CN104415367A - Medical ultrasonic diagnosis contrast agent hollow composite microsphere system - Google Patents

Medical ultrasonic diagnosis contrast agent hollow composite microsphere system Download PDF

Info

Publication number
CN104415367A
CN104415367A CN201310379329.9A CN201310379329A CN104415367A CN 104415367 A CN104415367 A CN 104415367A CN 201310379329 A CN201310379329 A CN 201310379329A CN 104415367 A CN104415367 A CN 104415367A
Authority
CN
China
Prior art keywords
microsphere
contrast agent
layer
hollow
silicon dioxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310379329.9A
Other languages
Chinese (zh)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Green Kht Science And Technology Ltd
Original Assignee
Chengdu Green Kht Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Green Kht Science And Technology Ltd filed Critical Chengdu Green Kht Science And Technology Ltd
Priority to CN201310379329.9A priority Critical patent/CN104415367A/en
Publication of CN104415367A publication Critical patent/CN104415367A/en
Pending legal-status Critical Current

Abstract

The invention discloses a medical ultrasonic diagnosis contrast agent hollow composite microsphere system. The microsphere has a hollow inorganic/organic/inorganic three-layer structure, wherein a cavity is formed in the center of the microsphere and is filled with air inside; Fe3O4 magnetic particles are formed on the outer layer of the cavity; an intermediate layer is formed by a core/shell polymer nano microsphere obtained through free radical copolymerization of a polybutylene-polymethylacrylic acid random copolymer, polymethylacrylic acid and divinyl benzene; coordinate bonds or ionic bonds can be formed between the copolymer and the Fe3O4 magnetic particles on the inner layer of the copolymer via carboxyl on the inner surface of the microsphere and iron salt, so that the microsphere is stable; an outer layer is formed by silicon dioxide and is connected with the intermediate layer through hydrogen-bond intersection between carboxyl on the surface of the microsphere and silicon hydroxyl on the surface of silicon dioxide. The material has the advantages that the polymer microsphere belongs to nanoparticles; the contrast agent can achieve targeted localization via the Fe3O4 magnetic particles on the inner layer; the silicon dioxide hollow microsphere has good biocompatibility and mechanical stability, and the inside cavity can generate strong echo signals in a contrast mode.

Description

A kind of medical ultrasound diagnostic contrast agent hollow complex microsphere system
Technical field
The present invention relates to a kind of medical detection contrast agent, particularly relate to a kind of Nano microsphere with the multilamellar organic/inorganic composite construction of magnetic function, belong to medicine technology field.
Background technology
In recent years, molecular image technology can provide important information and be paid close attention to widely (Campbell R.E., Chang C.J.Curr Opin Chem Biol, 2010,14 (1): 1-2.) for the medical diagnosis on disease of biological tissue and monitoring due to it.In numerous imaging pattern, ultra sonic imaging, as the AT biomedical imaging pattern of one, has important researching value because it has the advantages such as imaging and timely, cheap, the light and fast of diagnosis safety, utilization are extensive.But the difference of echo-signal usually can hinder the accuracy of diagnosis between different biological tissue; in order to obtain the accurate information of particular organization better; people adopt the method adding ultra sonic imaging contrast agent to realize (R.D í az-L ó PBz usually; Tsapisa N.; Libong D.; et al.Biomaterials, 2009,30 (8): 1462-1472.).
Usually contrast agent used is mainly microvesicle, and its shell is that the amphipathic small molecules such as saccharide, protein or polymer are formed, inner filling C 3f 8, SF 6vesicle (Ferrara K.W., Borden M.A., Zhang H.Acc Chem Res, 2009,42 (7): 881-892.) is formed Deng gas.These contrast agent can change or strengthen ultrasound echo signal and provide better surface or organizational information.But due to laplace pressure, blood pressure, oxidative metabolism and hyperacoustic effect, these gas microbubbles are just dissolved and are broken after injection blood a few second, and particle diameter is difficult to control (Schutt E.G., Klein D.H., Mattrey R.M., et al.Angew Chem Int Ed, 2003,42 (28): 3218-3235.).SiO 2 hollow microsphere has good biocompatibility and mechanical stability, and has larger cavity, can produce stronger echo-signal under imaging mode, can solve the problem.(the Lin P.L. such as Hall, Eckersley R.J., Elizabeth A.H.Adv Mater, 2009,21 (38-39): 3949-3952.) with PB ball for template, change surface charge by polyallyl acid hydrochloride (PAH) and prepared the tiny balloon that particle diameter is 2.8 μm, shell thickness is less than 30nm, and have studied its ultra sonic imaging effect under different mechanical index condition.Linear ultrasonic imaging (B-model) result shows, this hollow SiO 2bead has very strong ultrasonic signal under water environment.But these class methods still have certain limitation, as hollow SiO 2the size of bead is too large, does not reach nanoscale structures, is difficult to for living imaging, and does not carry out modified with functional group and be difficult to connect further.Therefore, the contrast agent of current clinical middle use can't be taken into account good biocompatibility, mechanical stability, Targeting Performance, nanostructured simultaneously, can be carried out the requirements such as modified with functional group.
Summary of the invention
The present invention is directed to above problem, there is provided herein a kind of medical ultrasound diagnostic contrast agent hollow complex microsphere system, it is a kind of multilamellar organic/inorganic composite construction magnetic Nano microsphere, have hollow type inorganic/organic/inorganic three-layer composite structure:
What be positioned at microsphere center is cavity, inner filling air;
Intermediate layer is macromolecule layer, is the copolymer of polymethylacrylic acid and divinylbenzene;
Be four oxidation three body magnetic nano-particles between cavity and intermediate layer, be deposited on macromolecule layer inner surface by coordinate bond or ionic bond;
Outer for there being mesoporous Nano particles of silicon dioxide, outside with macromolecule layer by hydrogen bond action absorption.
The technical solution adopted for the present invention to solve the technical problems is:
1) preparation of core/shell polymer microsphere double-layer nanometer microsphere
This microsphere is prepared based on a kind of core/shell polymer microsphere double-layer nanometer microsphere.First utilize butylene and methacrylic acid to carry out copolymerization and obtain dispersed nano microsphere, it is structure shown in following chemical formula:
Wherein x is the integer of 5 ~ 50;
Y is the integer of 0 ~ 15;
2) the outer cross-linked structure of double-layer nanometer microsphere is prepared
Then by above-mentioned dispersed nano microsphere and polymethylacrylic acid, divinylbenzene, by Solution Free Radical copolymerization process, obtain microsphere layer structure, it is structure shown in following chemical formula:
Wherein n is the integer of 0 ~ 50
3) core/shell polymer microsphere double-layer nanometer microsphere is prepared by " from dispersion " polyreaction
Utilize the carboxyl on the surface of double-layer nanometer microsphere can produce hydrogen bond action with the silicone hydroxyl of silica surface, make silicon dioxide in aggregate surface hydrolysis and polycondensation formation shell structurre.Its interaction chemical formula is as follows:
4) preparation of hollow polymeric-silicon dioxide nanosphere
Utilize acetone to extract kernel and form hollow polymeric-silicon dioxide nanosphere structure.In reaction system, add chloroform dissolve, stirred for several hour, after utilizing chloroform to dissolve PB core, obtain SiO 2tiny balloon, its form keeps stable and structural integrity, has a good spherical structure.Preparation process schematic diagram as shown in Figure 4;
5) preparation of magnetic macromolecular microsphere
Finally, utilize microsphere inner surface carboxyl and the iron salt being entered internal layer by silicon dioxide micropore permeation, form coordinate bond or ionic bond, by adsorbing the Fe of hollow ball inside 2+and Fe 3+deng reactant, make internal layer in conjunction with Fe 3 O 4 magnetic particle.Its reaction principle is as follows:
Fe 2++2Fe 3++8OH -→Fe 3O 4+4H 2O
By above technical scheme, tool of the present invention has the following advantages: 1) this medical ultrasound diagnostic contrast agent hollow composite microspheres cording has good biocompatibility;
2) this medical ultrasound diagnostic contrast agent hollow composite microspheres cording has volume little, has nanoscale structures, can by various human body barriers;
3) this medical ultrasound diagnostic contrast agent hollow complex microsphere system system is due to the Fe3O4 containing superparamagnetism, therefore has Targeting Performance;
4) this medical ultrasound diagnostic contrast agent hollow complex microsphere system architecture is stable, mechanical stability is high.
This type of medical ultrasound diagnostic contrast agent hollow complex microsphere system can overcome the problems such as traditional contrast agent poor stability, echo signal are weak, poor biocompatibility.
Accompanying drawing explanation
Fig. 1 is the structural representation of this medical ultrasound diagnostic contrast agent hollow complex microsphere;
Fig. 2 is the particle diameter test pattern of this medical ultrasound diagnostic contrast agent hollow complex microsphere;
Fig. 3 is the AFM scintigram of this medical ultrasound diagnostic contrast agent hollow complex microsphere;
Fig. 4 is the preparation flow schematic diagram of hollow polymeric microspheres.
Detailed description of the invention
For making enforcement object of the present invention, technical scheme and advantage more clear, below in conjunction with the drawings and specific embodiments of the present invention, the present invention is described in detail:
As shown in Figure 1, be the structural representation of this medical ultrasound diagnostic contrast agent hollow complex microsphere.This Nano microsphere has hollow type machine/organic/inorganic three-layer composite structure, has successively: outermost layer be Nano particles of silicon dioxide 1.; Intermediate layer be macromolecule layer 2.; Internal layer be four oxidation three body magnetic nano-particles 3.; Be positioned at microsphere center be cavity 4., inner fill air.Wherein Nano particles of silicon dioxide layer 1. in should have meso-hole structure.
Polymethylacrylic acid-divinylbenzene crosslinking copolymerization macromolecule as macromolecule layer 2., outside adsorbs silica particle 1. simultaneously, and internal layer in conjunction with four oxidation three body magnetic nano-particles 3. as a preferably embodiment: utilize butylene and polymethylacrylic acid to carry out copolymerization and obtain internal layer microsphere, then internal layer is carried out copolymerization by polymethylacrylic acid and divinylbenzene, obtain double-deck solid nano polymer microspheres.Utilize the carboxyl on the surface of double-layer nanometer microsphere can produce hydrogen bond action with the silicone hydroxyl of silica surface, make silicon dioxide be hydrolyzed also polycondensation in aggregate surface and form shell structurre 1..Meanwhile, utilize the meso-hole structure of Nano particles of silicon dioxide, with an organic solvent method (acetone) extracts kernel and forms hollow polymeric-silicon dioxide double-layer nanometer micro-sphere structure.Finally, utilize microsphere inner surface carboxyl and iron salt can form coordinate bond or ionic bond, entered the Fe of hollow ball inside by adsorption and permeation 2+and Fe 3+deng reactant, make internal layer in conjunction with Fe 3 O 4 magnetic particle 3..
Figure 2 shows that the particle diameter test pattern utilizing dynamic light scattering method to magnetic Nano microsphere, can find out, Nano microsphere particle diameter is less than 1 micron, and particle size distribution is narrower, proves that this Nano microsphere volume is little, good dispersion.
Figure 3 shows that the AFM scanogram of this medical ultrasound diagnostic contrast agent hollow complex microsphere.Prove that macromolecule forms globular micelle structure homogeneous, good dispersion, does not reunite in aqueous.Be conducive to the targeting of contrast agent in body fluid to locate and dispersion.
Provide embodiment below to be specifically described the present invention; but it is worthy of note that following examples are only used to further illustrate the present invention; can not be interpreted as limiting the scope of the invention, some nonessential improvement that the person skilled in the art in this field makes the present invention according to the invention described above content and adjustment still belong to protection scope of the present invention.
Embodiment 1:
The preparation of 1. core/shell polymeric Nano microsphere
Step one: the method first adopting " from dispersion " to be polymerized prepares single dispersing (PB-PMAA) copolymer microsphere.Butylene and each 0.2mol, AIBN(azo-bis-isobutyl cyanide of methacrylic acid is added in 500mL tri-mouthfuls of round bottom reaction bulbs) 0.98g, butyl acetate 280mL; under nitrogen protection; constant temperature 70 DEG C reaction 12 hours; product is dried in 55 DEG C of baking ovens, obtains single dispersing (PB-PMAA) copolymer microsphere.
Step 2: prepare core/shell polymer microsphere by seed " from dispersion " polyreaction.By (PB-PMAA) copolymer microsphere 3.65g, methacrylic acid and each 0.038mol of divinylbenzene, AIBN0.09g, butyl acetate 100mL, normal hexane 35mL; add in reaction bulb; under nitrogen protection, constant temperature 75 DEG C reaction 13 hours, obtains two-layer core/shell polymeric Nano microsphere.
2. silicon dioxide carries out gathering at microsphere surface and forms shell structurre
With the two-layer core prepared in above-mentioned steps/shell polymeric Nano microsphere for template, generate the homogeneous and SiO of regular appearance of thickness by sol-gel process at PMAA surface in situ 2shell.Adopt method ( w., Fink A., Bohn E.J Colloid Interface Sci, 1968,26 (1): 62-69.), adding 55mL ammonia is catalyst, utilizes ethyl orthosilicate (TEOS) 16.5g, after poly-condensation and hydrolysis, synthesizes SiO 2.
With PMAA surface PB core as templated deposition SiO 2time, generally can generate the independent SiO of about 35nm 2particle.Because PB checks SiO 2adsorptivity weak, if direct PB precipitates SiO as masterplate 2, be difficult to obtain uniform SiO 2shell structurre.And when after the surface and copolymerized PMAA of PB core, because of the carboxyl on PMAA chain or carboxylate radical can with the hydrolyzate of ethyl orthosilicate and SiO 2the hydroxyl of particle surface forms hydrogen bond, thus induction SiO 2nucleating growth, finally forms regular shell structurre.
3. hollow type polymer-SiO 2the preparation of Nano microsphere
Get the SiO prepared in 2.7g above-mentioned steps 2core/shell polymeric Nano microsphere, adds 15mL chloroform and dissolves, stir 7 hours in reaction system, obtains SiO after utilizing chloroform to dissolve PB core 2tiny balloon, its form keeps stable and structural integrity, has a good spherical structure.
4. the preparation of hollow type magnetic Nano microsphere contrast agent
Hollow polymer microsphere 1.2g, the FeCl of gained in above-mentioned reactions steps is added in 250mL tri-mouthfuls of round bottom reaction bulbs 36H 2o5.8g, FeCl 24H 2o3.3g, deionized water 180mL, under nitrogen protection, stir 1h, ultrasonic 2.5h, sucking filtration, deionized water rinsing 3 ~ 5 times.Then by filter microsphere adds in deoxygenation deionized water, in 85 DEG C, drip NH under high-speed stirred 3h 2o adjust ph is 11 ~ 12, under nitrogen protection, and isothermal reaction 2h.Above-mentioned microsphere is added in bag filter, with the dialysis of 1000mL pure water, refreshes the water periodically.After dialysis solution membrane filtration, lyophilization obtains hollow type magnetic Nano microsphere contrast agent.
Finally it should be noted that, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted, although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art should understand, can a point technical scheme for invention be modified or be replaced on an equal basis, and not departing from the spirit and scope of technical solution of the present invention, it all should be encompassed in the middle of right of the present invention.

Claims (5)

1. a medical ultrasound diagnostic contrast agent hollow complex microsphere system, it is characterized in that having hollow type inorganic/organic/inorganic three-layer composite structure:
1) what be positioned at microsphere center is cavity, inner filling air;
2) intermediate layer is macromolecule layer, is the copolymer of polymethylacrylic acid and divinylbenzene;
3) between cavity and intermediate layer be ferroferric oxide magnetic nano-particles;
4) skin is Nano particles of silicon dioxide.
2. a kind of medical ultrasound diagnostic contrast agent hollow complex microsphere system according to claim 1, this material is prepared as follows:
1) polybutene-methacrylic acid random copolymerization single dispersing core/shell polymeric Nano microsphere is prepared;
2) silicon dioxide is assembled at microsphere surface;
3) hollow type polymer-SiO is prepared 2nano microsphere;
4) preparation of hollow type magnetic Nano microsphere contrast agent.
3. a kind of medical ultrasound diagnostic contrast agent hollow complex microsphere system according to claim 1 and 2, be further characterized in that above-mentioned steps 1) in core/shell polymeric Nano microsphere of being formed be double-decker, and be all adopt polymethylacrylic acid as hydrophilic segment, it is characterized in that:
1) its internal layer is polybutene-methacrylic acid random copolymer;
2) its skin is polymethylacrylic acid and divinyl benzene crosslinked polymer.
4. a kind of medical ultrasound diagnostic contrast agent hollow complex microsphere system according to claim 1 and 2, is further characterized in that: have meso-hole structure in outermost Nano particles of silicon dioxide.
5. a kind of medical ultrasound diagnostic contrast agent hollow complex microsphere system according to claim 1 and 2, be further characterized in that: macromolecule layer is the copolymer of polymethylacrylic acid and divinylbenzene, macromolecule has double-deck polymethylacrylic acid structure, utilizes divinylbenzene bridging between molecule.
CN201310379329.9A 2013-08-27 2013-08-27 Medical ultrasonic diagnosis contrast agent hollow composite microsphere system Pending CN104415367A (en)