CN104446112B - 一种聚醚复合水泥助磨剂 - Google Patents
一种聚醚复合水泥助磨剂 Download PDFInfo
- Publication number
- CN104446112B CN104446112B CN201410658007.2A CN201410658007A CN104446112B CN 104446112 B CN104446112 B CN 104446112B CN 201410658007 A CN201410658007 A CN 201410658007A CN 104446112 B CN104446112 B CN 104446112B
- Authority
- CN
- China
- Prior art keywords
- grinding aid
- polyethers
- parts
- cement
- cement grinding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种聚醚复合水泥助磨剂,按重量配比的以下组分:聚醚10‑12份、二乙醇单异丙醇胺6‑8份、三乙醇胺2‑4份、乙酸钠1‑2份、羟乙基纤维素2‑3份、造纸黑液4‑6份。和现有技术的产品相比较,在不同的掺量下可以明显提高3天抗压强度和28天抗压强度。
Description
技术领域
本发明属于水泥生产加工技术领域,具体涉及一种聚醚复合水泥助磨剂。
背景技术
我国是水泥生产大国,水泥产量连续多年位居世界首位。但制约我国水泥工业发展的关键问题,是水泥粉磨阶段的能耗高且利用率低。水泥工业是高能耗、高污染行业,是节能减排重点行业。针对这类问题,除了从设备、技术工艺方面进行改进外,在粉磨过程中加入少量水泥助磨剂是一种有效途径。
水泥助磨剂是一种改善水泥粉磨效果和性能的化学添加剂,可以显著提高水泥台时产量、各龄期水泥强度,改善其流动性。水泥助磨剂能大幅度降低粉磨过程中形成的静电吸附包球现象,并可以降低粉磨过程中形成的超细颗粒的再次聚结趋势。水泥助磨剂也能显著改善水泥流动性,提高磨机的研磨效果和选粉机的选粉效率,从而降低粉磨能耗。使用助磨剂生产的水泥具有较低的压实聚结趋势,从而有利于水泥的装卸,并可减少水泥库的挂壁现象。作为一种化学添加剂,助磨剂能改善水泥颗粒分布并激发水化动力,从而提高水泥早期强度和后期强度。
水泥助磨剂的作用是能够有助于水泥熟料粉磨过程的性能,改善粉磨质量,从主要成分上来看,主要有有机的醇化物、金属盐类、氨成分、糖蜜、木质素减水剂和表面活性剂。其中金属盐类起到分散和增加水泥矿物成分的作用,醇化物起到润滑的作用,氨的成分容易与醇化物产生氨化反应,糖蜜起到缓凝的作用,木质素起到减水的作用,而表面活性剂则起到减小分子间引力的作用。目前,使用的配方中醇胺的用量都比较大,约占30%以上,三乙醇胺、三异丙醇胺是石化原料,价格受石油影响大,价格一直居高不下,导致助磨剂成本上升,影响其推广应用。由于三乙醇胺价格高,故各个厂家都在尝试降低三乙醇胺的使用量或寻找一种替代品,不过虽然成本降低了,但往往造成水泥助磨剂效果的下降,使水泥及混凝土适应性降低。
木质素在助磨剂中也广泛应用。木质素是以苯丙烷基为基本结构单元,具有网状结构的一类无定形高聚物,结构复杂、分子质量不均,与纤维素、半纤维素同在植物体中,其主要是细胞壁组成成分。木质素这种产量巨大、可再生、可生物降解的天然高分子化合物由于其结构的复杂性、大分子的多分散性以及物理化学性质的不均一性,使得它至今尚未得到充分有效的利用。造纸黑液中含有大量难以去除的有机物质及无机物质,有机物质一般包括木质素及其衍生物、多糖、醇类、有机酸、树脂、果胶、酚类化合物等,其木质素占废液总量的1-2%,占总固形物的30%。每年全世界约可产生木质素600万亿吨,是人类可依存的最大资源。目前可作为工业原料的木质素主要是造纸工业的副产品,来源于制浆废液,其中只有百分之一作为水溶性木质素磺酸盐这种初级工业品应用,其余绝大部分作为燃料烧掉,如利用造纸黑液中的木质素为原料,应用在水泥助磨剂中,具有很好的市场前景。
发明内容
本发明的目的是克服现有技术的不足,提供一种聚醚复合水泥助磨剂,能明显提高水泥强度和改善性能。
为达到上述目的,本发明是通过如下技术方案实现的,一种聚醚复合水泥助磨剂,包括按重量配比的以下组分:
聚醚10-12份、二乙醇单异丙醇胺6-8份、三乙醇胺2-4份、乙酸钠1-2份、羟乙基纤维素2-3份、造纸黑液4-6份。
相比现有技术,本发明的优点在于:
1、目前常用的液体助磨剂原料主要为三乙醇胺与三异丙醇胺,本发明采用聚醚、二乙醇单异丙醇胺取代三乙醇胺与三异丙醇胺,二乙醇单异丙醇胺与三乙醇胺、三乙丙醇胺及其他醇、胺、脂类物质有良好的配伍性能,具有极好的助磨效果,同时可以有效降低三乙醇胺与三异丙醇胺的使用量,节约成本。
2、本发明采用造纸黑液作为原料,充分利用了工业废弃物及其副产物,一方面使得造纸工业产生的废液可以直接使用,省略了造纸黑液提取木质素或木质素磺酸盐再应用于助磨剂的繁琐过程,变废为宝,减少了木质素磺酸盐的直接加入量,另一方面,造纸黑液中除了木质素,还含有木质素衍生物、多糖、醇类、有机酸、树脂、果胶、酚类化合物等,可以显著增加物料流动性,提高磨机粉磨效率,提高磨机台时产量。
3、本发明使用了羟乙基纤维素,具有良好的增稠、悬浮、分散、乳化、粘合、成膜、保护水分和提供保护胶体等特性,在助磨剂中可以明显解决粉体团聚现象,改善颗粒的级配,增加微粉颗粒含量。
具体实施方式
下面以实施例对本发明作进一步说明,但本发明并不局限于这些实施例。
实施例1:
按重量份配比称取以下原料:聚醚10kg、二乙醇单异丙醇胺8kg、三乙醇胺2kg、乙酸钠2kg、羟乙基纤维素2kg、造纸黑液6kg,混合搅拌30分钟即得水泥助磨剂产品。
实施例2:
按重量份配比称取以下原料:聚醚12kg、二乙醇单异丙醇胺6kg、三乙醇胺4kg、乙酸钠1kg、羟乙基纤维素3kg、造纸黑液4kg,混合搅拌30分钟即得水泥助磨剂产品。
实施例3:
按重量份配比称取以下原料:聚醚11kg、二乙醇单异丙醇胺9kg、三乙醇胺3kg、乙酸钠2kg、羟乙基纤维素3kg、造纸黑液5kg,混合搅拌30分钟即得水泥助磨剂产品。
对比例:
聚醚10kg、丙三醇2kg、乙二醇2kg、二乙二醇2kg、山梨糖醇2kg、异丙醇2kg、葡萄糖酸钠1kg,混合搅拌30分钟即得水泥助磨剂产品。
结果:
通过以上实验数据,表明本发明得到的产品,和现有技术的产品相比较,在不同的掺量下可以明显提高3天抗压强度和28天抗压强度。
Claims (1)
1.一种聚醚复合水泥助磨剂,其特征在于:按重量配比的以下组分:
聚醚10-12份、二乙醇单异丙醇胺6-8份、三乙醇胺2-4份、乙酸钠1-2份、羟乙基纤维素2-3份、造纸黑液4-6份。