CN104448881A - Breathing plastic material - Google Patents
Breathing plastic material Download PDFInfo
- Publication number
- CN104448881A CN104448881A CN201410717503.0A CN201410717503A CN104448881A CN 104448881 A CN104448881 A CN 104448881A CN 201410717503 A CN201410717503 A CN 201410717503A CN 104448881 A CN104448881 A CN 104448881A
- Authority
- CN
- China
- Prior art keywords
- plastic
- plastic material
- melting
- soil
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a breathing plastic material. The breathing plastic material is prepared by the following steps: melting a 95 to 50 percent by weight of a plastic raw material to a hot melting state, then adding 5 to 50 percent by weight of porous far-infrared calcining soil into the hot-melting-state plastic, mixing the soil and the plastic for a period of time to obtain a mixture, and pressing the mixture to obtain a hot-melting plastic strip; then cooling the hot-melting plastic strip, and granulating the hot-melting plastic to form plastic particles made of the breathing plastic material. A plastic finished product prepared from the breathing plastic material can naturally generate multilayer far-infrared shockwaves, has the effects of no toxicity, deodorization and sterilization, and can appropriately release negative ions and release birth light waves in the wavelength of 3 to 14 micrometers so as to maintain the health of a human body.
Description
[technical field]
The present invention relates to a kind of plastic material that can breathe, particularly one can produce far infrared rays multi-level Sasser by nature, reaches nontoxic, deodorizing, antibacterial, and can the plastic material of anion releasing in good time.
[background technology]
At present, the particles of general existing plastic material, naturally the multi-level Sasser of far infrared rays cannot be produced, carry out bacteria growing inhibiting, or the fertility light wave of release 3 ~ 14 micron wave lengths, cause the crisper utilizing the particles of this existing plastic material to make, its fresh-keeping effect is limited, the freshness of food cannot be maintained for a long time, quite not convenient.
As can be seen here, above-mentioned existing article still have many disappearances, a real non-kindhearted design, and are urgently improved.
[summary of the invention]
Contriver is because the shortcoming of aforementioned prior art, be manufacturing experience and the technology accumulation of being engaged in various plastics according to it, concentrate one's attention on to study the method for various solution for above-mentioned defect, through constantly study, test with improve after, finally development and Design goes out the invention of a kind of plastic material completely newly can breathed of the present invention, to the defect that prior art of forgoing produces.
Main purpose of the present invention, thering is provided a kind of plastic material that can breathe, it can produce far infrared rays multi-level Sasser by nature, reaches nontoxic, deodorizing, antibacterial, and can in good time anion releasing and release 3 ~ 14 micron wave lengths fertility light wave, keep the health of human body.
According to above-mentioned object, the plastic material that can breathe of the present invention, its be by mass percent be first 95% ~ 50% plastics (as: polypropylene (PP)) raw material melt into a hot melt state, by weight percent be again 5% ~ 50% porousness far infrared rays calcined earth add in the plastics of this hot melt state, and mix, after making mixing for some time, extrude a hot melt plastic material strip; Then, after cooling process, pull into spool, then carry out a pelletizing, namely form the plastic pellet of the plastic material for a moment breathed.
Further, wherein this plastic product is a crisper or a top ceiling.
Further, wherein this plastic raw materials is the segmented copolymer of a polypropylene, an acrylonitrile-butadiene-styrene copolymer, a polystyrene, a polyethylene, a polycarbonate, an impact resistant polystyrene, a polyvinyl chloride, an acryl, a polyacetal, a PA plastic cement, a thermoplastic elastomer, a polyurethane, a vinylbenzene and divinyl, a transparent styrenebutadiene copolymer compound, a Teflon, a poly(lactic acid) or a plastic cement fiber.
Further, wherein this porousness far infrared rays calcined earth makes according to following steps:
(1) mode utilizing longitudinal section to cross over different soils layer adopts to obtain soil, to obtain the soil mixture once mixing Different Strata soil;
(2) soil mixture is made to calcine at high temperature 1300 DEG C to 2000 DEG C;
(3) a porousness far infrared rays calcined earth is obtained after cooling.
So, the plastic product (as: crisper, top ceiling) utilizing this plastic pellet to make, can produce far infrared rays multi-level Sasser by nature, reach nontoxic, deodorizing, antibacterial, and can in good time anion releasing and release 3 ~ 14 micron wave lengths fertility light wave, keep the health of human body.
For just your juror to object of the present invention, shape, constructing apparatus feature and effect thereof, can do further understanding and understanding, hereby coordinate graphic for embodiment, be described in detail as follows:
[accompanying drawing explanation]
The present invention is further illustrated in conjunction with the embodiments with reference to the accompanying drawings.
Fig. 1 is the schematic appearance of the plastic pellet of the plastic material that the present invention can breathe.
Fig. 2 is the crisper schematic diagram that the plastic material utilizing the present invention to breathe is made.
Fig. 3 is the top ceiling schematic diagram that the plastic material utilizing the present invention to breathe is made.
Nomenclature is as follows:
Plastic pellet 10 crisper 11 top ceiling 12
[embodiment]
The present invention relates to a kind of plastic material that can breathe, refer to shown in Fig. 1, the plastic material that can breathe of the present invention, its by mass percent be first 95% ~ 50% plastic raw materials melt into a hot melt state, by mass percent be again 5% ~ 50% porousness far infrared rays calcined earth add in the plastics of this hot melt state, and mix, after making mixing for some time, extrude a hot melt plastic material strip; Then, after cooling process, pull into spool, then carry out a pelletizing, namely form the plastic pellet 10 of the plastic material for a moment breathed.
So, utilize the plastic product that this plastic pellet is made, far infrared rays multi-level Sasser can be produced by nature, reach nontoxic, deodorizing, antibacterial, and can anion releasing and discharge the fertility light wave of 3 ~ 14 micron wave lengths in good time, keep the health of human body.
Refer to shown in Fig. 2, this plastic product can be a crisper 11, and utilize the crisper 11 that this plastic pellet 10 is made, naturally can produce the multi-level Sasser of far infrared rays, and can in 24 hours antibacterial 82%, the fertility light wave of 3 ~ 14 micron wave lengths can also be discharged, and increase the fresh keeping time of 2 to 3 times than general commercially available crisper, can apply to eggs, fresh meat, fish and shrimp fresh-keeping, and fresh meat, fish and shrimp are with freezen protective, after moving back ice, former delicate flavour does not run off.
Refer to shown in Fig. 3, this plastic product can be a top ceiling 12, utilize the top ceiling 12 that this plastic pellet 10 is made, naturally the multi-level Sasser of far infrared rays can be produced, and the releasing far infrared and negative ion of energy, there is great advantage to human body, and the fertility light wave of 3 ~ 14 micron wave lengths can be discharged, keep the health of human body.
Refer to again shown in Fig. 1, this plastic raw materials can be a polypropylene (PP), one acrylonitrile-butadiene-styrene copolymer (ABS), one polystyrene (PS), one polyethylene (PE), one polycarbonate (PC), one impact resistant polystyrene (HIPS), one polyvinyl chloride (PVC), one acryl (PMMA), one polyacetal (POM), one PA plastic cement, one thermoplastic elastomer (TPR), one polyurethane (PU), the segmented copolymer (K glue) of one vinylbenzene and divinyl, one transparent styrenebutadiene copolymer compound (Q glue), one Teflon (PTFE), one poly(lactic acid) (PLA) or a plastic cement fiber.
This porousness far infrared rays calcined earth makes according to the following step:
(1) mode utilizing longitudinal section to cross over different soils layer adopts to obtain soil, to obtain the soil mixture once mixing Different Strata soil;
(2) soil mixture is made to calcine at high temperature 1300 DEG C to 2000 DEG C;
(3) a porousness far infrared rays calcined earth is obtained after cooling.
The plastic material that can breathe provided by the present invention, when mutually comparing with aforementioned prior art, has more following advantage:
1, the plastic product made by plastic pellet 10 of plastic material that can breathe of use, the multi-level Sasser of far infrared rays can be produced by nature, reach nontoxic, deodorizing, antibacterial, and can the fertility light wave of anion releasing and release 3 ~ 14 micron wave lengths in good time, keep the health of human body.
Described on comprehensive, the plastic material that can breathe of the present invention, has unprecedented innovative structure really, and it had not both seen any publication, and on the market also there are no any similar product, therefore, it has novelty should without doubt.In addition, the specific characteristic that the present invention has and function are far from prior art and can compare, so it has more its progressive than prior art really, and meet the regulation of the application important document of China's patent law Invention patent, be mention patent application in accordance with the law.
Although the foregoing describe the specific embodiment of the present invention; but be familiar with those skilled in the art to be to be understood that; specific embodiment described by us is illustrative; instead of for the restriction to scope of the present invention; those of ordinary skill in the art, in the modification of the equivalence done according to spirit of the present invention and change, should be encompassed in scope that claim of the present invention protects.
Claims (4)
1. the plastic material that can breathe, it is characterized in that: its by mass percent be first 95% ~ 50% plastic raw materials melt into a hot melt state, by mass percent be again 5% ~ 50% porousness far infrared rays calcined earth add in the plastics of this hot melt state, and mix, after making mixing for some time, extrude a hot melt plastic material strip; Then, after cooling process, pull into spool, then carry out a pelletizing, namely form the plastic pellet of the plastic material for a moment breathed.
2. the plastic material that can breathe according to claim 1, is characterized in that: wherein this plastic product is a crisper or a top ceiling.
3. the plastic material that can breathe according to claim 1, is characterized in that: wherein this plastic raw materials is the segmented copolymer of a polypropylene, an acrylonitrile-butadiene-styrene copolymer, a polystyrene, a polyethylene, a polycarbonate, an impact resistant polystyrene, a polyvinyl chloride, an acryl, a polyacetal, a PA plastic cement, a thermoplastic elastomer, a polyurethane, a vinylbenzene and divinyl, a transparent styrenebutadiene copolymer compound, a Teflon, a poly(lactic acid) or a plastic cement fiber.
4. the plastic material that can breathe according to claim 1, is characterized in that: wherein this porousness far infrared rays calcined earth makes according to following steps:
(1) mode utilizing longitudinal section to cross over different soils layer adopts to obtain soil, to obtain the soil mixture once mixing Different Strata soil;
(2) soil mixture is made to calcine at high temperature 1300 DEG C to 2000 DEG C;
(3) a porousness far infrared rays calcined earth is obtained after cooling.