic acid | 4.0% |
Lithium Hydroxide Monohydrate, molecular formula is LiOHH 2O | 17.0% |
Polyisobutene | 4.0% |
2-hydroxyl-4-octyloxybenzophenone (uv-531) | 0.5% |
Copper 8-quinolinolate | 0.3% |
Alkyl imidazoline | 1.0% |
Titanium white | 3.0% |
Sodium Nitrite | 0.3% |
The key technical indexes of embodiment 1 product:
Project | Quality index |
Drawing cone in-degree/0.1mm | 323 |
Dropping point/DEG C | 253 |
Water drenches number of dropouts (38 DEG C, 4h)/% | 9 |
Wastage (104 DEG C, 6h) | 4.5 |
Extreme pressure property (four-ball tester method P D),N | 3189 |
ZMZ | 451 |
Extreme pressure property (terraced Mu Kenfa) OK value/N | 166 |
Anticorrosion test (52 DEG C, 48h), level | 1 |
Extend Drawing cone in-degree velocity of variation/%, 100000 times | 17 |
Volatile grade (180 DEG C, 1h) | 4 |
Stencil oil-dividing (100 DEG C, 24h) | 4 |
Oxidation stability Pressure Drop (99 DEG C, 100h, 0.770MPa)/MPa | 0.070 |
Corrosion (T 2Copper sheet, 100 DEG C, 24h) | Copper sheet redgreen or black |
The key technical indexes of embodiment 2 product:
Project | Quality index |
Drawing cone in-degree/0.1mm | 326 |
Dropping point/DEG C | 255 |
Water drenches number of dropouts (38 DEG C, 4h)/% | 8 |
Wastage (104 DEG C, 6h) | 4.9 |
Extreme pressure property (four-ball tester method P D),N | 3195 |
ZMZ | 458 |
Extreme pressure property (terraced Mu Kenfa) OK value/N | 169 |
Anticorrosion test (52 DEG C, 48h), level | 1 |
Extend Drawing cone in-degree velocity of variation/%, 100000 times | 18 |
Volatile grade (180 DEG C, 1h) | 4 |
Stencil oil-dividing (100 DEG C, 24h) | 4 |
Oxidation stability Pressure Drop (99 DEG C, 100h, 0.770MPa)/MPa | 0.071 |
Corrosion (T 2Copper sheet, 100 DEG C, 24h) | Copper sheet redgreen or black |
The key technical indexes of embodiment 3 product:
Project | Quality index |
Drawing cone in-degree/0.1mm | 319 |
Dropping point/DEG C | 263 |
Water drenches number of dropouts (38 DEG C, 4h)/% | 10 |
Wastage (104 DEG C, 6h) | 4.3 |
Extreme pressure property (four-ball tester method P D),N | 3181 |
ZMZ | 449 |
Extreme pressure property (terraced Mu Kenfa) OK value/N | 169 |
Anticorrosion test (52 DEG C, 48h), level | 1 |
Extend Drawing cone in-degree velocity of variation/%, 100000 times | 16 |
Volatile grade (180 DEG C, 1h) | 4 |
Stencil oil-dividing (100 DEG C, 24h) | 4 |
Oxidation stability Pressure Drop (99 DEG C, 100h, 0.770MPa)/MPa | 0.073 |
Corrosion (T 2Copper sheet, 100 DEG C, 24h) | Copper sheet redgreen or black |
Claims (10)
1. a castor-oil plant base degradable plastic cement compound lithium base grease composite, is characterized in that: adopt oil based on poly-internal olefin and castor-oil plant base DI(2ETHYLHEXYL)SEBACATE compound, coordinate multiple composite additive, the mass percent of its each component is:
。
2. a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite according to claim 1, is characterized in that, base oil is poly-internal olefin and 50% ~ 30% castor-oil plant base DI(2ETHYLHEXYL)SEBACATE compound of mass ratio 50% ~ 70%.
3. a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite according to claim 1, is characterized in that, the phenyl-a-naphthylamine of oxidation inhibitor mass ratio 60% ~ 50% and the 2,4,6-trimethyl phenol compound of 40% ~ 50%.
4. a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite according to claim 1, it is characterized in that, auxiliary agent is castor-oil plant base sebacic acid; Lithium hydroxide is Lithium Hydroxide Monohydrate, and molecular formula is LiOHH
2o.
5. a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite according to claim 1, it is characterized in that, viscosity-temperature characteristics improving agent is polyisobutene.
6. a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite according to claim 1, is characterized in that, photostabilizer is 2-hydroxyl-4-octyloxybenzophenone.
7. a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite according to claim 1, it is characterized in that, mould inhibitor is copper 8-quinolinolate.
8. a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite according to claim 1, it is characterized in that, static inhibitor is alkyl imidazoline.
9. a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite according to claim 1, it is characterized in that, photomask agent is titanium white.
10. a kind of castor-oil plant base degradable plastic cement compound lithium base grease composite according to claim 1, it is characterized in that, strengthening agent is Sodium Nitrite.