CN1044181A - A kind of unsaturated polyester luminous plate and manufacture method - Google Patents

A kind of unsaturated polyester luminous plate and manufacture method Download PDF

Info

Publication number
CN1044181A
CN1044181A CN 90105027 CN90105027A CN1044181A CN 1044181 A CN1044181 A CN 1044181A CN 90105027 CN90105027 CN 90105027 CN 90105027 A CN90105027 A CN 90105027A CN 1044181 A CN1044181 A CN 1044181A
Authority
CN
China
Prior art keywords
luminous plate
layer
unsaturated polyester
minutes
ground floor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 90105027
Other languages
Chinese (zh)
Inventor
刘军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 90105027 priority Critical patent/CN1044181A/en
Publication of CN1044181A publication Critical patent/CN1044181A/en
Pending legal-status Critical Current

Abstract

A kind of unsaturated polyester luminous plate and manufacture method, principal feature is to produce under 12~30 ℃ of temperature, and technology is simple, and production cost is low, be applicable to and make traffic marker indication, ban indication, safety notice, dwelling house sign, direction board etc., can make various handicrafts again.

Description

A kind of unsaturated polyester luminous plate and manufacture method
The invention belongs to unsaturated polyester luminous plate research manufacturing technology field.Be applicable to that making noctilucence shows board, label, trail guide board and luminous artistic articles etc., and can be used as secondary light source.
Present luminous plate manufacture method is that to adopt tygon be raw material, the method that high temperature is synthetic, but its shortcoming is often once high temperature, has just quickened the ageing process of luminescent powder, has reduced the luminescent properties of luminescent powder, has reduced the serviceable life of luminous plate.
The purpose of this invention is to provide a kind of employing unsaturated polyester resin is raw material, and the method for making under 12~30 ℃ of temperature is to overcome the variety of issue that is produced by the high temperature process manufacturing.
Technological process of the present invention is: (1) batching; (2) stirring is synthetic; (3) furnishing material die casting; (4) molding integer; (5) cast glass sheet metal forming; (6) play mould product integer.Its manufacture method is; Earlier unsaturated polyester resin, hardening agent, luminescent powder, promoter were pressed 100: 4: 10 respectively: 2 weight ratio batching, it is earlier hardening agent to be dropped in the vibrin in proper order, requires to stir.Add luminescent powder again, stir, add promoter again, the same requirement stirs.After preparing material, be injected in the mould (can by produce different product designing mould).After waiting to have annotated, be cured, finalize the design with 30~60 minutes.Play the mould integer then.Promptly make the light tiles of different pattern.Temperature during manufacturing is between 12~30 ℃, treated the mould integer after, carry out the cast glass sheet metal forming, the process of moulding by casting is: prepare burden earlier and afterwards pour into a mould.Get unsaturated polyester resin 100 weight portions, hardening agent 4 weight portions, promoter 2 weight portions cooperate, and stir.Then in worktable upper berth one glass plate (glass plate specification press products made thereby size and decide), with the material for preparing about 2 millimeters thick on glass plate that pave, form the ground floor polyester resin layer, the light tiles with moulding is layered on the resin bed then, leaves standstill to solidify about 30~60 minutes.After waiting to solidify, be coated with one deck additive color polyester material again, the proportioning of this polyester material is unsaturated polyester resin 100 weight portions, hardening agent 4 weight portions, and promoter 2 weight portions, mill base can require an amount of the input according to the color of different product, mixes well.Leave standstill again after waiting to be coated with and solidified 30~60 minutes.The polyester material that the one deck that paves again after waiting to solidify still cooperates by ground floor vibrin stratum proportion, the layer overlay glass fabric leaves standstill and solidified 30~60 minutes simultaneously.After treating full solidification, play the mould integer, product.
The every technical indicator of the present invention
The menu bit data
Heatproof-40~80 ℃
Tensile strength kg/cm 22200kg
The anti-nature corrosion of chemical stability 10~20 years
Light-receiving time second 1~180
Fluorescent lifetime hours 4~6
Luminosity 8
Producing luminous plate at present is to adopt the tygon raw material, with the synthetic luminous plate of high temperature process, because of poly melt temperature is about 200 ℃, like this, the luminescent powder of adding has just quickened ageing process, reduced luminescent properties, with the present invention's be subjected to light equally 1 second~3 minutes time conditions under, fluorescent lifetime has only 1~2 hour, luminosity is at 1~3 degree.Have only 3~5 years the serviceable life of its product, and the processing technology complexity, and production cost is high, is not easy to promote.It is unsaturated polyester resin that the present invention uses the tygon main material instead, and be under 12~30 ℃ of conditions, to produce luminous plate, overcome employing tygon raw material, the problem that luminous plate produced that high-temperature synthesis is produced, every technical indicator is all above with tygon being the synthetic luminous plate of producing of main material, high temperature, technology is simple, and production cost is low, is easy to apply.
The present invention does not have figure.
Embodiment:
Get final product with reference to described process of instructions and formula for raw stock.

Claims (1)

  1. A kind of unsaturated polyester luminous plate and manufacture method, it is characterized in that constituting by five layers, ground floor is a vibrin, and the second layer is a luminous plate, and the 3rd layer for adding chromoresin, the 4th layer is vibrin, layer 5 is a glass fabric, its manufacturing process by batching, stir synthetic, furnishing material die casting, molding integer, cast glass sheet metal forming, molding product integer, totally six procedures constitute, the whole operation process is to carry out under 12~30 ℃ of temperature
    The job operation of the ground floor polyester resin layer of luminous plate is, with unsaturated polyester resin, hardening agent, promoter, throw in by 100: 4: 2 weight ratio successively, stir, pave on glass plate, leave standstill then and solidified 30~60 minutes, the job operation of second layer luminous plate is, with unsaturated polyester resin, hardening agent, luminescent powder, promoter, successively by 100: 4: 10: 2 weight ratio is thrown in, mix thoroughly, shape is made luminous plate on demand, leaves standstill to solidify 30~60 minutes, after the curing luminous plate is layered on the ground floor resin bed, the job operation of the 3rd layer additive color resin bed is, with unsaturated polyester resin, hardening agent, promoter is thrown in by 100: 4: 2 weight ratio successively, and is added suitable mill base, to add chromoresin then is coated on luminous plate and the resin bed, leave standstill and solidified 30~60 minutes, the 4th strata ester resin that paves then, its job operation is identical with ground floor, stick glass fabric simultaneously, leave standstill afterwards and solidified 30~60 minutes.
CN 90105027 1990-02-10 1990-02-10 A kind of unsaturated polyester luminous plate and manufacture method Pending CN1044181A (en)