CN104420781A - Radiation protection solid wood door sheet and production method thereof - Google Patents
Radiation protection solid wood door sheet and production method thereof Download PDFInfo
- Publication number
- CN104420781A CN104420781A CN201310382007.XA CN201310382007A CN104420781A CN 104420781 A CN104420781 A CN 104420781A CN 201310382007 A CN201310382007 A CN 201310382007A CN 104420781 A CN104420781 A CN 104420781A
- Authority
- CN
- China
- Prior art keywords
- solid wood
- wood door
- described step
- solidstate
- energy during
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a radiation protection solid wood door sheet and a production method thereof. The radiation protection solid wood door sheet comprises a solid wood door sheet body, wherein a metal braid layer is arranged on the surface of the solid wood door sheet body; a UV curing paint layer is arranged at the periphery of the metal braid layer, and consists of a UV putty layer, a UV elastic primer and a UV elastic finishing coat layer from inside to outside in sequence; and a PORELLE microporous film layer is arranged on the outer surface of the UV curing paint layer. The metal braid layer capable of preventing electromagnetic radiation is arranged on the surface of the solid wood door sheet body, so that the harm to human health from electromagnetic waves is reduced; and the UV curing paint layer and the PORELLE microporous film layer are arranged on the surface (the periphery of the metal braid layer) of the solid door wood sheet body in sequence through a specific process, so that the waterproof effect is good, and the defects of deformation, warping and rupture generation and shorter service life due to dry shrinkage and wet expansion of a traditional solid wood door sheet generated along with the change of temperature and humidity of ambient environment are overcome.
Description
Technical field
The present invention relates to a kind of radiation proof solid wood door plate and manufacture method thereof, belong to timber field.
Background technology
Timber is the important end product of wood working industry.The high speed development of China's realty industry and the quickening of urbanization paces; for timber industry provides great development space; adapt with batch demand; China's timber changes the image of " carpenter visits " home built tradition and the single practicality of product; proceed to rapidly the brand-new stage that " scale customized design ", large-scale industrial production and product are developed to decoration, Environmental-protection comprehensive by practicality, make China become timber production base maximum in the world and consumption market between several years.
There is following defect in existing solid wood door plate: (1) waterproof effect is poor, and easily with the humidity of surrounding environment, the change of temperature and produce drying shrinkage and bulking, thus cause distortion, warpage and cracking, application life is shorter; (2) there is no radiation proof function, the injury that the health of human body of electromagnetic wave to people causes can not be reduced.
Summary of the invention
The object of the invention is to, a kind of radiation proof solid wood door plate is provided.The waterproof effect that the present invention not only overcomes existing for existing solid wood door plate is poor, easily with the humidity of surrounding environment, the change of temperature and produce drying shrinkage and bulking, thus cause distortion, warpage and cracking, the defect that application life is shorter, but also the defect without radiation proof function overcome existing for existing solid wood door plate, decrease the injury that the health of human body of electromagnetic wave to people causes.
Technical scheme of the present invention: a kind of radiation proof solid wood door plate, comprises solid wood door plate body, and the surface of solid wood door plate body is provided with wire sheathing, the outer UV that is arranged with of wire sheathing solidifies enamelled coating; The formation that described UV solidifies enamelled coating is by inner and be followed successively by UV putty layer, UV elastic primer and UV elastic surface enamelled coating outward; The external surface that described UV solidifies enamelled coating is provided with the micro-porous film layer of PORELLE.
In aforesaid radiation proof solid wood door plate, described wire sheathing is steel fibre braid.
Manufacture the method for aforesaid radiation proof solid wood door plate, comprise the following steps:
1. sanding is carried out to solid wood door plate body;
2. roller coat UV water-based adhesive agent, dries;
3. wire sheathing is set;
4. roller coat UV putty, semi-solid preparation;
5. roller coat UV elastic primer, all solidstate;
6. roller coat UV elasticity finish paint, all solidstate;
7. the micro-porous membrane of PORELLE is pasted; Obtain product.
Aforesaid method is optimized,
Described step 2. in, bake out temperature is 90 ~ 110 DEG C, and drying time is 50 ~ 70s;
Described step 4. in, the coating weight of UV putty is 25 ~ 35g/m
2, UV energy during semi-solid preparation is 90 ~ 110mj/cm
2;
Described step 5. in, the coating weight of UV elastic primer is 20 ~ 30g/m
2, UV energy during all solidstate is 300 ~ 400mj/cm
2;
Described step 6. in, the coating weight of UV elasticity finish paint is 15 ~ 20g/m
2, UV energy during all solidstate is 400 ~ 500mj/cm
2.
Aforesaid method is optimized further,
Described step 2. in, bake out temperature is 95 ~ 105 DEG C, and drying time is 55 ~ 65s;
Described step 4. in, the coating weight of UV putty is 28 ~ 32g/m
2, UV energy during semi-solid preparation is 95 ~ 105mj/cm
2;
Described step 5. in, the coating weight of UV elastic primer is 22 ~ 28g/m
2, UV energy during all solidstate is 325 ~ 375mj/cm
2;
Described step 6. in, the coating weight of UV elasticity finish paint is 16 ~ 18g/m
2, UV energy during all solidstate is 425 ~ 475mj/cm
2.
Aforesaid method is further optimized,
Described step 2. in, bake out temperature is 100 DEG C, and drying time is 60s;
Described step 4. in, the coating weight of UV putty is 30g/m
2, UV energy during semi-solid preparation is 100mj/cm
2;
Described step 5. in, the coating weight of UV elastic primer is 25g/m
2, UV energy during all solidstate is 350mj/cm
2;
Described step 6. in, the coating weight of UV elasticity finish paint is 17g/m
2, UV energy during all solidstate is 450mj/cm
2.
Compared with prior art, the present invention can the wire sheathing of anti-electromagnetic radiation by arranging on the surface of solid wood door plate body, decreases the injury that the health of human body of electromagnetic wave to people causes; The present invention is by utilizing specific technique, set gradually UV on the surface (periphery of wire sheathing) of solid wood door plate body and solidify enamelled coating and the micro-porous film layer of PORELLE, good water-proof effect, overcome existing solid wood door plate and can produce drying shrinkage and bulking with the change of the temperature of surrounding environment, humidity, thus cause distortion, warpage and cracking, the defect that application life is shorter.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention.
Being labeled as in accompanying drawing: 1-solid wood door plate body, 2-wire sheathing, 3-UV putty layer, 4-UV elastic primer, 5-UV elastic surface enamelled coating, the micro-porous film layer of 6-PORELLE.
Detailed description of the invention
Below in conjunction with drawings and Examples, the present invention is further illustrated, but not as the foundation limited the present invention.
Embodiment 1.A kind of radiation proof solid wood door plate, form as shown in Figure 1, comprise solid wood door plate body 1, the surface of solid wood door plate body 1 is provided with wire sheathing 2, and the outer UV that is arranged with of wire sheathing 2 solidifies enamelled coating; The formation that described UV solidifies enamelled coating is by inner and be followed successively by UV putty layer 3, UV elastic primer 4 and UV elastic surface enamelled coating 5 outward; The external surface that described UV solidifies enamelled coating is provided with the micro-porous film layer 6 of PORELLE.Described wire sheathing 2 is steel fibre braid.
Manufacture the method for aforesaid radiation proof solid wood door plate, comprise the following steps:
1. sanding is carried out to solid wood door plate body; Three abrasive-belt sand-light machines can be adopted to carry out sanding to solid wood base material, and abrasive band model can be 120#, 150# and 180#;
2. roller coat UV water-based adhesive agent, dries; Bake out temperature is 100 DEG C, and drying time is 60s; UV water-based adhesive agent can be Jiangsu Himonia Technology Co., Ltd. produce model be 108010511 UV water-based adhesive agent; Drying plant can be infrared leveling machine;
3. wire sheathing is set;
4. roller coat UV putty, semi-solid preparation; The coating weight of UV putty is 30g/m
2, UV energy during semi-solid preparation is 100mj/cm
2; UV putty can be Jiangsu Himonia Technology Co., Ltd. produce model be 208060511 UV putty;
5. roller coat UV elastic primer, all solidstate; The coating weight of UV elastic primer is 25g/m
2, UV energy during all solidstate is 350mj/cm
2.UV elastic primer can be Jiangsu Himonia Technology Co., Ltd. produce model be 128200511 rich jade for asking rain priming paint;
6. roller coat UV elasticity finish paint, all solidstate; The coating weight of UV elasticity finish paint is 17g/m
2, UV energy during all solidstate is 450mj/cm
2; UV elasticity finish paint can be Jiangsu Himonia Technology Co., Ltd. produce model be 288040511 the high-elastic finish paint of UV;
7. the micro-porous membrane of PORELLE is pasted; Obtain product.
Embodiment 2.A kind of radiation proof solid wood door plate, form as shown in Figure 1, comprise solid wood door plate body 1, the surface of solid wood door plate body 1 is provided with wire sheathing 2, and the outer UV that is arranged with of wire sheathing 2 solidifies enamelled coating; The formation that described UV solidifies enamelled coating is by inner and be followed successively by UV putty layer 3, UV elastic primer 4 and UV elastic surface enamelled coating 5 outward; The external surface that described UV solidifies enamelled coating is provided with the micro-porous film layer 6 of PORELLE.Described wire sheathing 2 is steel fibre braid.
Manufacture the method for aforesaid radiation proof solid wood door plate, comprise the following steps:
1. sanding is carried out to solid wood door plate body; Three abrasive-belt sand-light machines can be adopted to carry out sanding to solid wood base material, and abrasive band model can be 120#, 150# and 180#;
2. roller coat UV water-based adhesive agent, dries; Bake out temperature is 90 DEG C, and drying time is 50s; UV water-based adhesive agent can be Jiangsu Himonia Technology Co., Ltd. produce model be 108010511 UV water-based adhesive agent; Drying plant can be infrared leveling machine;
3. wire sheathing is set;
4. roller coat UV putty, semi-solid preparation; The coating weight of UV putty is 25g/m
2, UV energy during semi-solid preparation is 90mj/cm
2; UV putty can be Jiangsu Himonia Technology Co., Ltd. produce model be 208060511 UV putty;
5. roller coat UV elastic primer, all solidstate; The coating weight of UV elastic primer is 20g/m
2, UV energy during all solidstate is 300mj/cm
2.UV elastic primer can be Jiangsu Himonia Technology Co., Ltd. produce model be 128200511 rich jade for asking rain priming paint;
6. roller coat UV elasticity finish paint, all solidstate; The coating weight of UV elasticity finish paint is 15g/m
2, UV energy during all solidstate is 400mj/cm
2; UV elasticity finish paint can be Jiangsu Himonia Technology Co., Ltd. produce model be 288040511 the high-elastic finish paint of UV;
7. the micro-porous membrane of PORELLE is pasted; Obtain product.
Embodiment 3.A kind of radiation proof solid wood door plate, form as shown in Figure 1, comprise solid wood door plate body 1, the surface of solid wood door plate body 1 is provided with wire sheathing 2, and the outer UV that is arranged with of wire sheathing 2 solidifies enamelled coating; The formation that described UV solidifies enamelled coating is by inner and be followed successively by UV putty layer 3, UV elastic primer 4 and UV elastic surface enamelled coating 5 outward; The external surface that described UV solidifies enamelled coating is provided with the micro-porous film layer 6 of PORELLE.Described wire sheathing 2 is steel fibre braid.
Manufacture the method for aforesaid radiation proof solid wood door plate, comprise the following steps:
1. sanding is carried out to solid wood door plate body; Three abrasive-belt sand-light machines can be adopted to carry out sanding to solid wood base material, and abrasive band model can be 120#, 150# and 180#;
2. roller coat UV water-based adhesive agent, dries; Bake out temperature is 110 DEG C, and drying time is 70s; UV water-based adhesive agent can be Jiangsu Himonia Technology Co., Ltd. produce model be 108010511 UV water-based adhesive agent; Drying plant can be infrared leveling machine;
3. wire sheathing is set;
4. roller coat UV putty, semi-solid preparation; The coating weight of UV putty is 35g/m
2, UV energy during semi-solid preparation is 110mj/cm
2; UV putty can be Jiangsu Himonia Technology Co., Ltd. produce model be 208060511 UV putty;
5. roller coat UV elastic primer, all solidstate; The coating weight of UV elastic primer is 30g/m
2, UV energy during all solidstate is 400mj/cm
2.UV elastic primer can be Jiangsu Himonia Technology Co., Ltd. produce model be 128200511 rich jade for asking rain priming paint;
6. roller coat UV elasticity finish paint, all solidstate; The coating weight of UV elasticity finish paint is 20g/m
2, UV energy during all solidstate is 500mj/cm
2; UV elasticity finish paint can be Jiangsu Himonia Technology Co., Ltd. produce model be 288040511 the high-elastic finish paint of UV;
7. the micro-porous membrane of PORELLE is pasted; Obtain product.
The generality of the above-mentioned invention to relating in the application describes and the description of its detailed description of the invention be should not be understood as to the restriction formed this invention technical scheme.Those skilled in the art's disclosing according to the application, can under the prerequisite without prejudice to involved invention inscape, above-mentioned generality is described or/and the public technology feature in detailed description of the invention (comprising embodiment) increases, reduces or combines, forms other the technical scheme belonging to described invention.
Claims (6)
1. a radiation proof solid wood door plate, is characterized in that: comprise solid wood door plate body (1), and the surface of solid wood door plate body (1) is provided with wire sheathing (2), and the outer UV that is arranged with of wire sheathing (2) solidifies enamelled coating; The formation that described UV solidifies enamelled coating is by inner and be followed successively by UV putty layer (3), UV elastic primer (4) and UV elastic surface enamelled coating (5) outward; The external surface that described UV solidifies enamelled coating is provided with the micro-porous film layer of PORELLE (6).
2. radiation proof solid wood door plate according to claim 1, is characterized in that: described wire sheathing (2) is steel fibre braid.
3. the method for the radiation proof solid wood door plate described in manufacturing claims 1 or 2, is characterized in that, comprise the following steps:
1. sanding is carried out to solid wood door plate body;
2. roller coat UV water-based adhesive agent, dries;
3. wire sheathing is set;
4. roller coat UV putty, semi-solid preparation;
5. roller coat UV elastic primer, all solidstate;
6. roller coat UV elasticity finish paint, all solidstate;
7. the micro-porous membrane of PORELLE is pasted; Obtain product.
4. method according to claim 3, is characterized in that:
Described step 2. in, bake out temperature is 90 ~ 110 DEG C, and drying time is 50 ~ 70s;
Described step 4. in, the coating weight of UV putty is 25 ~ 35g/m
2, UV energy during semi-solid preparation is 90 ~ 110mj/cm
2;
Described step 5. in, the coating weight of UV elastic primer is 20 ~ 30g/m
2, UV energy during all solidstate is 300 ~ 400mj/cm
2;
Described step 6. in, the coating weight of UV elasticity finish paint is 15 ~ 20g/m
2, UV energy during all solidstate is 400 ~ 500mj/cm
2.
5. method according to claim 4, is characterized in that:
Described step 2. in, bake out temperature is 95 ~ 105 DEG C, and drying time is 55 ~ 65s;
Described step 4. in, the coating weight of UV putty is 28 ~ 32g/m
2, UV energy during semi-solid preparation is 95 ~ 105mj/cm
2;
Described step 5. in, the coating weight of UV elastic primer is 22 ~ 28g/m
2, UV energy during all solidstate is 325 ~ 375mj/cm
2;
Described step 6. in, the coating weight of UV elasticity finish paint is 16 ~ 18g/m
2, UV energy during all solidstate is 425 ~ 475mj/cm
2.
6. method according to claim 5, is characterized in that:
Described step 2. in, bake out temperature is 100 DEG C, and drying time is 60s;
Described step 4. in, the coating weight of UV putty is 30g/m
2, UV energy during semi-solid preparation is 100mj/cm
2;
Described step 5. in, the coating weight of UV elastic primer is 25g/m
2, UV energy during all solidstate is 350mj/cm
2;
Described step 6. in, the coating weight of UV elasticity finish paint is 17g/m
2, UV energy during all solidstate is 450mj/cm
2.