CN104387998A - High-strength acrylate adhesive - Google Patents
High-strength acrylate adhesive Download PDFInfo
- Publication number
- CN104387998A CN104387998A CN201410598291.9A CN201410598291A CN104387998A CN 104387998 A CN104387998 A CN 104387998A CN 201410598291 A CN201410598291 A CN 201410598291A CN 104387998 A CN104387998 A CN 104387998A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylate adhesive
- strength
- adhesive
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength acrylate adhesive. The high-strength acrylate adhesive is prepared from the following raw materials in parts by weight: 6-10 parts of styrene, 15-24 parts of acrylic ester, 3-9 parts of furan resin, 4-7 parts of flame-retardant polyether polyol, 5-7 parts of phosphoric acid, 4-8 parts of magnesium hydrate, 9-15 parts of an acrylic emulsion, 2-4 parts of an adhesive, 5-11 parts of EVA, 6-8 parts of oxidized polypropylene ester, 3-6 parts of methylsilicone oil, 1-5 parts of a catalyst, 8-11 parts of 2,6-di-tert-butyl-4-methyl phenol, 1-6 parts of vanadium acetylacetonate, 4-9 parts of tert-butyl hydroperoxide and 8-16 parts of epoxy modified acrylate resin. The high-strength acrylate adhesive has the beneficial effects of high strength and hardness, high shear resistance and long service life.
Description
Technical field
The present invention relates to a kind of acrylate adhesive of high strength.
Background technology
Along with the high stratification of building, automotive light weight technology, electrical equipment high zinc foods, furniture are superior, the development of industrial large-sizedization, sizing agent has obtained and has applied increasingly widely in modern industry field and daily life.Acrylate adhesive has following characteristics: 1, high strength, shock-resistant 2, weathering resistance good 3, can Sealant 4, easy to use, shock resistance and shearing force strong.But the acrylate adhesive on existing market can not meet service requirements, intensity, corrosion resistance nature all do not reach service requirements.Therefore, need a kind of better acrylate adhesive to meet and use needs.
Summary of the invention
For the deficiencies in the prior art, the technical problem to be solved in the present invention is, provides a kind of acrylate adhesive of high strength, has good intensity and hardness, and cohesiveness glue, has good anti-shearing force, long service life simultaneously.
For solving the deficiencies in the prior art, the technical scheme that the present invention takes is: a kind of acrylate adhesive of high strength, is made up of the raw material of following parts by weight:
Vinylbenzene 6-10 part, acrylate 15-24 part, furane resin 3-9 part, flame retardant polyether polyol 4-7 part, phosphoric acid 5-7 part, magnesium hydroxide 4-8 part, ACRYLIC EMULSION 9-15 part, tackiness agent 2-4 part, EVA5-11 part, its chlorinated polypropylene ester 6-8 part, methyl-silicone oil 3-6 part, catalyzer 1-5 part, 2,6 di tert butyl 4 methyl phenol 8-11 part, vanadium acetylacetonate 1-6 part, tertbutyl peroxide 4-9 part, epoxy modified acrylic resin 8-16 part.
The invention has the beneficial effects as follows that the acrylate adhesive of high strength of the present invention has good intensity and hardness, cohesiveness glue, has good anti-shearing force, long service life simultaneously.
Embodiment
embodiment 1
An acrylate adhesive for high strength, be made up of the raw material of following parts by weight:
Vinylbenzene 6 parts, acrylate 15 parts, furane resin 3 parts, flame retardant polyether polyol 4 parts, phosphoric acid 5 parts, magnesium hydroxide 4 parts, ACRYLIC EMULSION 9 parts, 2 parts, tackiness agent, EVA5 part, its chlorinated polypropylene ester 6 parts, methyl-silicone oil 3 parts, catalyzer 1 part, 2,6 di tert butyl 4 methyl phenol 8 parts, vanadium acetylacetonate 1 part, tertbutyl peroxide 4 parts, epoxy modified acrylic resin 8 parts.
embodiment 2
An acrylate adhesive for high strength, be made up of the raw material of following parts by weight:
Vinylbenzene 10 parts, acrylate 24 parts, furane resin 9 parts, flame retardant polyether polyol 7 parts, phosphoric acid 7 parts, magnesium hydroxide 8 parts, ACRYLIC EMULSION 15 parts, 4 parts, tackiness agent, EVA11 part, its chlorinated polypropylene ester 8 parts, methyl-silicone oil 6 parts, catalyzer 5 parts, 2,6 di tert butyl 4 methyl phenol 11 parts, vanadium acetylacetonate 6 parts, tertbutyl peroxide 9 parts, epoxy modified acrylic resin 16 parts.
Claims (1)
1. an acrylate adhesive for high strength, is characterized in that: be made up of the raw material of following parts by weight:
Vinylbenzene 6-10 part, acrylate 15-24 part, furane resin 3-9 part, flame retardant polyether polyol 4-7 part, phosphoric acid 5-7 part, magnesium hydroxide 4-8 part, ACRYLIC EMULSION 9-15 part, tackiness agent 2-4 part, EVA5-11 part, its chlorinated polypropylene ester 6-8 part, methyl-silicone oil 3-6 part, catalyzer 1-5 part, 2,6 di tert butyl 4 methyl phenol 8-11 part, vanadium acetylacetonate 1-6 part, tertbutyl peroxide 4-9 part, epoxy modified acrylic resin 8-16 part.