CN104449690A - Praseodymium-doped alkaline earth aluminoborate up-conversion luminescent material as well as preparation method and application thereof - Google Patents

Praseodymium-doped alkaline earth aluminoborate up-conversion luminescent material as well as preparation method and application thereof Download PDF

Info

Publication number
CN104449690A
CN104449690A CN201310442105.8A CN201310442105A CN104449690A CN 104449690 A CN104449690 A CN 104449690A CN 201310442105 A CN201310442105 A CN 201310442105A CN 104449690 A CN104449690 A CN 104449690A
Authority
CN
China
Prior art keywords
alkaline earth
luminescent material
conversion luminescent
doped alkaline
aluminium borate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310442105.8A
Other languages
Chinese (zh)
Inventor
周明杰
陈吉星
王平
钟铁涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Oceans King Lighting Science and Technology Co Ltd
Shenzhen Oceans King Lighting Science and Technology Co Ltd
Shenzhen Oceans King Lighting Engineering Co Ltd
Original Assignee
Oceans King Lighting Science and Technology Co Ltd
Shenzhen Oceans King Lighting Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Oceans King Lighting Science and Technology Co Ltd, Shenzhen Oceans King Lighting Engineering Co Ltd filed Critical Oceans King Lighting Science and Technology Co Ltd
Priority to CN201310442105.8A priority Critical patent/CN104449690A/en
Publication of CN104449690A publication Critical patent/CN104449690A/en
Pending legal-status Critical Current

Abstract

The invention discloses a praseodymium-doped alkaline earth aluminoborate up-conversion luminescent material with a chemical formula of aMO-bB2O3-cAl2O3:xPr<3+>, wherein a is 0.2-0.5, b is 0.2-0.4, c is 0.1-0.5, x is 0.05-0.12, and M is one of a magnesium element, a calcium element, a strontium element, and a barium element. In the photoluminescence spectra of the praseodymium-doped alkaline earth aluminoborate up-conversion luminescent material, the excitation wavelength of the praseodymium-doped alkaline earth aluminoborate up-conversion luminescent material is 578nm; in a 483nm-wavelength region, a photoluminescence peak is formed by virtue of transition radiation from 3Po to 3H4 of Pr<3+>, so that the praseodymium-doped alkaline earth aluminoborate up-conversion luminescent material can be used as a blue electroluminescent material. The invention further provides a preparation method of the praseodymium-doped alkaline earth aluminoborate up-conversion luminescent material and an organic light emitting diode using the praseodymium-doped alkaline earth aluminoborate up-conversion luminescent material.

Description

Praseodymium doped alkaline earth aluminium borate up-conversion luminescent material, preparation method and application thereof
Technical field
The present invention relates to a kind of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material, preparation method and Organic Light Emitting Diode.
Background technology
Organic Light Emitting Diode (OLED) because unit construction is simple, the characteristic such as cheap, the luminous of production cost, reaction times is short, flexible, and obtain a very wide range of application.But because the OLED blue light material obtaining stability and high efficiency is at present more difficult, significantly limit the development of white light OLED device and light source industry.
Upconverting fluorescent material can launch visible ray under long wave (as infrared) radiation excitation, even UV-light, is with a wide range of applications in the field such as optical fiber communication technology, fibre amplifier, 3 D stereo display, biomolecules fluorescence labelling, infrared detective.But, can by infrared, the long-wave radiations such as red-green glow inspire the praseodymium doped alkaline earth aluminium borate up-conversion luminescent material of blue emission, have not yet to see report.
Summary of the invention
Based on this, being necessary to provide a kind of can inspire the praseodymium doped alkaline earth aluminium borate up-conversion luminescent material of blue light, preparation method by long-wave radiation and use the Organic Light Emitting Diode of this praseodymium doped alkaline earth aluminium borate up-conversion luminescent material.
A kind of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material, its chemical formula is aMO-bB 2o 3-cAl 2o 3: xPr 3+, wherein, a is 0.2 ~ 0.5, b be 0.2 ~ 0.4, c be 0.1 ~ 0.5, x be 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element.
Described a is 0.31, b be 0.3, c be 0.31, x is 0.08.
A preparation method for praseodymium doped alkaline earth aluminium borate up-conversion luminescent material, comprises the following steps
Step one, according to aMO-bB 2o 3-cAl 2o 3: xPr 3+the stoichiometric ratio of each element takes MO, B 2o 3, Al 2o 3and Pr 2o 3powder, wherein, a is 0.2 ~ 0.5, b be 0.2 ~ 0.4, c be 0.1 ~ 0.5, x be 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element;
Step 2, the powder taken mixed obtain presoma in described step one;
Step 3, by the calcination 0.5 hour ~ 5 hours at 800 DEG C ~ 1000 DEG C of the presoma in described step 2,
Step 4, the precursor after process in described step 3 is cooled to 100 DEG C ~ 300 DEG C, then be incubated 0.5 hour ~ 3 hours, cool to room temperature, obtaining chemical general formula is aMO-bB 2o 3-cAl 2o 3: xPr 3+praseodymium doped alkaline earth aluminium borate up-conversion luminescent material.
Described MO, B 2o 3, Al 2o 3and Pr 2o 3the each component molar of powder is than being (0.2 ~ 0.5): (0.2 ~ 0.4): (0.1 ~ 0.5): (0.05 ~ 0.12).
Described MO, B 2o 3, Al 2o 3and Pr 2o 3the each component molar of powder is than being 0.31:0.3:0.31:0.08.
Described in step 2, mixing is that described powder is ground 20 minutes ~ 60 minutes in corundum alms bowl.
By the calcination 3 hours at 950 DEG C of described presoma in step 3.
Cooling temperature in step 4 is 250 DEG C, and soaking time is 2 hours.
A kind of Organic Light Emitting Diode, comprise the substrate, negative electrode, organic luminous layer, anode and the transparent encapsulated layer that stack gradually, it is characterized in that, be dispersed with praseodymium doped alkaline earth aluminium borate up-conversion luminescent material in described transparent encapsulated layer, the chemical formula of described praseodymium doped alkaline earth aluminium borate up-conversion luminescent material is aMO-bB 2o 3-cAl 2o 3: xPr 3+, wherein, a is 0.2 ~ 0.5, b be 0.2 ~ 0.4, c be 0.1 ~ 0.5, x be 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element.
Described a is 0.31, b be 0.3, c be 0.31, x is 0.08.
The preparation method of above-mentioned praseodymium doped alkaline earth aluminium borate up-conversion luminescent material is comparatively simple, and cost is lower, produces, comparatively environmental protection in simultaneous reactions process without the three wastes; In the photoluminescence spectra of the praseodymium doped alkaline earth aluminium borate up-conversion luminescent material of preparation, the excitation wavelength of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material is 578nm, in 483nm wavelength zone by Pr 3+ion 3p 03h 4transition radiation formed glow peak, can as blue light emitting material.
Accompanying drawing explanation
Fig. 1 is the structural representation of the Organic Light Emitting Diode of an embodiment.
Fig. 2 is the photoluminescence spectrogram of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material prepared by embodiment 1.
Fig. 3 is the Raman spectrum of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material prepared by embodiment 1.
Fig. 4 is the spectrogram forming the Organic Light Emitting Diode emitted white light in the transparent encapsulated layer of embodiment 1 preparation doped with praseodymium doped alkaline earth aluminium borate up-conversion luminescent material material.
Embodiment
Below in conjunction with the drawings and specific embodiments, praseodymium doped alkaline earth aluminium borate up-conversion luminescent material and preparation method thereof is illustrated further.
The praseodymium doped alkaline earth aluminium borate up-conversion luminescent material of one embodiment, its chemical formula is aMO-bB 2o 3-cAl 2o 3: xPr 3+, wherein, a is 0.2 ~ 0.5, b be 0.2 ~ 0.4, c be 0.1 ~ 0.5, x be 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element.
Preferably, a is 0.31, b be 0.3, c be 0.31, x is 0.08.
In the photoluminescence spectra of this praseodymium doped alkaline earth aluminium borate up-conversion luminescent material, the excitation wavelength of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material is 578nm, when material is subject to the radiation of long wavelength (as 578nm) time, and Pr 3+ion has just been in 3p 0excited state, then to 3h 4transition, just sends the blue light of 483nm, can as blue light emitting material.
The preparation method of above-mentioned praseodymium doped alkaline earth aluminium borate up-conversion luminescent material, comprises the following steps:
Step S11, according to aMO-bB 2o 3-cAl 2o 3: xPr 3+the stoichiometric ratio of each element takes MO, B 2o 3, Al 2o 3and Pr 2o 3powder, wherein, a is 0.2 ~ 0.5, b be 0.2 ~ 0.4, c be 0.1 ~ 0.5, x be 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element.
In this step, described MO, B 2o 3, Al 2o 3and Pr 2o 3the each component molar of powder is than being (0.2 ~ 0.5): (0.2 ~ 0.4): (0.1 ~ 0.5): (0.05 ~ 0.12).
In this step, preferred MO, B 2o 3, Al 2o 3and Pr 2o 3the each component molar of powder is than being 0.31:0.3:0.31:0.08.
Step S13, the powder taken mixed obtain presoma in step S11.
In this step, powder is ground in corundum alms bowl the presoma obtaining mixing for 20 minutes ~ 60 minutes, preferred grinding 40 minutes.
Step S15, by presoma calcination 0.5 hour ~ 5 hours at 800 DEG C ~ 1000 DEG C,
Preferably, presoma calcination 3 hours at 950 DEG C.
Step S17, be cooled to 100 DEG C ~ 500 DEG C by after the precursor after process in step S15, then be incubated 0.5 hour ~ 3 hours, cool to room temperature, obtaining chemical general formula is aMO-bB 2o 3-cAl 2o 3: xPr 3+, wherein, a is 0.2 ~ 0.5, b be 0.2 ~ 0.4, c be 0.1 ~ 0.5, x be 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element.
Preferably, the precursor after process in step S15 is cooled to 250 DEG C, then is incubated 2 hours.
Preferably, described a is 0.31, b be 0.3, c be 0.31, x is 0.08.
The preparation method of above-mentioned praseodymium doped alkaline earth aluminium borate up-conversion luminescent material is comparatively simple, and cost is lower, produces, comparatively environmental protection in simultaneous reactions process without the three wastes; In the photoluminescence spectra of the praseodymium doped alkaline earth aluminium borate up-conversion luminescent material of preparation, the excitation wavelength of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material is 578nm, in 483nm wavelength zone by Pr 3+ion 3p 03h 4transition radiation formed glow peak, can as blue light emitting material.
Refer to Fig. 1, the Organic Light Emitting Diode 100 of an embodiment, this Organic Light Emitting Diode 100 comprises the substrate 1, negative electrode 2, organic luminous layer 3, transparent anode 4 and the transparent encapsulated layer 5 that stack gradually.Be dispersed with praseodymium doped alkaline earth aluminium borate up-conversion luminescent material 6 in transparent encapsulated layer 5, the chemical formula of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material is aMO-bB 2o 3-cAl 2o 3: xPr 3+wherein, a is 0.2 ~ 0.5, b is 0.2 ~ 0.4, c is 0.1 ~ 0.5, x is 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element, organic luminous layer 3 in this device sends red-green glow, and part red-green glow excites in transparent encapsulated layer 5 and is dispersed with praseodymium doped alkaline earth aluminium borate up-conversion luminescent material 6 and sends blue light, and last redgreenblue just blendes together white light.
Be specific embodiment below.
Embodiment 1
Select purity be 99.99% powder, by MgO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.31mmol by mole number, 0.3mmol, 0.31mmol and 0.08mmol grinds and makes its Homogeneous phase mixing in 40 minutes in corundum mortar, then calcination 3 hours at 950 DEG C in retort furnace, then 250 DEG C are cooled to be incubated 2 hours, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.31MgO-0.3B 2o 3-0.31Al 2o 3: 0.08Pr 3+up-conversion phosphor.
Process prepared by Organic Light Emitting Diode
The substrate 1 stacked gradually uses soda-lime glass, negative electrode 2 uses metal A g layer, organic luminous layer 3 uses Ir (piq) 2 (acac) Chinese name (methyl ethyl diketone) closes iridium (III), transparent anode 4 uses tin indium oxide ITO two (1-phenyl-isoquinoline 99.9), and transparent encapsulated layer 5 tetrafluoroethylene.Be dispersed with praseodymium doped alkaline earth aluminium borate up-conversion luminescent material 6 in transparent encapsulated layer 5, the chemical formula of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material is 0.31MgO-0.3B 2o 3-0.31Al 2o 3: 0.08Pr 3+.
Refer to Fig. 2, Figure 2 shows that the photoluminescence spectra figure of the praseodymium doped alkaline earth aluminium borate up-conversion luminescent material obtained.As seen from Figure 2, the excitation wavelength of the praseodymium doped alkaline earth aluminium borate up-conversion luminescent material that curve 1 the present embodiment obtains is 578nm, in 483nm wavelength zone by Pr 3+ion 3p 03h 4transition radiation formed glow peak, this praseodymium doped alkaline earth aluminium borate up-conversion luminescent material can be used as blue light emitting material.
Refer to Fig. 3, in Fig. 3, curve is the Raman spectrum of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material prepared by enforcement 1, Raman peaks in figure is depicted as alkaline earth aluminium borate characteristic peak, there is not the peak of doped element and other impurity, illustrate that doped element and substrate material define good bonding.
Refer to Fig. 4, Fig. 4 curve 1 is the spectrogram forming the Organic Light Emitting Diode emitted white light in transparent encapsulated layer doped with praseodymium doped alkaline earth aluminium borate up-conversion luminescent material material, and curve 2 is not doped with the contrast of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material material in transparent encapsulated layer.Can find out in figure, praseodymium doped alkaline earth aluminium borate up-conversion luminescent material by the red light of long wave, can inspire the blue light of shortwave, forms white light after blue light mixes with ruddiness.
Embodiment 2
Select purity be 99.99% powder, by MgO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.46mmol by mole number, 0.39mmol, 0.1mmol and 0.05mmol grinds and makes its Homogeneous phase mixing in 20 minutes in corundum mortar, then calcination 0.5 hour at 800 DEG C in retort furnace, then 100 DEG C are cooled to be incubated 3 hours, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.46MgO-0.39B 2o 3-0.1Al 2o 3: 0.05Pr 3+up-conversion phosphor.
Embodiment 3
Select purity be 99.99% powder, by MgO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.2mmol by mole number, 0.22mmol, 0.44mmol and 0.12mmol grinds and makes its Homogeneous phase mixing in 60 minutes in corundum mortar, then calcination 0.5 hour at 1000 DEG C in retort furnace, then 500 DEG C are cooled to be incubated 0.5 hour, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.2MgO-0.22B 2o 3-0.44Al 2o 3: 0.12Pr 3+up-conversion phosphor.
Embodiment 4
Select purity be 99.99% powder, by CaO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.31mmol by mole number, 0.3mmol, 0.31mmol and 0.08mmol grinds and makes its Homogeneous phase mixing in 40 minutes in corundum mortar, then calcination 3 hours at 950 DEG C in retort furnace, then 250 DEG C are cooled to be incubated 2 hours, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.31CaO-0.3B 2o 3-0.31Al 2o 3: 0.08Pr 3+up-conversion phosphor.
Embodiment 5
Select purity be 99.99% powder, by CaO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.46mmol by mole number, 0.39mmol, 0.1mmol and 0.05mmol grinds and makes its Homogeneous phase mixing in 20 minutes in corundum mortar, then calcination 5 hours at 800 DEG C in retort furnace, then 100 DEG C are cooled to be incubated 3 hours, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.46CaO-0.39B 2o 3-0.1Al 2o 3: 0.05Pr 3+up-conversion phosphor.
Embodiment 6
Select purity be 99.99% powder, by CaO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.2mmol by mole number, 0.22mmol, 0.44mmol and 0.12mmol grinds and makes its Homogeneous phase mixing in 60 minutes in corundum mortar, then calcination 3 hours at 1000 DEG C in retort furnace, then 500 DEG C are cooled to be incubated 0.5 hour, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.2CaO-0.22B 2o 3-0.44Al 2o 3: 0.12Pr 3+up-conversion phosphor.
Embodiment 7
Select purity be 99.99% powder, by SrO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.31mmol by mole number, 0.3mmol, 0.31mmol and 0.08mmol grinds and makes its Homogeneous phase mixing in 40 minutes in corundum mortar, then calcination 3 hours at 950 DEG C in retort furnace, then 250 DEG C are cooled to be incubated 2 hours, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.31SrO-0.3B 2o 3-0.31Al 2o 3: 0.08Pr 3+up-conversion phosphor.
Embodiment 8
Select purity be 99.99% powder, by SrO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.46mmol by mole number, 0.39mmol, 0.1mmol and 0.05mmol grinds and makes its Homogeneous phase mixing in 20 minutes in corundum mortar, then calcination 5 hours at 800 DEG C in retort furnace, then 100 DEG C are cooled to be incubated 3 hours, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.46SrO-0.39B 2o 3-0.1Al 2o 3: 0.05Pr 3+up-conversion phosphor.
Embodiment 9
Select purity be 99.99% powder, by SrO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.2mmol by mole number, 0.22mmol, 0.44mmol and 0.12mmol grinds and makes its Homogeneous phase mixing in 60 minutes in corundum mortar, then calcination 3 hours at 1000 DEG C in retort furnace, then 500 DEG C are cooled to be incubated 0.5 hour, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.2SrO-0.22B 2o 3-0.44Al 2o 3: 0.12Pr 3+up-conversion phosphor.
Embodiment 10
Select purity be 99.99% powder, by BaO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.31mmol by mole number, 0.3mmol, 0.31mmol and 0.08mmol grinds and makes its Homogeneous phase mixing in 40 minutes in corundum mortar, then calcination 3 hours at 950 DEG C in retort furnace, then 250 DEG C are cooled to be incubated 2 hours, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.31BaO-0.3B 2o 3-0.31Al 2o 3: 0.08Pr 3+up-conversion phosphor.
Embodiment 11
Select purity be 99.99% powder, by BaO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.46mmol by mole number, 0.39mmol, 0.1mmol and 0.05mmol grinds and makes its Homogeneous phase mixing in 20 minutes in corundum mortar, then calcination 5 hours at 800 DEG C in retort furnace, then 100 DEG C are cooled to be incubated 3 hours, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.46BaO-0.39B 2o 3-0.1Al 2o 3: 0.05Pr 3+up-conversion phosphor.
Embodiment 12
Select purity be 99.99% powder, by BaO, B 2o 3, Al 2o 3and Pr 2o 3the each component of powder is 0.2mmol by mole number, 0.22mmol, 0.44mmol and 0.12mmol grinds and makes its Homogeneous phase mixing in 60 minutes in corundum mortar, then calcination 3 hours at 1000 DEG C in retort furnace, then 500 DEG C are cooled to be incubated 0.5 hour, furnace cooling takes out to room temperature again, and obtain block materials, can obtain chemical general formula after pulverizing is 0.2BaO-0.22B 2o 3-0.44Al 2o 3: 0.12Pr 3+up-conversion phosphor.
The above embodiment only have expressed several embodiment of the present invention, and it describes comparatively concrete and detailed, but therefore can not be interpreted as the restriction to the scope of the claims of the present invention.It should be pointed out that for the person of ordinary skill of the art, without departing from the inventive concept of the premise, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection domain of patent of the present invention should be as the criterion with claims.

Claims (10)

1. a praseodymium doped alkaline earth aluminium borate up-conversion luminescent material, is characterized in that: its chemical general formula is aMO-bB 2o 3-cAl 2o 3: xPr 3+, wherein, a is 0.2 ~ 0.5, b be 0.2 ~ 0.4, c be 0.1 ~ 0.5, x be 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element.
2. praseodymium doped alkaline earth aluminium borate up-conversion luminescent material according to claim 1, is characterized in that, described a is 0.31, b be 0.3, c be 0.31, x is 0.08.
3. a preparation method for praseodymium doped alkaline earth aluminium borate up-conversion luminescent material, is characterized in that, comprise the following steps:
Step one, according to aMO-bB 2o 3-cAl 2o 3: xPr 3+the stoichiometric ratio of each element claims MO, B 2o 3, Al 2o 3and Pr 2o 3powder, wherein, a is 0.2 ~ 0.5, b be 0.2 ~ 0.4, c be 0.1 ~ 0.5, x be 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element;
Step 2, the powder taken mixed obtain presoma in described step one;
Step 3, by the calcination 0.5 hour ~ 5 hours at 800 DEG C ~ 1000 DEG C of described presoma,
Step 4, the precursor after process in described step 3 is cooled to 100 DEG C ~ 500 DEG C, then be incubated 0.5 hour ~ 3 hours, cool to room temperature, obtaining chemical general formula is aMO-bB 2o 3-cAl 2o 3: xPr 3+praseodymium doped alkaline earth aluminium borate up-conversion luminescent material.
4. the preparation method of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material according to claim 3, is characterized in that, described MO, B 2o 3, Al 2o 3and Pr 2o 3the each component molar of powder is than being (0.2 ~ 0.5): (0.2 ~ 0.4): (0.1 ~ 0.5): (0.05 ~ 0.12).
5. the preparation method of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material according to claim 3, is characterized in that, described MO, B 2o 3, Al 2o 3and Pr 2o 3the each component molar of powder is than being 0.31:0.3:0.31:0.08.
6. the preparation method of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material according to claim 3, is characterized in that, described in step 2, mixing is that described powder is ground 20 minutes ~ 60 minutes in corundum alms bowl.
7. the preparation method of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material according to claim 3, is characterized in that, by the calcination 3 hours at 950 DEG C of described presoma in step 3.
8. the preparation method of praseodymium doped alkaline earth aluminium borate up-conversion luminescent material according to claim 3, it is characterized in that, the cooling temperature in step 4 is 250 DEG C, and soaking time is 2 hours.
9. an Organic Light Emitting Diode, this Organic Light Emitting Diode comprises the substrate, negative electrode, organic luminous layer, anode and the transparent encapsulated layer that stack gradually, it is characterized in that, be dispersed with praseodymium doped alkaline earth aluminium borate up-conversion luminescent material in described transparent encapsulated layer, the chemical formula of described praseodymium doped alkaline earth aluminium borate up-conversion luminescent material is aMO-bB 2o 3-cAl 2o 3: xPr 3+, wherein, a is 0.2 ~ 0.5, b be 0.2 ~ 0.4, c be 0.1 ~ 0.5, x be 0.05 ~ 0.12, M is magnesium elements, calcium constituent, a kind of in strontium element and barium element.
10. Organic Light Emitting Diode according to claim 9, is characterized in that, described a is 0.31, b be 0.3, c be 0.31, x is 0.08.
CN201310442105.8A 2013-09-25 2013-09-25 Praseodymium-doped alkaline earth aluminoborate up-conversion luminescent material as well as preparation method and application thereof Pending CN104449690A (en)