CN104449320A - Finishing coat for woodware - Google Patents

Finishing coat for woodware Download PDF

Info

Publication number
CN104449320A
CN104449320A CN201410767020.1A CN201410767020A CN104449320A CN 104449320 A CN104449320 A CN 104449320A CN 201410767020 A CN201410767020 A CN 201410767020A CN 104449320 A CN104449320 A CN 104449320A
Authority
CN
China
Prior art keywords
parts
finishing coat
woodware
present
lacquer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410767020.1A
Other languages
Chinese (zh)
Inventor
倪建平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU YULINSHIJIA REDWOOD FURNITURE Co Ltd
Original Assignee
JIANGSU YULINSHIJIA REDWOOD FURNITURE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU YULINSHIJIA REDWOOD FURNITURE Co Ltd filed Critical JIANGSU YULINSHIJIA REDWOOD FURNITURE Co Ltd
Priority to CN201410767020.1A priority Critical patent/CN104449320A/en
Publication of CN104449320A publication Critical patent/CN104449320A/en
Pending legal-status Critical Current

Abstract

The invention discloses a finishing coat for woodware. The finishing coat is prepared from the following components in parts by weight: 23 parts of a water soluble polyurethane emulsion, 3.2 parts of nano silicon dioxide, 4.5 parts of ethanol, 1.7 parts of triethyl citrate, 2.1 parts of carbon dioxide and 0.5 part of low arsenic ferric oxide. The finishing coat for woodware disclosed by the invention has excellent dirt resistance and adhesive force.

Description

Lacquer as woodenware finish
Technical field
The present invention relates to lacquer as woodenware finish.
Background technology
Existing lacquer as woodenware finish, its anti-stain characteristic and sticking power all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of lacquer as woodenware finish, it has excellent anti-stain characteristic and sticking power.
For achieving the above object, technical scheme of the present invention is a kind of lacquer as woodenware finish of design, composed of the following components by weight:
23 parts of aqurous ployurethane emulsions,
3.2 parts of nano silicons,
4.5 parts of ethanol,
1.7 parts of triethyl citrates,
2.1 parts of silicon-dioxide,
0.5 part low arsenic ferric oxide.
Advantage of the present invention and beneficial effect are: provide a kind of lacquer as woodenware finish, and it has excellent anti-stain characteristic and sticking power.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
A kind of lacquer as woodenware finish, composed of the following components by weight:
23 parts of aqurous ployurethane emulsions,
3.2 parts of nano silicons,
4.5 parts of ethanol,
1.7 parts of triethyl citrates,
2.1 parts of silicon-dioxide,
0.5 part low arsenic ferric oxide.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (1)

1. lacquer as woodenware finish, is characterized in that, composed of the following components by weight:
23 parts of aqurous ployurethane emulsions,
3.2 parts of nano silicons,
4.5 parts of ethanol,
1.7 parts of triethyl citrates,
2.1 parts of silicon-dioxide,
0.5 part low arsenic ferric oxide.
CN201410767020.1A 2014-12-15 2014-12-15 Finishing coat for woodware Pending CN104449320A (en)