CN104446250A - 一种高韧性建筑材料 - Google Patents

一种高韧性建筑材料 Download PDF

Info

Publication number
CN104446250A
CN104446250A CN201410694572.4A CN201410694572A CN104446250A CN 104446250 A CN104446250 A CN 104446250A CN 201410694572 A CN201410694572 A CN 201410694572A CN 104446250 A CN104446250 A CN 104446250A
Authority
CN
China
Prior art keywords
parts
high tenacity
toughness
construction
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410694572.4A
Other languages
English (en)
Other versions
CN104446250B (zh
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Huangshi Zhenhua Construction Technology Co ltd
Original Assignee
Taicang Shunrucheng Building Materials Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Shunrucheng Building Materials Co ltd filed Critical Taicang Shunrucheng Building Materials Co ltd
Priority to CN201410694572.4A priority Critical patent/CN104446250B/zh
Publication of CN104446250A publication Critical patent/CN104446250A/zh
Application granted granted Critical
Publication of CN104446250B publication Critical patent/CN104446250B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高韧性建筑材料，包括以下重量份数的原料组成：复合纤维材料20~40份，硅酸盐水泥30~50份，碳酸钙10~15份，粉煤灰5~10份，硅粉3~8份，分散剂1~5份，减水剂0.5~2份，增稠剂1~3份，增韧剂0.5~3份。本发明提出的高韧性建筑材料，提高了材料的韧性以及阻裂作用，所述复合纤维通过分散剂均匀分布，并且改变了力学性能，显著提高了材料的抵抗变形的能力，混凝土的发生开裂和断裂的概率降低。

Description

一种高韧性建筑材料
技术领域
本发明涉及一种建筑材料，具体为一种高韧性建筑材料。
背景技术
建筑材料是建筑工程的基础，而混凝土是应用最广泛的建筑材料，料，其主要成分包括水泥、掺合物和骨料，加水搅拌后硬化而成，具有工艺简单、防火性能等优点。但混凝土具有抗拉强度低、韧性差和开裂后裂缝宽度难以控制等缺点，因此，在传统的钢筋混凝土结构中，由于裂缝导致钢筋锈蚀而出现的工程事故经常发生。混凝土结构裂缝直接影响着结构的耐久性和工程的使用寿命，最终导致混凝土结构过早地劣化甚至完全丧失使用功能。为克服混凝土这些缺点，聚丙烯纤维混凝土和钢纤维混凝土等应运而生，这类混凝土的纤维掺量通常小于2%，这样做虽然一定程度上起到了减轻混凝土早期开裂，提高材料抗弯韧度等作用，但在直接拉伸荷载作用下仍发生应变软化破坏，开裂后裂缝马上进入局部化扩展阶段。
因此，针对上述问题，本发明提出了一种新的技术方案。
发明内容
本发明的目的是提供一种提高韧性，减少开裂和断裂的高韧性建筑材料。
本发明是通过以下技术方案来实现的：
一种高韧性建筑材料，包括以下重量份数的原料组成：复合纤维材料20~40份，硅酸盐水泥30~50份，碳酸钙10~15份，粉煤灰5~10份，硅粉3~8份，分散剂1~5份，减水剂0.5~2份，增稠剂1~3份，增韧剂0.5~3份。
进一步地，所述复合材料为碳纤维、竹纤维和聚乙烯醇纤维的混合物。
进一步地，所述碳纤维、竹纤维和聚乙烯醇纤维的重量份数比为：1.5：1：0.8。
进一步地，所述分散剂为硬脂酸铜，所述减水剂为聚羧酸酯，所述增稠剂为甲基纤维素，所述增韧剂为乙烯-醋酸乙烯酯共聚物。
本发明的有益效果是：本发明提出的高韧性建筑材料，提高了材料的韧性以及阻裂作用，所述复合纤维通过分散剂均匀分布，并且改变了力学性能，显著提高了材料的抵抗变形的能力，混凝土的发生开裂和断裂的概率降低。
具体实施方式
下面结合实施例对本发明做进一步地说明。
实施例1
一种高韧性建筑材料，包括以下重量份数的原料组成：碳纤维10.4份，竹纤维6.8份，聚乙烯醇纤维5.5份，硅酸盐水泥30份，碳酸钙10份，粉煤灰5份，硅粉3份，硬脂酸铜1份，聚羧酸酯0.5份，甲基纤维素1份，乙烯-醋酸乙烯酯共聚物0.5份。
实施例2
一种高韧性建筑材料，包括以下重量份数的原料组成：碳纤维15份，竹纤维10份，聚乙烯醇纤维8份，硅酸盐水泥40份，碳酸钙12份，粉煤灰8份，硅粉5份，硬脂酸铜3份，聚羧酸酯1份，甲基纤维素2份，乙烯-醋酸乙烯酯共聚物2份。
实施例3
一种高韧性建筑材料，包括以下重量份数的原料组成：碳纤维19.5份，竹纤维13.3份，聚乙烯醇纤维10.5份，硅酸盐水泥50份，碳酸钙15份，粉煤灰10份，硅粉8份，硬脂酸铜5份，聚羧酸酯2份，甲基纤维素3份，乙烯-醋酸乙烯酯共聚物3份。
本发明提出的高韧性建筑材料，提高了材料的韧性以及阻裂作用，所述复合纤维通过分散剂均匀分布，并且改变了力学性能，显著提高了材料的抵抗变形的能力，混凝土的发生开裂和断裂的概率降低。
以上所述，仅是本发明的实施例而已，并非是对本发明作任何其他形式的限制，而依据本发明的技术实质所作的任何修改或等同变化，仍属于本发明所要求保护的范围。

Claims (4)

1.一种高韧性建筑材料，其特征在于：包括以下重量份数的原料组成：复合纤维材料20~40份，硅酸盐水泥30~50份，碳酸钙10~15份，粉煤灰5~10份，硅粉3~8份，分散剂1~5份，减水剂0.5~2份，增稠剂1~3份，增韧剂0.5~3份。
2.根据权利要求1所述一种高韧性建筑材料，其特征在于：所述复合材料为碳纤维、竹纤维和聚乙烯醇纤维的混合物。
3.根据权利要求2所述一种高韧性建筑材料，其特征在于：所述碳纤维、竹纤维和聚乙烯醇纤维的重量份数比为：1.5：1：0.8。
4.根据权利要求1所述一种高韧性建筑材料，其特征在于：所述分散剂为硬脂酸铜，所述减水剂为聚羧酸酯，所述增稠剂为甲基纤维素，所述增韧剂为乙烯-醋酸乙烯酯共聚物。
CN201410694572.4A 2014-11-27 2014-11-27 一种高韧性建筑材料 Active CN104446250B (zh)