CN1044423A - High-carbon steel, the moistureproof drawing powder of steel alloy - Google Patents
High-carbon steel, the moistureproof drawing powder of steel alloy Download PDFInfo
- Publication number
- CN1044423A CN1044423A CN 90105405 CN90105405A CN1044423A CN 1044423 A CN1044423 A CN 1044423A CN 90105405 CN90105405 CN 90105405 CN 90105405 A CN90105405 A CN 90105405A CN 1044423 A CN1044423 A CN 1044423A
- Authority
- CN
- China
- Prior art keywords
- stearate
- moistureproof
- steel
- carbon steel
- drawing powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The moistureproof drawing powder of a kind of high-carbon steel, steel alloy at draw metal, particularly draws in the process of high-carbon steel, steel alloy and uses, and can reach: the one, and humidity resistance is good; The 2nd, it is good, lubricated good to bear high temperature, high pressure, tack in pulling process; The 3rd, draw high-carbon steel, the steel alloy wire quality is good; The 4th, can prolong service life of mould.
Description
The present invention is that a kind of humidity resistance is good, is applicable to the powdery lubricant product that drawing high-carbon steel or steel alloy wire rod are used.
At present, homemade dry type drawing powder.Ubiquity adhesion property and humidity resistance are relatively poor, thereby when using in the bigger area of rainy season or southern humidity, often because of the moisture absorption makes water content excessive, cause insufficient lubrication, influence the wire drawing effect.For this reason, will carry out drying every day putting baking oven into surplus drawing powder, to guarantee the time spent reasonable effect arranged again.
The objective of the invention is to avoid the deficiency in the above-mentioned existing product, and a kind of high-carbon steel, the moistureproof drawing powder lubricant of steel alloy product are provided.
Purpose of the present invention can reach by following measure: this high-carbon steel, the moistureproof drawing powder of steel alloy are made up of odium stearate, calcium stearate, barium stearate, molybdenum bisuphide, sulphur, additive, calcium hydroxide.Its composition scope (percentage by weight) is that odium stearate 0～8%, calcium stearate 38～14%, barium stearate 8～32%, molybdenum bisuphide 0.5～3%, sulphur 3～0.5%, additive 11～19%, calcium hydroxide are supplemented to 100%, and summation of each group is 100%.Its manufacture method is the employing drying, pulverizes, sieves, and allocates sulphur then into and mixes.
The present invention has following advantage: the one, use this moistureproof drawing powder, and humidity resistance is good; The 2nd, it is good, lubricated good to bear high temperature, high pressure, tack in drawing process; The 3rd, draw high-carbon steel, the steel alloy wire quality is good; The 4th, can prolong service life of mould.
The present invention is described in further detail in conjunction with the following example:
1. consider according to the factors such as work temperature rise of the hydrophilic, hydrophobic of material and silk mould, selected odium stearate 4%, calcium stearate 14%, barium stearate 34.5%, additive 15%, molybdenum bisuphide 1%, sulphur 2.5%, calcium hydroxide are supplemented to 100%, and each organizes summation (weight) is 100%.
2. odium stearate, calcium stearate, barium stearate, molybdenum bisuphide, calcium hydroxide, additive are fully mixed according to selected percentage by weight and an amount of water.
3. compound is carried out drying at 110 ℃～130 ℃, dried compound is pulverized, sieve.
4. the mixture after will sieving is allocated sulphur into and is mixed, and promptly becomes product.
Product granularity is:＜1.5mm.
Product water content :≤2%.
Claims (2)
1, a kind of draw metal wire rod that is used for, the moistureproof drawing powder used of drawing high-carbon steel or steel alloy wire rod particularly, it is characterized in that this drawing powder is made up of odium stearate, calcium stearate, barium stearate, molybdenum bisuphide, sulphur, additive, calcium hydroxide, the percentage of its each composition weight is:
Odium stearate 0～8%
Calcium stearate 38～14%
Barium stearate 8～32%
Molybdenum bisuphide 0.5～3%
Sulphur 3～0.5%
Additive 11～19%
Calcium hydroxide is supplemented to 100%
The summation of each component is 100%
2, the manufacture method of a kind of high-carbon steel, the moistureproof wire drawing powder of steel alloy:
1. odium stearate, calcium stearate, barium stearate, molybdenum bisuphide, calcium hydroxide, additive are fully mixed according to selected percentage by weight and an amount of water.
2. compound is carried out drying at 110 ℃～130 ℃, dried compound is pulverized, sieved.
3. the mixture after will sieving is allocated sulphur into and is mixed, and promptly becomes product.
Product granularity:＜1.5mm.
Product water content :≤2%.