CN104449755A - 一种疏水性沙子及其制备方法 - Google Patents
一种疏水性沙子及其制备方法 Download PDFInfo
- Publication number
- CN104449755A CN104449755A CN201410599667.8A CN201410599667A CN104449755A CN 104449755 A CN104449755 A CN 104449755A CN 201410599667 A CN201410599667 A CN 201410599667A CN 104449755 A CN104449755 A CN 104449755A
- Authority
- CN
- China
- Prior art keywords
- sand
- mixed solution
- employ
- continued
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种疏水性沙子,由下述原料组成:沙粒、热固性酚醛树脂、糠醇树脂、甲基硅酸钠、环氧树脂、缩醛树脂、丙酮、邻苯二甲酸二丁酯、乙二胺、硅烷偶联剂,将上述各组分按科学的顺序和方法进行混合、加热、冷却、风干等处理,最终得到本发明的疏水性沙子,本发明的疏水性沙子疏水性好,无毒、无害、无污染,可重复利用,节省资源。
Description
技术领域
本发明涉及土壤改良领域,具体涉及一种疏水性沙子及其制备方法。
背景技术
目前改良土壤的肥料或改良剂,虽然能起到改良土壤的作用,但是这些肥料或改良剂的透气性、疏水性和分解效果差,不能有效地分解天然形成的各种纤维和人工合成的部分化学物质,且肥料的肥效或改良剂的改良性能不能持久,投入就会增加,不适合长期使用。
发明内容
本发明的目的在于克服现有技术中存在的不足而提供一种疏水性沙子及其制备方法。
本发明的技术方案是这样实现的:
一种疏水性沙子,由下述重量配比的原料组成:沙粒90%-~94%,热固性酚醛树脂1%~3%,糠醇树脂1%~3%,甲基硅酸钠1%~5%,环氧树脂1%~3%,缩醛树脂0.5%~1.5%,丙酮0.4%~1.2%,邻苯二甲酸二丁酯0.05%~0.2%,乙二胺0.03%~0.08%,硅烷偶联剂0.02%~0.05%。
一种疏水性沙子的制备方法,包括以下步骤:
步骤1)筛选,挑选纯净无土的粒度为0.5mm~1.5mm的沙粒;
步骤2)将上述重量配比的环氧树脂加入到糠醇树脂中,混合均匀,得到的混合物留用;
步骤3)将缩醛树脂加入到丙酮内,搅拌,溶解,混合,得到的混合液留用;
步骤4)将步骤2)中得到的混合物加入步骤3)所得的混合液中,搅拌,溶解,得到的混合液留用;
步骤5)将邻苯二甲酸二丁酯和硅烷偶联剂加入步骤4)所得的混合液中,搅拌,得到的混合液留用;
步骤6)将热固性酚醛树脂加入步骤5)所得的混合液中,搅拌,所得到的混合液留用;
步骤7)将乙二胺加入步骤6)所得的混合液中,搅拌均匀,所得到的混合液留用;
步骤8)在上述步骤7)中得到的混合液中加入挑选好的沙子,混合后放入搅拌机中,边搅拌边固化,每20分钟搅拌一次,每次搅拌10分钟,4小时后停止搅拌,沙子被包覆上一层混合树脂;
步骤9)将步骤8)所得到的沙子放入烤箱或炉子内加热,加热温度为120℃~180℃,加热时间为2~3小时;
步骤10)取出上述步骤8)中加热后的沙子自然冷却至常温;
步骤11)将冷却后的沙子放入破碎机内粉碎;
步骤12)过筛,选出粒度为16mm~30mm的沙子;
步骤13)在甲基硅酸钠中添加处理剂,处理剂为乙醇,再加入30%~70%的水,使乙醇和甲基硅酸钠充分混合并搅拌均匀;
步骤14)将步骤12)中得到的沙子加入到步骤13)所得的混合液内,浸湿沙子;
步骤15)将步骤14)中浸湿后的沙子风干后加热,加热温度为40℃~80℃,加热时间为3~4小时;
步骤16)将上述步骤15)处理后的沙子自然冷却后即可。
本发明具有以下积极效果:本发明采用科学的方法,制得的疏水性沙子有以下优点:一、疏水性好,透气不透水;二、无毒、无害、无污染;三、可重复利用,且耐水冲、耐火烧、抗老化;四、温室大棚和室外土地均可使用。
具体实施方式
一种疏水性沙子,由下述重量配比的原料组成:沙粒90%-~94%,热固性酚醛树脂1%~3%,糠醇树脂1%~3%,甲基硅酸钠1%~5%,环氧树脂1%~3%,缩醛树脂0.5%~1.5%,丙酮0.4%~1.2%,邻苯二甲酸二丁酯0.05%~0.2%,乙二胺0.03%~0.08%,硅烷偶联剂0.02%~0.05%。
一种疏水性沙子的制备方法,包括以下步骤:
步骤1)筛选,挑选纯净无土的粒度为0.5mm~1.5mm的沙粒;
步骤2)将上述重量配比的环氧树脂加入到糠醇树脂中,混合均匀,得到的混合物留用;
步骤3)将缩醛树脂加入到丙酮内,搅拌,溶解,混合,得到的混合液留用;
步骤4)将步骤2)中得到的混合物加入步骤3)所得的混合液中,搅拌,溶解,得到的混合液留用;
步骤5)将邻苯二甲酸二丁酯和硅烷偶联剂加入步骤4)所得的混合液中,搅拌,得到的混合液留用;
步骤6)将热固性酚醛树脂加入步骤5)所得的混合液中,搅拌,所得到的混合液留用;
步骤7)将乙二胺加入步骤6)所得的混合液中,搅拌均匀,所得到的混合液留用;
步骤8)在上述步骤7)中得到的混合液中加入挑选好的沙子,混合后放入搅拌机中,边搅拌边固化,每20分钟搅拌一次,每次搅拌10分钟,4小时后停止搅拌,沙子被包覆上一层混合树脂;
步骤9)将步骤8)所得到的沙子放入烤箱或炉子内加热,加热温度为120℃~180℃,加热时间为2~3小时;
步骤10)取出上述步骤8)中加热后的沙子自然冷却至常温;
步骤11)将冷却后的沙子放入破碎机内粉碎;
步骤12)过筛,选出粒度为16mm~30mm的沙子;
步骤13)在甲基硅酸钠中添加处理剂,处理剂为乙醇,再加入30%~70%的水,使乙醇和甲基硅酸钠充分混合并搅拌均匀;
步骤14)将步骤12)中得到的沙子加入到步骤13)所得的混合液内,浸湿沙子;
步骤15)将步骤14)中浸湿后的沙子风干后加热,加热温度为40℃~80℃,加热时间为3~4小时;
步骤16)将上述步骤15)处理后的沙子自然冷却后即可。
下面结合数据来说明本发明的疏水性沙子的积极效果:
疏水性时间 | |
实验组 | 疏水性好,持久不渗水 |
对照组 | 6-10小时即渗水 |
表1
根据表1所得的结论可知,本发明所得的疏水性沙子具有持久性的良好的疏水性,将本发明的疏水性沙子均匀铺设或撒在土壤表面,可以达到改良土壤的效果。由于本发明疏水性沙子的良好的疏水性,土壤可充分吸水并增加土壤的透气性,本发明的疏水性沙子无毒、无害、无污染,不会对土壤上的种植物产生不良效果,本发明的疏水性沙子耐水冲、耐火烧、抗老化,因此可以重复利用,减少投入,并且温室大棚和户外土壤均可使用。本发明的疏水性沙子还可放入鱼缸内养鱼用,不会污染鱼缸内的环境,还很有利于养鱼。
Claims (2)
1.一种疏水性沙子,其特征在于由下述重量配比的原料组成:沙粒90%-~94%,热固性酚醛树脂1%~3%,糠醇树脂1%~3%,甲基硅酸钠1%~5%,环氧树脂1%~3%,缩醛树脂0.5%~1.5%,丙酮0.4%~1.2%,邻苯二甲酸二丁酯0.05%~0.2%,乙二胺0.03%~0.08%,硅烷偶联剂0.02%~0.05%。
2.如权利要求1所述的疏水性沙子的制备方法,其特征在于包括以下步骤:
步骤1)筛选,挑选纯净无土的粒度为0.5mm~1.5mm的沙粒;
步骤2)将上述重量配比的环氧树脂加入到糠醇树脂中,混合均匀,得到的混合物留用;
步骤3)将缩醛树脂加入到丙酮内,搅拌,溶解,混合,得到的混合液留用;
步骤4)将步骤2)中得到的混合物加入步骤3)所得的混合液中,搅拌,溶解,得到的混合液留用;
步骤5)将邻苯二甲酸二丁酯和硅烷偶联剂加入步骤4)所得的混合液中,搅拌,得到的混合液留用;
步骤6)将热固性酚醛树脂加入步骤5)所得的混合液中,搅拌,所得到的混合液留用;
步骤7)将乙二胺加入步骤6)所得的混合液中,搅拌均匀,所得到的混合液留用;
步骤8)在上述步骤7)中得到的混合液中加入挑选好的沙子,混合后放入搅拌机中,边搅拌边固化,每20分钟搅拌一次,每次搅拌10分钟,4小时后停止搅拌,沙子被包覆上一层混合树脂;
步骤9)将步骤8)所得到的沙子放入烤箱或炉子内加热,加热温度为120℃~180℃,加热时间为2~3小时;
步骤10)取出上述步骤8)中加热后的沙子自然冷却至常温;
步骤11)将冷却后的沙子放入破碎机内粉碎;
步骤12)过筛,选出粒度为16mm~30mm的沙子;
步骤13)在甲基硅酸钠中添加处理剂,处理剂为乙醇,再加入30%~70%的水,使乙醇和甲基硅酸钠充分混合并搅拌均匀;
步骤14)将步骤12)中得到的沙子加入到步骤13)所得的混合液内,浸湿沙子;
步骤15)将步骤14)中浸湿后的沙子风干后加热,加热温度为40℃~80℃,加热时间为3~4小时;
步骤16)将上述步骤15)处理后的沙子自然冷却后即可。